Multilayer trench isolation process and structure
Assignee: Motorola Solutions Inc
•
Filing: 1988-12-23
•
Granted: 1989-10-03
•
Expires: 2008-12-23
Abstract
Abstract Dielectric filled isolation walls for semiconductor devices and integrated circuits of improved characteristics and ease of manufacture are formed by etching trenches in a semiconductor substrate and refilling the trenches with multiple layers of silicon oxy-nitride. Alternative oxygen rich and nitrogen rich oxy-nitride layers are used. For the narrowest trenches two layers suffice. Where trenches of different widths are present the wider trenches receive multiple layer pairs. A cap layer of oxy-nitride is added to insure filling of any trench intersections. The oxy-nitride desirably has a composition Si x O y N z where x, y, and z are in the range 0.25-0.4, 0.27-0.6, and 0.0-0.35, respectively, for the oxygen rich material and where x, y, and z are in the range 0.34-0.43 m 0.0-0.35, and 0.28-0.6, respectively, for the nitrogen rich material, expressed in atomic fraction and x+y+z=1. Both compositions of oxy-nitride are formed in the same LPCVD reactor by changing the conditions during layer deposition.
Inventors
- 👤 Bridgette A. Bergami
- 👤 Phillip H. Williams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 13:57
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6927; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/66; H10P14/662; H10P14/69215; H10P14/694; H10P14/6943; H10P14/69433; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0143; H10W10/10; H10W10/17
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
101 words
A process for forming dielectric filled trenches, comprising: providing a substrate having a semiconductor surface; providing multiple trenches in the substrate comprising a first trench having a first width and at least a second trench having a second width larger than the first width, wherein the trenches have sidewalls extending from the surface into the substrate and bottoms separated from the surface; and covering the sidewalls and bottoms with multiple dielectric layer pairs of alternating composition and etch rate, including odd-numbered layers of oxygen rich oxy-nitride and even-numbered layers of nitrogen rich oxy-nitride, thicker than layers formed from a native oxide.
Claim 2
Dependent Claim
101 words
A process for forming dielectric filled trenches, comprising: providing a substrate having a semiconductor surface; providing multiple trenches in the substrate comprising a first trench having a first width and at least a second trench having a second width larger than the first width, wherein the trenches have sidewalls extending from the surface into the substrate and bottoms separated from the surface; and covering the sidewalls and bottoms with multiple dielectric layer pairs of alternating composition and etch rate, including odd-numbered layers of oxygen rich oxy-nitride and even-numbered layers of nitrogen rich oxy-nitride, thicker than layers formed from a native oxide.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the covering step comprises providing even-numbered layers thinner than the odd-numbered layers.
Claim 4
Dependent Claim
15 words
The process of claim 1 wherein the composition within individual dielectric layers is substantially uniform.
Claim 5
Dependent Claim
26 words
The process of claim 1 wherein the multiple layers are sequentially formed in a single reactor by varying the composition of reactant gases within the reactor.
Claim 6
Dependent Claim
25 words
The process of claim 1 further comprising prior to the covering step, forming on the sidewalls and bottom a thin base layer of silicon oxide.
Claim 7
Dependent Claim
28 words
The process of claim 1 further comprising after the covering step, depositing a further layer of oxygen rich silicon oxy-nitride on the layers deposited in the covering step.
Claim 8
Dependent Claim
25 words
The process of claim 6 wherein the depositing step is performed in the same reactor and during the same depositing operation as the covering step.
Claim 9
Dependent Claim
116 words
A process for forming dielectric filled trenches, comprising: providing a substrate having a surface; providing multiple trenches in the substrate, comprising a first trench having a first width and at least a second trench having a second width larger than the first width; and at least partially filling the trenches with alternating dielectric layers, at least two in the first trench and at least four in the second trench, wherein odd-numbered layers have a first composition and a first etch rate and even-numbered layers have a second composition different than the first composition and a second etch rate different than the first etch rate, and the layers are thicker than layers formed from a native oxide.
Claim 10
Dependent Claim
116 words
A process for forming dielectric filled trenches, comprising: providing a substrate having a surface; providing multiple trenches in the substrate, comprising a first trench having a first width and at least a second trench having a second width larger than the first width; and at least partially filling the trenches with alternating dielectric layers, at least two in the first trench and at least four in the second trench, wherein odd-numbered layers have a first composition and a first etch rate and even-numbered layers have a second composition different than the first composition and a second etch rate different than the first etch rate, and the layers are thicker than layers formed from a native oxide.
Claim 11
Dependent Claim
29 words
The process of claim 8 wherein the filling step comprises providing odd-numbered layers of an oxygen rich silicon oxy-nitride and providing even-numbered layers of a nitrogen rich silicon oxy-nitride.
Claim 12
Dependent Claim
55 words
The process of claim 8 wherein the step of substantially filled the trenches with alternating dielectric layers comprises providing the alternating dielectric layers in the same reactor by reacting a silicon source material with source of oxygen and nitrogen of a first composition for the odd-numbered layers and a second composition for the even-numbered layers.
Claim 13
Dependent Claim
36 words
The process of claim 10 wherein the step of reacting a silicon source material with sources of oxygen and nitrogen is performed at temperatures of about 900° C. or less and pressures less than atmospheric pressure.
Claim 14
Dependent Claim
31 words
The process of claim 8 further comprising, prior to the step of substantially filling the trenches with alternating dielectric layers, lining the trenches with a thin base layer of silicon oxide.
Claim 15
Dependent Claim
28 words
The process of claim 12 wherein the step of substantially filling the trenches with alternating dielectric layers comprises, providing odd-numbered layers substantially thicker than the thin base layer.
Claim 16
Dependent Claim
25 words
The process of claim 8 wherein the step of substantially filling the trenches with alternating dielectric layers comprises, providing even-numbered layers of substantially equal thickness.
Claim 17
Dependent Claim
24 words
The process of claim 8 wherein the step of substantially filling the trenches with alternating dielectric layers comprises, providing odd-numbered layers substantially equal thickness.
Claim 18
Dependent Claim
25 words
The process of claim 8 wherein the step of substantially filling the trenches with alternating dielectric layers comprises, providing odd-numbered layers thicker than even-numbered layers.
Claim 19
Dependent Claim
40 words
The process of claim 8 further comprising after the step of substantially filling the trenches with alternating dielectric layers, depositing a further layer of oxygen rich silicon oxy-nitride to fill any remaining depressions in the trenches having the largest width.
Claim 20
Dependent Claim
37 words
The process of claim 7 wherein the depositing step is performed in the same reactor as the step of substantially filling the trenches with alternating dielectric layers and during the same run by varying reactant gas composition.
References Cited (Backward Citations)
US204A
Cited
US3883889A
Cited
US4471525A
Cited
US4454646A
Cited
US4454647A
Cited
JPS59181640A
Cited
JPS59182538A
Cited
JPS59193044A
Cited
US4582565A
Cited
US4584763A
Cited
US4569701A
Cited
US4580330A
Cited
US4589193A
Cited
US4571819A
Cited
USH204H
Cited
US4621414A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-02 | 1993-04-03 | 1993-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-02 | 1997-04-03 | 1997-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-02 | 2001-04-03 | 2001-10-03 | $7700.00 | Window Closed / Lapsed |