Slurry formulation for chemical mechanical polishing of metals
Assignee: National Semiconductor Corp
•
Filing: 1996-06-19
•
Granted: 1999-02-02
•
Expires: 2016-06-19
Abstract
Abstract Buffered slurries are used in a semiconductor process for chemical mechanical polishing of metal layers, such as aluminum or titanium. The slurries may comprise an oxidant capable of causing a passive oxide film to form on a metal based layer. The oxidant may comprise a diluent and may be optionally formulated with a separate oxidizing agent, such as ammonium peroxydisulfate. The slurries may include a buffer that maintains a slurry pH where the passive metal oxide film is stable. This pH may be between about 4 and about 9.
Inventors
- 👤 Ronald A. Carpio
- 👤 Rahul Jairath
- 👤 Jayashree Kalpathy-Cramer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 21:14
CPC Classifications
C; C09; C09G; C09G1/00; C09G1/02; C09K; C09K3/00; C09K3/14; C09K3/1454; C09K3/1463
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
107 words
A solution for use in chemical mechanical polishing of an aluminum based metal layer on a semiconductor substrate, said solution comprising: a buffer capable of maintaining the pH of the solution between about 4 and about 9; and an oxidant capable of causing a passive oxide film to form on the aluminum based metal, said oxidant comprising a separate oxidizing agent in said solution; wherein said passive oxide film allows smooth surfaces to be formed during the chemical mechanical polishing process, and wherein said oxidizing agent comprises at least one of an alkali or metal peroxydisulfate salt, an iodate, a bromate, a chlorate or a mixture thereof.
Claim 2
Dependent Claim
107 words
A solution for use in chemical mechanical polishing of an aluminum based metal layer on a semiconductor substrate, said solution comprising: a buffer capable of maintaining the pH of the solution between about 4 and about 9; and an oxidant capable of causing a passive oxide film to form on the aluminum based metal, said oxidant comprising a separate oxidizing agent in said solution; wherein said passive oxide film allows smooth surfaces to be formed during the chemical mechanical polishing process, and wherein said oxidizing agent comprises at least one of an alkali or metal peroxydisulfate salt, an iodate, a bromate, a chlorate or a mixture thereof.
Claim 3
Dependent Claim
18 words
The solution of claim 1, wherein the pH of the solution is between about 4 and about 6.
Claim 4
Dependent Claim
13 words
The solution of claim 1, wherein the separate oxidizing agent comprises ammonium peroxydisulfate.
Claim 5
Dependent Claim
23 words
The solution of claim 3, wherein a concentration of ammonium peroxydisulfate in said solution is from about 1% to about 5% by weight.
Claim 6
Dependent Claim
47 words
The solution of claim 1, wherein the buffer comprises at least one of acetic acid, phosphoric acid, carbonic acid, ammonium chloride, or a mixture thereof mixed with at least one of sodium hydroxide, sodium acetate, ammonium hydroxide, tetramethyl-anmmonium hydroxide, tetraethyl-ammonium hydroxide, tetrabutyl-ammonium hydroxide, or a mixture thereof.
Claim 7
Dependent Claim
23 words
The solution of claim 5, wherein the buffer is present in the solution in a concentration of from about 0.1M to about 1M.
Claim 8
Dependent Claim
30 words
The solution of claim 6, wherein the oxidant comprises a separate oxidizing agent, said separate oxidizing agent comprising from about 1% to about 5% by weight of ammonium peroxydisulfate oxidant.
Claim 9
Dependent Claim
41 words
A solution for use in chemical mechanical polishing of an aluminum based metal layer on a semiconductor substrate, said solution comprising an ammonium peroxydisulfate oxidant and a buffer, wherein said solution has a pH of between about 4 and about 9.
Claim 10
Dependent Claim
41 words
A solution for use in chemical mechanical polishing of an aluminum based metal layer on a semiconductor substrate, said solution comprising an ammonium peroxydisulfate oxidant and a buffer, wherein said solution has a pH of between about 4 and about 9.
Claim 11
Dependent Claim
12 words
The solution of claim 8, wherein the solution comprises an aqueous diluent.
Claim 12
Dependent Claim
47 words
The solution of claim 8, wherein the buffer comprises at least one of acetic acid, phosphoric acid, carbonic acid, ammonium chloride, or a mixture thereof mixed with at least one of sodium hydroxide, sodium acetate, ammonium hydroxide, tetramethyl-ammonium hydroxide, tetraethyl-ammonium hydroxide, tetrabutyl-ammonium hydroxide, or a mixture thereof.
Claim 13
Dependent Claim
23 words
The solution of claim 8, wherein a concentration of ammonium peroxydisulfate in said solution is from about 1% to about 5% by weight.
Claim 14
Dependent Claim
18 words
The solution of claim 8, wherein the pH of the solution is between about 4 and about 6.
Claim 15
Dependent Claim
23 words
The slurry of claim 10, wherein the buffer is present in the slurry in a concentration of from about 0.1M to about 1M.
Claim 16
Dependent Claim
95 words
A solution for use in chemical mechanical polishing of an aluminum based metal layer on a semiconductor substrate, wherein said solution has a pH of between about 4 and about 9 and comprises a separate oxidizing agent capable of causing a passive oxide film to form on the metal based layer, and wherein said passive oxide film allows smooth surfaces to be formed during the chemical mechanical polishing process, and wherein said oxidizing agent comprises at least one of an alkali or metal peroxydisulfate salt, an iodate, a bromate, a chlorate or a mixture thereof.
Claim 17
Dependent Claim
95 words
A solution for use in chemical mechanical polishing of an aluminum based metal layer on a semiconductor substrate, wherein said solution has a pH of between about 4 and about 9 and comprises a separate oxidizing agent capable of causing a passive oxide film to form on the metal based layer, and wherein said passive oxide film allows smooth surfaces to be formed during the chemical mechanical polishing process, and wherein said oxidizing agent comprises at least one of an alkali or metal peroxydisulfate salt, an iodate, a bromate, a chlorate or a mixture thereof.
Claim 18
Dependent Claim
13 words
The solution of claim 14, wherein the separate oxidizing agent comprises ammonium peroxydisulfate.
Claim 19
Dependent Claim
129 words
A solution for use in chemical mechanical polishing of a metal layer on a semiconductor substrate, wherein said metal has a standard reduction potential that is more negative than about -1.0 volts, said solution comprising: a buffer capable of maintaining the pH of the solution between about 4 and about 9; and an oxidant capable of causing a passive oxide film to form on said metal at a pH of between about 4 and about 9, said oxidant comprising a separate oxidizing agent in said solution; wherein said passive oxide film allows smooth surfaces to be formed during the chemical mechanical polishing process, and wherein said oxidizing agent comprises at least one of an alkali or metal peroxydisulfate salt, an iodate, a bromate, a chlorate or a mixture thereof.
Claim 20
Dependent Claim
129 words
A solution for use in chemical mechanical polishing of a metal layer on a semiconductor substrate, wherein said metal has a standard reduction potential that is more negative than about -1.0 volts, said solution comprising: a buffer capable of maintaining the pH of the solution between about 4 and about 9; and an oxidant capable of causing a passive oxide film to form on said metal at a pH of between about 4 and about 9, said oxidant comprising a separate oxidizing agent in said solution; wherein said passive oxide film allows smooth surfaces to be formed during the chemical mechanical polishing process, and wherein said oxidizing agent comprises at least one of an alkali or metal peroxydisulfate salt, an iodate, a bromate, a chlorate or a mixture thereof.
Claim 21
Dependent Claim
22 words
The solution of claim 16, wherein the metal layer is comprised of at least one of aluminum, titanium, or a mixture thereof.
Claim 22
Dependent Claim
13 words
The solution of claim 17, wherein the metal layer is comprised of aluminum.
Claim 23
Dependent Claim
13 words
The solution of claim 17, wherein the metal layer is comprised of titanium.
Claim 24
Dependent Claim
18 words
The solution of claim 17, wherein the pH of the slurry is between about 4 and about 6.
Claim 25
Dependent Claim
13 words
The solution of claim 16, wherein the separate oxidizing agent comprises ammonium peroxydisulfate.
Claim 26
Dependent Claim
23 words
The solution of claim 21, wherein a concentration of ammonium peroxydisulfate in said solution is from about 1% to about 5% by weight.
Claim 27
Dependent Claim
47 words
The solution of claim 17, wherein the buffer comprises at least one of acetic acid, phosphoric acid, carbonic acid, ammonium chloride, or a mixture thereof mixed with at least one of sodium hydroxide, sodium acetate, ammonium hydroxide, tetramethyl-ammonium hydroxide, tetraethyl-ammonium hydroxide, tetrabutyl-ammonium hydroxide, or a mixture thereof.
Claim 28
Dependent Claim
20 words
The solution of claim 23, wherein the buffer is present in a concentration of from about 0.1M to about 1M.
Claim 29
Dependent Claim
35 words
The solution of claim 24, wherein the oxidant comprises a separate ammonium peroxydisulfate oxidizing agent, and wherein a concentration of said ammonium peroxydisulfate in said slurry is from about 1% to about 5% by weight.
References Cited (Backward Citations)
US2171546A
Cited
US2434021A
Cited
US2939772A
Cited
US3351555A
Cited
US3442810A
Cited
US3464908A
Cited
US3498823A
Cited
JPS4945451A
Cited
US3964956A
Cited
US4022625A
Cited
US4070193A
Cited
US4138228A
Cited
US4154660A
Cited
US4512859A
Cited
US4728552A
Cited
US4600469A
Cited
US4944836A
Cited
US4988369A
Cited
US4956313A
Cited
US4793895A
Cited
US4959113C1
Cited
US4959113A
Cited
US5166093A
Cited
US5203883A
Cited
US5373047A
Cited
US5234470A
Cited
US5449313A
Cited
US5209816A
Cited
US5225034A
Cited
US5578362A
Cited
US5364510A
Cited
US5407526A
Cited
US5340370A
Cited
US5472370A
Cited
US5527423A
Cited
US5533923A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-02-01 | 2002-08-03 | 2003-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-02-01 | 2006-08-03 | 2007-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-02-01 | 2010-08-03 | 2011-02-02 | $7700.00 | Window Closed / Lapsed |