Tracking-resistant, electrical-insulating material containing silane-modified polyolefins
Assignee: Shawcor Ltd
•
Filing: 2000-10-17
•
Granted: 2002-10-22
•
Expires: 2020-10-17
Abstract
Abstract A tracking resistant electrical insulating material or article suitable for medium to high voltage applications comprising a silane-modified polyolefin, and a heat-shrinkable article prepared therefrom. Said material or article is preferably prepared by a process comprising: (a) reacting polyolefin with a silane in the presence of a free-radical initiator to form a silane-grafted polyolefin, or copolymerising a polyolefin with silane; (b) preparing a mixture of one or more silane-modified polyolefins prepared in (a) with optionally one or more non silane-modified polyolefins, antitrack ingredients, and a silanol condensation catalyst; (c) forming the insulating material or article by melt extruding or moulding said mixture; and (d) crosslinking the insulating material or article by exposing it to moisture, preferably at elevated temperature. The silane-modified, moisture-crosslinkable polyolefin provides the insulating material with high resistance to tracking even in the absence of conventional anti-tracking fillers.
Inventors
- 👤 Peter Jackson
- 👤 Marcus P. Heydrich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:31
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/44; H01B3/441; H01B7/00; H01B7/17; H01B7/28; Y; Y02; Y02A; Y02A30/00; Y02A30/14; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
125 words
A method of protecting electrical equipment from damage due to tracking and spark erosion, comprising: (a) forming a mixture comprised of a silane-modified polyolefin with a silanol condensation catalyst, said silane-modified polyolefin comprising either a silane-grafted polyolefin or a silane-olefin copolymer; (b) melt extruding or moulding the mixture formed in step (a) to form an article; (c) crosslinking the article by exposing it to moisture, preferably at elevated temperature, such that the article is softened but does not melt when heated to a temperature above its softening point; (d) applying the article to said electrical equipment so as to form an external, insulating layer on said equipment; and (e) exposing said equipment with said insulating layer to electrical and atmospheric conditions conducive to surface tracking.
Claim 2
Independent Claim
125 words
A method of protecting electrical equipment from damage due to tracking and spark erosion, comprising: (a) forming a mixture comprised of a silane-modified polyolefin with a silanol condensation catalyst, said silane-modified polyolefin comprising either a silane-grafted polyolefin or a silane-olefin copolymer; (b) melt extruding or moulding the mixture formed in step (a) to form an article; (c) crosslinking the article by exposing it to moisture, preferably at elevated temperature, such that the article is softened but does not melt when heated to a temperature above its softening point; (d) applying the article to said electrical equipment so as to form an external, insulating layer on said equipment; and (e) exposing said equipment with said insulating layer to electrical and atmospheric conditions conducive to surface tracking.
Claim 3
Dependent Claim
22 words
The method according to claim 1 , wherein the mixture formed in step (a) further comprises one or more non silane-modified polyolefins.
Claim 4
Dependent Claim
73 words
The method according to claim 1 , where the article is heat-shrinkable, and the process additionally comprises the following step between steps (c) and (d): stretching the article produced in step (c) above its softening or melting point, and then cooling the article so as to freeze it in its stretched form; and wherein the step of applying the article to the electrical equipment includes heat shrinking the article onto the electrical equipment.
Claim 5
Dependent Claim
37 words
The method according to claim 2 , wherein the silane-modified polyolefin and the non-silane modified polyolefin are selected from the group comprising polyethylene and copolymers of ethylene with an olefin having from 3 to 20 carbon atoms.
Claim 6
Dependent Claim
41 words
The method according to claim 2 , wherein the silane-modified polyolefin and the non-silane modified polyolefin comprise a copolymer of ethylene with one or more of propylene, butylene, hexene, octene, methylene norbornene, vinyl acetate, methyl acrylate, ethyl acrylate and butyl acrylate.
Claim 7
Dependent Claim
29 words
The method according to claim 2 , wherein the density of the silane-modified polyolefin and the non silane-modified polyolefin is from about 0.85 to about 0.95 g/cm 3 .
Claim 8
Dependent Claim
60 words
The method according to claim 1 , wherein the silane-modified polyolefin comprises a polyolefin which has been reacted with a silane of the general formula RR′SiY 2 wherein R represents a monovalent olefinically unsaturated hydrocarbon or hydrocarbonoxy radical, Y represents a hydrolysable organic radical and R′ represents a monovalent olefinically unsaturated hydrocarbon or hydrocarbonoxy radical or a hydrolysable organic radical.
Claim 9
Dependent Claim
29 words
The method according to claim 7 , wherein the monovalent olefinically unsaturated hydrocarbon or hydrocarbonoxy radical is selected from the group comprising vinyl, allyl, butenyl, cyclohexenyl, cyclopentadienyl, and cyclohexadienyl.
Claim 10
Dependent Claim
71 words
The method according to claim 7 , wherein Y represents a hydrolysable organic radical selected from the group comprising methoxy, ethoxy, butoxy, formyloxy, acetoxy, propionoxy; oximo radicals selected from —ON═C(CH 3 ) 2 , —ON═CCH 3 C 2 H 5 and ON═C(C 6 H 5 ) 2 ; or substituted alkylamino or arylamino radicals selected from -NHCH 3 , —NHC 2 H 5 and —NH(C 6 H 5 ) 2 .
Claim 11
Dependent Claim
26 words
The method according to claim 7 , wherein the silane has general formula RSiY 3 , with R being vinyl and Y being methoxy or ethoxy.
Claim 12
Dependent Claim
32 words
The method according to claim 7 , wherein the amount of the silane reacted with the ethylene-based polyolefin is from about 0.5 to about 2.5 percent by weight of the silane-modified polyolefin.
Claim 13
Dependent Claim
24 words
The method according to claim 1 , wherein a reaction between the polyolefin and the silane is initiated by an organic peroxide free-radical initiator.
Claim 14
Dependent Claim
36 words
The method according to claim 2 , wherein the non saline-modified polyolefin is added to the mixture of step (a) in an amount of from about 10 to about 70 percent by weight of the article.
Claim 15
Dependent Claim
23 words
The method according to claim 1 , wherein the silanol condensation catalyst is selected from the group comprising dibutyltin dilaurate and dibutyltin oxide.
Claim 16
Dependent Claim
34 words
The method according to claim 1 , wherein the silanol condensation catalyst is added to the mixture of step (b) in an amount of about 0.05 to 0.2 percent by weight of the article.
Claim 17
Dependent Claim
36 words
The method according to claim 1 , wherein said article additionally comprises ingredients selected from one or more members of the group comprising antioxidants, anti-track fillers, colorants, UV stabilizers, process aids, anti-wetting agents and additional polymers.
Claim 18
Dependent Claim
21 words
The method according to claim 16 , wherein the antioxidants are selected from the group comprising hindered phenols, dihydroquinolines and phosphites.
Claim 19
Dependent Claim
14 words
The method according to claim 16 , wherein the anti-track filler is alumina trihydrate.
Claim 20
Dependent Claim
13 words
The method according to claim 16 , wherein the colorant is ferric oxide.
Claim 21
Dependent Claim
25 words
The method according to claim 16 , wherein the process aid or anti-wetting agent is a polytetrafluoroethylene powder, polyethylene wax, fafty acid or silicone oil.
Claim 22
Dependent Claim
15 words
The method according to claim 16 , wherein the additional polymer is a silicone rubber.
Claim 23
Dependent Claim
44 words
The method according to claim 1 , wherein the article has a time-to-track of greater than about 100 minutes and an initial tracking voltage of greater than about 1,500 V, the time-to-track and the initial tracking voltage being determined in accordance with ASTM D2303.
Claim 24
Dependent Claim
16 words
The method according to claim 1 , wherein the article is substantially free of anti-track fillers.
Claim 25
Independent Claim
90 words
A method of protecting electrical equipment from damage due to tracking and spark erosion, comprising: (a) providing said electrical equipment with an insulating layer comprising: (i) a silane-modified polyolefin comprising either a silane-grafted polyolefin or a silane-olefin copolymer; and (ii) a silanol condensation catalyst; wherein the insulating layer is moisture crosslinked to a degree such that it is softened but does not melt when heated to a temperature above its softening point; and (b) exposing said equipment with said insulating layer to electrical and atmospheric conditions conducive to surface tracking.
Claim 26
Independent Claim
90 words
A method of protecting electrical equipment from damage due to tracking and spark erosion, comprising: (a) providing said electrical equipment with an insulating layer comprising: (i) a silane-modified polyolefin comprising either a silane-grafted polyolefin or a silane-olefin copolymer; and (ii) a silanol condensation catalyst; wherein the insulating layer is moisture crosslinked to a degree such that it is softened but does not melt when heated to a temperature above its softening point; and (b) exposing said equipment with said insulating layer to electrical and atmospheric conditions conducive to surface tracking.
Claim 27
Dependent Claim
19 words
The method according to claim 24 , wherein said insulating layer further comprises one or more non silane-modified polyolefins.
Claim 28
Dependent Claim
22 words
The method of claim 24 , wherein the insulating layer is heat shrunk during application to the electrical equipment by heat shrinking.
Claim 29
Dependent Claim
17 words
The method according to claim 24 , wherein the insulating layer is substantially free of anti-track fillers.
Claim 30
Dependent Claim
93 words
An electrical insulating material suitable for high voltage applications which is resistant to tracking and spark erosion, comprising a silane-modified, moisture-crosslinked polymeric material formed by a process comprising: (a) creating a mixture of a silane-modified polyolefin comprising either a silane-grafted polyolefin or a silane-olefin copolymer, with one or more non silane-modified polyolefins and a silanol condensation catalyst; (b) forming the insulating material by melt extruding, or moulding, the mixture prepared in step (a); and (c) moisture crosslinking the insulating material; said insulating material further comprising a colorant, wherein the colorant is ferric oxide.
Claim 31
Dependent Claim
93 words
An electrical insulating material suitable for high voltage applications which is resistant to tracking and spark erosion, comprising a silane-modified, moisture-crosslinked polymeric material formed by a process comprising: (a) creating a mixture of a silane-modified polyolefin comprising either a silane-grafted polyolefin or a silane-olefin copolymer, with one or more non silane-modified polyolefins and a silanol condensation catalyst; (b) forming the insulating material by melt extruding, or moulding, the mixture prepared in step (a); and (c) moisture crosslinking the insulating material; said insulating material further comprising a colorant, wherein the colorant is ferric oxide.
Claim 32
Dependent Claim
50 words
An electrical insulating material according to claim 28 , wherein the insulating material is heat-shrinkable, and the process additionally comprises: (d) stretching the insulating material produced in step (c) above its softening or melting point, and then cooling the insulating material so as to freeze it in its stretched form.
Claim 33
Dependent Claim
19 words
An electrical insulating material according to claim 28 , wherein the insulating material is substantially free of anti-track fillers.
References Cited (Backward Citations)
US3646155A
Cited
US4058583A
Cited
JPS5321248A
Cited
US4228255A
Cited
US4329536A
Cited
GB2093760A
Cited
US4549041A
Cited
US4680319A
Cited
US4529750A
Cited
US4921916A
Cited
GB2172895A
Cited
US4870136A
Cited
US4902460A
Cited
US4732939A
Cited
US5002996A
Cited
US5237014A
Cited
US5773145A
Cited
US5384369A
Cited
EP0575111A2
Cited
US5367030A
Cited
JPH06335967A
Cited
US5430091A
Cited
JPH07330979A
Cited
US5492760A
Cited
US5824718A
Cited
US5756023A
Cited
US5837939A
Cited
WO1998023687A1
Cited
JPH10245456A
Cited
US5919565A
Cited
US6043306A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2005-10-21 | 2006-04-22 | 2006-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2009-10-21 | 2010-04-22 | 2010-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2013-10-21 | 2014-04-22 | 2014-10-22 | $7700.00 | Window Closed / Lapsed |