Solar cell with chalcopyrite absorber layer
Assignee: Saint Gobain Glass France SAS
•
Filing: 1995-12-01
•
Granted: 1997-05-06
•
Expires: 2015-12-01
Abstract
Abstract A substrate-independent manufacturing method for a solar cell with chalcopyrite absorber layer (4, 5) is proposed wherein a desired alkali content is obtained in the finished absorber layer by dosed addition of Na, K, or Li during the manufacturing process. An additional drive-in of alkali ions from a potentially alkali-containing substrate (1) is prevented by providing a diffusion barrier layer (2) between substrate and absorber layer.
Inventors
- 👤 Volker Probst
- 👤 Joerk Rimmasch
- 👤 Hauke Harms
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 20:27
CPC Classifications
H; H10; H10F; H10F10/00; H10F10/10; H10F10/16; H10F10/167; H10F77/00; H10F77/10; H10F77/12; H10F77/126; H10F77/1265; H10F77/16; H10F77/169; H10F77/1694; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/541
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
43 words
A solar cell comprising a chalcopyrite absorber layer including a controlled amount of a dopant selected from alkali metals and alkali metal compounds of from about 10 14 to about 10 17 alkali metal atoms per square centimeter of said chalcopyrite absorber layer.
Claim 2
Dependent Claim
43 words
A solar cell comprising a chalcopyrite absorber layer including a controlled amount of a dopant selected from alkali metals and alkali metal compounds of from about 10 14 to about 10 17 alkali metal atoms per square centimeter of said chalcopyrite absorber layer.
Claim 3
Dependent Claim
98 words
A solar cell comprising: a substrate having a surface; a diffusion barrier layer disposed on said surface sufficient to prevent diffusion of alkali metal ions from the substrate across said diffusion barrier layer; a back electrode layer disposed on said diffusion barrier layer; a chalcopyrite absorber layer disposed on said back electrode layer, a lower portion of said chalcopyrite absorber layer adjacent said back electrode layer including a controlled amount of dopant selected from alkali metals and alkali metal compounds; a window layer disposed on the chalcopyrite absorber layer; and a front electrode disposed on said window layer.
Claim 4
Dependent Claim
98 words
A solar cell comprising: a substrate having a surface; a diffusion barrier layer disposed on said surface sufficient to prevent diffusion of alkali metal ions from the substrate across said diffusion barrier layer; a back electrode layer disposed on said diffusion barrier layer; a chalcopyrite absorber layer disposed on said back electrode layer, a lower portion of said chalcopyrite absorber layer adjacent said back electrode layer including a controlled amount of dopant selected from alkali metals and alkali metal compounds; a window layer disposed on the chalcopyrite absorber layer; and a front electrode disposed on said window layer.
Claim 5
Dependent Claim
19 words
A solar cell as defined in claim 2, wherein said substrate includes alkali metal or alkaline earth metal contaminants.
Claim 6
Dependent Claim
13 words
A solar cell as defined in claim 2, wherein said substrate comprises glass.
Claim 7
Dependent Claim
35 words
A solar cell as defined in claim 2, wherein said diffusion barrier layer comprises TiN, Al 2 O 3 , SiO 2 , Si 3 N 4 , ZrO 2 , or TiO 2 .
Claim 8
Dependent Claim
24 words
A solar cell as defined in claim 2, wherein said diffusion barrier layer has a thickness of from about 20 to about 100 nm.
Claim 9
Dependent Claim
26 words
A solar cell as defined in claim 2, wherein said back electrode layer comprises molybdenum, titanium, palladium, platinum, or compounds of any of the foregoing elements.
Claim 10
Dependent Claim
23 words
A solar cell as defined in claim 2, wherein said chalcopyrite absorber layer comprises CuInSe 2 (CIS) or CuIn(Ga)Se 2 (S 2 )(=CIGS).
Claim 11
Dependent Claim
15 words
A solar cell as defined in claim 2, wherein said window layer comprises cadmium sulfide.
Claim 12
Dependent Claim
18 words
A solar cell as defined in claim 2, wherein said front electrode layer comprises a transparent conductive oxide.
Claim 13
Dependent Claim
73 words
A solar cell comprising: an alkali-free substrate having a surface; a back electrode disposed on said surface; a chalcopyrite absorber layer disposed on said back electrode, a lower portion of said chalcopyrite absorber layer adjacent said back electrode layer including a controlled amount of a dopant selected from alkali metals and alkali metal compounds; a window layer disposed on said chalcopyrite absorber layer; and a front electrode layer disposed on said window layer.
Claim 14
Dependent Claim
73 words
A solar cell comprising: an alkali-free substrate having a surface; a back electrode disposed on said surface; a chalcopyrite absorber layer disposed on said back electrode, a lower portion of said chalcopyrite absorber layer adjacent said back electrode layer including a controlled amount of a dopant selected from alkali metals and alkali metal compounds; a window layer disposed on said chalcopyrite absorber layer; and a front electrode layer disposed on said window layer.
Claim 15
Dependent Claim
25 words
A solar cell as defined in claim 11, further comprising a diffusion barrier layer disposed intermediate said back electrode layer and said chalcopyrite absorber layer.
Claim 16
Dependent Claim
16 words
A solar cell as defined in claim 12, wherein said diffusion barrier layer is electrically conductive.
Claim 17
Independent Claim
98 words
A method for making a solar cell, comprising the steps of: providing a substrate having a surface; depositing a diffusion barrier layer on the surface of the substrate capable of preventing diffusion of alkali metal ions from the substrate across said diffusion barrier layer; depositing a back electrode layer on said diffusion barrier layer; forming a chalcopyrite absorber layer including a controlled amount of a dopant selected from alkali metals and alkali metal compounds on said back electrode layer; depositing a window layer on the chalcopyrite absorber layer; and depositing a front electrode layer on said window layer.
Claim 18
Independent Claim
98 words
A method for making a solar cell, comprising the steps of: providing a substrate having a surface; depositing a diffusion barrier layer on the surface of the substrate capable of preventing diffusion of alkali metal ions from the substrate across said diffusion barrier layer; depositing a back electrode layer on said diffusion barrier layer; forming a chalcopyrite absorber layer including a controlled amount of a dopant selected from alkali metals and alkali metal compounds on said back electrode layer; depositing a window layer on the chalcopyrite absorber layer; and depositing a front electrode layer on said window layer.
Claim 19
Dependent Claim
112 words
A method as defined in claim 14, wherein said chalcopyrite absorber layer comprises a compound semiconductor of CuInSe 2 (CIS) or CuIn(Ga)Se 2 (S 2 )(=CIGS) and said forming step further includes the steps of sputtering targets to form a sputter deposited layer generally having appropriate stoichiometric amounts of each element, said targets being selected from the group consisting of copper, indium, gallium, selenium, sulfur, an alkali metal selected from sodium, potassium, lithium, and binary compounds of any of the foregoing to form said sputter deposited layer; and thereafter, heating the sputter deposited layer to temperatures above about 500° C. to convert the sputtered elements into said compound semiconductor chalcopyrite absorber layer.
Claim 20
Dependent Claim
102 words
A method as defined in claim 14, wherein said chalcopyrite absorber layer comprises a compound semiconductor of CuInSe 2 (CIS) or CuIn(Ga)Se 2 (S 2 ) (=CIGS) and said foxing step further includes the steps of vapor depositing generally appropriate stoichiometric amounts of elements selected from the group consisting of copper, indium, gallium, selenium, sulfur, an alkali metal selected from sodium, potassium, lithium, and binary compounds of any of the foregoing elements to form a vapor-deposited layer; and thereafter, heating said vapor-deposited layer to a temperature above about 500° C. to convert the vapor-deposited elements into said compound semiconductor chalcopyrite absorber layer.
Claim 21
Dependent Claim
134 words
A method as defined in claim 14, wherein said chalcopyrite absorber layer comprises a compound semiconductor of CuInSe 2 (CIS)) or CuIn(Ga)Se 2 (S 2 ) (=CIGS) and said forming step further includes the steps of sputtering or vapor depositing generally appropriate stoichiometric amounts of elements selected from Cu, In, Ga, Se, S, an alkali metal selected from the group consisting of Na, K, and Li, and binary compounds of any of the foregoing and wherein said stoichiometric amounts of Se or S are at least partially introduced by performing said sputtering or vapor depositing in an atmosphere comprising Se or S, respectively, to form a precursor layer; and thereafter, heating said precursor layer to temperatures above about 500° C. to convert the sputtered or vapor-deposited elements into said composite semiconductor chalcopyrite absorber layer.
Claim 22
Dependent Claim
143 words
A method as defined in claim 14, wherein said chalcopyrite absorber layer comprises a compound semiconductor of CuInSe 2 (CIS) or CuIn(Ga)Se 2 (S 2 ) (=CIGS) and said forming step further includes the steps of depositing said controlled amount of dopant by sputtering or vapor depositing an alkali metal selected from the group consisting of Na, K, Li, and binary compounds of any of the foregoing with Se or S to form a first layer on said back electrode layer; sputtering or vapor depositing generally appropriate stoichiometric amounts of elements selected from the group consisting of: Cu, In, Ga, Se, S, and binary compounds of any of the foregoing onto said first layer to form a second layer; and thereafter, heating to a temperature above about 500° C. to convert the first and second layers into said compound semiconductor chalcopyrite absorber layer.
Claim 23
Independent Claim
69 words
A method for making a solar cell, comprising the steps of: providing an alkali-free substrate having a surface; depositing a back electrode layer on said surface; forming a chalcopyrite absorber layer including a controlled amount of dopant selected from alkali metals and alkali metal compounds on said back electrode layer; depositing a window layer on said chalcopyrite absorber layer; and depositing a front electrode layer on said window layer.
Claim 24
Independent Claim
69 words
A method for making a solar cell, comprising the steps of: providing an alkali-free substrate having a surface; depositing a back electrode layer on said surface; forming a chalcopyrite absorber layer including a controlled amount of dopant selected from alkali metals and alkali metal compounds on said back electrode layer; depositing a window layer on said chalcopyrite absorber layer; and depositing a front electrode layer on said window layer.
Claim 25
Dependent Claim
32 words
A method for making a solar cell as defined in claim 19, further comprising the step of depositing an electrically conductive diffusion barrier on said back electrode prior to said forming step.
References Cited (Backward Citations)
US4004342A
Cited
US4818357A
Cited
US5141564A
Cited
US5137835A
Cited
US5422304A
Cited
US5506426A
Cited
US5296674A
Cited
US5445847A
Cited
US5474622A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-05-05 | 2000-11-04 | 2001-05-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-05-05 | 2004-11-04 | 2005-05-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-05-05 | 2008-11-04 | 2009-05-06 | $7700.00 | Window Closed / Lapsed |