Reaction sintered boride-oxide-silicon nitride for ceramic cutting tools
Assignee: Corning Inc
•
Filing: 1988-08-24
•
Granted: 1989-10-24
•
Expires: 2008-08-24
Abstract
Abstract This invention is directed to the production of oxide-boride-silicon nitride ceramics consisting essentially of ceramic bodies of oxide and boride phases which have silicon nitride added to improve the properties of the ceramic body for use as wear material, durable interface material, and cutting tool inserts. The addition of Si3N4 to the oxide-boride body provides a durable ceramic material which provides a range of cutting speeds that may be utilized in both turning and milling operations.
Inventors
- 👤 Thomas P. DeAngelis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:08
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/117; C04B35/50; C04B35/51; C04B35/515; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/58078; C04B35/584; C04B35/597; C04B35/622; C04B35/64; C04B35/645; C04B35/65
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
228 words
A ceramic composition consisting essentially of a dense homogeneous sintered body whose composition is selected from: (a) composition A consisting essentially of a dense homogeneous sintered body consisting on a mole percent basis, of 2 to 53% silicon nitride, where some or all of the silicon nitride is present as a separate phase or in solid solution with aluminum oxide as silicon-aluminum-oxynitride, and about 10 to 61% boride phase or phases of one or both of the elements Ti and Zr, and 37 to 88% oxide phase or phases of one or more of the elements of groups 3a, 4a, 3b, including lanthanide and actinide series elements, 4b, 5b, 6b and 8 of the periodic chart; and mixtures of any of the foregoing, or (b) composition B consisting essentially of a dense homogeneous sintered body consisting, on a mole percent basis, of 5 to 48% silicon nitride, where some or all of the silicon nitride is present as a separate phase or in solid solution with aluminum oxide as silicon-aluminum-oxynitride, and about 37 to 80% boride phase or phases of one or both of the elements Ti and Zr, and 15 to 25% oxide phase or phases of one or more of the elements of groups 3a, 4a, 3b, including lanthanide and actinide series elements, 5b, 6b, and 8 of the periodic table; and mixtures of the foregoing.
Claim 2
Dependent Claim
228 words
A ceramic composition consisting essentially of a dense homogeneous sintered body whose composition is selected from: (a) composition A consisting essentially of a dense homogeneous sintered body consisting on a mole percent basis, of 2 to 53% silicon nitride, where some or all of the silicon nitride is present as a separate phase or in solid solution with aluminum oxide as silicon-aluminum-oxynitride, and about 10 to 61% boride phase or phases of one or both of the elements Ti and Zr, and 37 to 88% oxide phase or phases of one or more of the elements of groups 3a, 4a, 3b, including lanthanide and actinide series elements, 4b, 5b, 6b and 8 of the periodic chart; and mixtures of any of the foregoing, or (b) composition B consisting essentially of a dense homogeneous sintered body consisting, on a mole percent basis, of 5 to 48% silicon nitride, where some or all of the silicon nitride is present as a separate phase or in solid solution with aluminum oxide as silicon-aluminum-oxynitride, and about 37 to 80% boride phase or phases of one or both of the elements Ti and Zr, and 15 to 25% oxide phase or phases of one or more of the elements of groups 3a, 4a, 3b, including lanthanide and actinide series elements, 5b, 6b, and 8 of the periodic table; and mixtures of the foregoing.
Claim 3
Dependent Claim
14 words
The composition as defined in claim 1 wherein the selected composition is composition A.
Claim 4
Dependent Claim
14 words
The composition as defined in claim 1 wherein the selected composition is composition B.
Claim 5
Dependent Claim
14 words
The composition as defined in claim 2 containing about 5 to 53% silicon nitride.
Claim 6
Dependent Claim
14 words
The composition as defined in claim 2 containing about 5 to 50% silicon nitride.
Claim 7
Dependent Claim
14 words
The composition as defined in claim 2 containing about 5 to 40% silicon nitride.
Claim 8
Dependent Claim
14 words
The composition as defined in claim 2 containing about 10 to 61% titanium diboride.
Claim 9
Dependent Claim
14 words
The composition as defined in claim 2 containing about 10 to 55% titanium diboride.
Claim 10
Dependent Claim
14 words
The composition as defined in claim 2 containing about 12 to 35% titanium diboride.
Claim 11
Dependent Claim
13 words
The composition as defined in claim 2 containing about 37 to 70% alumina.
Claim 12
Dependent Claim
13 words
A ceramic insert cutting tool with a composition as defined in claim 1.
Claim 13
Dependent Claim
109 words
A reaction sintered oxide-boride-silicon nitride ceramic body as in claim 1 consisting essentially of a fine-grained, homogeneous, intimate interdispersion which body is prepared by the process comprising: (a) admixing particulate reactants of maximum particle size substantially (e.g. at least 95 volume percent) not greater than 150 μm and being elements, compounds, intermetallic compounds, alloys or combination thereof in stoichiometric proportions to substantially form the boride and oxide phases, and (b) shaping and heating the admixture to form the reaction sintered body, and heating being done in nonreactive atmosphere and at temperature at which the reaction and sintering occurs between the reactants to substantially form the boride and oxide phases.
Claim 14
Dependent Claim
14 words
The composition as defined in claim 1 having not greater than 5% open porosity.
Claim 15
Dependent Claim
14 words
The composition as defined in claim 1 having not greater than 2% open porosity.
Claim 16
Dependent Claim
21 words
The composition as defined in claim 1 having a maximum grain size of any product substantially not greater than 15 μm.
Claim 17
Dependent Claim
21 words
The composition as defined in claim 1 having a maximum grain size of any product substantially not greater than 5 μm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-23 | 1993-04-24 | 1993-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-23 | 1997-04-24 | 1997-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-23 | 2001-04-24 | 2001-10-24 | $7700.00 | Window Closed / Lapsed |