High impact strength blends of polybutylene terephthalate
Assignee: Bayer Corp
•
Filing: 1975-05-23
•
Granted: 1977-08-23
•
Expires: 1995-05-23
Abstract
Abstract A blend comprised of high molecular weight polybutylene terephthalate and up to about 20 wt.% of an aromatic polycarbonate resin wherein the mixture has a drop dart impact strength in excess of about 60 foot-pounds is prepared by intimately mixing the components, one of which is powdered. The polybutylene terephthalate has an intrinsic viscosity of at least about 0.95. The blend will tolerate the addition of up to 20 wt.% of a conventional flame retardant package such as decabromodiphenyl oxide and antimony trioxide while maintaining the 60 foot-pound minimum drop dart impact strength. The blend can achieve impact strengths in excess of 90 foot-pounds even when it contains flame retardant additives if the polybutylene terephthalate is blended in powder form.
Inventors
- 👤 Arthur L. Baron
- 👤 Herbert L. Rawlings
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:03
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/02; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K5/00; C08K5/02; C08K5/03; C08L69/00
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
151 words
A thermoplastic resin having a drop dart impact resistance of at least about 60 foot-pounds and comprising an intimate mechanical blend of: a. 60 to 90 wt.% of polybutylene terephthalate with an intrinsic viscosity of at least about 0.95, b. 10 to 20 wt.% of an aromatic polycarbonate having a melt index of 0.1 to 25 gm/10 min. at 572° F (ASTM - D-1238); and c. 0 to 20 wt.% of a flame retardant package comprising i. an aromatic bromine compound present in sufficient amount to provide about 3.5 to 10 wt.% bromine based on the total weight of the resin, and ii. an antimony containing compound present in sufficient amounts to provide about 3 to 8 wt.% of antimony based on the total weight of resin, at least one of said polybutylene terephthalate and said polycarbonate being in the form of a powder at the time the blend is produced.
Claim 2
Dependent Claim
151 words
A thermoplastic resin having a drop dart impact resistance of at least about 60 foot-pounds and comprising an intimate mechanical blend of: a. 60 to 90 wt.% of polybutylene terephthalate with an intrinsic viscosity of at least about 0.95, b. 10 to 20 wt.% of an aromatic polycarbonate having a melt index of 0.1 to 25 gm/10 min. at 572° F (ASTM - D-1238); and c. 0 to 20 wt.% of a flame retardant package comprising i. an aromatic bromine compound present in sufficient amount to provide about 3.5 to 10 wt.% bromine based on the total weight of the resin, and ii. an antimony containing compound present in sufficient amounts to provide about 3 to 8 wt.% of antimony based on the total weight of resin, at least one of said polybutylene terephthalate and said polycarbonate being in the form of a powder at the time the blend is produced.
Claim 3
Dependent Claim
103 words
The resin of claim 1 wherein the aromatic polycarbonate has the following reoccurring structural formula: ##STR6## wherein X is ##STR7## R 1 to R 4 represent hydrogen atoms, alkyl radicals, with 1-4 carbon atoms or halogen atoms and are the same or different, represents a single bond, an alkylene or alkylidene radical with 1-7 carbon atoms, a cycloalkylene or cycloalkylidene radical with 5 to 12 carbon atoms, --O--, --S--, --CO--, --SO--, --SO 2 -- or a radical of the formulae ##STR8## R 5 to R 8 represents alkyl radicals with 1 to 4 carbon atoms; and R 9 represents hydrogen, chlorine or bromine.
Claim 4
Dependent Claim
21 words
The resin of claim 2 wherein Y is a methylene radical, a propylidene radical, a cyclohexylene radical, a cyclohexylidene radical, ##STR9##
Claim 5
Dependent Claim
41 words
The resin of claim 1 wherein the polycarbonate has the following recurring structural formula ##STR10## wherein R 10 and R 11 represent chlorine, bromine or a 1-4 carbon alkyl radical and a and b are integers between 1 and 4 inclusive.
Claim 6
Dependent Claim
67 words
The resin of claim 1 containing 10 to 20 wt.% of a flame retardant package comprising a. an aromatic bromine compound present in sufficient amount to provide about 5 to 8 wt.% bromine based on the total weight of the resin, and b. an antimony containing compound present in sufficient amount to provide about 4.5 to 5.5 wt.% antimony based on the total weight of the resin.
Claim 7
Dependent Claim
19 words
The resin of claim 5 wherein the bromine compound is decarbromodiphenyl ether and the antimony compound is antimony trioxide.
Claim 8
Dependent Claim
15 words
The resin of claim 6 which contains up to about 2 wt.% of pigmentating agents.
Claim 9
Dependent Claim
12 words
The resin of claim 7 wherein the pigmentating agent includes titanium oxide.
Claim 10
Dependent Claim
18 words
The resin of claim 1 wherein the powdered component has a particle size less than about 10 mesh.
Claim 11
Dependent Claim
19 words
The resin of claim 9 wherien the powdered component has a particle size of about 10 to 200 mesh.
Claim 12
Dependent Claim
19 words
The resin of claim 10 wherein the powdered component has a particle size of about 20 to 100 mesh.
Claim 13
Dependent Claim
33 words
The resin of claim 1 wherein both the polycarbonate and the polybutylene terephthalate are in the form of a powder of about 10 to 200 mesh at the time the blend is formed.
Claim 14
Dependent Claim
29 words
The resin of claim 1 wherein the polybutylene terephthalate is in the form of a powder of about 10 to 200 mesh at the time the blend is formed.
Claim 15
Dependent Claim
29 words
The resin of claim 1 wherein the polycarbonate has the following reoccurring structural formula ##STR11## and a melt flow at 572° F of about 3 to 6 gm/10 minutes.
Claim 16
Dependent Claim
20 words
The resin of claim 14 wherein the aromatic bromine compound is decabromodiphenylether and the antimony containing compound is antimony trioxide.
Claim 17
Dependent Claim
35 words
The resin of claim 14 wherein the aromatic bromine compound is a carbonate oligomer having 2 to 20 repeating units of the formula ##STR12## wherein a and b are integers between 1 and 4 inclusive.
Claim 18
Dependent Claim
81 words
A process for the production of a high impact strength molding resin with a drop dart impact strength greater than about 60 foot-pound comprising forming an intimate blend of a. 80 to 90 wt.% of polybutylene terephthalate having an intrinsic viscosity above about 0.95 and b. 10 to 20 wt.% of an aromatic polycarbonate having a melt index of 0.1 to 25 gm/10 min. at 572° F (ASTM D-1238) wherein at least one of the components is blended in powdered form.
Claim 19
Dependent Claim
81 words
A process for the production of a high impact strength molding resin with a drop dart impact strength greater than about 60 foot-pound comprising forming an intimate blend of a. 80 to 90 wt.% of polybutylene terephthalate having an intrinsic viscosity above about 0.95 and b. 10 to 20 wt.% of an aromatic polycarbonate having a melt index of 0.1 to 25 gm/10 min. at 572° F (ASTM D-1238) wherein at least one of the components is blended in powdered form.
Claim 20
Independent Claim
148 words
A method of preparing a high impact strength thermoplastic molding resin with a drop dart impact resistance of at least about 60 foot-pounds comprising blending a. 60 to 90 wt. % of polybutylene terephthalate with an intrinsic viscosity of at least about 0.95, b. 10 to 20 wt. % of an aromatic polycarbonate having a melt index of 0.1 to 25 gm/10 at 572° F (ASTM D-1238), and c. 0 to about 20 wt. % of a flame retardant package comprising i. an aromatic bromine compound present in sufficient amount to provide 3.5 to 10 wt. % of bromine based on the total weight of the resin, and ii. an antimony containing compound present in sufficient amount to provide about 3 to 8 wt. % of antimony based on the total weight of the resin, wherein one of the polybutylene or the polycarbonate is blended in powdered form.
Claim 21
Independent Claim
148 words
A method of preparing a high impact strength thermoplastic molding resin with a drop dart impact resistance of at least about 60 foot-pounds comprising blending a. 60 to 90 wt. % of polybutylene terephthalate with an intrinsic viscosity of at least about 0.95, b. 10 to 20 wt. % of an aromatic polycarbonate having a melt index of 0.1 to 25 gm/10 at 572° F (ASTM D-1238), and c. 0 to about 20 wt. % of a flame retardant package comprising i. an aromatic bromine compound present in sufficient amount to provide 3.5 to 10 wt. % of bromine based on the total weight of the resin, and ii. an antimony containing compound present in sufficient amount to provide about 3 to 8 wt. % of antimony based on the total weight of the resin, wherein one of the polybutylene or the polycarbonate is blended in powdered form.
Claim 22
Dependent Claim
19 words
The process of claim 18 wherein the powdered component has a particle size no greater than about 10 mesh.
References Cited (Backward Citations)
US3218372A
Cited
US3470114A
Cited
US3624024A
Cited
US3644271A
Cited
US3751396A
Cited
US3855277A
Cited
US3833685A
Cited
US3835089A
Cited
US3883471A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-22 | 1981-02-21 | 1981-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-22 | 1985-02-21 | 1985-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-22 | 1989-02-21 | 1989-08-23 | $7700.00 | Window Closed / Lapsed |