Titanium diboride-eased composite articles with improved fracture toughness
Assignee: Verizon Laboratories Inc
•
Filing: 1989-08-31
•
Granted: 1992-01-07
•
Expires: 2009-08-31
Abstract
Abstract Composite articles, cutting tools and wear parts are prepared by densification of a mixture comprising whiskers, fibers, or particles of hard refractory transition metal carbides, nitrides or carbonitrides uniformly distributed in a titanium diboride matrix. Optionally, other dispersoids may also be incorporated. The preferred composite article or cutting tool has a fracture toughness equal to or greater than about 2.5 MN·m 1/2 . Methods of preparation and use are also disclosed.
Inventors
- 👤 Sergej-Tomislav V. Buljan
- 👤 Earl G. Geary, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:09
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/622; C04B35/64; C04B35/645; C04B35/71; C04B35/78; C04B35/80; Y; Y10; Y10T; Y10T407/00; Y10T407/27; Y10T408/00; Y10T408/03; Y10T408/78; Y10T409/00; Y10T409/30; Y10T409/303752; Y10T82/00; Y10T82/10
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
103 words
A method for continuous or interrupted machining of steel stock comprising the step of milling, turning, or boring the stock with a shaped, densified, hard, abrasion resistant ceramic-based composite cutting tool of improved fracture toughness consisting essentially of about 5-60 volume percent of one or more dispersoids selected from the group consisting of whiskers, chopped fibers, and particles of refractory carbides, nitrides, and carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, and solid solutions thereof, uniformly distributed in a matrix of titanium diboride; wherein the machining speed is about 100-1500 sfm and the feed rate is about 0.005-0.03 in/rev.
Claim 2
Independent Claim
103 words
A method for continuous or interrupted machining of steel stock comprising the step of milling, turning, or boring the stock with a shaped, densified, hard, abrasion resistant ceramic-based composite cutting tool of improved fracture toughness consisting essentially of about 5-60 volume percent of one or more dispersoids selected from the group consisting of whiskers, chopped fibers, and particles of refractory carbides, nitrides, and carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, and solid solutions thereof, uniformly distributed in a matrix of titanium diboride; wherein the machining speed is about 100-1500 sfm and the feed rate is about 0.005-0.03 in/rev.
Claim 3
Independent Claim
154 words
A method for continuous or interrupted machining of steel stock comprising milling, turning, or boring the stock with a shaped, densified, hard, abrasion resistant ceramic-based composite cutting tool of improved fracture toughness consisting essentially of: about 5-60 volume percent of one or more first dispersoids selected from the group consisting of whiskers, chopped fibers, and particles of refractory carbides, nitrides, and carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, and solid solutions thereof; and from 0 to about 55 volume percent of one or more other dispersoids selected from the group consisting of whiskers, fibers, and particles of hard refractory hafnium diboride, tungsten diboride, silicon nitride, alumina, zirconia, and hafnia, and solid solutions thereof, the combined percent of all dispersoids not exceeding about 60 volume percent; uniformly distributed in a matrix of titanium diboride; wherein the machining speed is about 100-1500 sfm and the feed rate is about 0.005-0.03 in/rev.
Claim 4
Independent Claim
154 words
A method for continuous or interrupted machining of steel stock comprising milling, turning, or boring the stock with a shaped, densified, hard, abrasion resistant ceramic-based composite cutting tool of improved fracture toughness consisting essentially of: about 5-60 volume percent of one or more first dispersoids selected from the group consisting of whiskers, chopped fibers, and particles of refractory carbides, nitrides, and carbonitrides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, and tungsten, and solid solutions thereof; and from 0 to about 55 volume percent of one or more other dispersoids selected from the group consisting of whiskers, fibers, and particles of hard refractory hafnium diboride, tungsten diboride, silicon nitride, alumina, zirconia, and hafnia, and solid solutions thereof, the combined percent of all dispersoids not exceeding about 60 volume percent; uniformly distributed in a matrix of titanium diboride; wherein the machining speed is about 100-1500 sfm and the feed rate is about 0.005-0.03 in/rev.
References Cited (Backward Citations)
US3972161A
Cited
US4205964A
Cited
JPS61270265A
Cited
US4789277A
Cited
US4789277B1
Cited
US4863490A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-06 | 1995-07-08 | 1996-01-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-06 | 1999-07-08 | 2000-01-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-06 | 2003-07-08 | 2004-01-07 | $7700.00 | Window Closed / Lapsed |