Submicron carbon-containing titanium boride powder and method for preparing same
Assignee: PPG Industries Inc
•
Filing: 1978-12-04
•
Granted: 1981-05-12
•
Expires: 1998-12-04
Abstract
Abstract Submicron carbon-containing titanium diboride powder and other hard, refractory metal boride powders, such as zirconium diboride and hafnium diboride powders, are prepared by vapor phase reaction of the corresponding metal halide, e.g., titanium halide, vaporous carbon source, and boron source reactants in the presence of hydrogen in a reaction zone and in the substantial absence of oxygen, either combined or elemental. In a preferred embodiment, the metal halide, e.g., titanium tetrachloride, carbon source, e.g., halogenated hydrocarbon, and boron source, e.g., boron trichloride, reactants are mixed with a hot stream of hydrogen produced by heating hydrogen in a plasma heater. The reaction zone is maintained at metal boride forming temperatures and submicron solid, carbon-containing metal boride powder is removed promptly from the reactor and permitted to cool. The preponderant number of metal boride particles comprising the powder product have a particle size in the range of between 0.05 and 0.7 microns. The metal boride powder product contains a minor amount of carbon, e.g., from above 0.1 to about 5 percent by weight total carbon. Alternatively, submicron metal carbide powders, e.g., titanium, zirconium, hafnium or boron carbide powders, or finely-divided carbon can be blended physically with submicron metal boride powder prepared as described above but in the absence of the carbon source reactant to provide metal borides containing a minor concentration of carbon in the amounts previously indicated. The above described carbon-containing titanium diboride powder compositions can be hot pressed, or cold pressed and sintered to articles having densities of at least 95 percent of theoretical. Such articles can be used as current conducting elements, e.g., cathodes, in electrolytic cells for production of aluminum.
Inventors
- 👤 Roger A. Steiger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 06:53
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58078; C01; C01B; C01B35/00; C01B35/02; C01B35/04; C04B35/58071; B; B01; B01J; B01J2219/00; B01J2219/08; B01J2219/0894
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
116 words
Submicron titanium diboride powder having dispersed therein solid submicron carbon-containing additive selected from the group elemental carbon, titanium carbide and mixtures of elemental carbon and titanium carbide, the total carbon content of said additive being from about 0.3 to about 2 weight percent based on titanium diboride, and wherein the titanium diboride powder has a surface area of between about 3 and 15 square meters per gram and the nominal sectional diameter of at least 90 percent of the titanium diboride particles of the powder are less than one micron, said particles being tabular to equidimensional hexagonal crystals having well developed faces, the number median particle size of said particles being between 0.08 and 0.6 microns.
Claim 2
Dependent Claim
116 words
Submicron titanium diboride powder having dispersed therein solid submicron carbon-containing additive selected from the group elemental carbon, titanium carbide and mixtures of elemental carbon and titanium carbide, the total carbon content of said additive being from about 0.3 to about 2 weight percent based on titanium diboride, and wherein the titanium diboride powder has a surface area of between about 3 and 15 square meters per gram and the nominal sectional diameter of at least 90 percent of the titanium diboride particles of the powder are less than one micron, said particles being tabular to equidimensional hexagonal crystals having well developed faces, the number median particle size of said particles being between 0.08 and 0.6 microns.
Claim 3
Dependent Claim
24 words
The powder of claim 1 wherein the surface area of the titanium diboride powder is between about 3 and 15 square meters per gram.
Claim 4
Dependent Claim
25 words
The powder of claim 2 wherein at least 60 percent of the titanium diboride particles have a nominal sectional diameter of 0.7 microns or less.
Claim 5
Dependent Claim
26 words
The powder of claim 2 wherein the ratio of the nominal sectional diameter to thickness of the titanium diboride tabular crystals is from 1.5:1 to 10:1.
Claim 6
Dependent Claim
21 words
The powder of claim 4 wherein the total carbon content of the additive is from about 0.3 to 1 weight percent.
Claim 7
Dependent Claim
32 words
The powder of claim 5 wherein the carbon-containing additive and titanium diboride are coproduced by vapor phase reaction of titanium halide, boron source and carbon source reactants in the presence of hydrogen.
Claim 8
Dependent Claim
17 words
The powder of claim 6 wherein the titanium diboride powder contains less than 0.25 weight percent oxygen.
Claim 9
Dependent Claim
23 words
The powder of claim 7 wherein the titanium diboride powder contains less than 0.20 weight percent halogen as determined by X-ray spectrographic analysis.
Claim 10
Dependent Claim
18 words
The powder of claim 8 wherein the titanium diboride powder contains less than 0.4 weight percent metal impurities.
Claim 11
Dependent Claim
44 words
The powder of claim 7 wherein the titanium halide is titanium tetrachloride, the boron source is boron trichloride, and the titanium diboride powder contains less than 0.20 weight percent chlorine as determined by X-ray spectroscopic analysis and less than 0.4 weight percent metal impurities.
Claim 12
Dependent Claim
25 words
The powder of claim 10 wherein the surface area of the titanium diboride powder is from about 5 to about 10 square meters per gram.
Claim 13
Dependent Claim
101 words
A dense titanium diboride article of manufacture consisting essentially of titanium diboride and carbon-containing additive selected from the group consisting essentially of elemental carbon, titanium carbide and mixtures of elemental carbon and titanium carbide, the total carbon content of said additive being from about 0.3 to about 2 weight percent based on titanium diboride, said article having a density of at least 90 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains with contiguous grain boundaries.
Claim 14
Dependent Claim
101 words
A dense titanium diboride article of manufacture consisting essentially of titanium diboride and carbon-containing additive selected from the group consisting essentially of elemental carbon, titanium carbide and mixtures of elemental carbon and titanium carbide, the total carbon content of said additive being from about 0.3 to about 2 weight percent based on titanium diboride, said article having a density of at least 90 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains with contiguous grain boundaries.
Claim 15
Dependent Claim
22 words
The article of claim 12 wherein the total carbon content of the additive is from about 0.3 to about 1 weight percent.
Claim 16
Dependent Claim
20 words
The article of claim 13 wherein the density is at least 95 percent of the theoretical density for titanium diboride.
Claim 17
Dependent Claim
20 words
The article of claim 13 wherein the density is at least 98 percent of the theoretical density for titanium diboride.
Claim 18
Dependent Claim
95 words
A dense titanium diboride article of manufacture consisting essentially of titanium diboride and carbon-containing additive selected from the group consisting of titanium carbide, elemental carbon and mixtures thereof, the total carbon content of said additives being from about 0.3 to about 2 weight percent based on titanium diboride, said article having a density of at least 93 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains with contiguous grain boundaries.
Claim 19
Dependent Claim
95 words
A dense titanium diboride article of manufacture consisting essentially of titanium diboride and carbon-containing additive selected from the group consisting of titanium carbide, elemental carbon and mixtures thereof, the total carbon content of said additives being from about 0.3 to about 2 weight percent based on titanium diboride, said article having a density of at least 93 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains with contiguous grain boundaries.
Claim 20
Dependent Claim
22 words
The article of claim 16 wherein the total carbon content of the additive is between about 0.3 and about 1 weight percent.
Claim 21
Dependent Claim
16 words
The article of claim 17 wherein the microstructure is characterized by a predominantly fine grain size.
Claim 22
Dependent Claim
29 words
The article of claim 17 wherein the density is at least 98 percent of the theoretical density for titanium diboride and the article is substantially impermeable to molten aluminum.
Claim 23
Dependent Claim
15 words
The article of claim 19 wherein the electrical resistivity is less than 10 microhm centimeters.
Claim 24
Dependent Claim
17 words
The article of claims 12, 16, 17 or 19 wherein said article is a current conducting element.
Claim 25
Dependent Claim
24 words
The article of claims 16, 17 or 19 wherein said article is a cathodic element in an electrolytic cell for the production of aluminum.
Claim 26
Dependent Claim
99 words
A cold formed and sintered dense titanium diboride article of manufacture consisting essentially of titanium diboride and carbon-containing additive selected from the group consisting of titanium carbide, elemental carbon and mixtures thereof, the total carbon content of said additives being from about 0.3 to about 2 weight percent based on titanium diboride, said article having a density of at least 93 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains with contiguous grain boundaries.
Claim 27
Dependent Claim
99 words
A cold formed and sintered dense titanium diboride article of manufacture consisting essentially of titanium diboride and carbon-containing additive selected from the group consisting of titanium carbide, elemental carbon and mixtures thereof, the total carbon content of said additives being from about 0.3 to about 2 weight percent based on titanium diboride, said article having a density of at least 93 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains with contiguous grain boundaries.
Claim 28
Dependent Claim
26 words
The cold formed and sintered article of claim 23 wherein the total carbon content of the additive is between about 0.3 and about 1 weight percent.
Claim 29
Dependent Claim
122 words
A cold formed and sintered dense titanium diboride article of manufacture consisting essentially of titanium diboride and coproduced carbon-containing additive selected from the group consisting of titanium carbide, elemental carbon and mixtures thereof, said additive being coproduced by vapor phase reaction of titanium halide, boron source and carbon source reactants in the presence of hydrogen, the total carbon content of said additives being from about 0.3 to about 2 weight percent baed on titanium diboride, said article having a density of at least 93 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains with contiguous grain boundaries.
Claim 30
Dependent Claim
122 words
A cold formed and sintered dense titanium diboride article of manufacture consisting essentially of titanium diboride and coproduced carbon-containing additive selected from the group consisting of titanium carbide, elemental carbon and mixtures thereof, said additive being coproduced by vapor phase reaction of titanium halide, boron source and carbon source reactants in the presence of hydrogen, the total carbon content of said additives being from about 0.3 to about 2 weight percent baed on titanium diboride, said article having a density of at least 93 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains with contiguous grain boundaries.
Claim 31
Dependent Claim
41 words
The cold formed and sintered article of claim 25 wherein the total carbon content of the additive is between about 0.3 and about 1 weight percent and wherein the microstructure is composed of predominantly fine grains of essentially a single phase.
Claim 32
Dependent Claim
113 words
A thermal shock resistant dense titanium diboride article of manufacture consisting essentially of titanium diboride and carbon-containing additive selected from the group consisting of titanium carbide, elemental carbon and mixtures thereof, the total carbon content of said additive being from about 0.3 to about 1 weight percent based on titanium diboride, said article having a density of at least 95 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains of essentially a single phase with contiguous grain boundaries, said microstructure having discernible submicron microcracks at the grain boundaries.
Claim 33
Dependent Claim
113 words
A thermal shock resistant dense titanium diboride article of manufacture consisting essentially of titanium diboride and carbon-containing additive selected from the group consisting of titanium carbide, elemental carbon and mixtures thereof, the total carbon content of said additive being from about 0.3 to about 1 weight percent based on titanium diboride, said article having a density of at least 95 percent of the theoretical density for titanium diboride, essentially closed porosity in the form of substantially submicron intragranular pores that are essentially uniformly distributed throughout the article, and a microstructure of substantially equidimensional grains of essentially a single phase with contiguous grain boundaries, said microstructure having discernible submicron microcracks at the grain boundaries.
Claim 34
Dependent Claim
13 words
The article of clalm 27 wherein the density is at least 98 percent.
Claim 35
Dependent Claim
13 words
The article of clalm 27 wherein the density is at least 98 percent.
References Cited (Backward Citations)
GB1010492A
Cited
US3979500A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-11 | 1984-11-10 | 1985-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-11 | 1988-11-10 | 1989-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-11 | 1992-11-10 | 1993-05-12 | $7700.00 | Window Closed / Lapsed |