High strength high toughness TiB2 ceramics
Assignee: JFE Engineering Corp
•
Filing: 1989-06-22
•
Granted: 1990-06-12
•
Expires: 2009-06-22
Abstract
Abstract A ceramic sintered body comprising TiB 2 as the principal component, 0.5 to 30 wt. % of SiC and 2 to 40 wt. % of ZrO 2 . In some cases ZrO 2 includes stabilizers for tetragonal crystal, such as Y 2 O 3 , MgO or CeO 2 . The sintered body has a dense structure where TiB 2 , ZrO 2 and SiC uniformly disperse. ZrO 2 is located at the grain boundary of TiB 2 , and inhibits the grain growth of TiB 2 as well as improves the strength of the sintered body by binding it to TiB 2 strongly. SiC is located not only at the grain boundary but also on the inside of both grains. Since the contract of SiC during cooling process of the sintered body is less than TiB 2 and ZrO 2 , compressive stress is produced in SiC and around thereof. The sintered body is remarkably strengthened by the residual compressive stress, and simultaneously, the high fracture toughness is also achieved.
Inventors
- 👤 Hiroaki Nishio
- 👤 Shiro Torizuka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:11
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/622; C04B35/64; C04B35/645
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
49 words
A ceramic sintered body consisting essentially of 50 to 95.5 wt. % TiB 2 , 0.5 to 30 wt. % of SiC and 2 to 40 wt. % of ZrO 2 , the ceramic sintered body having a three-point flexural strength of not less than 110 kgf/mm 2 .
Claim 2
Dependent Claim
49 words
A ceramic sintered body consisting essentially of 50 to 95.5 wt. % TiB 2 , 0.5 to 30 wt. % of SiC and 2 to 40 wt. % of ZrO 2 , the ceramic sintered body having a three-point flexural strength of not less than 110 kgf/mm 2 .
Claim 3
Dependent Claim
31 words
The ceramic sintered body of claim 1 of which the content of SiC is 1 to 10 wt. % and the content of ZrO 2 is 5 to 30 wt. %.
Claim 4
Dependent Claim
66 words
A ceramic sintered body consisting essentially of TiB 2 as the principal component, 0.5 to 30 wt. % of SiC and 2 to 40 wt. % of ZrO 2 , and at least one of, 1 to 8% of Y 2 O 3 , 1 to 4% of MgO and 10 to 21% of CeO 2 , as per cent by weight to ZrO 2 .
Claim 5
Dependent Claim
66 words
A ceramic sintered body consisting essentially of TiB 2 as the principal component, 0.5 to 30 wt. % of SiC and 2 to 40 wt. % of ZrO 2 , and at least one of, 1 to 8% of Y 2 O 3 , 1 to 4% of MgO and 10 to 21% of CeO 2 , as per cent by weight to ZrO 2 .
Claim 6
Dependent Claim
56 words
A ceramic sintered body consisting of essentially of TiB 2 as the principal component, with an SiC content of 1 to 10 wt. % and ZrO 2 content of 5 to 30 wt. %, wherein the ZrO 2 contains 3 to 7% of Y 2 O 3 as per cent by weight to ZrO 2 .
Claim 7
Dependent Claim
56 words
A ceramic sintered body consisting of essentially of TiB 2 as the principal component, with an SiC content of 1 to 10 wt. % and ZrO 2 content of 5 to 30 wt. %, wherein the ZrO 2 contains 3 to 7% of Y 2 O 3 as per cent by weight to ZrO 2 .
Claim 8
Dependent Claim
66 words
A ceramic sintered body consisting essentially of TiB 2 as the principal component, 0.5 to 30 wt. % of SiC and 2 to 40 wt. % of ZrO 2 , which further contains 0.5 to 20 wt. % of one of more compounds selected from the group consisting of metal carbides other than SiC, metal nitrides, metal carbonitrides and metal borides other than TiB 2 .
Claim 9
Dependent Claim
66 words
A ceramic sintered body consisting essentially of TiB 2 as the principal component, 0.5 to 30 wt. % of SiC and 2 to 40 wt. % of ZrO 2 , which further contains 0.5 to 20 wt. % of one of more compounds selected from the group consisting of metal carbides other than SiC, metal nitrides, metal carbonitrides and metal borides other than TiB 2 .
Claim 10
Dependent Claim
41 words
The ceramic sintered body of claim 5 wherein said one or more compounds are selected from the group consisting of TiC, VC, ZrC, NbC, Cr 3 C 2 , TaC, TiN, Ti(CN), TaB 2 , ZrB 2 and NbB 2 .
Claim 11
Dependent Claim
46 words
The ceramic sintered body of claim 5 or claim 6 wherein the ZrO 2 contains 1 to 8% of Y 2 O 3 , 1 to 4% of MgO and/or 10 to 21% of CeO 2 , as per cent by weight to ZrO 2 .
Claim 12
Dependent Claim
43 words
The ceramic sintered body of claim 4 which further contains 0.5 to 20 wt. % of one or more compounds selected from the group consisting of metal carbides other than SiC, metal nitrides, metal carbonitrides and metal borides other than TiB 2 .
Claim 13
Dependent Claim
41 words
The ceramic sintered body of claim 8 wherein said one or more compounds are selected from the group consisting of TiC, VC, ZrC, NbC, Cr 3 C 2 , TaC, TiN, Ti(CN), TaB 2 , ZrB 2 and NbB 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-06-11 | 1993-12-11 | 1994-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-06-11 | 1997-12-11 | 1998-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-06-11 | 2001-12-11 | 2002-06-12 | $7700.00 | Window Closed / Lapsed |