Method for the manufacture of metal silicide layers by means of reduced pressure gas phase deposition
Assignee: Siemens AG
•
Filing: 1985-03-22
•
Granted: 1986-08-26
•
Expires: 2005-03-22
Abstract
Abstract A method for the deposition of a silicide layer of a high melting metal onto a substrate of silicon or silicon dioxide wherein reaction gases consisting of a decomposable silicon-containing hydrogen compound, or a halogenated silane and a metal halide are pyrolytically decomposed in a reaction zone to form a reaction mixture from which a metal silicide is deposited on the substrate at reduced pressures. During the decomposition of the gases and deposition of the metal silicide, the gas pressure in the reaction zone is maintained between 1.3×10 -3 to 5×10 -2 mbar. This type of pressure is most conveniently maintained by means of a turbomolecular pump.
Inventors
- 👤 Konrad Hieber
- 👤 Manfred Stolz
- 👤 Claudia Wieczorek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 02:13
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/42; C23C16/44; C23C16/455; H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
103 words
A method for the deposition of a silicide layer of a high melting metal onto a substrate of silicon and/or silicon dioxide which comprises: pyrolytically decomposing gases including a decomposable silicon containing hydrogen compound, or a halogenated silane, and a metal halide to form a reaction mixture in a reaction zone, depositing a metal silicide from said reaction mixture from the gas phase at reduced pressure, and during the decomposition of the gases and deposition of the metal silicide, maintaining the gas pressure in the reaction zone in the range between 1.3×10 -3 to 5×10 -2 mbar by means of a turbomolecular pump.
Claim 2
Independent Claim
103 words
A method for the deposition of a silicide layer of a high melting metal onto a substrate of silicon and/or silicon dioxide which comprises: pyrolytically decomposing gases including a decomposable silicon containing hydrogen compound, or a halogenated silane, and a metal halide to form a reaction mixture in a reaction zone, depositing a metal silicide from said reaction mixture from the gas phase at reduced pressure, and during the decomposition of the gases and deposition of the metal silicide, maintaining the gas pressure in the reaction zone in the range between 1.3×10 -3 to 5×10 -2 mbar by means of a turbomolecular pump.
Claim 3
Dependent Claim
22 words
A method according to claim 1 wherein said gas pressure is maintained in the range between 2×10 -3 and 4×10 -2 mbar.
Claim 4
Dependent Claim
27 words
Use of the method of claim 1 for the manufacture of disilicide layers of tantalum, titanium, tungsten, molybdenum, or niobium as metallization layers for integrated semiconductor circuits.
Claim 5
Dependent Claim
29 words
A method according to claim 1 which includes the step of: rinsing the bearings of said turbomolecular pump with an inert gas during pumping and utilizing a corrosion-protected rotor.
Claim 6
Dependent Claim
45 words
A method according to claim 1 which includes the step of: conducting said decomposition and deposition at a pressure in excess of 3×10 -2 mbar and throttling the suction power of said turbomolecular pump while operating at such pressure to generate the necessary pressure gradient.
Claim 7
Dependent Claim
30 words
A method according to claim 1 wherein said silicon compound is silicochloroform (SiHCl 3 ) or silicon tetrachloride (SiCl 4 ) and supplying to said reaction zone plasma-activated atomic hydrogen.
Claim 8
Dependent Claim
24 words
A method according to claim 1 wherein said metal halide is transported into said reaction zone by means of hydrogen or a hydrogen-containing gas.
Claim 9
Dependent Claim
19 words
A method according to claim 7 wherein said hydrogen-containing gas is a mixture of hydrogen and an inert gas.
Claim 10
Dependent Claim
13 words
A method according to claim 1 wherein said metal halide is tantalum pentachloride.
References Cited (Backward Citations)
US4359490A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-25 | 1990-02-24 | 1990-08-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-25 | 1994-02-24 | 1994-08-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-25 | 1998-02-24 | 1998-08-26 | $7700.00 | Window Closed / Lapsed |