Process for making group IV semiconductor substrate treated with one or more group IV elements to form one or more barrier regions capable of inhibiting migration of dopant materials in substrate
Assignee: Bell Semiconductor LLC
•
Filing: 1995-05-04
•
Granted: 1997-08-05
•
Expires: 2015-05-04
Abstract
Abstract Formation of a barrier region in a single crystal group IV semiconductor substrate at a predetermined spacing from a doped region in the substrate is described to prevent or inhibit migration of dopant materials from an adjacent doped region through the barrier region. By implantation of group IV materials into a semiconductor substrate to a predetermined depth in excess of the depth of a doped region, a barrier region can be created in the semiconductor to prevent migration of the dopants from the doped region through the barrier region. The treatment of the single crystal substrate with the group IV material is carried out at a dosage and energy level sufficient to provide such a barrier region in the semiconductor substrate, but insufficient to result in amorphization (destruction) of the single crystal lattice of the semiconductor substrate. In another embodiment, a similar barrier region may be formed in the semiconductor substrate but at a depth less than that of the doped region to inhibit migration of the dopant to the surface of the substrate. Such barrier regions may be formed in the substrate both above and below the doped region to inhibit migration of the dopant in the doped region in either direction.
Inventors
- 👤 Sheldon Aronowitz
- 👤 James Kimball
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:21
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10P30/208; H10P30/21; H10P30/224; H10P30/225
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
146 words
A process for forming a group IV single crystal semiconductor substrate having first and second barrier regions in said substrate comprising implanted group IV atoms capable of inhibiting migration through said substrate of dopant atoms in a doped region in said semiconductor substrate which comprises: a) implanting said group IV single crystal semiconductor material with group IV atoms to form said first barrier region without amorphizing said single crystal substrate, at a depth of the Rp of said group IV first barrier region, with respect to the Rp of said doped region, ranging from about 1/4 ΔRp to about 10 ΔRp of said dopant; and b) forming a second barrier region between said doped region and a surface of said substrate by implanting said group IV single crystal semiconductor material with group IV atoms to form said second barrier region without amorphizing said single crystal substrate.
Claim 2
Dependent Claim
146 words
A process for forming a group IV single crystal semiconductor substrate having first and second barrier regions in said substrate comprising implanted group IV atoms capable of inhibiting migration through said substrate of dopant atoms in a doped region in said semiconductor substrate which comprises: a) implanting said group IV single crystal semiconductor material with group IV atoms to form said first barrier region without amorphizing said single crystal substrate, at a depth of the Rp of said group IV first barrier region, with respect to the Rp of said doped region, ranging from about 1/4 ΔRp to about 10 ΔRp of said dopant; and b) forming a second barrier region between said doped region and a surface of said substrate by implanting said group IV single crystal semiconductor material with group IV atoms to form said second barrier region without amorphizing said single crystal substrate.
Claim 3
Dependent Claim
46 words
The process of claim 1 wherein said step of implanting said substrate with said group IV atoms to form said first and second barrier regions further comprises implanting a single crystal silicon substrate with group IV atoms selected from the group consisting of germanium and silicon.
Claim 4
Dependent Claim
77 words
The process of claim 1 which includes the further step of implanting said group IV single crystal semiconductor substrate with one or more dopants selected from the group consisting of group III and group V atoms to form said doped region in said substrate between said first and second barrier regions in said substrate, wherein said first and second barrier regions will inhibit migration of said dopant from said doped region upon subsequent annealing of said substrate.
Claim 5
Dependent Claim
127 words
A process for forming a group IV single crystal semiconductor substrate having a barrier region in said substrate comprising implanted group IV atoms which comprises: a) forming a doped region in said substrate; b) implanting Group IV atoms in said substrate between said doped region and a surface of said substrate without amorphizing said single crystal substrate to form a first barrier region of interstitial group IV atoms in said substrate spaced from said doped region a distance between the Rp of said first barrier region and the Rp of said dopant region which ranges from about 1/4 ΔRp to about 6 ΔRp of the dopant in said doped region; and c) forming a second barrier region at least partially below said doped region in said substrate.
Claim 6
Dependent Claim
127 words
A process for forming a group IV single crystal semiconductor substrate having a barrier region in said substrate comprising implanted group IV atoms which comprises: a) forming a doped region in said substrate; b) implanting Group IV atoms in said substrate between said doped region and a surface of said substrate without amorphizing said single crystal substrate to form a first barrier region of interstitial group IV atoms in said substrate spaced from said doped region a distance between the Rp of said first barrier region and the Rp of said dopant region which ranges from about 1/4 ΔRp to about 6 ΔRp of the dopant in said doped region; and c) forming a second barrier region at least partially below said doped region in said substrate.
Claim 7
Dependent Claim
48 words
The process of claim 4 wherein said semiconductor substrate comprises a single crystal silicon group IV semiconductor substrate and said barrier region in said substrate also comprises single crystal silicon semiconductor material having interstitial group IV atoms implanted therein selected from the group consisting of germanium and silicon.
Claim 8
Dependent Claim
35 words
The process of claim 4 wherein said doped region located beneath said barrier region and said surface of said substrate contains a dopant selected from the group consisting of group III and group V dopants.
Claim 9
Dependent Claim
202 words
A process for forming a single crystal group IV semiconductor substrate having a doped region and barrier regions in said substrate above and below said doped region comprising: a) implanting the crystal lattice of said single crystal group IV substrate with Group IV atoms to form a first barrier layer of interstitial group IV atoms implanted therein without amorphizing said single crystal substrate; b) forming a doped region in said substrate between a portion of said first barrier region and a surface of said substrate; c) spacing said first barrier region a distance between the Rp of said first barrier region and the Rp of said dopant region which ranges from about 1/4 ΔRp to about 10 ΔRp of the dopant in said doped region; and d) implanting the crystal lattice of said single crystal group IV substrate with Group IV atoms to form a second barrier layer of interstitial group IV atoms implanted therein between said doped region and said surface of said substrate without amorphizing said single crystal substrate; whereby said first and second barrier regions of interstitial group IV atoms are capable of inhibiting migration therethrough of dopant atoms from said doped region in said group IV semiconductor substrate.
Claim 10
Dependent Claim
202 words
A process for forming a single crystal group IV semiconductor substrate having a doped region and barrier regions in said substrate above and below said doped region comprising: a) implanting the crystal lattice of said single crystal group IV substrate with Group IV atoms to form a first barrier layer of interstitial group IV atoms implanted therein without amorphizing said single crystal substrate; b) forming a doped region in said substrate between a portion of said first barrier region and a surface of said substrate; c) spacing said first barrier region a distance between the Rp of said first barrier region and the Rp of said dopant region which ranges from about 1/4 ΔRp to about 10 ΔRp of the dopant in said doped region; and d) implanting the crystal lattice of said single crystal group IV substrate with Group IV atoms to form a second barrier layer of interstitial group IV atoms implanted therein between said doped region and said surface of said substrate without amorphizing said single crystal substrate; whereby said first and second barrier regions of interstitial group IV atoms are capable of inhibiting migration therethrough of dopant atoms from said doped region in said group IV semiconductor substrate.
Claim 11
Dependent Claim
51 words
The process of claim 7 which further comprises spacing said second barrier region from said doped region a distance between the Rp of said second barrier region and the Rp of said dopant region which ranges from about 1/4 ΔRp to about 6 ΔRp of the dopant in said doped region.
Claim 12
Dependent Claim
35 words
The process of claim 8 wherein the distance between the Rp of said first barrier region and the Rp of said dopant region ranges from about 1 ΔRp to about 6 ΔRp of said dopant.
Claim 13
Dependent Claim
35 words
The process of claim 8 wherein said doped region located between said first and second barrier regions in said substrate contains a dopant selected from the group consisting of group III and group V dopants.
Claim 14
Dependent Claim
28 words
The process of claim 10 wherein said doped region is formed by implanting said substrate with a dopant selected from the group consisting of boron, phosphorus, and arsenic.
Claim 15
Dependent Claim
199 words
A process for forming a doped single crystal silicon semiconductor substrate having a doped region and barrier regions capable of retaining said doped region within said substrate which comprises: a) forming a first barrier region of interstitial atoms in said substrate spaced from a surface of said single crystal silicon substrate by implanting interstitial group IV atoms therein without amorphizing said single crystal substrate; b) forming a doped region in said substrate between said surface and said first barrier region comprising implanted dopant atoms selected from the group consisting of boron, phosphorus, and arsenic; and c) forming a second barrier layer of interstitial atoms in said substrate between said doped layer and said surface of said single crystal silicon substrate without amorphizing said single crystal substrate by implanting interstitial group IV atoms therein spaced from said doped region a distance between the Rp of said second barrier region and the Rp of said dopant region which ranges from about 1/4 ΔRp to about 6 ΔRp of the dopants in said doped region; wherein said first and second barrier regions are capable of inhibiting migration therethrough of dopants atoms implanted in said silicon semiconductor substrate to form said doped region.
Claim 16
Dependent Claim
199 words
A process for forming a doped single crystal silicon semiconductor substrate having a doped region and barrier regions capable of retaining said doped region within said substrate which comprises: a) forming a first barrier region of interstitial atoms in said substrate spaced from a surface of said single crystal silicon substrate by implanting interstitial group IV atoms therein without amorphizing said single crystal substrate; b) forming a doped region in said substrate between said surface and said first barrier region comprising implanted dopant atoms selected from the group consisting of boron, phosphorus, and arsenic; and c) forming a second barrier layer of interstitial atoms in said substrate between said doped layer and said surface of said single crystal silicon substrate without amorphizing said single crystal substrate by implanting interstitial group IV atoms therein spaced from said doped region a distance between the Rp of said second barrier region and the Rp of said dopant region which ranges from about 1/4 ΔRp to about 6 ΔRp of the dopants in said doped region; wherein said first and second barrier regions are capable of inhibiting migration therethrough of dopants atoms implanted in said silicon semiconductor substrate to form said doped region.
Claim 17
Dependent Claim
38 words
The process of claim 12 which further comprises spacing the Rp of said first barrier region and the Rp of said dopant region within the range of from about 1 ΔRp to about 6 ΔRp of said dopant.
Claim 18
Dependent Claim
43 words
The process of claim 12 wherein said steps of implanting said substrate with said group IV atoms to form said barrier regions further comprises implanting a single crystal silicon substrate with group IV atoms selected from the group consisting of germanium and silicon.
References Cited (Backward Citations)
US3622382A
Cited
US4278475A
Cited
US5075751A
Cited
US4889819A
Cited
US5098852A
Cited
US5145794A
Cited
US5102826A
Cited
US5298435A
Cited
US5554883A
Cited
US5223445A
Cited
EP0485830A1
Cited
US5254484A
Cited
DE4035842A1
Cited
US5296387A
Cited
JPH05190849A
Cited
US5389563A
Cited
JPH06151348A
Cited
JPH06163574A
Cited
US5420049A
Cited
US5508211A
Cited
US5401674A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-08-04 | 2001-02-03 | 2001-08-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-08-04 | 2005-02-03 | 2005-08-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-08-04 | 2009-02-03 | 2009-08-05 | $7700.00 | Window Closed / Lapsed |