Method for the preparation of a sintered body of silicon carbide
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1987-02-24
•
Granted: 1988-08-09
•
Expires: 2007-02-24
Abstract
Abstract Sintered bodies of silicon carbide having remarkably increased volume resistivity and thermal conductivity can be obtained by heating a green body shaped of a fine silicon carbide powder admixed with boron or a boron compound, e.g. boron carbide, titanium boride and boron oxide, as a sintering aid at 1800 DEG to 2200 DEG C. in the presence of or in the vicinity of a shaped body of a powdery mixture of a fine silicon carbide powder admixed with boron nitride in the same furnace. The improvements in the volume resistivity and thermal conductivity of the sintered body are particularly remarkable when the fine silicon carbide powder is a pyrolysis product of a methyl hydrogen silane compound such as tetramethyl disilane.
Inventors
- 👤 Morinobu Endo
- 👤 Minoru Takamizawa
- 👤 Tatsuhiko Hongu
- 👤 Akira Hayashida
- 👤 Nobuaki Urasato
- 👤 Hiromi Ohsaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 19:32
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/571
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
202 words
A method for the preparation of a sintered body of silicon carbide exhibiting extremely high volume resistivity and thermal conductivity and high density, which comprises the steps of: (a) admixing a fine powder of silicon carbide with boron or a boron compound selected from the group consisting of boron carbide, titanium boride and boron oxide in an amount in the range from 0.1 to 5% by weight as boron based on the silicon carbide powder to give a powdery mixture; (b) shaping the powdery mixture by compression to give a first green body of silicon carbide; and (c) sintering the first green body at a temperature in the range from 1800° to 2200° C. in the same furnace, at the same time and at substantially the same temperature as a second shaped body or powdery mixture composed of a fine powder of silicon carbide admixed with boron nitride in an amount in the range from 0.01 to 50% by weight, whereby the presence of the second shaped body or powdery mixture of boron nitride and silicon carbide during sintering has the effect of imparting extremely high volume resistivity and thermal conductivity and high density to the sintered first body of silicon carbide.
Claim 2
Independent Claim
202 words
A method for the preparation of a sintered body of silicon carbide exhibiting extremely high volume resistivity and thermal conductivity and high density, which comprises the steps of: (a) admixing a fine powder of silicon carbide with boron or a boron compound selected from the group consisting of boron carbide, titanium boride and boron oxide in an amount in the range from 0.1 to 5% by weight as boron based on the silicon carbide powder to give a powdery mixture; (b) shaping the powdery mixture by compression to give a first green body of silicon carbide; and (c) sintering the first green body at a temperature in the range from 1800° to 2200° C. in the same furnace, at the same time and at substantially the same temperature as a second shaped body or powdery mixture composed of a fine powder of silicon carbide admixed with boron nitride in an amount in the range from 0.01 to 50% by weight, whereby the presence of the second shaped body or powdery mixture of boron nitride and silicon carbide during sintering has the effect of imparting extremely high volume resistivity and thermal conductivity and high density to the sintered first body of silicon carbide.
Claim 3
Dependent Claim
34 words
The method for the preparation of a sintered body fo silicon carbide as claimed in claim 1 wherein the fine powder of silicon carbide is a pyrolysis product of a methyl hydrogen silane compound.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-09 | 1992-02-08 | 1992-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-09 | 1996-02-08 | 1996-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-09 | 2000-02-08 | 2000-08-09 | $7700.00 | Window Closed / Lapsed |