Thick film capacitor
Assignee: Toshiba Corp
•
Filing: 1987-09-18
•
Granted: 1988-09-20
•
Expires: 2007-09-18
Abstract
Abstract Disclosed is a thick film capacitor comprising (a) a sintered layer of a ferroelectric material mainly consisting of one or more ferroelectric inorganic compounds having a perovskite structure and an inorganic binder having a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of the ferroelectric inorganic compounds, and (b) at least two electrodes formed on both surfaces of the sintered layer of the ferroelectric material. In the thick film capacitor of this invention, the perovskite structure of the ferroelectric inorganic compounds is not destroyed upon sintering. Therefore, a high degree of sintering, a good dielectric characteristic and high moisture and migration resistances can be obtained.
Inventors
- 👤 Takaaki Yasumoto
- 👤 Osamu Furukawa
- 👤 Nobuo Iwase
- 👤 Mitsuo Harata
- 👤 Masao Segawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:04
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/495; C04B35/497; C04B35/499; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/129; H01G4/30; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
91 words
A thick film capacitor comprising: (a) a sintered layer of a ferroelectric material consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure and an inoranic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder having a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said at least one ferroelectric inorganic compound; and (b) at least one electrode formed on each surface of said sintered layer of the ferroelectric material.
Claim 2
Dependent Claim
91 words
A thick film capacitor comprising: (a) a sintered layer of a ferroelectric material consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure and an inoranic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder having a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said at least one ferroelectric inorganic compound; and (b) at least one electrode formed on each surface of said sintered layer of the ferroelectric material.
Claim 3
Dependent Claim
28 words
A capacitor according to claim 1, wherein said inorganic binder is present at grain boundaries of said ferroelectric inorganic compounds in said sintered layer of the ferroelectric material.
Claim 4
Dependent Claim
27 words
A capacitor according to claim 1, wherein said inorganic binder is diffused in crystals of said ferroelectric inorganic compounds in said sintered layer of the ferroelectric material.
Claim 5
Dependent Claim
31 words
A capacitor according to claim 1, wherein said inorganic binder is present at grain boundaries and in crystals of said ferroelectric inorganic compounds in said sintered layer of the ferroelectric material.
Claim 6
Dependent Claim
52 words
A capacitor according to claim 1, wherein said ferroelectric inorganic compounds are selected from the group consisting of the following compounds: Pb(Fe 1/2 Nb 1/2 )O 3 -Ba(Cu 1/2 W 1/2 )O 3 , BaTiO 3 , PbTiO 3 , and (Pb,Ba){(Zn 1/3 Nb 2/3 )(Mg 1/3 Nb 2/3 )Ti}O 3 .
Claim 7
Dependent Claim
60 words
A capacitor according to claim 1, wherein said inorganic binder is selected from the group consisting of the following eutectic compositions: PbO-CuO, PbO-WO 3 , PbO-Nb 2 O 5 , PbO-Fe 2 O 3 , PbO-ZnO, PbO-TiO 2 , PbO-CaO, PbO-Sb 2 O 3 , BaO-WO 3 , Nb 2 O 3 -TiO 2 , TiO 2 -MgO, and PbO-MgO.
Claim 8
Dependent Claim
28 words
A capacitor according to claim 6, wherein said inorganic binder is selected from the group consisting of compositions which are converted to eutectic compositions by oxidation during sintering.
Claim 9
Dependent Claim
44 words
A capacitor according to claim 1, wherein said sintered layer of the ferroelectric material comprises a central layer having a small content of said inorganic binder and layers formed on and under said central layer and having a large content of said inorganic binder.
Claim 10
Dependent Claim
121 words
A thick film capacitor comprising: (a) a first metal electrode layer formed on an insulating substrate; (b) a sintered layer of a ferroelectric material directly stacked on said first metal electrode layer and consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure and an inorganic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder hving a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said at least one ferroelectric inorganic compound; and (c) a second metal electrode layer directly formed on said sintered layer of a ferroelectric material sandwiched between said insulating substrate and said first metal electrode layer.
Claim 11
Dependent Claim
121 words
A thick film capacitor comprising: (a) a first metal electrode layer formed on an insulating substrate; (b) a sintered layer of a ferroelectric material directly stacked on said first metal electrode layer and consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure and an inorganic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder hving a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said at least one ferroelectric inorganic compound; and (c) a second metal electrode layer directly formed on said sintered layer of a ferroelectric material sandwiched between said insulating substrate and said first metal electrode layer.
Claim 12
Dependent Claim
26 words
A capacitor according to claim 9, further comprising a sintered layer of a ferroelectric material sandwiched between said insulating substrate and said first metal electrode layer.
Claim 13
Dependent Claim
125 words
A thick film capacitor comprising: (a) a first metal electrode layer formed on an insulating substrate; (b) a sintered layer of a ferroelectric material directly stacked on said first metal electrode layer and consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure and an inorganic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder having a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said at least one ferroelectric inorganic compound; and (c) a second metal electrode layer directly formed on said sintered layer of the ferroelectric material, and wherein said thick film capacitor is cut into a tip having a desired size.
Claim 14
Dependent Claim
125 words
A thick film capacitor comprising: (a) a first metal electrode layer formed on an insulating substrate; (b) a sintered layer of a ferroelectric material directly stacked on said first metal electrode layer and consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure and an inorganic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder having a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said at least one ferroelectric inorganic compound; and (c) a second metal electrode layer directly formed on said sintered layer of the ferroelectric material, and wherein said thick film capacitor is cut into a tip having a desired size.
Claim 15
Dependent Claim
35 words
A capacitor according to claim 11, wherein at least one multilayered structure consisting of said sintered layer of the ferroelectric material and said second metal electrode layer is stacked on said second metal electrode layer.
Claim 16
Dependent Claim
26 words
A capacitor according to claim 11, further comprising a sintered layer of a ferroelectric material sandwiched between said insulating substrate and said first metal electrode layer.
Claim 17
Dependent Claim
135 words
A thick film capacitor manufactured by the process comprising the steps of: (a) forming a first metal paste layer on an insulating substrate; (b) stacking on said first metal paste layer a ferroelectric paste layer consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure, an inorganic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder having a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said ferroelectric compound, at least one organic binder and a solvent; (c) forming a second metal paste layer directly stacked on said ferroelectric paste layer; and (d) sintering the laminate formed at steps (a) to (c) at a temperature lower than the sintering temperature of said ferroelectric compound.
Claim 18
Dependent Claim
135 words
A thick film capacitor manufactured by the process comprising the steps of: (a) forming a first metal paste layer on an insulating substrate; (b) stacking on said first metal paste layer a ferroelectric paste layer consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure, an inorganic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder having a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said ferroelectric compound, at least one organic binder and a solvent; (c) forming a second metal paste layer directly stacked on said ferroelectric paste layer; and (d) sintering the laminate formed at steps (a) to (c) at a temperature lower than the sintering temperature of said ferroelectric compound.
Claim 19
Dependent Claim
141 words
A thick film capacitor manufactured by the process comprising the steps of: (a) forming a first metal paste layer on an insulating substrate; (b) stacking on said first metal paste layer a ferroelectric paste layer consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure, an inorganic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder having a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said ferroelectric compound, at least one organic binder and a solvent; (c) forming a second metal paste layer directly stacked on said ferroelectric paste layer; (d) sintering the laminate formed at steps (a) to (c) at a temperature lower than the sintering temperature of said ferroelectric compound, and (e) performing aging at high temperatures.
Claim 20
Dependent Claim
141 words
A thick film capacitor manufactured by the process comprising the steps of: (a) forming a first metal paste layer on an insulating substrate; (b) stacking on said first metal paste layer a ferroelectric paste layer consisting essentially of at least one ferroelectric inorganic compound having a perovskite structure, an inorganic binder for sintering said at least one ferroelectric inorganic compound without destroying the perovskite structure thereof, said inorganic binder having a eutectic composition which experiences a liquid phase at a temperature lower than the sintering temperature of said ferroelectric compound, at least one organic binder and a solvent; (c) forming a second metal paste layer directly stacked on said ferroelectric paste layer; (d) sintering the laminate formed at steps (a) to (c) at a temperature lower than the sintering temperature of said ferroelectric compound, and (e) performing aging at high temperatures.
References Cited (Backward Citations)
US3157835A
Cited
US3305394A
Cited
US3591504A
Cited
US3600652A
Cited
JPS5514665A
Cited
US4392180A
Cited
US4625258A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-20 | 1992-03-21 | 1992-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-20 | 1996-03-21 | 1996-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-20 | 2000-03-21 | 2000-09-20 | $7700.00 | Window Closed / Lapsed |