US5122387A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Developing solution and pattern forming method using the same
Assignee: Panasonic Holdings Corp
•
Filing: 1989-11-28
•
Granted: 1992-06-16
•
Expires: 2009-11-28
Abstract
Abstract The invention relates to a developing solution of polydimethyl glutarimide containing acetone, ethyl alcohol, or propyl alcohol and, water, and alkali, and a pattern forming method using the same. According to the invention, a finer pattern than before may be formed by using PMGI resist film. At the same time, a liftoff process excellent in dimensional controllability and high in reliability than in the prior art will be realized. Besides, in the wet etching process of using the two-layer resist pattern of the invention as the mask on the GaAs substrate, since the adhesion of the lower layer resist to the substrate is superior, the recess width when etching the substrate can be stably controlled, so that a device of high performance may be obtained. Furthermore, in the process of using the PMGI resist film in the lower layer and the PMMA resist film in the upper layer, since the PMMA resist film and PMGI resist film possess mutually appropriate electron beam sensitivity and deep ultraviolet light sensitivity, mixed exposure by electron beam and deep ultraviolet light may be applied, so that a stable hybrid exposure may be effected at a high through-put.
Inventors
- 👤 Hiroshi Takenaka
- 👤 Yoshihiro Todokoro
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:26
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/061; H10D30/0612; G; G03; G03F; G03F7/00; G03F7/004; G03F7/09; G03F7/095; G03F7/26; G03F7/30; G03F7/32; G03F7/322; H10D30/015; H10D64/00; H10D64/01; H10D64/012; H10D64/0124; H10D64/0125; H10P; H10P76/00; H10P76/20; H10P76/202
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
143 words
A pattern forming method comprising: a. applying and baking a film consisting of essentially of polydimethyl glutarimide on a substrate, b. applying and baking a polymer film having a sensitivity due to chain scission of the polymer caused by charged particle beam or short wavelength electromagnetic waves, on said polydimethyl glutarimide film, c. Substantially simultaneously exposing said polymer film and said polydimethyl glutarimide film to said charged particle beam or short wavelength electromagnetic waves in a specified area of two-layer film composed of said polydimethyl glutarimide film and said polymer film, d. developing said specified area of said polymer film by using an organic solvent whereby said specified area of polymer film is removed, and e. developing said specified area of said polydimethyl glutarimide film by using a solution containing an organic alkali whereby said specified area of polydimethyl glutarimide film is removed.
Claim 2
Dependent Claim
143 words
A pattern forming method comprising: a. applying and baking a film consisting of essentially of polydimethyl glutarimide on a substrate, b. applying and baking a polymer film having a sensitivity due to chain scission of the polymer caused by charged particle beam or short wavelength electromagnetic waves, on said polydimethyl glutarimide film, c. Substantially simultaneously exposing said polymer film and said polydimethyl glutarimide film to said charged particle beam or short wavelength electromagnetic waves in a specified area of two-layer film composed of said polydimethyl glutarimide film and said polymer film, d. developing said specified area of said polymer film by using an organic solvent whereby said specified area of polymer film is removed, and e. developing said specified area of said polydimethyl glutarimide film by using a solution containing an organic alkali whereby said specified area of polydimethyl glutarimide film is removed.
Claim 3
Dependent Claim
26 words
The pattern forming method of claim 1, wherein the baking temperature of said polymer film is lower than the baking temperature of said polydimethyl glutarimide film.
Claim 4
Dependent Claim
32 words
The pattern forming method of claim 2, wherein an unexposed portion of said polydimethyl glutarimide film is not dissolved in an organic solvent which is the developing solution of said polymer film.
Claim 5
Dependent Claim
34 words
The pattern forming method of claim 2, wherein an exposed portion of said polymer film is not dissolved in a solution containing an organic alkali as the developing solution of said polydimethyl glutarimide film.
Claim 6
Dependent Claim
25 words
The pattern forming method of claim 2, wherein the sensitivity of said polymer film is nearly equal to the sensitivity of said polydimethyl glutarimide film.
Claim 7
Dependent Claim
16 words
The pattern forming method according to claim 1 wherein the organic alkali is tetramethyl ammonium hydroxide.
Claim 8
Dependent Claim
253 words
A pattern forming method comprising: a. applying and baking a film consisting essentially of polydimethyl glutarimide on a substrate, b. applying and baking a polymer film having a sensitivity due to chain scission of the polymer caused by charged particle beam or short wavelength electromagnetic wave, on said polydimethyl glutarimide film, c. substantially simultaneously exposing said polymer film and said polydimethyl glutarimide film to said charged particle beam or short wavelength electromagnetic waves in a specified area of two-layer film composed of said polydimethyl glutarimide film and said polymer film, d. developing said specified area of said polymer film by using an organic solvent whereby said specified area of polymer film is removed to provide an opening through said film, e. developing said specified area of the polydimethyl glutarimide film by using a solution containing an organic alkali whereby said specified area of polydimethyl glutarimide film is removed to provide an opening through said film, wherein the remaining film portion of said polymer film after development is in an overhang shape wherein the opening through said polymer film is broader at the bottom surface than the top surface of said polymer film, and wherein the opening through said polydimethyl glutarimide film is narrower than the opening of the upper part of said polymer film after development, f. etching an area of said substrate which is exposed by said developing steps, g. depositing a metal film on the entire surface of said substrate, and h. removing said polymer film and said polydimethyl glutarimide film.
Claim 9
Dependent Claim
253 words
A pattern forming method comprising: a. applying and baking a film consisting essentially of polydimethyl glutarimide on a substrate, b. applying and baking a polymer film having a sensitivity due to chain scission of the polymer caused by charged particle beam or short wavelength electromagnetic wave, on said polydimethyl glutarimide film, c. substantially simultaneously exposing said polymer film and said polydimethyl glutarimide film to said charged particle beam or short wavelength electromagnetic waves in a specified area of two-layer film composed of said polydimethyl glutarimide film and said polymer film, d. developing said specified area of said polymer film by using an organic solvent whereby said specified area of polymer film is removed to provide an opening through said film, e. developing said specified area of the polydimethyl glutarimide film by using a solution containing an organic alkali whereby said specified area of polydimethyl glutarimide film is removed to provide an opening through said film, wherein the remaining film portion of said polymer film after development is in an overhang shape wherein the opening through said polymer film is broader at the bottom surface than the top surface of said polymer film, and wherein the opening through said polydimethyl glutarimide film is narrower than the opening of the upper part of said polymer film after development, f. etching an area of said substrate which is exposed by said developing steps, g. depositing a metal film on the entire surface of said substrate, and h. removing said polymer film and said polydimethyl glutarimide film.
Claim 10
Dependent Claim
64 words
The pattern forming method of claim 7, wherein if said specified area of said polydimethyl glutarimide film has a width of less than 5 μm, it is exposed with a dose larger than the exposure dose of said specified area having a width of 5 μm or more, so that said polymer film and said polydimethyl glutarimide film are exposed at the same time.
Claim 11
Dependent Claim
85 words
The pattern forming method of claim 7, wherein the region where the width of said specified area of said polydimethyl glutarimide film is 5 μm or more is irradiated with said charged particle beam or said short wavelength electromagnetic waves, and then the periphery of said specified area is exposed to a dose larger than the exposure dose of the specified portion of 5 μm or more, so that said polymer film and said polydimethyl glutarimide film are margined and exposed at the same time.
Claim 12
Dependent Claim
221 words
A pattern forming method comprising: a. applying and baking a film consisting essentially of polydimethyl glutarimide on a substrate, b. applying and baking a polymer film having a sensitivity due to chain scission of the polymer caused by charged particle beam or short wavelength electromagnetic wave, on said polydimethyl glutarimide film, c. substantially simultaneously exposing said polymer film and said polydimethyl glutarimide film by said charged particle beam or said short wavelength electromagnetic waves in a specified area of said polydimethyl glutarimide film and said polymer film, d. developing said specified area of said polymer film by using an organic solvent whereby said specified area of polymer film is removed, e. developing said specified area of said polydimethyl glutarimide film by using a solution containing organic alkali whereby said specified area of polydimethyl glutarimide film is removed, wherein a remaining film portion of said polymer film after development is trapezoidal, and the pattern width of said remaining film portion of said polydimethyl glutarimide film after development is narrower than pattern width of the bottom of the trapezoidal shape of said polymer film after development, f. etching an area of said substrate which is exposed by said developing steps, g. depositing a metal film on the entire surface of said substrate, and h. removing said polymer film and said polydimethyl glutarimide film.
Claim 13
Dependent Claim
221 words
A pattern forming method comprising: a. applying and baking a film consisting essentially of polydimethyl glutarimide on a substrate, b. applying and baking a polymer film having a sensitivity due to chain scission of the polymer caused by charged particle beam or short wavelength electromagnetic wave, on said polydimethyl glutarimide film, c. substantially simultaneously exposing said polymer film and said polydimethyl glutarimide film by said charged particle beam or said short wavelength electromagnetic waves in a specified area of said polydimethyl glutarimide film and said polymer film, d. developing said specified area of said polymer film by using an organic solvent whereby said specified area of polymer film is removed, e. developing said specified area of said polydimethyl glutarimide film by using a solution containing organic alkali whereby said specified area of polydimethyl glutarimide film is removed, wherein a remaining film portion of said polymer film after development is trapezoidal, and the pattern width of said remaining film portion of said polydimethyl glutarimide film after development is narrower than pattern width of the bottom of the trapezoidal shape of said polymer film after development, f. etching an area of said substrate which is exposed by said developing steps, g. depositing a metal film on the entire surface of said substrate, and h. removing said polymer film and said polydimethyl glutarimide film.
Claim 14
Dependent Claim
16 words
The pattern forming method according to claim 10 wherein the organic alkali is tetramethyl ammonium hydroxide.
References Cited (Backward Citations)
US3964908A
Cited
US4212935A
Cited
US4384037A
Cited
US4536421A
Cited
US4415652A
Cited
US4524121A
Cited
US4699870A
Cited
US4693954A
Cited
US4725524A
Cited
US4957988A
Cited
US4833067A
Cited
US4737438A
Cited
US4873177A
Cited
US4912018A
Cited
US4939070A
Cited
US4791171A
Cited
US4770739A
Cited
US4814258A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-16 | 1995-12-16 | 1996-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-16 | 1999-12-16 | 2000-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-16 | 2003-12-16 | 2004-06-16 | $7700.00 | Window Closed / Lapsed |