Method of nucleating tungsten on titanium nitride by CVD without silane
Assignee: Tokyo Electron Ltd
•
Filing: 1992-06-15
•
Granted: 1994-08-30
•
Expires: 2012-06-15
Abstract
Abstract Nucleation of a refractory metal such as tungsten is initiated on a substrate of TiN without the use of silane by introducing hydrogen into a CVD reactor before the introduction of the reactant gas containing the metal, brought to reaction temperature and to reaction pressure. The process is most useful for CVD of tungsten onto patterned TiN coated silicon semiconductor wafers. Alternatively, hydrogen is introduced in a mixture with the metal containing gas, such as WF 6 , and maintained at subreaction pressure, of for example 100 mTorr, until the substrate is stabilized at a reaction temperature of approximately 400° C. or higher, to cause the dissociation of hydrogen on the wafer surface, then elevated to a relatively high reaction pressure of, for example, 60 Torr at which nucleation is achieved. Also, the reduction reaction that deposits the tungsten film proceeds without the need for a two step nucleation-deposition process.
Inventors
- 👤 Robert F. Foster
- 👤 Damodaran Srinivas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:03
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/40; H10P14/42; H10P14/43; C; C23; C23C; C23C16/00; C23C16/02; C23C16/0209; C23C16/0218; C23C16/04; C23C16/06; C23C16/08; C23C16/14
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
98 words
A method of nucleating tungsten in a tungsten CVD process performed in a vacuum chamber without the use of silane to deposit elemental tungsten onto a substrate, the method comprising the steps of: injecting hydrogen into the chamber and bringing the chamber to a pressure and temperature sufficient to produce a hydrogen dissociation reaction at the substrate before the introduction of WF 6 into the chamber; and then injecting WF 6 into the chamber in a ratio with H 2 and at a pressure and temperature to produce a reduction reaction resulting in tungsten deposition onto the substrate.
Claim 2
Independent Claim
98 words
A method of nucleating tungsten in a tungsten CVD process performed in a vacuum chamber without the use of silane to deposit elemental tungsten onto a substrate, the method comprising the steps of: injecting hydrogen into the chamber and bringing the chamber to a pressure and temperature sufficient to produce a hydrogen dissociation reaction at the substrate before the introduction of WF 6 into the chamber; and then injecting WF 6 into the chamber in a ratio with H 2 and at a pressure and temperature to produce a reduction reaction resulting in tungsten deposition onto the substrate.
Claim 3
Dependent Claim
37 words
The method of claim 1 wherein: the hydrogen is injected into the chamber and brought to a pressure and temperature sufficient to produce a WF 6 reduction reaction before the introduction of WF 6 into the chamber.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein: the reaction pressure is above approximately 3 Torr.
Claim 5
Dependent Claim
14 words
The method of claim 1 wherein: the reaction pressure is above approximately 50 Torr.
Claim 6
Dependent Claim
14 words
The method of claim 1 wherein: the reaction temperature is above approximately 400° C.
Claim 7
Dependent Claim
16 words
The method of claim 1 wherein: the substrate has a surface film thereon formed of TiN.
Claim 8
Independent Claim
106 words
A method of nucleating tungsten in a tungsten CVD process performed in a vacuum chamber without the use of silane to deposit elemental tungsten onto a substrate, the method comprising the steps of: injecting a gas mixture of hydrogen and WF 6 into the chamber and maintaining the chamber at a subreaction pressure below that for a WF 6 reduction reaction at the temperature of the substrate; and before increasing the pressure from the subreaction pressure, maintaining the temperature of the substrate at least at that for the dissociation of hydrogen; and then increasing the pressure in the chamber to a WF 6 reduction reaction pressure.
Claim 9
Independent Claim
106 words
A method of nucleating tungsten in a tungsten CVD process performed in a vacuum chamber without the use of silane to deposit elemental tungsten onto a substrate, the method comprising the steps of: injecting a gas mixture of hydrogen and WF 6 into the chamber and maintaining the chamber at a subreaction pressure below that for a WF 6 reduction reaction at the temperature of the substrate; and before increasing the pressure from the subreaction pressure, maintaining the temperature of the substrate at least at that for the dissociation of hydrogen; and then increasing the pressure in the chamber to a WF 6 reduction reaction pressure.
Claim 10
Dependent Claim
14 words
The method of claim 7 wherein: the subreaction pressure is below approximately 1 Torr.
Claim 11
Dependent Claim
14 words
The method of claim 7 wherein: the reaction pressure is above approximately 3 Torr.
Claim 12
Dependent Claim
14 words
The method of claim 7 wherein: the reaction pressure is above approximately 50 Torr.
Claim 13
Dependent Claim
14 words
The method of claim 7 wherein: the maintained temperature is above approximately 400° C.
Claim 14
Dependent Claim
16 words
The method of claim 7 wherein: the substrate has a surface film thereon formed of TiN.
Claim 15
Independent Claim
117 words
A method of nucleating tungsten in a CVD process performed by reduction of WF 6 in a vacuum chamber without the use of silane to deposit a metal onto a substrate, the method comprising the steps of: injecting a gas including hydrogen into the chamber; injecting a gas including WF 6 into the chamber with or following the introduction of hydrogen into the chamber; elevating the pressure of the gas within the chamber from a subreaction pressure to at least a minimum reaction pressure; elevating the temperature of the substrate and the gases within the chamber to at least a minimum reaction temperature before WF 6 gas within the chamber is raised to the minimum reaction pressure.
Claim 16
Independent Claim
117 words
A method of nucleating tungsten in a CVD process performed by reduction of WF 6 in a vacuum chamber without the use of silane to deposit a metal onto a substrate, the method comprising the steps of: injecting a gas including hydrogen into the chamber; injecting a gas including WF 6 into the chamber with or following the introduction of hydrogen into the chamber; elevating the pressure of the gas within the chamber from a subreaction pressure to at least a minimum reaction pressure; elevating the temperature of the substrate and the gases within the chamber to at least a minimum reaction temperature before WF 6 gas within the chamber is raised to the minimum reaction pressure.
Claim 17
Dependent Claim
31 words
The method of claim 13 wherein: the substrate has a surface formed of material selected from the group consisting of CVD TiN, reactively sputtered TiN, or rapid thermal process formed TiN.
Claim 18
Dependent Claim
14 words
The method of claim 13 wherein: the reaction pressure is above approximately 50 Torr.
Claim 19
Dependent Claim
14 words
The method of claim 13 wherein: the reaction temperature is above approximately 400° C.
Claim 20
Dependent Claim
37 words
The method of claim 13 wherein: WF 6 gas within the reaction chamber, prior to the elevation of the substrate temperature to the reaction temperature, is maintained at a pressure of not more than approximately 1 Torr.
Claim 21
Dependent Claim
61 words
The method of claim 13 wherein: from prior to introduction of the H 2 and WF 6 gases until after completion of a tungsten deposition process on the wafer, the wafer is rotated about its center at a speed sufficient to thin a boundary layer across the wafer and to facilitate the transfer of mass between the gases and the wafer.
Claim 22
Dependent Claim
70 words
The method of claim 13 further comprising the preliminary steps of: depositing a TiN film on the wafer in a first vacuum processing chamber of a wafer processing apparatus; transferring the wafer having the TiN film thereon to a second vacuum processing chamber of a wafer processing apparatus; and performing the gas injecting steps, pressure elevating step and temperature elevating step on the wafer in the second vacuum processing chamber.
Claim 23
Dependent Claim
72 words
The method of claim 19 wherein: the first and second chambers are connected in the same wafer processing apparatus having a wafer transfer path therebetween containing inert gas maintained at a vacuum pressure level; the step of transferring the wafer is performed with the wafer maintained in the inert gas at the vacuum pressure level while from the first to the second chamber without exposure of the wafer to an external environment.
References Cited (Backward Citations)
US4404235A
Cited
US4650698A
Cited
US4851295A
Cited
US4629635A
Cited
US4650696A
Cited
US4684542A
Cited
JPS6365075A
Cited
US4830891A
Cited
US4874642A
Cited
US4892843A
Cited
EP0371854A2
Cited
EP0411646A1
Cited
WO1993011558A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-29 | 1998-02-28 | 1998-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-29 | 2002-02-28 | 2002-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-29 | 2006-02-28 | 2006-08-30 | $7700.00 | Window Closed / Lapsed |