Dispersions of high melting polyesters in polyhydroxyl compounds, a process for their preparation and their use in the production of polyurethanes

Claim 2

A dispersion comprising (a) 1 to 40% by weight based on the whole dispersion of a polyester, polyester amide or segmented copolyether ester having a melting point above 100° C., as the disperse phase; in (b) 99 to 60% by weight based on the whole dispersion of a polyhydroxyl compound having a melting point below 50° C. and a molecular weight of from 62 to 12,000 and in which said disperse phase is substantially insoluble, as the continuous phase; said disperse phase further characterized as containing more than 50% by weight of dispersed particles in a size range of from 0.05 to 10μ.

Claim 3

A dispersion as claimed in claim 1, wherein said disperse phase contains more than 50% by weight, preferably more than 75% by weight, of the dispersed particles having a size of from 0.5 to 4.0μ.

Claim 4

A dispersion as claimed in claim 1, wherein said disperse phase contains more than 50% by weight, preferably more than 75% by weight, of the dispersed particles having a size of from 0.2 to 2.0μ.

Claim 5

A dispersion as claimed in claim 1, wherein component (a) has a melting point range of from 110° C. to 280° C. and a molecular weight range of from 254 to 50,000.

Claim 6

A dispersion as claimed in claim 1, wherein component (a) is a polyester polyol having 2 to 4 hydroxyl groups, all or part of said hydroxyl groups optionally blocked with isocyanates or carboxylic acid anhydrides.

Claim 7

A dispersion as claimed in claim 1, wherein component (a) is a polyester of terephthalic acid and 1,4-butanediol and/or hexanediol and/or ethylene glycol.

Claim 8

A dispersion as claimed in claim 1, wherein component (b) has a melting point below 20° C.

Claim 9

A dispersion as claimed in claim 1, wherein component (b) is a polyether polyol having 2 to 8 hydroxyl groups and having a molecular weight of from 400 to 10,000.

Claim 10

A dispersion as claimed in claim 1, wherein component (b) is a polyether polyol having 2 to 4, preferably 2, hydroxyl groups and having a molecular weight of from 400 to 6,000.

Claim 11

A process for preparing dispersions comprising: (i) vigorously mixing (a) 1 to 40% by weight, based on the whole dispersion, of a polyester, polyester amide or segmented copolyether ester having a melting point above 100° C., as the disperse phase; and (b) 99 to 60% by weight, based on the whole dispersion, of a polyhydroxyl compound having a melting point below 50° C. and a molecular weight of from 62 to 12,000 and in which said disperse phase is substantially insoluble, as the continuous phase; together at a temperature above the melting point of component (a); (ii) simultaneously subjecting said components (a) and (b) to high shearing forces; and (iii) lowering the temperature below the melting point of said component (a) while continuing said vigorous stirring.

Claim 12

A process for preparing dispersions comprising: (i) vigorously mixing (a) 1 to 40% by weight, based on the whole dispersion, of a polyester, polyester amide or segmented copolyether ester having a melting point above 100° C., as the disperse phase; and (b) 99 to 60% by weight, based on the whole dispersion, of a polyhydroxyl compound having a melting point below 50° C. and a molecular weight of from 62 to 12,000 and in which said disperse phase is substantially insoluble, as the continuous phase; together at a temperature above the melting point of component (a); (ii) simultaneously subjecting said components (a) and (b) to high shearing forces; and (iii) lowering the temperature below the melting point of said component (a) while continuing said vigorous stirring.

Claim 13

A process for the preparation of dispersions comprising: (i) dissolving (a) 1 to 40% by weight, based on the whole dispersion, of a polyester, polyester amide or segmented copolyether ester having a melting point above 100° C. as the disperse phase; in a solvent with vigorous stirring; (ii) mixing, optionally portionwise, dissolved component (a) with (b) 99 to 60% by weight, based on the whole dispersion, of a polyhydroxyl compound having a melting point below 50° C. and a molecular weight of from 62 to 12,000 and in which said disperse phase is substantially insoluble, as the continuous phase; optionally dissolved in solvent, with vigorous stirring; and (iii) distilling off said solvents either during step (ii) or after completing step (ii), optionally under vacuum.

Claim 14

A process for the preparation of dispersions comprising: (i) dissolving (a) 1 to 40% by weight, based on the whole dispersion, of a polyester, polyester amide or segmented copolyether ester having a melting point above 100° C. as the disperse phase; in a solvent with vigorous stirring; (ii) mixing, optionally portionwise, dissolved component (a) with (b) 99 to 60% by weight, based on the whole dispersion, of a polyhydroxyl compound having a melting point below 50° C. and a molecular weight of from 62 to 12,000 and in which said disperse phase is substantially insoluble, as the continuous phase; optionally dissolved in solvent, with vigorous stirring; and (iii) distilling off said solvents either during step (ii) or after completing step (ii), optionally under vacuum.

Claim 15

A process for the preparation of cellular or non-cellular polyurethanes by reacting (i) polyisocyanates; (ii) relatively high molecular weight polyhydroxyl compounds containing organic fillers; and optionally (iii) other compounds having isocyanate reactive groups; optionally in the presence of (iv) blowing agents, activators and other known additives; the improvement comprising using as component (ii) dispersions comprising: (a) 1 to 40% by weight based on the whole dispersion of a polyester, polyester amide or segmented copolyether ester having a melting point above 100° C., as the disperse phase; in (b) 99 to 60% by weight, based on the whole dispersion, of a polyhydroxyl compound having a melting point below 50° C. and a molecular weight of from 62 to 12,000 and in which said disperse phase is substantially insoluble as the continuous phase; said disperse phase further characterized as containing more than 50% by weight of dispersed particles in a size range of from 0.05 to 10μ, characterized in that the temperature of the reaction mixture of components (i), (ii) and (iii) is maintained below the melting point of said organic filler dispersed in component (ii).

Claim 16

A process for the preparation of cellular or non-cellular polyurethanes by reacting (i) polyisocyanates; (ii) relatively high molecular weight polyhydroxyl compounds containing organic fillers; and optionally (iii) other compounds having isocyanate reactive groups; optionally in the presence of (iv) blowing agents, activators and other known additives; the improvement comprising using as component (ii) dispersions comprising: (a) 1 to 40% by weight based on the whole dispersion of a polyester, polyester amide or segmented copolyether ester having a melting point above 100° C., as the disperse phase; in (b) 99 to 60% by weight, based on the whole dispersion, of a polyhydroxyl compound having a melting point below 50° C. and a molecular weight of from 62 to 12,000 and in which said disperse phase is substantially insoluble as the continuous phase; said disperse phase further characterized as containing more than 50% by weight of dispersed particles in a size range of from 0.05 to 10μ, characterized in that the temperature of the reaction mixture of components (i), (ii) and (iii) is maintained below the melting point of said organic filler dispersed in component (ii).

Claim 17

A dispersion as claimed in claim 1, wherein component (a) has a melting point range of from 120° to 220° C. and a molecular weight range of from 300 to 25,000.