Process using tungsten for multilevel metallization
Assignee: Intersil Corp
•
Filing: 1985-10-01
•
Granted: 1987-03-17
•
Expires: 2005-10-01
Abstract
Abstract A process is provided for making semiconductor devices with refractory metal metallization layers in place of aluminum metallization layers. An insulative layer is deposited onto a silicon substrate and a pattern is formed in the insulative layer. Prior to deposition of the metallization layer onto the patterned insulative layer, a layer of polycrystalline silicon is deposited onto the patterned insulative layer by means of a low pressure chemical vapor deposition process. The polycrystalline silicon is deposited to a thickness of preferably 700-800 Angstroms. After deposition of the polycrystalline silicon layer, refractory metal is deposited by means of a low pressure chemical vapor deposition process. Preferably, the refractory metal is deposited to a thickness of one micrometer at a temperature of 300°-600° C. depending on the desired deposition rate. The refractory metal vapor deposition process etches away 300-400 Angstroms of the polysilicon layer, thereby leaving 300-400 Angstroms of polysilicon for the purpose of adhering the insulative layer to the refractory metal layer. The composite is then heat treated to reduce the vertical resistivity due to the pressure of the high resistance polycrystalline silicon layer.
Inventors
- 👤 Joseph S. Raby
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:25
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0113; H10P; H10P14/00; H10P14/40; H10P14/412; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/056; H10W20/064; H10W20/066
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
91 words
A process for adhering a metallization layer to a patterned insulative layer in a semiconductor device comprising: vapor depositing a 500 Angstrom to 1000 Angstrom thick layer of polycrystalline silicon onto said insulative layer, vapor depositing a pure refractory metal layer onto said polycrystalline silicon layer from an atmosphere conducive to depositing said refractory metal layer as a pure layer and at a deposition temperature conducive to maintenance of at least a portion of said polycrystalline silicon layer sufficient to cause said refractory metal layer to adhere to said insulative layer.
Claim 2
Dependent Claim
91 words
A process for adhering a metallization layer to a patterned insulative layer in a semiconductor device comprising: vapor depositing a 500 Angstrom to 1000 Angstrom thick layer of polycrystalline silicon onto said insulative layer, vapor depositing a pure refractory metal layer onto said polycrystalline silicon layer from an atmosphere conducive to depositing said refractory metal layer as a pure layer and at a deposition temperature conducive to maintenance of at least a portion of said polycrystalline silicon layer sufficient to cause said refractory metal layer to adhere to said insulative layer.
Claim 3
Dependent Claim
39 words
A process according to claim 1, wherein said refractory metal layer is initially deposited at a deposition temperature of less than about 500° C. and wherein initially said deposition temperature is thereafter increased to between 500° and 600° C.
Claim 4
Dependent Claim
15 words
A process according to claim 2, wherein said deposition temperature is initially about 300° C.
Claim 5
Dependent Claim
21 words
A process according to claim 3, wherein said polycrystalline silicon layer is deposited at a deposition temperature of about 640° C.
Claim 6
Dependent Claim
31 words
A process according to claim 3, wherein said semiconductor device is heat treated at a temperature of between about 650° C. and 700° C. after deposition of said refractory metal layer.
Claim 7
Dependent Claim
80 words
A process for adhering a metallization layer to an insulative layer in a semiconductor device comprising: vapor depositing polycrystalline silicon onto said insulative surface to form a polysilicon adhesive layer, vapor depositing a refractory metal layer onto said polysilicon adhesive layer, thereby forming a laminate, and heat treating said laminate to cause said refractory metal to migrate along polycrystalline silicon grain boundaries, said migration causing a reduction in vertical resistance of said semiconductor device and without forming substantial metal silicide.
Claim 8
Dependent Claim
80 words
A process for adhering a metallization layer to an insulative layer in a semiconductor device comprising: vapor depositing polycrystalline silicon onto said insulative surface to form a polysilicon adhesive layer, vapor depositing a refractory metal layer onto said polysilicon adhesive layer, thereby forming a laminate, and heat treating said laminate to cause said refractory metal to migrate along polycrystalline silicon grain boundaries, said migration causing a reduction in vertical resistance of said semiconductor device and without forming substantial metal silicide.
Claim 9
Dependent Claim
21 words
A process according to claim 6, wherein said polysilicon layer is deposited to a thickness of between 500 and 1000 Angstroms.
Claim 10
Dependent Claim
22 words
A process according to claim 7, wherein said polycrystalline silicon layer is deposited to a thickness of between 700 and 800 Angstroms.
Claim 11
Dependent Claim
20 words
A process according to claim 6, wherein said refractory metal is selected from the group consisting of tungsten and molybdenum.
Claim 12
Dependent Claim
13 words
A process according to claim 9, wherein said refractory metal is tungsten .
Claim 13
Dependent Claim
19 words
A process according to claim 10, wherein said refractory metal layer is deposited to a thickness of 1 micron.
Claim 14
Dependent Claim
25 words
A process according to claim 6, wherein said polycrystalline silicon and metallization layers are heat treated at a temperature of less than about 700° C.
Claim 15
Dependent Claim
25 words
A process according to claim 12, wherein said polycrystalline silicon and metallization layers are heated at a temperature of about 650° C. to 700° C.
Claim 16
Dependent Claim
16 words
A process according to claim 13, wherein said heat treatment is applied for about one hour.
Claim 17
Dependent Claim
23 words
A process according to claim 6. wherein an additional layer of polycrystalline silicon is deposited onto said metal layer after said heat treating.
Claim 18
Dependent Claim
24 words
A process according to claim 6, wherein said insulative layer comprises a material selected from the group consisting of silicon dioxide and silicon nitride.
Claim 19
Dependent Claim
24 words
A process according to claim 6, wherein said polycrystalline and refractory metal layers are vapor deposited by a low pressure chemical vapor deposition process.
Claim 20
Dependent Claim
23 words
A process to claim 10, wherein said polycrystalline and refractory metal layers are vapor deposited by a low pressure chemical vapor deposition process.
Claim 21
Dependent Claim
100 words
A process for adhering a metallization layer to a patterned insulative layer in a semiconductor device comprising: vapor depositing a 500 Angstrom to 1000 Angstrom thick layer of polycrystalline silicon onto said insulative layer, and vapor depositing a layer of pure refractory metal onto said polycrystalline silicon layer, said pure refractory metal being vapored deposited from an atomsphere containing hydrogen gas and a hexaflouride compound of said refractory metal and at a deposition temperature conducive to maintenance of at least a portion of said polycrystalline silicon layer sufficient to cause said refractory metal layer to adhere to said insulative layer.
Claim 22
Dependent Claim
100 words
A process for adhering a metallization layer to a patterned insulative layer in a semiconductor device comprising: vapor depositing a 500 Angstrom to 1000 Angstrom thick layer of polycrystalline silicon onto said insulative layer, and vapor depositing a layer of pure refractory metal onto said polycrystalline silicon layer, said pure refractory metal being vapored deposited from an atomsphere containing hydrogen gas and a hexaflouride compound of said refractory metal and at a deposition temperature conducive to maintenance of at least a portion of said polycrystalline silicon layer sufficient to cause said refractory metal layer to adhere to said insulative layer.
Claim 23
Dependent Claim
36 words
A process according to claim 19, wherein said laminate is heat-treated to cause said refractory metal to migrate along polycrystalline and silicon grain boundaries, said migration causing a reduction in vertical resistance of said semicondutor device.
Claim 24
Dependent Claim
33 words
A process according to claim 20, wherein said vapor depositing of said polycrystalline silicon layer and said refractory metal layer and said heat treating are conducted at temperatures of less than 700° C.
Claim 25
Dependent Claim
43 words
A process according to claim 19, wherein said refractory metal is initially deposited at a deposition temperature of about 300° C., said deposition temperature being gradually increased to about 600° C., said heat treating minimizing depletion of silicon from said polycrystalline silicon layer.
Claim 26
Dependent Claim
44 words
A process according to claim 22, wherein said deposition temperature is reduced to about 300° C. after said heat treating at about 600° C. and prior to exposure of said semiconductor device to an oxidizing atmosphere, thereby preventing oxidation of said refractory metal layer.
References Cited (Backward Citations)
US3477872A
Cited
US3669724A
Cited
US3785862A
Cited
US3881242A
Cited
US4152823A
Cited
US4356622A
Cited
US4425700A
Cited
US4392299A
Cited
US4404235A
Cited
US4349408A
Cited
US4441247A
Cited
EP0077535A1
Cited
US4517225A
Cited
US4584207A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-16 | 1990-09-15 | 1991-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-16 | 1994-09-15 | 1995-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-16 | 1998-09-15 | 1999-03-17 | $7700.00 | Window Closed / Lapsed |