US4902460A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for preparation of molecularly oriented, silane-crosslinked ultra-high-molecular-weight polyethylene molded article
Assignee: Mitsui Chemicals Inc
•
Filing: 1988-04-14
•
Granted: 1990-02-20
•
Expires: 2008-04-14
Abstract
Abstract If ultra-high-molecular-weight polyethylene having an intrinsic viscosity (β) of at least 5 dl/g is grafted with a silane compound in the presence of a radical initiator and extrusion-molded and the extrudate is impregnated with a silanol condensation catalyst after or during drawing and is then exposed to water to effect crosslinking, there is obtained a novel molecularly oriented molded article in which increase of the melting temperature, which is not observed in conventional drawmolded or crosslinked molded articles of polyethylene, can be attained, and even if this molecularly oriented molded article is exposed to a temperature of 180° C. for 10 minutes, the molded article is not fused but the shape is retained and even after this heat history, a high strength retention ratio can be maintained. In this draw-molded article, the adhesiveness and creep resistance are prominently improved while high elastic modulus and high tensile strength inherent to a drawmolded article of ultra-high-molecular-weight polyethylene are retained.
Inventors
- 👤 Kazuo Yagi
- 👤 Hitoshi Mantoku
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:23
CPC Classifications
C; C08; C08F; C08F255/00; C08F255/02; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; C08L2666/00; C08L2666/02; C08L43/00; C08L43/04; D; D01; D01F; D01F11/00; D01F11/04; D01F11/06; D01F6/00; D01F6/02; D01F6/04; C08L2207/00; C08L2207/06; C08L2207/068; C08L2312/00; C08L2312/08; C08L51/00; C08L51/06; C08L91/00
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
187 words
A process for the preparation of a molecularly oriented, silane-cross-linked ultra-high-molecular-weight polyethylene molded article, which comprises (i) melt-kneading a mixture of (a) an ultra-high-molecular-weight polyethylene having an intrinsic viscosity (η) of at least 5 dl/g, (b) 0.1 to 10 parts by weight, per 100 parts by weight of the component (a), of a silane compound having both of a radical-polymerizable organic group and a hydrolyzable organic group, (c) 0.01 to 3 parts by weight, per 100 parts by weight of the component (a), of a radical initiator and 9900 to 33 parts by weight, per 100 parts by weight of the component (a), of a diluent, (ii) melt-extruding the resultant kneaded composition through a spinneret or a die to form an undrawn molded article, (iii) subjecting the obtained undrawn molded article of the silane-grafted ultra-high-molecular-weight polyethylene to a drawing treatment so that the drawn molded article has an orientation degree(F) of at least 0.90, (iv) impregnating the molded article with a silanol condensation catalyst during or after the drawing step (iii), and (v) contacting the drawn molded article impregnated with the catalyst with water to effect cross-linking.
Claim 2
Dependent Claim
187 words
A process for the preparation of a molecularly oriented, silane-cross-linked ultra-high-molecular-weight polyethylene molded article, which comprises (i) melt-kneading a mixture of (a) an ultra-high-molecular-weight polyethylene having an intrinsic viscosity (η) of at least 5 dl/g, (b) 0.1 to 10 parts by weight, per 100 parts by weight of the component (a), of a silane compound having both of a radical-polymerizable organic group and a hydrolyzable organic group, (c) 0.01 to 3 parts by weight, per 100 parts by weight of the component (a), of a radical initiator and 9900 to 33 parts by weight, per 100 parts by weight of the component (a), of a diluent, (ii) melt-extruding the resultant kneaded composition through a spinneret or a die to form an undrawn molded article, (iii) subjecting the obtained undrawn molded article of the silane-grafted ultra-high-molecular-weight polyethylene to a drawing treatment so that the drawn molded article has an orientation degree(F) of at least 0.90, (iv) impregnating the molded article with a silanol condensation catalyst during or after the drawing step (iii), and (v) contacting the drawn molded article impregnated with the catalyst with water to effect cross-linking.
Claim 3
Dependent Claim
49 words
A process according to claim 1, wherein the silane compound is a compound represented by the following formula: R.sub.n SiY.sub.4-n wherein R stands for an organic group containing a radical polymerizable ethylenic unsaturation, Y stands for a hydrolyzable organic group and n is a number of 1 or 2.
Claim 4
Dependent Claim
15 words
A process according to claim 1, wherein the silane compound is vinyltriethoxysilane, vinyltrimethoxysilane or vinyltris(methoxyethoxy)silane.
Claim 5
Dependent Claim
24 words
A process according to claim 1, wherein the radical initiator is a radical initiator having a half-value period temperature of 100° to 200° C.
Claim 6
Dependent Claim
38 words
A process according to claim 1, wherein the diluent is a solvent having a boiling point higher than the melting point of the ultra-high-molecular-weight polyethylene or a wax or waxy substance having a compatibility with the ultra-high-molecular-weight polyethylene.
Claim 7
Dependent Claim
50 words
A process according to claim 1, wherein the silane compound, the radical initiator and the diluent are incorporated in amounts of 0.2 to 5.0 parts by weight, 0.05 to 0.5 parts by weight and 1900 to 100 parts by weight, respectively, per 100 parts by weight of the ultra-high-molecular-weight polyethylene.
Claim 8
Dependent Claim
27 words
A process according to claim 1, wherein the composition comprising the ultra-high-molecular-weight polyethylene, the silane compound, the radical initiator and the diluent is melt-extruded through a spinneret.
Claim 9
Dependent Claim
31 words
A process according to claim 1, wherein the silane-grafted polyethylene molded article is drawn at a draw ratio of 5 to 80 in a heat medium at 40° to 160° C.
Claim 10
Dependent Claim
35 words
A process according to claim 8, wherein the heat medium is a solvent capable of removing the diluent by extraction and having a boiling point higher than the melting point of the molded article composition.
Claim 11
Dependent Claim
22 words
A process according to claim 1, wherein the silanol condensation catalyst is a dialkyl tin dicarboxylate, an organic titanate or lead naphthenate.
Claim 12
Dependent Claim
28 words
A process according to claim 1, wherein crosslinking is effected by contacting the drawn molded article with water at 50° to 130° C. for 3 to 24 hours.
Claim 13
Dependent Claim
20 words
A process according to claim 1 wherein the ultra-high-molecular-weight polyethylene has an intrinsic viscosity of from 7 to 30 dl/g.
Claim 14
Dependent Claim
23 words
A process according to claim 1 wherein the melt-kneading step (i) is carried out at a temperature of from 150° C.to 300° C.
Claim 15
Dependent Claim
53 words
A process according to claim 1 wherein the filament melt-extruded through the spinneret is drafted at a draft ratio V/Vo, wherein Vo stands for the extrusion speed of the molten resin in the die orifice and V stands for the winding speed of the cooled and solidified, drawn extrudate, of at least 3.
Claim 16
Dependent Claim
24 words
A process according to claim 1 wherein the drawing treatment step (iii) is carried out at a temperature from 40° C. to 160° C.
Claim 17
Dependent Claim
225 words
A process for the preparation of a molecularly oriented, silane-cross-linked ultra-high-molecular-weight polyethylene molded article, which comprises (i) melt-kneading a mixture of (a) an ultra-high-molecular-weight polyethylene having an intrinsic viscosity (η) of at least 5 dl/g, (b) 0.1 to 10 parts by weight, per 100 parts by weight of the component (a), of a silane compound represented by the following formula: R.sub.n SiY.sub.4-n wherein R stands for an organic group containing a radical-polymerizable ethylenic unsaturation, Y stands for a hydrolyzable organic group and n is a number of 1 or 2, (c) 0.01 to 3 parts by weight, per 100 parts by weight of the component (a), of a radical initiator having a half-value period temperature of 100° to 200° C. and (d) 1900 to 100 parts by weight, per 100 parts by weight of the component (a), of a wax or waxy substance having a compatibility with said ultra-high-molecular-weight polyethylene, (ii) melt-extruding the resultant kneaded composition through a spinneret or a die to form an undrawn molded article, (iii) subjecting the obtained undrawn molded article of the silane-grafted ultra-high-molecular-weight polyethylene to a drawing treatment at a draw ratio of 5 to 80, (iv) impregnating the molded article with a silanol condensation catalyst during or after the drawing step (iii), and (v) contacting the drawn molded article impregnated with the catalyst with water to effect cross-linking.
Claim 18
Dependent Claim
225 words
A process for the preparation of a molecularly oriented, silane-cross-linked ultra-high-molecular-weight polyethylene molded article, which comprises (i) melt-kneading a mixture of (a) an ultra-high-molecular-weight polyethylene having an intrinsic viscosity (η) of at least 5 dl/g, (b) 0.1 to 10 parts by weight, per 100 parts by weight of the component (a), of a silane compound represented by the following formula: R.sub.n SiY.sub.4-n wherein R stands for an organic group containing a radical-polymerizable ethylenic unsaturation, Y stands for a hydrolyzable organic group and n is a number of 1 or 2, (c) 0.01 to 3 parts by weight, per 100 parts by weight of the component (a), of a radical initiator having a half-value period temperature of 100° to 200° C. and (d) 1900 to 100 parts by weight, per 100 parts by weight of the component (a), of a wax or waxy substance having a compatibility with said ultra-high-molecular-weight polyethylene, (ii) melt-extruding the resultant kneaded composition through a spinneret or a die to form an undrawn molded article, (iii) subjecting the obtained undrawn molded article of the silane-grafted ultra-high-molecular-weight polyethylene to a drawing treatment at a draw ratio of 5 to 80, (iv) impregnating the molded article with a silanol condensation catalyst during or after the drawing step (iii), and (v) contacting the drawn molded article impregnated with the catalyst with water to effect cross-linking.
Claim 19
Dependent Claim
20 words
A process according to claim 16 wherein the ultra-high-molecular-weight polyethylene has an intrinsic viscosity of from 7 to 30 dl/g.
Claim 20
Dependent Claim
39 words
A process according to claim 16 wherein the step of melt-kneading (i) is at a temperature of from 150° C. to 300° C. and the drawing treatment step (iii) is at a temperature from 40° C. to 160° C.
Claim 21
Dependent Claim
39 words
A process according to claim 16 wherein the step of melt-kneading (i) is at a temperature of from 170° C. to 270° C. and the drawing treatment step (iii) is at a temperature from 80° C. to 145° C.
Claim 22
Dependent Claim
15 words
A process according to claim 16 wherein the silane compound is vinyltriethoxysilane, vinyltrimethoxysilane or vinyltris(methoxyethoxy)silane.
Claim 23
Dependent Claim
39 words
A process according to claim 16 wherein the diluent is a solvent having a boiling point higher than that the melting point of the ultra-high-molecular-weight polyethylene or a wax or waxy substance having a compatibility with the ultra-high-molecular-weight polyethylene.
Claim 24
Dependent Claim
42 words
A process according to claim 16 wherein the silane compound and the radical initiator are incorporated in amounts of 0.2 to 0.5 parts by weight and 0.05 to 0.5 parts by weight, respectively, per 100 parts by weight of the ultra-high-molecular-weight polyethylene.
Claim 25
Dependent Claim
67 words
A process according to claim 16 wherein in step (ii) the resultant kneaded composition is melted-extruded through a spinneret to form a filament and wherein said filament is drafted at a draft ratio, V/Vo, wherein Vo stands for the extrusion speed of the molten resin in the die orifice and V stands for the winding speed of the cooled and solidified, drawn extrudate, of at least 3.
Claim 26
Dependent Claim
33 words
A process according to claim 16 wherein the drawing treatment step (ii) is a draw ratio of 10 to 50 and is carried out in a heat medium at 80° to 145° C.
Claim 27
Dependent Claim
35 words
A process according to claim 24 wherein the heat medium is a solvent capable of removing the diluent by extraction and having a boiling point higher than the melting point of the molded article composition.
Claim 28
Dependent Claim
22 words
A process according to claim 16 wherein the silanol condensation catalyst is a dialkyl tin dicarboxylate, an organic titanate or lead naphthenate.
Claim 29
Dependent Claim
27 words
A process according to claim 16 wherein the cross-linking step (v) is carried out at a temperature of 50° to 130° C. for 3 to 24 hours.
References Cited (Backward Citations)
US3646155A
Cited
US4136132A
Cited
JPS52154872A
Cited
JPS53104673A
Cited
US4422993A
Cited
US4430383A
Cited
JPS575913A
Cited
JPS5837391A
Cited
US4545950A
Cited
US4595546A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-19 | 1993-08-21 | 1994-02-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-19 | 1997-08-21 | 1998-02-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-19 | 2001-08-21 | 2002-02-20 | $7700.00 | Window Closed / Lapsed |