US5372859A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Enhanced fatigue and retention in ferroelectric thin film memory capacitors by post-top electrode anneal treatment
Assignee: GOVERNMENT OF UNITED STATES AS REPRESENTED BY NASA
•
Filing: 1992-10-20
•
Granted: 1994-12-13
•
Expires: 2012-10-20
Abstract
Abstract Thin film ferroelectric capacitors (10) comprising a ferroelectric film (18) sandwiched between electrodes (16 and 20) for nonvolatile memory operations are rendered more stable by subjecting the capacitors to an anneal following deposition of the top electrode (20). The anneal is done so as to form the interface (22) between the ferroelectric film and the top electrode. Heating in an air oven, laser annealing, or electron bombardment may be used to form the interface. Heating in an air oven is done at a temperature at least equal to the crystallization temperature of the ferroelectric film. Where the ferroelectric film comprises lead zirconate titanate, annealing is done at about 550° to 600° C. for about 10 to 15 minutes. The formation treatment reduces the magnitude of charge associated with the non-switching pulse in the thin film ferroelectric capacitors. Reduction of this charge leads to significantly more stable nonvolatile memory operations in both digital and analog memory devices. The formation treatment also reduces the ratio of change of the charge associated with the non-switching pulse as a function of retention time. These improved memory devices exhibit greater performance in retention and reduced fatigue in memory arrays.
Inventors
- 👤 Sarita Thakoor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 20:35
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/682; H10D1/692
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
192 words
A method of improving non-volatile memory capabilities in thin film ferroelectric capacitors to provide more stable non-volatile memory operations in memory devices employing said thin film ferroelectric capacitors, said thin film ferroelectric capacitors comprising a bottom electrode, a top electrode, and a layer of ferroelectric material sandwiched therebetween, said ferroelectric material having a crystallization temperature and said layer of ferroelectric material and said top electrode forming an interface, said method comprising: (a) depositing said layer of ferroelectric material on said bottom electrode; (b) annealing said layer of ferroelectric material and said bottom electrode to crystallize said ferroelectric material; (c) depositing said top electrode on said layer of ferroelectric material, said top electrode comprising an electrically conductive material selected from the group consisting of platinum and conducting oxides; and (d) stabilizing said interface after forming said top electrode on said layer of ferroelectric material, said stabilizing being done by (1) annealing said ferroelectric capacitors at a temperature ranging from said crystallization temperature to a temperature less than that at which any metal-rich filament would form or (2) laser annealing said ferroelectric capacitors through said top electrode or (3) electron bombarding said ferroelectric capacitors.
Claim 2
Independent Claim
192 words
A method of improving non-volatile memory capabilities in thin film ferroelectric capacitors to provide more stable non-volatile memory operations in memory devices employing said thin film ferroelectric capacitors, said thin film ferroelectric capacitors comprising a bottom electrode, a top electrode, and a layer of ferroelectric material sandwiched therebetween, said ferroelectric material having a crystallization temperature and said layer of ferroelectric material and said top electrode forming an interface, said method comprising: (a) depositing said layer of ferroelectric material on said bottom electrode; (b) annealing said layer of ferroelectric material and said bottom electrode to crystallize said ferroelectric material; (c) depositing said top electrode on said layer of ferroelectric material, said top electrode comprising an electrically conductive material selected from the group consisting of platinum and conducting oxides; and (d) stabilizing said interface after forming said top electrode on said layer of ferroelectric material, said stabilizing being done by (1) annealing said ferroelectric capacitors at a temperature ranging from said crystallization temperature to a temperature less than that at which any metal-rich filament would form or (2) laser annealing said ferroelectric capacitors through said top electrode or (3) electron bombarding said ferroelectric capacitors.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein said ferroelectric material is a titanate composition having a perovskite structure.
Claim 4
Dependent Claim
13 words
The method of claim 2 wherein said ferroelectric material comprises lead zirconate titanate.
Claim 5
Dependent Claim
20 words
The method of claim 3 wherein said lead zirconate titanate has a thickness ranging from about 0.10 to 0.20 μm.
Claim 6
Dependent Claim
44 words
The method of claim 1 wherein said ferroelectric material comprises lead zirconate titanate and wherein said annealing of step (d)(1) is done at a temperature of about 550° C. to 600° C. for a period of time ranging from about 10 to 15 minutes.
Claim 7
Dependent Claim
17 words
The method of claim 5 wherein said annealing is done at a temperature of about 560° C.
Claim 8
Dependent Claim
31 words
The method of claim 1 wherein said ferroelectric material comprises lead zirconate titanate and wherein said laser annealing is done at a energy of about 20 to 40 μJ/cm 2 .
Claim 9
Dependent Claim
22 words
The method of claim 7 wherein said laser annealing is done at a energy of about 20 to 24 μJ/cm 2 .
Claim 10
Dependent Claim
23 words
The method of claim 1 wherein said stabilizing is done by electron bombardment of said ferroelectric thin film capacitors through said top electrode.
Claim 11
Dependent Claim
40 words
The method of claim 9 wherein said ferroelectric material comprises lead zirconate titanate and wherein said electron bombardment is done at a fluence of greater than about 10 13 electrons/cm 2 and less than about 10 14 electrons/cm 2 .
Claim 12
Dependent Claim
25 words
The method of claim 1 wherein said top electrode consists essentially of platinum having a thickness within the range of about 100 to 300 Å.
Claim 13
Independent Claim
146 words
A method of improving non-volatile memory capabilities in thin film ferroelectric capacitors to provide more stable non-volatile memory operations in memory devices employing said thin film ferroelectric capacitors, said thin film ferroelectric capacitors comprising a bottom electrode, a top electrode, and a layer of ferroelectric material comprising lead zirconate titanate sandwiched therebetween, said method comprising: (a) depositing said layer of ferroelectric material on said bottom electrode; (b) annealing said layer of ferroelectric material and said bottom electrode to crystallize said ferroelectric material; (c) depositing said top electrode on said layer of ferroelectric material, said top electrode consisting essentially of platinum having a thickness ranging from about 100 to 300 Å; and (d) annealing said thin film ferroelectric capacitor at a temperature ranging from about 550° to 600° C. for a period of time ranging from about 10 to 15 minutes, following deposition of said top electrode.
Claim 14
Independent Claim
146 words
A method of improving non-volatile memory capabilities in thin film ferroelectric capacitors to provide more stable non-volatile memory operations in memory devices employing said thin film ferroelectric capacitors, said thin film ferroelectric capacitors comprising a bottom electrode, a top electrode, and a layer of ferroelectric material comprising lead zirconate titanate sandwiched therebetween, said method comprising: (a) depositing said layer of ferroelectric material on said bottom electrode; (b) annealing said layer of ferroelectric material and said bottom electrode to crystallize said ferroelectric material; (c) depositing said top electrode on said layer of ferroelectric material, said top electrode consisting essentially of platinum having a thickness ranging from about 100 to 300 Å; and (d) annealing said thin film ferroelectric capacitor at a temperature ranging from about 550° to 600° C. for a period of time ranging from about 10 to 15 minutes, following deposition of said top electrode.
Claim 15
Dependent Claim
40 words
The method of claim 12 wherein said annealing of step (d) is accomplished by inserting said capacitors into a pre-heated air oven, maintaining said capacitors in said oven for said period of time, and extracting said capacitors from said oven.
Claim 16
Dependent Claim
20 words
The method of claim 12 wherein said lead zirconate titanate has a thickness ranging from about 0.10 to 0.20 μm.
References Cited (Backward Citations)
US4195355A
Cited
US4232094A
Cited
US4701592A
Cited
US5089426A
Cited
US4772985A
Cited
US4865923A
Cited
US5046043A
Cited
US5029128A
Cited
US5198269A
Cited
US5070026A
Cited
US5053917A
Cited
US5089932A
Cited
US5031144A
Cited
US5088002A
Cited
US5027253A
Cited
US5031143A
Cited
US5094977A
Cited
US5072329A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-12-12 | 1998-06-13 | 1998-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-12-12 | 2002-06-13 | 2002-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-12-12 | 2006-06-13 | 2006-12-13 | $7700.00 | Window Closed / Lapsed |