US4228255A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing crosslinked polyethylenes
Assignee: Fujikura Cable Works Ltd
•
Filing: 1979-06-28
•
Granted: 1980-10-14
•
Expires: 1999-06-28
Abstract
Abstract A novel method for crosslinking a polyolefin comprising reacting a polyolefin, which is a low density polyethylene having a density less than 0.93 and melt index of 0.1-0.5 g/10 min. or a polyolefin mixture containing a low density polyethylene having a density less than 0.93 as major component, with an organic silane and a free radical generating compound to form a silane-grafted polyolefin, then mixing silane-grafted polyolefin with a silanol condensation catalyst, and heating them. According to this method, the crosslinking takes place concurrently with forming by extrusion, and a shaped article having a high degree of crosslinking with smooth surface is obtained. The method according to this invention is especially suited for covering electrical wires with polyolefin.
Inventors
- 👤 Ikuo Fujimoto
- 👤 Setsuya Isshiki
- 👤 Yoshikazu Kurita
- 👤 Yoji Sato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 01:54
CPC Classifications
C; C08; C08F; C08F230/00; C08F230/04; C08F230/08; C08F230/085; C08F255/00; C08F255/02
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
129 words
A method for producing a crosslinked polyolefin comprising reacting a polyolefin which is a low density polyethylene having a density less than 0.93 and a melt index of 0.1 to 0.5 g/10 min. or a polyolefin mixture containing a low density polyethylene having a density less than 0.93 as major component, with a free radical generating compound and an organic silane having the general formula RR'SiY 2 , wherein R represents a monovalent olefinically unsaturated hydrocarbon or hydrocarbonoxy radical, each Y represents a hydrolyzable organic radical, and R' represents a monovalent hydrocarbon radical with the exception of aliphatically unsaturated hydrocarbon radicals, or a Y radical, to form a silane-grafted polyolefin, then mixing said silane-grafted polyolefin with a silanol condensation catalyst, and heating the mixture in the absence of water.
Claim 2
Independent Claim
129 words
A method for producing a crosslinked polyolefin comprising reacting a polyolefin which is a low density polyethylene having a density less than 0.93 and a melt index of 0.1 to 0.5 g/10 min. or a polyolefin mixture containing a low density polyethylene having a density less than 0.93 as major component, with a free radical generating compound and an organic silane having the general formula RR'SiY 2 , wherein R represents a monovalent olefinically unsaturated hydrocarbon or hydrocarbonoxy radical, each Y represents a hydrolyzable organic radical, and R' represents a monovalent hydrocarbon radical with the exception of aliphatically unsaturated hydrocarbon radicals, or a Y radical, to form a silane-grafted polyolefin, then mixing said silane-grafted polyolefin with a silanol condensation catalyst, and heating the mixture in the absence of water.
Claim 3
Independent Claim
160 words
A method for producing a crosslinked polyolefin comprising reacting a polyolefin which is a low density polyethylene having a density less than 0.93 and a melt index of 0.1 to 0.5 g/10 min., or a polyolefin mixture having a melt index of 0.1 to 0.5 g/10 min. and consisting of a low density polyethylene having a density less than 0.93, polyproplyene or a high density polyethylene in an amount of not more than 15% by weight based on the total weight of the polyolefin mixture, with a free radical generating compound and an organic silane having the general formula RR'SiY 2 , wherein R represents a monovalent olefinically unsaturated hydrocarbon or hydrocarbonoxy radical, each Y represents a hydrolyzable organic radical, and R' represents a monovalent hydrocarbon radical except aliphatically unsaturated hydrocarbon radicals, or a Y radical, to form a silane-grafted polyolefin, then mixing said silane-grafted polyolefin with a silanol condensation catalyst, and heating the mixture in the absence of water.
Claim 4
Independent Claim
160 words
A method for producing a crosslinked polyolefin comprising reacting a polyolefin which is a low density polyethylene having a density less than 0.93 and a melt index of 0.1 to 0.5 g/10 min., or a polyolefin mixture having a melt index of 0.1 to 0.5 g/10 min. and consisting of a low density polyethylene having a density less than 0.93, polyproplyene or a high density polyethylene in an amount of not more than 15% by weight based on the total weight of the polyolefin mixture, with a free radical generating compound and an organic silane having the general formula RR'SiY 2 , wherein R represents a monovalent olefinically unsaturated hydrocarbon or hydrocarbonoxy radical, each Y represents a hydrolyzable organic radical, and R' represents a monovalent hydrocarbon radical except aliphatically unsaturated hydrocarbon radicals, or a Y radical, to form a silane-grafted polyolefin, then mixing said silane-grafted polyolefin with a silanol condensation catalyst, and heating the mixture in the absence of water.
Claim 5
Dependent Claim
37 words
A method as described in claim 2 wherein said organic silane is vinyltrimethoxysilane or vinyltriethoxysilane, and the organic silane is employed in an amount of 1-10 parts by weight per 100 parts by weight of said polyolefin.
Claim 6
Dependent Claim
53 words
A method as described in claim 2 wherein said free radical generating compound has a half-life of not more than 6 minutes at a temperature of 140° C. or more, and the free radical generating compound is employed in an amount of from 0.0002 to 0.002 moles per 100 g of said polyolefin.
Claim 7
Dependent Claim
42 words
A method as described in claim 2 wherein said silanol condensation catalyst is an organometallic compound, and the silanol condensation catalyst is used in an amount of 0.05 to 0.5 parts by weight per 100 parts by weight of said silane-grafted polyolefin.
Claim 8
Independent Claim
130 words
A method for producing a crosslinked polyethylene comprising reacting a polyethylene mixture consisting of a low density polyethylene having a density less than 0.93 in an amount of 50 to 99% by weight and a high density polyethylene having a density not less than 0.93 in an amount of 50 to 1% by weight, with a free radical generating compound and an organic silane having the general formula RR'SiY 2 , wherein R represents a monovalent olefinically unsaturated hydrocarbon or hydrocarbonoxy radical, each Y represents a hydrolyzable organic radical, and R' represents a monovalent hydrocarbon radical with the exception of aliphatically unsaturated hydrocarbon radicals, or a Y radical, to form a silane-grafted polyethylene, then mixing said silane-grafted polyethylene with a silanol condensation catalyst, and heating in the absence of water.
Claim 9
Independent Claim
130 words
A method for producing a crosslinked polyethylene comprising reacting a polyethylene mixture consisting of a low density polyethylene having a density less than 0.93 in an amount of 50 to 99% by weight and a high density polyethylene having a density not less than 0.93 in an amount of 50 to 1% by weight, with a free radical generating compound and an organic silane having the general formula RR'SiY 2 , wherein R represents a monovalent olefinically unsaturated hydrocarbon or hydrocarbonoxy radical, each Y represents a hydrolyzable organic radical, and R' represents a monovalent hydrocarbon radical with the exception of aliphatically unsaturated hydrocarbon radicals, or a Y radical, to form a silane-grafted polyethylene, then mixing said silane-grafted polyethylene with a silanol condensation catalyst, and heating in the absence of water.
Claim 10
Dependent Claim
40 words
A method as described in claim 6 wherein said organic silane is vinyltrimethoxysilane, or vinyltriethoxysilane, and the organic silane is employed in an amount of 1 to 10 parts by weight per 100 parts by weight of said polyethylene mixture.
Claim 11
Dependent Claim
54 words
A method as described in claim 6 wherein said free radical generating compound has a half-life of not more than 6 minutes at a temperature of 140° C. or more, and the free radical generating compound is employed in an amount of from 0.0002 to 0.002 moles per 100 g of said polyethylene mixture.
Claim 12
Dependent Claim
42 words
A method as described in claim 6 wherein said silanol condensation catalyst is an organometallic compound, and the silanol condensation catalyst is used in an amount of 0.05 to 0.5 parts by weight per 100 parts by weight of said silane-grafted polyethylene.
References Cited (Backward Citations)
US3936523A
Cited
US4058583A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-14 | 1984-04-14 | 1984-10-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-14 | 1988-04-14 | 1988-10-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-14 | 1992-04-14 | 1992-10-14 | $7700.00 | Window Closed / Lapsed |