Molecular oriented, silane-crosslinked ultra-high-molecular-weight polyethylene molded article and process for preparation thereof

Claim 2

A molecularly oriented, silane-crosslinked ultra-high-molecular-weight polyethylene molded article, wherein when the molded article is analyzed in the constrained state by a differential scanning calorimeter, at least two crystal-melting peaks (Tp) appear at temperatures higher by at least 10° C. than the inherent crystal-melting temperature (Tm) of the ultra-high-molecular-weight polyethylene obtained as the main melting peak at the second temperature elevation and the melting calorific value of the crystal-melting peaks (Tp) is at least 50% of the total melting calorific value, and the sum of calorific values of high temperature side melting peaks (Tp1) appearing at temperatures in the range of from (Tm+35° C.) to (Tm+120° C.) is at least 5% of the total melting calorific value.

Claim 3

A molded article as set forth in claim 1, wherein the heat-resistant creep characteristic of the molded article is such that if the molded article is placed at 70° C. under a load corresponding to 30% of the breaking load at room temperature, the molded article is not broken for at least 1 minute.

Claim 4

A molded article as set forth in claim 1, wherein after the molded article is heated at 180° C. for 10 minutes, the molded article has a strength retention ratio of at least 60%.

Claim 5

A molded article as set forth in claim 1, wherein the molded article contains a grafted silane in an amount of 0.01 to 5% by weight as the content of Si based on the ultra-high-molecular-weight polyethylene.

Claim 6

A molded article as set forth in claim 1, which is in the form of a filament.

Claim 7

A molded article as set forth in claim 5, wherein the orientation degree (F) is at least 0.90.

Claim 8

A molded article as set forth in claim 5, wherein the elasticity modulus is at least 20 GPa and the tensile strength is at least 1.2 GPa.

Claim 9

A molded article as set forth in claim 1 wherein the ultra-high-molecular-weight polyethylene has an intrinsic viscosity of from 7 to 30 dl/g as measured at 135° C. in decalin.

Claim 10

A molded article as set forth in claim 1, which is in the form of a film, sheet or tape.

Claim 11

A molded article as set forth in claim 1 wherein the sum of calorific values of high temperature side melting peaks (Tp1) appearing at temperatures in the range of from (Tm+35° C.) to (Tm+120° C.) is at least 10% of the total melting calorific value.

Claim 12

A molecularly oriented, silane-crosslinked ultra-high-molecular-weight polyethylene molded article said article being obtained by spinning a silane-grafted ultra-high-molecular-weight polyethylene into a filament, drawing the grafted filament and then crosslinking the drawn grafted filament; wherein said ultra-high-molecular-weight polyethylene has an intrinsic viscosity (η) of at least 5 dl/g and said article contains the grafted silane in an amount of 0.01 to 5% by weight as the content of Si based on the ultra-high-molecular-weight polyethylene; said article having at least two crystal-melting peaks (Tp) appearing at temperatures higher by at least 10° C. than the inherent crystal-melting temperature (Tm) of the ultra-high-molecular-weight polyethylene obtained as the main melting peak at the second temperature elevation, when the molded article is analyzed in the constrained state by a differential scanning calorimeter, the melting calorific value of the crystal-melting peaks (Tp) is at least 50% of the total melting calorific value, the sum of calorific values of high temperature side melting peaks (Tp1) appearing at temperatures in the range of from (Tm+35° C.) to (Tm+120° C.) is at least 5% of the total melting calorific value, and said article having an elasticity of at least 20 GPa, a tensile strength of at least 1.2 GPa and a strength retention ratio of at least 60% after the article is heated at 180° C. for 10 minutes.

Claim 13

A molecularly oriented, silane-crosslinked ultra-high-molecular-weight polyethylene molded article said article being obtained by spinning a silane-grafted ultra-high-molecular-weight polyethylene into a filament, drawing the grafted filament and then crosslinking the drawn grafted filament; wherein said ultra-high-molecular-weight polyethylene has an intrinsic viscosity (η) of at least 5 dl/g and said article contains the grafted silane in an amount of 0.01 to 5% by weight as the content of Si based on the ultra-high-molecular-weight polyethylene; said article having at least two crystal-melting peaks (Tp) appearing at temperatures higher by at least 10° C. than the inherent crystal-melting temperature (Tm) of the ultra-high-molecular-weight polyethylene obtained as the main melting peak at the second temperature elevation, when the molded article is analyzed in the constrained state by a differential scanning calorimeter, the melting calorific value of the crystal-melting peaks (Tp) is at least 50% of the total melting calorific value, the sum of calorific values of high temperature side melting peaks (Tp1) appearing at temperatures in the range of from (Tm+35° C.) to (Tm+120° C.) is at least 5% of the total melting calorific value, and said article having an elasticity of at least 20 GPa, a tensile strength of at least 1.2 GPa and a strength retention ratio of at least 60% after the article is heated at 180° C. for 10 minutes.