System for preventing decomposition of silicon carbide articles during sintering
Assignee: Stemcor Corp
•
Filing: 1985-04-01
•
Granted: 1987-03-10
•
Expires: 2005-04-01
Abstract
Abstract A system to prevent, retard or reverse the decomposition of silicon carbide articles during high temperature plasma sintering. Preferably, the system comprises sintering a silicon carbide refractory or ceramic green body in a closed sintering environment, such as a covered crucible, with strategic placement of the plasma torch or torches, exhaust outlet and crucibles. As sintering proceeds, a silicon vapor pressure builds up within the crucible, retarding the decomposition of the silicon carbide body. The plasma torch, exhaust outlet, and crucibles are positioned so that buoyant convective flow is maximized to increase the heat transfer and energy efficiency. In another embodiment, a "sacrificial" source of silicon carbide is placed into the sintering furnace. The silicon carbide in the sacrificial source starts to decompose before the silicon carbide refractory or ceramic article, creating a supersaturated atmosphere of silicon vapor species in the furnace. This prevents, retards or reverses the silicon carbide decomposition reactions and thus maintains the integrity of the refractory or ceramic article being sintered. Preferably, the sacrificial source is placed in a closed sintering environment along with the silicon carbide article being sintered.
Inventors
- 👤 Jonathan J. Kim
- 👤 Joel D. Katz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:34
CPC Classifications
F; F27; F27D; F27D99/00; F27D99/0001; F27D99/0006; C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/622; C04B35/64; F27B; F27B17/00; F27B17/0016; F27B5/00; F27B5/06; F27B5/10
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
88 words
A method for preventing, halting, retarding or reversing the decomposition of silicon carbide articles during high temperature sintering in a plasma furnace comprising: placing formed silicon carbide articles into at least one covered crucible within a plasma furnace; and sintering said silicon carbide articles in a plasma gas environment so that a partial pressure of silicon gas builds up within the closed environment rendered by the covered crucible, thereby saturating the environment with silicon gas and other silicon vapor species, halting further decomposition of said silicon carbide articles.
Claim 2
Independent Claim
88 words
A method for preventing, halting, retarding or reversing the decomposition of silicon carbide articles during high temperature sintering in a plasma furnace comprising: placing formed silicon carbide articles into at least one covered crucible within a plasma furnace; and sintering said silicon carbide articles in a plasma gas environment so that a partial pressure of silicon gas builds up within the closed environment rendered by the covered crucible, thereby saturating the environment with silicon gas and other silicon vapor species, halting further decomposition of said silicon carbide articles.
Claim 3
Dependent Claim
14 words
A method in accordance with claim 1 wherein said crucible is made from graphite.
Claim 4
Dependent Claim
26 words
A method in accordance with claim 1 comprising at least two stacked crucibles, wherein a space of at least 0.5 inches is provided between said crucibles.
Claim 5
Dependent Claim
22 words
A method in accordance with claim 1 further comprising positioning at least one primary plasma torch near the top of said furnace.
Claim 6
Dependent Claim
29 words
A method in accordance with claim 4 further comprising positioning at least one additional plasma torch through the center wall of said furnace and opposite said primary plasma torch.
Claim 7
Dependent Claim
19 words
A method in accordance with claim 4 further comprising positioning an exhaust outlet near the bottom of said furnace.
Claim 8
Dependent Claim
34 words
A method in accordance with claim 1 further comprising placing a sacrificial source of silicon carbide in said furnace, said sacrificial source of silicon carbide beginning decomposition before the silicon carbide articles being sintered.
Claim 9
Dependent Claim
29 words
A method in accordance with claim 7 wherein said sacrificial source of silicon carbide has a higher surface area than the particles of the silicon carbide articles being sintered.
Claim 10
Dependent Claim
30 words
A method in accordance with claim 7 wherein said sacrificial source of silicon carbide has a smaller radius of curvature than the particles of the silicon carbide articles being sintered.
Claim 11
Dependent Claim
22 words
A method in accordance with claim 7 wherein said sacrificial source of silicon carbide is in the form of a meta-stable material.
Claim 12
Dependent Claim
19 words
A method in accordance with claim 7 wherein said sacrificial source of silicon carbide is placed into said crucible.
Claim 13
Dependent Claim
23 words
A method in accordance with claim 11 wherein said sacrificial source of silicon carbide comprises a coating on the inside of said crucible.
Claim 14
Dependent Claim
23 words
A method in accordance with claim 11 wherein said sacrificial source of silicon carbide comprises a powder on the bottom of said crucible.
Claim 15
Dependent Claim
20 words
A method in accordance with claim 7 wherein said sacrificial source of silicon carbide is placed into a shallow container.
Claim 16
Dependent Claim
23 words
A method in accordance with claim 7 wherein said sacrificial source of silicon carbide is placed near at least one plasma torch inlet.
Claim 17
Independent Claim
112 words
A method for preventing, halting. retarding or reversing the decomposition of silicon carbide articles during high temperature sintering in a plasma furnace comprising: placing formed silicon carbide articles into a plasma furnace; injecting a plasma arc heated gas from at least one primary torch which is positioned near the top of said furnace in order to avoid the formation of cold pockets; sintering said silicon carbide articles in a plasma gas environment produced by said primary plasma torch; and expending the exhaust produced by said plasma gas through an exhaust outlet positioned near the bottom of said furnace in order to minimize the buoyant effects of the convected heat transfer resulting therefrom.
Claim 18
Independent Claim
112 words
A method for preventing, halting. retarding or reversing the decomposition of silicon carbide articles during high temperature sintering in a plasma furnace comprising: placing formed silicon carbide articles into a plasma furnace; injecting a plasma arc heated gas from at least one primary torch which is positioned near the top of said furnace in order to avoid the formation of cold pockets; sintering said silicon carbide articles in a plasma gas environment produced by said primary plasma torch; and expending the exhaust produced by said plasma gas through an exhaust outlet positioned near the bottom of said furnace in order to minimize the buoyant effects of the convected heat transfer resulting therefrom.
Claim 19
Dependent Claim
29 words
A method in accordance with claim 16 further comprising positioning at least one additional plasma torch through the center wall of said furnace and opposite said primary plasma torch.
Claim 20
Dependent Claim
34 words
A method in accordance with claim 16 further comprising placing a sacrificial source of silicon carbide in said furnace, said sacrificial source of silicon carbide beginning decomposition before the silicon carbide articles being sintered.
Claim 21
Dependent Claim
29 words
A method in accordance with claim 18 wherein said sacrificial source of silicon carbide has a higher surface area than the particles of the silicon carbide articles being sintered.
Claim 22
Dependent Claim
30 words
A method in accordance with claim 18 wherein said sacrificial source of silicon carbide has a smaller radius of curvature than the particles of the silicon carbide articles being sintered.
Claim 23
Dependent Claim
22 words
A method in accordance with claim 18 wherein said sacrificial source of silicon carbide is in the form of a meta-stable material.
Claim 24
Dependent Claim
20 words
A method in accordance with claim 18 wherein said sacrificial source of silicon carbide is placed into a shallow container.
Claim 25
Dependent Claim
23 words
A method in accordance with claim 18 wherein said sacrificial source of silicon carbide is placed near at least one plasma gas inlet.
Claim 26
Dependent Claim
21 words
A method in accordance with claim 18 wherein said sacrificial source of silicon carbide comprises a coating on the furnace walls.
Claim 27
Independent Claim
69 words
A method for preventing, halting, retarding or reversing the decomposition of silicon carbide articles during high temperature sintering in a plasma furnace comprising: placing formed silicon carbide articles into a plasma furnace; placing a sacrificial source of silicon carbide in said plasma furnace, said sacrificial source of silicon carbide beginning decomposition before the silicon carbide articles during sintering; and; sintering said silicon carbide articles in a plasma gas environment.
Claim 28
Independent Claim
69 words
A method for preventing, halting, retarding or reversing the decomposition of silicon carbide articles during high temperature sintering in a plasma furnace comprising: placing formed silicon carbide articles into a plasma furnace; placing a sacrificial source of silicon carbide in said plasma furnace, said sacrificial source of silicon carbide beginning decomposition before the silicon carbide articles during sintering; and; sintering said silicon carbide articles in a plasma gas environment.
Claim 29
Dependent Claim
29 words
A method in accordance with claim 25 wherein said sacrificial source of silicon carbide has a higher surface area than the particles of the silicon carbide articles being sintered.
Claim 30
Dependent Claim
30 words
A method in accordance with claim 25 wherein said sacrificial source of silicon carbide has a smaller radius of curvature than the particles of the silicon carbide articles being sintered.
Claim 31
Dependent Claim
22 words
A method in accordance with claim 25 wherein said sacrificial source of silicon carbide is in the form of a meta-stable material.
Claim 32
Dependent Claim
20 words
A method in accordance with claim 25 wherein said sacrificial source of silicon carbide is placed into a shallow container.
Claim 33
Dependent Claim
23 words
A method in accordance with claim 25 wherein said sacrificial source of silicon carbide is placed near at least one plasma torch inlet.
Claim 34
Dependent Claim
21 words
A method in accordance with claim 25 wherein said sacrificial source of silicon carbide comprises a coating on the furnace walls.
Claim 35
Dependent Claim
70 words
A furnace for the high temperature sintering of silicon carbide articles and for preventing, halting, retarding or reversing the decomposition of said silicon carbide articles during sintering, comprising: a sintering chamber; at least one covered crucible for containing said silicon carbide articles within said sintering chamber; a plasma gas inlet positioned near the top of said sintering chamber; and, an exhaust outlet positioned near the bottom of said sintering chamber.
Claim 36
Dependent Claim
70 words
A furnace for the high temperature sintering of silicon carbide articles and for preventing, halting, retarding or reversing the decomposition of said silicon carbide articles during sintering, comprising: a sintering chamber; at least one covered crucible for containing said silicon carbide articles within said sintering chamber; a plasma gas inlet positioned near the top of said sintering chamber; and, an exhaust outlet positioned near the bottom of said sintering chamber.
Claim 37
Dependent Claim
16 words
A furnace in accordance with claim 32 wherein said sacrificial source is placed into said crucible.
Claim 38
Dependent Claim
36 words
A furnace in accordance with claim 32 wherein there are at least two crucibles which are stacked in a vertical direction within said sintering chamber, with a space of at least 0.5 inches between said crucibles.
Claim 39
Dependent Claim
96 words
A furnace for the high temperature sintering of silicon carbide articles and for preventing, halting, retarding or reversing the decomposition of said silicon carbide articles during sintering, comprising: a sintering chamber; at least one crucible for containing said silicon carbide articles within said sintering chamber; a plasma gas inlet positioned near the top of said sintering chamber; an exhaust outlet positioned near the bottom of said sintering chamber; and a sacrificial source of silicon carbide supported within said sintering chamber, wherein said sacrificial source of silicon carbide begins decomposition before the silicon carbide articles being sintered.
Claim 40
Dependent Claim
96 words
A furnace for the high temperature sintering of silicon carbide articles and for preventing, halting, retarding or reversing the decomposition of said silicon carbide articles during sintering, comprising: a sintering chamber; at least one crucible for containing said silicon carbide articles within said sintering chamber; a plasma gas inlet positioned near the top of said sintering chamber; an exhaust outlet positioned near the bottom of said sintering chamber; and a sacrificial source of silicon carbide supported within said sintering chamber, wherein said sacrificial source of silicon carbide begins decomposition before the silicon carbide articles being sintered.
Claim 41
Dependent Claim
21 words
A furnace in accordance with claim 35 wherein said sacrificial source is placed into a shallow container within said sintering chamber.
Claim 42
Dependent Claim
16 words
A furnace in accordance with claim 35 wherein said sacrificial source is placed into said crucible.
References Cited (Backward Citations)
US30286A
Cited
US3432296A
Cited
US3977837A
Cited
USRE30286E
Cited
US4141726A
Cited
US4179299A
Cited
EP0032100A2
Cited
US4381931A
Cited
FR2510986A1
Cited
US4501717A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-09 | 1990-09-08 | 1991-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-09 | 1994-09-08 | 1995-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-09 | 1998-09-08 | 1999-03-10 | $7700.00 | Window Closed / Lapsed |