US5037775A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for selectively depositing single elemental semiconductor material on substrates
Assignee: MCNC Research and Development Institute
•
Filing: 1989-09-05
•
Granted: 1991-08-06
•
Expires: 2009-09-05
Abstract
Abstract An alternating cyclic (A.C.) method for selectively depositing single element semiconductor materials, on the surface of a substrate without depositing the material on an adjacent mask layer. A gas of a reducible compound of the material and a reducing gas, preferably hydrogen, are simultaneously flowed through a reaction chamber to deposit the material on the substrate surface and to a lesser extent on the mask layer. Then, the flow of reducing gas is interrupted to cause the reducible compound gas to etch the material which forms on the mask layer in a disproportionation reaction. The deposition and etch steps are repeated in an alternating cyclic fashion until the requisite thickness is deposited. The process may take place in a single reaction chamber, using only the reducible compound gas and pulsed flow of the reducing gas.
Inventors
- 👤 Arnold Reisman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:32
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/40; H10P14/42; H10P14/43; H10P14/432; C; C23; C23C; C23C16/00; C23C16/04; C23C16/06; C23C16/08; C23C16/14; H10P50/00; H10P50/20; H10P50/24; H10P50/242; H10P50/244; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/056; H10W20/057; Y; Y10; Y10S; Y10S148/00; Y10S148/057; Y10S148/058
Claims Analysis
Total Claims: 60
Claim 1
Independent Claim
161 words
A method of selectively depositing a predetermined thickness of a single element semiconductor material on the surface of a substrate having a mask layer thereon and located in a reaction chamber, comprising the steps of: heating said reaction chamber; flowing a gas of a reducible compound of said single element semiconductor material and a reducing gas through said heated reaction chamber, to thereby react the reducible compound gas with the reducing gas and deposit said single element semiconductor material on said surface and to a lesser extent on said mask layer; interrupting the flow of the reducing gas while continuing the flow of the reducible compound gas, the continued flow of the reducible compound gas operating to etch said single element semiconductor material on said mask layer and to a lesser extent on said surface in a disproportionation reaction; and repeating said flowing and interrupting steps to selectively deposit said predetermined thickness of said single element semiconductor material on said surface.
Claim 2
Independent Claim
161 words
A method of selectively depositing a predetermined thickness of a single element semiconductor material on the surface of a substrate having a mask layer thereon and located in a reaction chamber, comprising the steps of: heating said reaction chamber; flowing a gas of a reducible compound of said single element semiconductor material and a reducing gas through said heated reaction chamber, to thereby react the reducible compound gas with the reducing gas and deposit said single element semiconductor material on said surface and to a lesser extent on said mask layer; interrupting the flow of the reducing gas while continuing the flow of the reducible compound gas, the continued flow of the reducible compound gas operating to etch said single element semiconductor material on said mask layer and to a lesser extent on said surface in a disproportionation reaction; and repeating said flowing and interrupting steps to selectively deposit said predetermined thickness of said single element semiconductor material on said surface.
Claim 3
Dependent Claim
33 words
The method of claim 1 wherein said single element semiconductor material is silicon and wherein the reducible compound gas is selected from the group consisting of silicon tetrachloride, silicon tetrabromide and silicon tetraiodide.
Claim 4
Dependent Claim
33 words
The method of claim 1 wherein said single element semiconductor material is germanium and wherein the reducible compound gas is selected from the group consisting of germanium tetrachloride, germanium tetrabromide and germanium tetraiodide.
Claim 5
Dependent Claim
25 words
The method of claim 1 wherein said flowing step is practiced for about 30 seconds and said interrupting step is practiced for about 15 seconds.
Claim 6
Dependent Claim
20 words
The method of claim 1 wherein the time ratio of said flowing step to said interrupting step is about 2:1.
Claim 7
Dependent Claim
18 words
The method of claim 1 wherein said flowing and interrupting steps are performed in an argon ambient atmosphere.
Claim 8
Independent Claim
96 words
A method of selectively depositing a single element semiconductor material on the surface of a substrate having a mask layer thereon, comprising the steps of: heating said substrate; and repeatedly exposing said heated substrate to a gas of a reducible compound of said single element semiconductor material and a reducing gas, followed by said gas of said reducible compound alone, said gas of said reducible compound alone operating to etch nucleation sites on said mask layer which are built up during the reaction of said reducible compound gas and said reducing gas in a disproportionation reaction.
Claim 9
Independent Claim
96 words
A method of selectively depositing a single element semiconductor material on the surface of a substrate having a mask layer thereon, comprising the steps of: heating said substrate; and repeatedly exposing said heated substrate to a gas of a reducible compound of said single element semiconductor material and a reducing gas, followed by said gas of said reducible compound alone, said gas of said reducible compound alone operating to etch nucleation sites on said mask layer which are built up during the reaction of said reducible compound gas and said reducing gas in a disproportionation reaction.
Claim 10
Dependent Claim
33 words
The method of claim 7 wherein said single element semiconductor material is silicon and wherein the reducible compound gas is selected from the group consisting of silicon tetrachloride, silicon tetrabromide and silicon tetraiodide.
Claim 11
Dependent Claim
33 words
The method of claim 7 wherein said single element semiconductor material is germanium and wherein the reducible compound gas is selected from the group consisting of germanium tetrachloride, germanium tetrabromide and germanium tetraiodide.
Claim 12
Dependent Claim
11 words
The method of claim 7 wherein the reducing gas is hydrogen.
Claim 13
Dependent Claim
33 words
The method of claim 7 wherein said substrate is exposed to the reducible compound and the reducing gas for about 30 seconds and to the reducible compound gas alone for about 15 seconds.
Claim 14
Dependent Claim
34 words
The method of claim 7 wherein the time ratio of exposing said substrate to the reducible compound gas and reducing gas to exposing said substrate to the reducible compound gas alone is about 2:1.
Claim 15
Dependent Claim
17 words
The method of claim 7 wherein said repeatedly exposing step is performed in an argon ambient atmosphere.
Claim 16
Independent Claim
110 words
A method of selectively depositing a single element semiconductor material on the surface of a substrate having a mask layer thereon, comprising the steps of: heating said substrate; and providing an ambient atmosphere of a gas of a reducible compound of said single element semiconductor material and pulses of a reducing gas, to thereby react said reducing gas with said reducible compound gas and deposit said single element semiconductor material on said surface and to a lesser extent on said mask layer during said pulses, and to cause said reducible compound gas to etch said single element semiconductor material on said mask layer between said pulses in a disproportionation reaction.
Claim 17
Independent Claim
110 words
A method of selectively depositing a single element semiconductor material on the surface of a substrate having a mask layer thereon, comprising the steps of: heating said substrate; and providing an ambient atmosphere of a gas of a reducible compound of said single element semiconductor material and pulses of a reducing gas, to thereby react said reducing gas with said reducible compound gas and deposit said single element semiconductor material on said surface and to a lesser extent on said mask layer during said pulses, and to cause said reducible compound gas to etch said single element semiconductor material on said mask layer between said pulses in a disproportionation reaction.
Claim 18
Dependent Claim
33 words
The method of claim 14 wherein said single element semiconductor material is silicon and wherein the reducible compound gas is selected from the group consisting of silicon tetrachloride, silicon tetrabromide and silicon tetraiodide.
Claim 19
Dependent Claim
33 words
The method of claim 14 wherein said single element semiconductor material is germanium and wherein the reducible compound gas is selected from the group consisting of germanium tetrachloride, germanium tetrabromide and germanium tetraiodide.
Claim 20
Dependent Claim
11 words
The method of claim 14 wherein the reducing gas is hydrogen.
Claim 21
Dependent Claim
25 words
The method of claim 14 wherein said pulses of reducing gas have a duration of about 30 seconds, with about 15 seconds between said pulses.
Claim 22
Dependent Claim
23 words
The method of claim 14 wherein the ratio of the time between said pulses to the duration of said pulses is about 1:2.
Claim 23
Independent Claim
138 words
A method of selectively depositing a predetermined thickness of a single element semiconductor material on the surface of a substrate having a mask layer thereon, comprising the steps of: heating said substrate; exposing said substrate to a gas of a reducible compound of said single element semiconductor material and a reducing gas to deposit said single element semiconductor material on said surface and to a lesser extent on said mask layer; removing the reducing gas while continuing to expose said substrate to the reducible compound gas to thereby cause said reducible compound gas to etch said single element semiconductor material on said mask layer and to a lesser extent on said surface in a disproportionation reaction; and repeating said exposing and removing steps to selectively deposit said predetermined thickness of said single element semiconductor material on said surface.
Claim 24
Independent Claim
138 words
A method of selectively depositing a predetermined thickness of a single element semiconductor material on the surface of a substrate having a mask layer thereon, comprising the steps of: heating said substrate; exposing said substrate to a gas of a reducible compound of said single element semiconductor material and a reducing gas to deposit said single element semiconductor material on said surface and to a lesser extent on said mask layer; removing the reducing gas while continuing to expose said substrate to the reducible compound gas to thereby cause said reducible compound gas to etch said single element semiconductor material on said mask layer and to a lesser extent on said surface in a disproportionation reaction; and repeating said exposing and removing steps to selectively deposit said predetermined thickness of said single element semiconductor material on said surface.
Claim 25
Dependent Claim
33 words
The method of claim 20 wherein said single element semiconductor material is silicon and wherein the reducible compound gas is selected from the group consisting of silicon tetrachloride, silicon tetrabromide and silicon tetraiodide.
Claim 26
Dependent Claim
33 words
The method of claim 20 wherein said single element semiconductor material is germanium and wherein the reducible compound gas is selected from the group consisting of germanium tetrachloride, germanium tetrabromide and germanium tetraiodide.
Claim 27
Dependent Claim
11 words
The method of claim 20 wherein the reducing gas is hydrogen.
Claim 28
Dependent Claim
25 words
The method of claim 20 wherein said exposing step is practiced for about 30 seconds and said removing step is practiced for about 15 seconds.
Claim 29
Dependent Claim
20 words
The method of claim 20 wherein the time ratio of said exposing step to said removing step is about 2:1.
Claim 30
Dependent Claim
18 words
The method of claim 20 wherein said exposing and removing steps are performed in an argon ambient atmosphere.
Claim 31
Dependent Claim
17 words
The method of claim 1 wherein said substrate is silicon and said mask layer is an insulator.
Claim 32
Dependent Claim
11 words
The method of claim 27 wherein said insulator is silicon dioxide.
Claim 33
Dependent Claim
11 words
The method of claim 27 wherein said insulator is silicon nitride.
Claim 34
Dependent Claim
15 words
The method of claim 1 wherein said reaction chamber is a hot wall reaction chamber.
Claim 35
Dependent Claim
10 words
The method of claim 1 wherein said substrate is germanium.
Claim 36
Dependent Claim
17 words
The method of claim 7 wherein said substrate is silicon and said mask layer is an insulator.
Claim 37
Dependent Claim
11 words
The method of claim 32 wherein said insulator is silicon dioxide.
Claim 38
Dependent Claim
11 words
The method of claim 32 wherein said insulator is silicon nitride.
Claim 39
Dependent Claim
10 words
The method of claim 7 wherein said substrate is germanium.
Claim 40
Dependent Claim
17 words
The method of claim 14 wherein said substrate is silicon and said mask layer is an insulator.
Claim 41
Dependent Claim
11 words
The method of claim 36 wherein said insulator is silicon dioxide.
Claim 42
Dependent Claim
11 words
The method of claim 36 wherein said insulator is silicon nitride.
Claim 43
Dependent Claim
13 words
The method of claim 14 further comprising the step of heating said substrate.
Claim 44
Dependent Claim
10 words
The method of claim 14 wherein said substrate is germanium.
Claim 45
Dependent Claim
23 words
The method of claim 14 wherein the ratio of the time between said pulses to the duration of said pulses is about 1:3.
Claim 46
Dependent Claim
19 words
The method of claim 14 wherein said providing step further comprises the step of providing an argon ambient atmosphere.
Claim 47
Dependent Claim
17 words
The method of claim 20 wherein said substrate is silicon and said mask layer is an insulator.
Claim 48
Dependent Claim
11 words
The method of claim 43 wherein said insulator is silicon dioxide.
Claim 49
Dependent Claim
11 words
The method of claim 43 wherein said insulator is silicon nitride.
Claim 50
Dependent Claim
13 words
The method of claim 20 further comprising the step of heating said substrate.
Claim 51
Dependent Claim
10 words
The method of claim 20 wherein said substrate is germanium.
Claim 52
Dependent Claim
25 words
The method of claim 20 wherein said removing step is practiced for about 10 seconds and said exposing step is practiced for about 30 seconds.
Claim 53
Dependent Claim
20 words
The method of claim 20 wherein the time ratio of said exposing step to said removing step is about 3:1.
Claim 54
Dependent Claim
58 words
The method of claim 1 wherein said flowing step comprises the step of flowing the reducible compound gas through said heated reaction chamber at a predetermined flow rate, and wherein said interrupting step comprises the step of interrupting the flow of the reducing gas while continuing the flow of the reducible compound gas at said predetermined flow rate.
Claim 55
Dependent Claim
43 words
The method of claim 7 wherein said repeatedly exposing step comprises the step of repeatedly exposing the heated substrate to the reducible compound gas at a predetermined concentration, and the reducing gas, followed by the reducible compound gas alone at said predetermined concentration.
Claim 56
Dependent Claim
61 words
The method of claim 20 wherein said step of exposing said substrate comprises the step of exposing said substrate to the reducible compound gas at a predetermined concentration, and to the reducing gas, and wherein said removing step comprises the step of removing said reducing gas while continuing to expose said substrate to said reducible compound gas at said predetermined concentration.
Claim 57
Dependent Claim
26 words
The method of claim 1 wherein said material and said substrate are selected from the group consisting of silicon, germanium and alloys of silicon and germanium.
Claim 58
Dependent Claim
29 words
The method of claim 7 wherein said single element semiconductor material and said substrate are selected from the group consisting of silicon, germanium and alloys of silicon and germanium.
Claim 59
Dependent Claim
29 words
The method of claim 14 wherein said single element semiconductor material and said substrate are selected from the group consisting of silicon, germanium and alloys of silicon and germanium.
Claim 60
Dependent Claim
29 words
The method of claim 20 wherein said single element semiconductor material and said substrate are selected from the group consisting of silicon, germanium and alloys of silicon and germanium.
References Cited (Backward Citations)
US3785862A
Cited
GB1330720A
Cited
US3998673A
Cited
US4404235A
Cited
US4343676A
Cited
US4349408A
Cited
US4549926A
Cited
US4497683A
Cited
US4673592A
Cited
US4578142A
Cited
US4698316A
Cited
JPS61224313A
Cited
US4653428A
Cited
US4617087A
Cited
US4741928A
Cited
EP0238024A2
Cited
US4786352A
Cited
US4837051A
Cited
EP0273629A2
Cited
US4740483A
Cited
US4786615A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-05 | 1995-02-04 | 1995-08-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-05 | 1999-02-04 | 1999-08-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-05 | 2003-02-04 | 2003-08-06 | $7700.00 | Window Closed / Lapsed |