Polymer mixture having aromatic polycarbonate, polyester and thermoplastic elastomer, article formed therefrom

Claim 2

A polymer mixture which comprises 40-80 parts by weight of an aromatic polycarbonate (A), 10-50 parts by weight of a polyester built up entirely or substantially from units derived from an alkanediol and a benzene dicarboxylic acid (B), and 1-10 parts by weight of a thermoplastic elastomer (C), calculated per 100 parts by weight of A+B+C, characterized in that the thermoplastic elastomer (C) is built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is a polyfunctional group having at most 30 carbon atoms and p has a value of 2 or 3, and in which the polyester units are built up from blocks having a number of ester units of the formula --OGOC(O)R 2 C(O)--and blocks having a number of ester units which are capable of forming a bifunctional polyester or polyester amide having a melting-point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at least 80 mol % of the G-groups being a tetra methylene group.

Claim 3

A polymer mixture claimed in claim 1, characterised in that the polymer mixture comprises in addition one or more conventionally used additives.

Claim 4

A polymer mixture as claimed in claim 2, chacterised in that the polymer mixture comprises in addition an agent to improve the impact strength.

Claim 5

Articles formed from the polymer mixture as claimed in claim 1.

Claim 6

A polymer mixture which comprises 67-75 parts by weight of an aromatic polycarbonate (A), 10-20 parts by weight of a polyester built up entirely or substantially from units derived from an alkanediol and benzene dicarboxylic acid (B), and 1-10 parts by weight of a thermoplastic elastomer (C), calculated per 100 parts by weight of A+B+C, characterized in that the thermoplastic elastomer (C) is built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is a polyfunctional group having at most 30 carbon atoms and p has a value of 2 or 3, and in which the polyester units are built up from blocks having a number of ester units in the formula --OGOC(O)R 2 C(O)--and blocks having a number of ester units which are capable of forming a bifunctional polyester or polyester amide having a melting-point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at least 80 mol % of the G-groups being a tetra methylene group.

Claim 7

A polymer mixture which comprises 67-75 parts by weight of an aromatic polycarbonate (A), 10-20 parts by weight of a polyester built up entirely or substantially from units derived from an alkanediol and benzene dicarboxylic acid (B), and 1-10 parts by weight of a thermoplastic elastomer (C), calculated per 100 parts by weight of A+B+C, characterized in that the thermoplastic elastomer (C) is built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is a polyfunctional group having at most 30 carbon atoms and p has a value of 2 or 3, and in which the polyester units are built up from blocks having a number of ester units in the formula --OGOC(O)R 2 C(O)--and blocks having a number of ester units which are capable of forming a bifunctional polyester or polyester amide having a melting-point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at least 80 mol % of the G-groups being a tetra methylene group.

Claim 8

A polymer mixture as claimed in claim 5, characterised in that the polymer mixture comprises in addition one or more conventionally used additives.

Claim 9

A polymer mixture as claimed in claim 6, characterised in that the polymer mixture comprises in addition an agent to improve the impact strength.

Claim 10

Articles formed from the polymer mixture as claimed in claim 5.

Claim 11

A polymer mixture which comprises 45-55 parts by weight of an aromatic polycarbonate (A), 30-40 parts by weight of a polyester built up of entirely or substantially from units derived from an alkanediol and a benzene dicarboxylic acid (B), and 1-10 parts by weight of a thermoplastic elastomer (C), calculated per 100 parts by weight of A+B+C, characterized in that the thermoplastic elastomer (C) is built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is a polyfunctional group having at most 30 carbon atoms and p has a value of 2 or 3, and in which the polyester-ester units are built up from blocks having a number of ester units of the formula --OGOC(O)R 2 C(O)--and blocks having a number of ester units which are capable of forming a bifunctional polyester or polyester amide having a melting-point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at least 80 mol % of the G-groups being a tetra methylene group.

Claim 12

A polymer mixture which comprises 45-55 parts by weight of an aromatic polycarbonate (A), 30-40 parts by weight of a polyester built up of entirely or substantially from units derived from an alkanediol and a benzene dicarboxylic acid (B), and 1-10 parts by weight of a thermoplastic elastomer (C), calculated per 100 parts by weight of A+B+C, characterized in that the thermoplastic elastomer (C) is built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is a polyfunctional group having at most 30 carbon atoms and p has a value of 2 or 3, and in which the polyester-ester units are built up from blocks having a number of ester units of the formula --OGOC(O)R 2 C(O)--and blocks having a number of ester units which are capable of forming a bifunctional polyester or polyester amide having a melting-point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at least 80 mol % of the G-groups being a tetra methylene group.

Claim 13

A polymer mixture as claimed in claim 9, characterised in that the polymer mixture comprises in addition one or more conventionally used additives.

Claim 14

A polymer mixture as claimed in claim 10, characterised in that the polymer mixture comprises in addition an agent to improve the impact strength.

Claim 15

Articles formed from the polymer mixture as claimed in claim 9.

Claim 16

A process for improving the flow properties of a polymer mixture of about 40 to about 80 parts by weight of an aromatic polycarbonate (A) and about 10 to about 50 parts by weight of a polyester built up substantially from units derived from an alkanediol and a benzene dicarboxylic acid (B), comprising, addition about 1 to about 10 parts by weight of a thermoplastic elastomer (C) to the polymer mixture to improve the melt viscosity of the polymer mixture, the parts by weight of thermoplastic elastomer (C) being calculated per 100 parts by weight of (A)+(B)+(C), wherein the thermoplastic elastomer (C) is a polyester urethane built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is polyfunctional group having at most 30 carbon atoms, and p has a value of 2 or 3, the polyester units being built up from blocks having a number of ester units of the formula: --OGOC(O)R.sub.2 C(O)-- and block having a number of ester units which are capable of forming a bifunctional polyester or polyester amide having a melting point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at least 80 mol % of the G-group being tetramethylene group.

Claim 17

A process for improving the flow properties of a polymer mixture of about 40 to about 80 parts by weight of an aromatic polycarbonate (A) and about 10 to about 50 parts by weight of a polyester built up substantially from units derived from an alkanediol and a benzene dicarboxylic acid (B), comprising, addition about 1 to about 10 parts by weight of a thermoplastic elastomer (C) to the polymer mixture to improve the melt viscosity of the polymer mixture, the parts by weight of thermoplastic elastomer (C) being calculated per 100 parts by weight of (A)+(B)+(C), wherein the thermoplastic elastomer (C) is a polyester urethane built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is polyfunctional group having at most 30 carbon atoms, and p has a value of 2 or 3, the polyester units being built up from blocks having a number of ester units of the formula: --OGOC(O)R.sub.2 C(O)-- and block having a number of ester units which are capable of forming a bifunctional polyester or polyester amide having a melting point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at least 80 mol % of the G-group being tetramethylene group.

Claim 18

The process of claim 13, further comprising adding one or more additives selected from the group consisting of pigment, dye, reinforcing fiber, stabiliser, transesterification inhibitor, flame retardant, mold release agent and an agent to improve the impact strength.

Claim 19

A process for improving the flow properties of a polymer mixture of about 65 to about 75 parts by weight of an aromatic polycarbonate (A) and about 10 to about 20 parts by weight of a polyester built up substantially from units derived from alkanediol and a benzene dicarboxylic acid (B) comprising, adding about 1 to about 10 parts by weight of a thermoplastic elastomer (C) to the polymer mixture to improve the melt viscosity of the polymer mixture, the parts of weight of thermoplastic elastomer (C) being calculated per 100 parts by weight of (A)+(B)+(C), wherein the thermoplastic elastomer (C) is a polyester urethane built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is a polyfunctional group having at most 30 carbon atoms, and p has a value of 2 or 3, the polyester-[ester] units being built up from blocks having a number of ester units of the formula: --OGOC(O)R.sub.2 C(O)-- and blocks having a number ester units which are capable of forming a bifunctional polyester or polyester amide having a melting point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at least 80 mol % of the G-groups being a tetramethylene group.

Claim 20

A process for improving the flow properties of a polymer mixture of about 65 to about 75 parts by weight of an aromatic polycarbonate (A) and about 10 to about 20 parts by weight of a polyester built up substantially from units derived from alkanediol and a benzene dicarboxylic acid (B) comprising, adding about 1 to about 10 parts by weight of a thermoplastic elastomer (C) to the polymer mixture to improve the melt viscosity of the polymer mixture, the parts of weight of thermoplastic elastomer (C) being calculated per 100 parts by weight of (A)+(B)+(C), wherein the thermoplastic elastomer (C) is a polyester urethane built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is a polyfunctional group having at most 30 carbon atoms, and p has a value of 2 or 3, the polyester-[ester] units being built up from blocks having a number of ester units of the formula: --OGOC(O)R.sub.2 C(O)-- and blocks having a number ester units which are capable of forming a bifunctional polyester or polyester amide having a melting point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at least 80 mol % of the G-groups being a tetramethylene group.

Claim 21

The process of claim 15 further comprising one or more additives selected from the group consisting of pigment, dye, reinforcing fiber, stabiliser, transesterification inhibitor, flame retardant, mold release agent and an agent to improve the impact strength.

Claim 22

A process for improving the flow properties of a polymer mixture of about 45 to about 55 parts by weight of an aromatic polycarbonate (A) and about 30 to about 40 parts by weight of a polyester built up substantially from units derived from an alkanediol and a benzene dicarboxylic acid (B) comprising, adding about 1 to about 10 parts by weight of a thermoplastic elastomer (C) to the polymer mixture to improve the melt viscosity of the polymer mixture, the parts by weight of thermoplastic elastomer (C) being calculated per 100 parts by weight of (A)+(B)+(C), wherein the thermoplastic elastomer (C) is a polyester urethane built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is a polyfunctional group having at most 30 carbon atoms, and p has a value of 2 or 3, the polyester units being built up from blocks having a number of ester units of the formula: --OGOC(O)R.sub.2 C(O)-- and blocks having a number of ester units which are capable of forming a bifunctional polyester or polyester amide having a melting point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at lest 80 mol % of the G-groups being a tetramethylene group.

Claim 23

A process for improving the flow properties of a polymer mixture of about 45 to about 55 parts by weight of an aromatic polycarbonate (A) and about 30 to about 40 parts by weight of a polyester built up substantially from units derived from an alkanediol and a benzene dicarboxylic acid (B) comprising, adding about 1 to about 10 parts by weight of a thermoplastic elastomer (C) to the polymer mixture to improve the melt viscosity of the polymer mixture, the parts by weight of thermoplastic elastomer (C) being calculated per 100 parts by weight of (A)+(B)+(C), wherein the thermoplastic elastomer (C) is a polyester urethane built up from polyester units which are bonded by means of groups of the formula R 1 [NHC(O)]p, wherein R 1 is a polyfunctional group having at most 30 carbon atoms, and p has a value of 2 or 3, the polyester units being built up from blocks having a number of ester units of the formula: --OGOC(O)R.sub.2 C(O)-- and blocks having a number of ester units which are capable of forming a bifunctional polyester or polyester amide having a melting point lower than 100° C., which blocks are bonded together by ester bonds, at least 80 mol % of the R 2 -groups being 1,4-phenylene radicals and at lest 80 mol % of the G-groups being a tetramethylene group.

Claim 24

The process of claim 17 further comprising one or more additives selected from the group consisting of pigment, dye, reinforcing fiber, stabiliser, transesterification inhibitor, flame retardant, mold release agent and an agent to improve the impact strength.