Method of depositing a refractory metal on a semiconductor substrate
Assignee: Intersil Corp
•
Filing: 1981-03-26
•
Granted: 1982-09-14
•
Expires: 2001-03-26
Abstract
Abstract A method for depositing a refractory on a semiconductor substrate passivated with silicon dioxide and/or oxygen doped polycrystalline silicon is disclosed. The usual undercutting of the oxygen doped polycrystalline silicon or of the silicon substrate at the edge where it meets the oxide is prevented by depositing a layer of phosphorus doped polycrystalline silicon over the passivation material before the metal is deposited.
Inventors
- 👤 Ming L. Tarng
- 👤 Walter A. Hicinbothem, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:25
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/012; H10D64/0121; H10P; H10P50/00; H10P50/60; H10P50/66; H10P50/663; H10P50/667; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/081; H10W20/082; Y; Y10; Y10S; Y10S438/00; Y10S438/909
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
134 words
A method of depositing a refractory metal on a silicon substrate, said method comprising: depositing an oxygen doped polycrystalline silicon layer on one surface of said substrate; depositing a phosphorus doped polycrystalline silicon layer on the outer surface of said oxygen doped polycrystalline silicon layer, said phosphorous doped polycrystalline silicon layer having a phosphorous concentration of at least about 10 19 atoms/cm 3 ; etching windows in said layers to expose said surface of said substrate in the areas where said refractory metal is to be deposited; and, heating said substrate to a temperature in a range of between about 500° C. to about 800° C. and then exposing said substrate to a gaseous refractory metal hexafluoride wherein the refractory metal of said hexafluoride is selected from the group consisting of tungsten and molybdenum.
Claim 2
Independent Claim
134 words
A method of depositing a refractory metal on a silicon substrate, said method comprising: depositing an oxygen doped polycrystalline silicon layer on one surface of said substrate; depositing a phosphorus doped polycrystalline silicon layer on the outer surface of said oxygen doped polycrystalline silicon layer, said phosphorous doped polycrystalline silicon layer having a phosphorous concentration of at least about 10 19 atoms/cm 3 ; etching windows in said layers to expose said surface of said substrate in the areas where said refractory metal is to be deposited; and, heating said substrate to a temperature in a range of between about 500° C. to about 800° C. and then exposing said substrate to a gaseous refractory metal hexafluoride wherein the refractory metal of said hexafluoride is selected from the group consisting of tungsten and molybdenum.
Claim 3
Dependent Claim
25 words
A method in accordance with claim 1 wherein a layer of oxide is grown on the outer surface of said phosphorus doped polycrystalline silicon layer.
Claim 4
Dependent Claim
22 words
A method in accordance with claim 1 wherein a corrosion resistant film is deposited on the outer surface of said refractory metal.
Claim 5
Dependent Claim
24 words
A method in accordance with claim 1 wherein said oxygen doped polycrystalline layer contains oxygen in the range of 2 to 45 atomic percent.
Claim 6
Dependent Claim
44 words
A method in accordance with claim 1 wherein the oxygen doped polycrystalline silicon layer and the phosphorus doped polycrystalline silicon layer are annealed at the same time an oxide layer is thermally grown on the outer surface of said phosphorus doped polycrystalline silicon layer.
Claim 7
Dependent Claim
84 words
A method in accordance with claim 1 wherein the substrate is heated to a temperature of at least about 700° C. to maintain the reaction between said hexafluoride and the silicon until about 500 Angstroms to about 2,000 Angstroms of metal is deposited, thereafter, lowering the temperature of said substrate to a temperature in a range of between about 500° C. to about 650° C. and exposing said substrate to a mixture of hexafluoride and hydrogen whereby additional metal is deposited on said substrate.
Claim 8
Dependent Claim
19 words
A method in accordance with claim 6 wherein the ratio of hydrogen to hexafluoride is at least about 10:1.
Claim 9
Dependent Claim
71 words
A method in accordance with claim 1 wherein a phosphosilicate glass layer is grown over said phosphorus doped polycrystalline silicon layer before said refractory metal is deposited, said refractory metal being deposited by a chemical vapor deposition technique whereby the refractory metal does not form on said phosphosilicate glass and wherein a corrosion resistant metal layer is deposited over said refractory metal and an adjacent portion of said phosphosilicate glass layer.
References Cited (Backward Citations)
US3785862A
Cited
US3945030A
Cited
US3906540A
Cited
US3892606A
Cited
US4062033A
Cited
US4086613A
Cited
US4085498A
Cited
US4119992A
Cited
SU711167A1
Cited
US4282647A
Cited
JPS5595339A
Cited
US4297149A
Cited
US4322453A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-09-13 | 1986-03-15 | 1986-09-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-09-13 | 1990-03-15 | 1990-09-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-09-13 | 1994-03-15 | 1994-09-14 | $7700.00 | Window Closed / Lapsed |