US4684542A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Low pressure chemical vapor deposition of tungsten silicide
Assignee: International Business Machines Corp
•
Filing: 1986-08-11
•
Granted: 1987-08-04
•
Expires: 2006-08-11
Abstract
Abstract A process for preparing tungsten silicide films using low pressure, low temperature chemical vapor deposition to deposit silicon-rich tungsten silicide films. As a source of silicon, higher order silanes, such as disilane and trisilane, are used. The gaseous tungsten source is WF 6 . The substrate temperature range is less than about 370° C., while the total pressure range is in the range 0.05-1 Torr. WF 6 flow rates are generally less than 25 sccm, while the higher order silane flow rates are generally less than about 400 sccm.
Inventors
- 👤 Joseph M. Jasinski
- 👤 Bernard S. Meyerson
- 👤 Bruce A. Scott
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:24
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/42; H; H10; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/01312
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
124 words
A method for depositing silicon-rich tungsten silicide films on a substrate, said method including the steps of: introducing WF 6 gas and a higher order silane gas given by the formula Si.sub.n H.sub.2n+2, where n=2, 3, . . . into a cold wall, hot susceptor CVD reactor with the substrate located on said susceptor, establishing a substrate temperature less than about 370° C. and a total system pressure less than 1 Torr, the flow rate of said WF 6 being less than about 25 sccm while the flow rate of said higher order silane is less than about 500 sccm, and reacting said higher order silane and said WF 6 at said substrate to deposit a silicon-rich film of tungsten silicide on said substrate.
Claim 2
Independent Claim
124 words
A method for depositing silicon-rich tungsten silicide films on a substrate, said method including the steps of: introducing WF 6 gas and a higher order silane gas given by the formula Si.sub.n H.sub.2n+2, where n=2, 3, . . . into a cold wall, hot susceptor CVD reactor with the substrate located on said susceptor, establishing a substrate temperature less than about 370° C. and a total system pressure less than 1 Torr, the flow rate of said WF 6 being less than about 25 sccm while the flow rate of said higher order silane is less than about 500 sccm, and reacting said higher order silane and said WF 6 at said substrate to deposit a silicon-rich film of tungsten silicide on said substrate.
Claim 3
Dependent Claim
37 words
The method of claim 1, where said substrate temperature is in the range of about 200°-300° C., said higher order silane flow is less than 400 sccm, and said total pressures is in the range 50-500 mTorr.
Claim 4
Dependent Claim
11 words
The method of claim 1, where substrate is comprised of silicon.
Claim 5
Dependent Claim
24 words
The method of claim 1, including the further step of annealing said silicon-rich tungsten silicide film to crystallize said film to WSi 2 .
Claim 6
Dependent Claim
16 words
The method of claim 1, where said higher order silane is Si 2 H 6 .
Claim 7
Independent Claim
145 words
A method for the formation of WSi 2 on a substrate including a semiconductor device, including the steps of: placing said substrate in a cold wall, hot susceptor CVD apparatus, introducing WF 6 gas and a higher order silane gas into said apparatus, said higher order silane gas being given by the formula Si.sub.n H.sub.2n+2 where n=2, 3, . . . , establishing a substrate temperature in the range of about 200°-300° C. and a total system pressure less than about 500 mTorr, the flow rate of said WF 6 being less than about 25 sccm and the flow rate of said higher order silane being less than about 400 sccm, reacting said higher order silane and said WF 6 at said substrate to deposit a silicon-rich tungsten silicide film thereon, and annealing said tungsten silicide film to crystallize said film to WSi 2 .
Claim 8
Independent Claim
145 words
A method for the formation of WSi 2 on a substrate including a semiconductor device, including the steps of: placing said substrate in a cold wall, hot susceptor CVD apparatus, introducing WF 6 gas and a higher order silane gas into said apparatus, said higher order silane gas being given by the formula Si.sub.n H.sub.2n+2 where n=2, 3, . . . , establishing a substrate temperature in the range of about 200°-300° C. and a total system pressure less than about 500 mTorr, the flow rate of said WF 6 being less than about 25 sccm and the flow rate of said higher order silane being less than about 400 sccm, reacting said higher order silane and said WF 6 at said substrate to deposit a silicon-rich tungsten silicide film thereon, and annealing said tungsten silicide film to crystallize said film to WSi 2 .
Claim 9
Dependent Claim
12 words
The method of claim 6, where said substrate is comprised of Si.
Claim 10
Dependent Claim
16 words
The method of claim 7, where said higher order silane is Si 2 H 6 .
References Cited (Backward Citations)
US4218291A
Cited
JPS587821A
Cited
US4359490A
Cited
US4501769A
Cited
US4565157A
Cited
US4629635A
Cited
US4504521A
Cited
US4608271A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-03 | 1991-02-02 | 1991-08-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-03 | 1995-02-02 | 1995-08-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-03 | 1999-02-02 | 1999-08-04 | $7700.00 | Window Closed / Lapsed |