Process for producing stretched articles of ultrahigh-molecular-weight polyethylene
Assignee: Mitsui Chemicals Inc
•
Filing: 1983-12-28
•
Granted: 1985-10-08
•
Expires: 2003-12-28
Abstract
Abstract Stretched articles of ultrahigh-molecular-weight polyethylene are prepared by melt-kneading a mixture of ultrahigh-molecular-weight polyethylene with a paraffinic wax having a melting point of 40 DEG to 120 DEG C. and a weight average molecular weight of at least 230 but less than 2000 in a screw extruder while maintaining the temperature of the mixture at 180 DEG to 280 DEG C. The molten mixture is melt-extruded through a die at a temperature of 180 DEG to 300 DEG C. and the resulting unstretched extrudate is cooled to solidify it. The unstretched solidified extrudate is then subjected to a stretching treatment at a temperature of 60 DEG to 140 DEG C. at a particular stretch ratio. Stretch shaped articles of ultrahigh-molecular-weight polyethylene having high tensile strength and modulus of elasticity are produced uniformly and reproducibly. The stretched shaped articles are substantially free from stretching uneveness. Examples of the paraffinic wax include n-alkanes having at least 22 carbon atoms.
Inventors
- 👤 Masanori Motooka
- 👤 Hitoshi Mantoku
- 👤 Takao Ohno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:14
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; B; B29; B29C; B29C48/00; B29C48/022; B29C48/03; B29C48/05; B29C48/07; B29C48/08; B29C48/25; B29C48/78; B29C48/80; B29C48/802; B29C48/86; B29C48/865; B29C48/88; B29C48/91; B29C48/919; C08F; C08F255/00; C08F255/02; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; D; D01; D01F; D01F6/00; D01F6/44; D01F6/46; B29C48/001; B29C48/0018; B29C48/15; B29C55/00; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2023/0658; B29K2023/0683; B29K2995/00; B29K2995/0037; B29K2995/0088; B29L; B29L2007/00; B29L2007/008; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/06
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
197 words
A process for producing a stretched article of ultrahigh-molecular-weight polyethylene, which comprises (1) melt-kneading a mixture composed of (A) 15 to 80 parts by weight, per 100 parts by weight of the components (A) and (B) combined, of ultrahigh-molecular-weight polyethylene having an inherent viscosity [η], determined at 135° C. in decalin, of at least 5 dl/g and (B) 85 to 20 parts by weight, per 100 parts by weight of the components (A) and (B) combined, of a paraffinic wax having a melting point, determined by the DSC method, of 40° to 120° C. and a weight average molecular weight (Mw), determined by the GPC method, of at least 230 but less than 2,000 in a screw extruder while maintaining the temperature of the mixture at 180 to 280° C., (2) melt-extruding the molten mixture through a die kept at a temperature of 180° to 300° C., under a draft condition at a draft ratio of not less than 2, (3) cooling the resulting unstretched extrudate to solidify it, and (4) subjecting the unstretched solidified extrudate to a stretching treatment at a temperature of 60° to 140° C. at a stretch ratio of at least about 3:1.
Claim 2
Dependent Claim
197 words
A process for producing a stretched article of ultrahigh-molecular-weight polyethylene, which comprises (1) melt-kneading a mixture composed of (A) 15 to 80 parts by weight, per 100 parts by weight of the components (A) and (B) combined, of ultrahigh-molecular-weight polyethylene having an inherent viscosity [η], determined at 135° C. in decalin, of at least 5 dl/g and (B) 85 to 20 parts by weight, per 100 parts by weight of the components (A) and (B) combined, of a paraffinic wax having a melting point, determined by the DSC method, of 40° to 120° C. and a weight average molecular weight (Mw), determined by the GPC method, of at least 230 but less than 2,000 in a screw extruder while maintaining the temperature of the mixture at 180 to 280° C., (2) melt-extruding the molten mixture through a die kept at a temperature of 180° to 300° C., under a draft condition at a draft ratio of not less than 2, (3) cooling the resulting unstretched extrudate to solidify it, and (4) subjecting the unstretched solidified extrudate to a stretching treatment at a temperature of 60° to 140° C. at a stretch ratio of at least about 3:1.
Claim 3
Dependent Claim
24 words
The process of claim 1 wherein the weight average molecular weight of the paraffinic wax (B) is at least 230 but less than 1,000.
Claim 4
Dependent Claim
19 words
The process of claim 1 wherein the inherent viscosity of the ultrahigh-molecular-weight polyethylene (A) is 5 to 30 dl/g.
Claim 5
Dependent Claim
19 words
The process of claim 1 wherein the melting point of the paraffinic wax (B) is 45° to 110° C.
Claim 6
Dependent Claim
69 words
The process of claim 1 wherein the paraffinic wax (B) is a member selected from the group consisting of n-alkanes having at least 22 carbon atoms, mixtures of a major proportion of the n-alkanes and a minor proportion of lower n-alkanes, paraffin wax, polyethylene waxes, ethylene copolymer waxes, heat-degraded polyethylene waxes, heat-degraded ethylene copolymer waxes, oxidation products of these waxes, and alpha, beta-unsaturated acid-modified products of the foregoing waxes.
Claim 7
Dependent Claim
19 words
The process of claim 1 wherein the stretch ratio in step (4) is from about 3:1 to about 50:1.
Claim 8
Dependent Claim
34 words
The process of claim 1 wherein the paraffinic wax (B) has a molecular weight of from about 800 to about 2,000 and wherein the stretch ratio in step (4) is at least about 5:1.
Claim 9
Dependent Claim
21 words
The process of claim 1 wherein the stretching treatment in step (4) is at a temperature of 100° to 135° C.
Claim 10
Dependent Claim
49 words
The process of claim 1 which comprises subjecting the unstretched solidified extrudate to said stretching treatment in a heated liquid medium which is a solvent for the paraffinic wax (B) whereby at least some of the paraffinic wax (B) is extracted from the extrudate simultaneously with the stretching treatment.
Claim 11
Dependent Claim
17 words
The process of claim 1 wherein the draft ratio in step (2) is from 2 to 50.
References Cited (Backward Citations)
US3502764A
Cited
GB1171442A
Cited
GB1171232A
Cited
US3665068A
Cited
US3903234A
Cited
US4422993A
Cited
US4430383A
Cited
US4327009A
Cited
US4413110A
Cited
JPS57193319A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-10-07 | 1989-04-08 | 1989-10-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-10-07 | 1993-04-08 | 1993-10-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-10-07 | 1997-04-08 | 1997-10-08 | $7700.00 | Window Closed / Lapsed |