Mixed ternary heterojunction solar cell
Assignee: Boeing Co
•
Filing: 1991-01-17
•
Granted: 1992-08-25
•
Expires: 2011-01-17
Abstract
Abstract A thin film heterojunction solar cell and a method of making it has a p-type layer of mixed ternary I-III-VI 2 semiconductor material in contact with an n-type layer of mixed binary II-VI semiconductor material. The p-type semiconductor material includes a low resistivity copper-rich region adjacent the back metal contact of the cell and a composition gradient providing a minority carrier mirror that improves the photovoltaic performance of the cell. The p-type semiconductor material preferably is CuInGaSe 2 or CuIn(SSe) 2 .
Inventors
- 👤 Wen S. Chen
- 👤 John M. Stewart
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:17
CPC Classifications
H; H10; H10F; H10F10/00; H10F10/10; H10F10/16; H10F10/167; H10F71/00; H10F71/137; H10F77/00; H10F77/10; H10F77/16; H10F77/169; H10F77/1696; H10F77/1698; H10F77/1699; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/541; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S438/00; Y10S438/93
Claims Analysis
Total Claims: 105
Claim 1
Independent Claim
84 words
A thin film polycrystalline heterojunction solar cell, comprising: a back metal contact; a p-type layer on the contact comprising a mixed ternary, I-III-VI 2 polycrystalline semiconductor material having a composition gradient in the direction of the thickness of the layer to form a minority carrier mirror within the layer, the layer having low resistivity region adjacent the back metal contact; an n-type layer of semiconductor material on the p-type layer to form a photovoltaically active heterojunction; and electrically conductive means on the n-type layer.
Claim 2
Dependent Claim
84 words
A thin film polycrystalline heterojunction solar cell, comprising: a back metal contact; a p-type layer on the contact comprising a mixed ternary, I-III-VI 2 polycrystalline semiconductor material having a composition gradient in the direction of the thickness of the layer to form a minority carrier mirror within the layer, the layer having low resistivity region adjacent the back metal contact; an n-type layer of semiconductor material on the p-type layer to form a photovoltaically active heterojunction; and electrically conductive means on the n-type layer.
Claim 3
Dependent Claim
17 words
The cell of claim 1 wherein the p-type material in CuIn l-x Ga x Se 2 .
Claim 4
Dependent Claim
22 words
The cell of claim 2 wherein the minority carrier mirror is formed by changing the concentration of gallium in the p-type layer.
Claim 5
Dependent Claim
26 words
The cell of claim 3 wherein the low resistivity region is rich in copper relative to the concentration of copper in the remainder of the layer.
Claim 6
Dependent Claim
24 words
The cell of claim 4 wherein said composition gradient is characterized by the p-type layer being relatively rich in gallium within said Cu-rich region.
Claim 7
Dependent Claim
15 words
The cell of claim 4 wherein the n-type layer is a mixed binary CdZnS semiconductor.
Claim 8
Dependent Claim
19 words
The cell of claim 6 wherein said CdZnS includes In or Ga as a dopant away from the junction.
Claim 9
Dependent Claim
14 words
The cell of claim 7 wherein the n-type layer comprises 12-50 atomic percent zinc.
Claim 10
Dependent Claim
15 words
The cell of claim 2 wherein the n-type layer is a mixed binary II-IV semiconductor.
Claim 11
Dependent Claim
37 words
The cell of claim 1 wherein the minority carrier mirror is defined by a first zone overlying the contact and having a higher bandgap, and a second zone overlying the first zone and having a lower bandgap.
Claim 12
Dependent Claim
21 words
The cell of claim 1 wherein said p-type layer has a bandgap in the range of from 1.0 to 1.7 eV.
Claim 13
Dependent Claim
27 words
The cell of claim 1 wherein the n-type layer consists essentially of Zn z Cd l-z S with z in the range of from 0 to 0.5.
Claim 14
Dependent Claim
15 words
The cell of claim 1 wherein the n-type layer is a mixed binary II-VI semiconductor.
Claim 15
Dependent Claim
26 words
The cell of claim 1 wherein said n-type layer comprises a material selected from the group consisting of ZnO, ZnSe, CdSnO 4 , CdSSe, and CdZnSe.
Claim 16
Dependent Claim
14 words
The cell of claim 1 wherein said electrically conductive means comprises a metal grid.
Claim 17
Dependent Claim
19 words
The cell of claim 15 further comprising an anti-reflective coating applied over the metal grid and the n-type layer.
Claim 18
Dependent Claim
14 words
The cell of claim 1 further comprising an anti-reflective coating over the n-type layer.
Claim 19
Dependent Claim
16 words
The cell of claim 17 wherein the anti-reflective coating comprises amorphous silicon oxide over silicon nitride.
Claim 20
Dependent Claim
18 words
The cell of claim 1 wherein the n-type layer has a thickness of less than about 3 micrometers.
Claim 21
Dependent Claim
18 words
The cell of claim 1 wherein the n-type layer has a thickness of less than about 500 angstroms.
Claim 22
Dependent Claim
112 words
A thin film polycrystalline heterojunction solar cell comprising: a conductive metal layer a p-type layer of CuIn l-x Ga x Se 2 semiconductor material on said conductive metal layer, wherein x is in the range of from 0 to 0.3, having a composition gradient of Cu and In in the direction of thickness and having a low resistivity Cu-rich region adjacent the conductive metal layer and a relatively Cu-poor region adjacent the junction; an n-type layer of CdZnS semiconductor material on said p-type material to form a photovoltaically active junction; an electrically conductive top contact on one surface of the n-type layer; and at least one anti-reflective coating over the top contact.
Claim 23
Dependent Claim
112 words
A thin film polycrystalline heterojunction solar cell comprising: a conductive metal layer a p-type layer of CuIn l-x Ga x Se 2 semiconductor material on said conductive metal layer, wherein x is in the range of from 0 to 0.3, having a composition gradient of Cu and In in the direction of thickness and having a low resistivity Cu-rich region adjacent the conductive metal layer and a relatively Cu-poor region adjacent the junction; an n-type layer of CdZnS semiconductor material on said p-type material to form a photovoltaically active junction; an electrically conductive top contact on one surface of the n-type layer; and at least one anti-reflective coating over the top contact.
Claim 24
Dependent Claim
14 words
The cell of claim 21 wherein the p-type layer includes a minority carrier mirror.
Claim 25
Dependent Claim
13 words
The cell of claim 21 wherein the anti-reflective coating includes amorphous silicon nitride.
Claim 26
Dependent Claim
18 words
The cell of claim 23 wherein said anti-reflective coating further includes amorphous silicon oxide over the silicon nitride.
Claim 27
Dependent Claim
18 words
The cell of claim 21 wherein the n-type layer has a thickness of less than about 3 micrometers.
Claim 28
Dependent Claim
24 words
The cell of claim 21 wherein the n-type layer has a thickness of less than about 500 angstroms permitting light transmission to the junction.
Claim 29
Independent Claim
188 words
A method of making on a substrate a thin film polycrystalline heterojunction solar cell comprised of a conductive metal layer; a p-type layer of polycrystalline, mixed ternary I-III-VI 2 material material having a low resistivity Cu-rich region adjacent said conductive metal layer, a higher bandgap region, within said Cu-rich region, and a lower bandgap region, the higher and lower bandgap regions defining a minority carrier mirror; a layer of polycrystalline n-type semiconductor material disposed on the p-type layer defining the heterojunction; and an electrically conductive means disposed on said n-type material, said method comprising the steps of: (a) introducing vapors of the elements from Groups I, III, and VI simultaneously into a vessel to form a vapor mixture comprising the components of the p-type layer; (b) independently controlling the vaporization rate of the elements; (c) depositing said vapor mixture on a substrate to form a p-type polycrystalline film of mixed ternary I-III-VI 2 material having a copper-rich region and a minority carrier mirror; (d) depositing the n-type semiconductor material on said p-type material; and (e) depositing an electrically conductive means on the surface of the n-type semiconductor material.
Claim 30
Independent Claim
188 words
A method of making on a substrate a thin film polycrystalline heterojunction solar cell comprised of a conductive metal layer; a p-type layer of polycrystalline, mixed ternary I-III-VI 2 material material having a low resistivity Cu-rich region adjacent said conductive metal layer, a higher bandgap region, within said Cu-rich region, and a lower bandgap region, the higher and lower bandgap regions defining a minority carrier mirror; a layer of polycrystalline n-type semiconductor material disposed on the p-type layer defining the heterojunction; and an electrically conductive means disposed on said n-type material, said method comprising the steps of: (a) introducing vapors of the elements from Groups I, III, and VI simultaneously into a vessel to form a vapor mixture comprising the components of the p-type layer; (b) independently controlling the vaporization rate of the elements; (c) depositing said vapor mixture on a substrate to form a p-type polycrystalline film of mixed ternary I-III-VI 2 material having a copper-rich region and a minority carrier mirror; (d) depositing the n-type semiconductor material on said p-type material; and (e) depositing an electrically conductive means on the surface of the n-type semiconductor material.
Claim 31
Dependent Claim
22 words
The method of claim 27 wherein the minority carrier mirror is formed by varying the rates of deposition of gallium and indium.
Claim 32
Dependent Claim
31 words
The method of claim 27 wherein the temperature of the substrate is controlled during the deposition of the p-type film such that the polycrystalline material has a generally uniform grain size.
Claim 33
Dependent Claim
8 words
The product of the process of claim 29.
Claim 34
Dependent Claim
64 words
The method claim 27 wherein the depositing step for forming the I-III-VI 2 material includes depositing the Cu-rich region on the substrate heated to a temperature in the range of from 400° C. to 500° C., and reducing the vaporization rate of copper within the vessel to complete the p-type film at a substrate temperature in the range of 450° C. to 550° C.
Claim 35
Dependent Claim
25 words
The method of claim 27 wherein the substrate is maintained at a temperature in the range of 350° C. to 550° C. during step (c).
Claim 36
Dependent Claim
97 words
A thin film polycrystalline heterojunction solar; cell, comprising: a conductive metal layer; a p-type layer of polycrystalline CuInS 2x Se 2 (l-x) semiconductor material on the conductive metal layer, wherein x is in the range of from 0 to 1.0, the layer having a composition gradient of S in the direction of the thickness of the layer to form a minority carrier mirror and having low resistivity Cu-rich region adjacent the conductive material layer; an n-type layer of semiconductor material on the p-type layer to form a photoactive heterojunction; and electrically conductive means on the n-type layer.
Claim 37
Dependent Claim
97 words
A thin film polycrystalline heterojunction solar; cell, comprising: a conductive metal layer; a p-type layer of polycrystalline CuInS 2x Se 2 (l-x) semiconductor material on the conductive metal layer, wherein x is in the range of from 0 to 1.0, the layer having a composition gradient of S in the direction of the thickness of the layer to form a minority carrier mirror and having low resistivity Cu-rich region adjacent the conductive material layer; an n-type layer of semiconductor material on the p-type layer to form a photoactive heterojunction; and electrically conductive means on the n-type layer.
Claim 38
Dependent Claim
24 words
The cell of claim 33 wherein said composition gradient is characterized by the layer of p-type material being relatively S-rich within the Cu-rich region.
Claim 39
Dependent Claim
25 words
The cell of claim 33 wherein the n-type layer is Zn y Cd l-y S wherein y is in the range from 0 to 0.5.
Claim 40
Dependent Claim
22 words
The cell of claim 33 wherein the n-type layer is selected from the group consisting of ZnO, ZnSe, and CdSnO 4 .
Claim 41
Dependent Claim
7 words
The cell of claim 33 wherein 0≦x≦0.3.
Claim 42
Dependent Claim
22 words
The cell of claim 33 wherein the minority carrier mirror is formed by varying the rates of deposition of sulfur and selenium.
Claim 43
Independent Claim
268 words
A method of making a thin film polycrystalline heterojunction solar cell on a substrate comprised of a conductive metal layer; a p-type layer of polycrystalline CuIn l-x Ga x Se 2 , wherein x is in the range from about 0 to 1.0, the layer having a low resistivity Cu-rich region adjacent said conductive metal layer, a Ga-rich higher bandgap region within said Cu-rich region, and a lower bandgap region adjacent to said Ga-rich region; a layer of polycrystalline n-type semiconductor material disposed on the p-type layer to form the heterojunction; and an electrically conductive means disposed on the n-type material, said method comprising the steps of: (a) introducing a vapor of copper to a vessel containing said substrate while simultaneously introducing vapors of gallium, indium, and selenium to form a vapor mixture comprising the components of said p-type layer; (b) controlling the temperature of said substrate; (c) independently controlling the vaporization rates of copper, indium, gallium, and selenium; (d) maintaining the temperature of said substrate at a first temperature while depositing said vapor mixture on said substrate to form said Cu-rich region of said p-type material; (e) raising the temperature of said substrate to a second temperature and decreasing the Ga/In ratio by decreasing the vaporization rate of gallium; (f) decreasing the amount of copper in the vapor mixture by decreasing the vaporization rate of copper; (g) continuing depositing at the new vaporization rates to form a film having the above recited composition profile; (h) depositing the n-type layer on said p-type layer; and (i) depositing an electrically conductive means on the surface of said n-type layer.
Claim 44
Independent Claim
268 words
A method of making a thin film polycrystalline heterojunction solar cell on a substrate comprised of a conductive metal layer; a p-type layer of polycrystalline CuIn l-x Ga x Se 2 , wherein x is in the range from about 0 to 1.0, the layer having a low resistivity Cu-rich region adjacent said conductive metal layer, a Ga-rich higher bandgap region within said Cu-rich region, and a lower bandgap region adjacent to said Ga-rich region; a layer of polycrystalline n-type semiconductor material disposed on the p-type layer to form the heterojunction; and an electrically conductive means disposed on the n-type material, said method comprising the steps of: (a) introducing a vapor of copper to a vessel containing said substrate while simultaneously introducing vapors of gallium, indium, and selenium to form a vapor mixture comprising the components of said p-type layer; (b) controlling the temperature of said substrate; (c) independently controlling the vaporization rates of copper, indium, gallium, and selenium; (d) maintaining the temperature of said substrate at a first temperature while depositing said vapor mixture on said substrate to form said Cu-rich region of said p-type material; (e) raising the temperature of said substrate to a second temperature and decreasing the Ga/In ratio by decreasing the vaporization rate of gallium; (f) decreasing the amount of copper in the vapor mixture by decreasing the vaporization rate of copper; (g) continuing depositing at the new vaporization rates to form a film having the above recited composition profile; (h) depositing the n-type layer on said p-type layer; and (i) depositing an electrically conductive means on the surface of said n-type layer.
Claim 45
Independent Claim
141 words
A method for making a mixed ternary, I-III-VI thin film semiconductor, comprising the steps of: (a) heating a substrate having a back metal contact on an exposed surface to a temperature of about 450° C. in a high vacuum chamber; (b) introducing simultaneously a mixed vapor of the preferred elements of Groups I, III, and VI into the vessel at predetermined fluxes for each element; (c) depositing a first region on the contact for a predetermined time to form a mixed ternary polycrystalline material; (d) altering at least one flux of the elements while increasing the substrate temperature to about 550° C; and (e) depositing for a predetermined time a second region over the first region to complete the film, the second region being a mixed ternary polycrystalline material having a different chemical composition from the composition of the first region.
Claim 46
Independent Claim
141 words
A method for making a mixed ternary, I-III-VI thin film semiconductor, comprising the steps of: (a) heating a substrate having a back metal contact on an exposed surface to a temperature of about 450° C. in a high vacuum chamber; (b) introducing simultaneously a mixed vapor of the preferred elements of Groups I, III, and VI into the vessel at predetermined fluxes for each element; (c) depositing a first region on the contact for a predetermined time to form a mixed ternary polycrystalline material; (d) altering at least one flux of the elements while increasing the substrate temperature to about 550° C; and (e) depositing for a predetermined time a second region over the first region to complete the film, the second region being a mixed ternary polycrystalline material having a different chemical composition from the composition of the first region.
Claim 47
Dependent Claim
16 words
The method of claim 40 wherein the step of altering includes reducing the flux of copper.
Claim 48
Dependent Claim
16 words
The method of claim 40 wherein the step of altering includes reducing the flux of gallium.
Claim 49
Dependent Claim
19 words
The method of claim 40 wherein the step of altering includes simultaneously reducing the fluxes of copper and gallium.
Claim 50
Dependent Claim
21 words
The product of the process of claim 41 wherein the film comprises CuIn l-x Ga x Se 2 , where 0.25≦x≦0.35.
Claim 51
Dependent Claim
28 words
The product of the process of claim 43 wherein the film comprises CuInGaSe 2 , and wherein the first region and second region define a minority carrier mirror.
Claim 52
Dependent Claim
28 words
The product of the process of claim 43 wherein the film comprises CuInGaSe 2 , and wherein the first region has a higher bandgap than the second region.
Claim 53
Dependent Claim
45 words
The method of claim 40 wherein the film comprises CuInGaSe 2 , wherein the step of altering includes reducing the flux of copper and reducing the flux of gallium, and wherein the film includes a copper-rich region adjacent the contact and a minority carrier mirror.
Claim 54
Dependent Claim
24 words
The method of claim 40 further comprising the step of depositing a II-VI semiconductor on the I-III-VI 2 film to form a photoactive heterojunction.
Claim 55
Dependent Claim
14 words
The method of claim 48 wherein the II-VI semiconductor comprises a mixed binary material.
Claim 56
Dependent Claim
8 words
The product of the process of claim 49.
Claim 57
Dependent Claim
8 words
The product of the process of claim 48.
Claim 58
Dependent Claim
29 words
A mixed ternary, I-III-VI 2 thin film semiconductor comprising: (a) a copper-rich region of CuInGaSe 2 ; and (b) a copper-deficient region of CuInGaSe 2 overlying the copper-rich region.
Claim 59
Dependent Claim
29 words
A mixed ternary, I-III-VI 2 thin film semiconductor comprising: (a) a copper-rich region of CuInGaSe 2 ; and (b) a copper-deficient region of CuInGaSe 2 overlying the copper-rich region.
Claim 60
Dependent Claim
21 words
The semiconductor of claim 52 wherein the copper-rich region includes a gallium-rich region and the copper-deficient region includes a gallium-deficient region.
Claim 61
Dependent Claim
17 words
The semiconductor of claim 53 wherein the gallium-rich region and gallium-poor region define a minority carrier mirror.
Claim 62
Dependent Claim
20 words
The semiconductor of claim 53 further comprising a II-VI thin film adjacent the copper-deficient region to define a photoactive heterojunction.
Claim 63
Dependent Claim
15 words
The semiconductor of claim 55 wherein the II-VI thin film is a mixed binary material.
Claim 64
Dependent Claim
10 words
The semiconductor of claim 56 wherein the material is CdZnS.
Claim 65
Dependent Claim
16 words
The semiconductor of claim 57 wherein the material has a thickness less than about 3 micrometers.
Claim 66
Dependent Claim
27 words
The semiconductor of claim 57 wherein the material has a thickness less than about 500 angstroms for transmission of incident light through the material to the junction.
Claim 67
Dependent Claim
41 words
The semiconductor of cliam 55 wherein the gallium-rich region and gallium-deficient region define a minority carrier mirror in the I-III-VI 2 semiconductor formed by the change in composition of the semiconductor from a higher bandgap material to a lower bandgap material.
Claim 68
Dependent Claim
41 words
The semiconductor of cliam 55 wherein the gallium-rich region and gallium-deficient region define a minority carrier mirror in the I-III-VI 2 semiconductor formed by the change in composition of the semiconductor from a higher bandgap material to a lower bandgap material.
Claim 69
Dependent Claim
20 words
The semiconductor of claim 52 further comprising a II-VI thin film adjacent the copper-deficient region to define a photoactive heterojunction.
Claim 70
Dependent Claim
12 words
The semiconductor of claim 61 wherein the II-VI thin film is CdZnS.
Claim 71
Dependent Claim
30 words
The semiconductor of claim 62 wherein the II-VI thin film has a thickness of less than about 500 angstroms for transmission of incident light through the material to the junction.
Claim 72
Dependent Claim
30 words
The semiconductor of claim 61 wherein the II-VI thin film has a thickness of less than about 500 angstroms for transmission of incident light through the material to the junction.
Claim 73
Dependent Claim
89 words
A mixed ternary, copper indium gallium selenide material for use in a I-III-VI 2 /II-VI heterojunction solar cell, comprising: (a) a low resistivity relatively high conductivity thin film region positionable adjacent a back metal contact in the cell and having a composition simultaneously rich in copper and gallium; and (b) a second thin film region overlying and forming an interface with the low resistivity thin film region and positionable adjacent the junction in the cell, the second thin film region having a composition simultaneously deficient in copper and gallium.
Claim 74
Dependent Claim
89 words
A mixed ternary, copper indium gallium selenide material for use in a I-III-VI 2 /II-VI heterojunction solar cell, comprising: (a) a low resistivity relatively high conductivity thin film region positionable adjacent a back metal contact in the cell and having a composition simultaneously rich in copper and gallium; and (b) a second thin film region overlying and forming an interface with the low resistivity thin film region and positionable adjacent the junction in the cell, the second thin film region having a composition simultaneously deficient in copper and gallium.
Claim 75
Dependent Claim
31 words
The material of claim 65 wherein the interface of the low resistivity region and the second region defines a minority carrier mirror formed by the change in bandgap of the material.
Claim 76
Dependent Claim
19 words
The material of claim 65 wherein the low resistivity region comprises about 2/3 of the thickness of the material.
Claim 77
Dependent Claim
30 words
The material of claim 65 wherein the concentration of gallium in the low resistivity region is about 0.35 and the concentration of gallium in the second region is about 0.25.
Claim 78
Dependent Claim
15 words
The material of claim 68 wherein both regions are polycrystalline and the material is p-type.
Claim 79
Dependent Claim
10 words
The material of claim 65 wherein both regions are polycrystalline.
Claim 80
Dependent Claim
7 words
The material of claim 65 being p-type.
Claim 81
Dependent Claim
21 words
The material of claim 65 further comprising a II-VI thin film adjacent the second thin film region to define the heterojunction.
Claim 82
Dependent Claim
21 words
The material of claim 72 wherein the low resistivity region comprises about 2/3 of the thickness of the I-III-VI 2 material.
Claim 83
Dependent Claim
18 words
The material of claim 73 wherein the II-VI thin film has a thickness less than about 3 micrometers.
Claim 84
Dependent Claim
17 words
The material of claim 74 wherein the II-VI thin film is a polycrystalline, mixed binary CdZnS semiconductor.
Claim 85
Dependent Claim
16 words
The material of claim 75 wherein the CdZnS semiconductor has an undoped region adjacent the junction.
Claim 86
Dependent Claim
17 words
The material of claim 76 further comprising a conductive contact layer of ZnO adjacent the CdZnS semiconductor.
Claim 87
Dependent Claim
9 words
A solar cell including the material of cliam 77.
Claim 88
Dependent Claim
9 words
A solar cell including the material of cliam 77.
Claim 89
Dependent Claim
9 words
A solar cell including the material of claim 76.
Claim 90
Dependent Claim
33 words
The material of claim 76 wherein the interface of the low resistivity region and the second thin film region defines a minority carrier mirror formed by the change in bandgap between the regions.
Claim 91
Dependent Claim
26 words
The material of claim 73 wherein the II-VI thin film has a thickness of less than about 500 angstroms for transmission of light to the junction.
Claim 92
Dependent Claim
15 words
The material of cliam 72 wherein the II-VI thin film is a mixed binary semiconductor.
Claim 93
Dependent Claim
15 words
The material of cliam 72 wherein the II-VI thin film is a mixed binary semiconductor.
Claim 94
Dependent Claim
12 words
The material of claim 82 wherein the mixed binary semiconductor is CdZnS.
Claim 95
Dependent Claim
9 words
A solar cell including the material of claim 72.
Claim 96
Dependent Claim
9 words
A solar cell including the material of claim 65.
Claim 97
Dependent Claim
63 words
A mixed ternary copper indium gallium selenide material for use in a I-III-VI 2 /II-VI heterojunction solar cell, comprising: a constant gallium concentration, polycrystalline material having a low resistivity, copper-rich region positionable adjacent a back metal contact in the cell and having a copper-deficient region overlying the copper-rich region and positionable adjacent the junction of the cell, wherein 0.25≦the mole fraction of gallium≦0.35.
Claim 98
Dependent Claim
63 words
A mixed ternary copper indium gallium selenide material for use in a I-III-VI 2 /II-VI heterojunction solar cell, comprising: a constant gallium concentration, polycrystalline material having a low resistivity, copper-rich region positionable adjacent a back metal contact in the cell and having a copper-deficient region overlying the copper-rich region and positionable adjacent the junction of the cell, wherein 0.25≦the mole fraction of gallium≦0.35.
Claim 99
Dependent Claim
9 words
A solar cell including the material of claim 86.
Claim 100
Dependent Claim
50 words
The material of claim 86 further comprising a polycrystalline thin film, CdZnS mixed binary semiconductor adjacent the copper-deficient region to define the junction, wherein the CdZnS semiconductor has a thickness less than about 3 micrometers permitting transmission of light to the junction and has a zinc-rich portion adjacent the junction.
Claim 101
Dependent Claim
9 words
A solar cell including the material of claim 88.
Claim 102
Dependent Claim
17 words
The material of claim 88 further comprising a conductive contact layer of ZnO adjacent the CdZnS semiconductor.
Claim 103
Dependent Claim
9 words
A solar cell including the material of claim 90.
Claim 104
Dependent Claim
197 words
A thin film polycrystalline heterojunction solar cell, comprising: (a) a substrate; (b) a base contact on one surface of the substrate; (c) a mixed ternary CuIn l-x Ga x Se 2 l p-type semiconductor layer deposited on the base contact and including, (i) a first region adjacent the contact and being simultaneously rich in copper relative to the ratio of Ga and In and rich in Ga relative to In; (ii) a second region on the first region being simultaneously deficient in copper relative to the ratio of Ga and In and deficient in Ga relative to the first region, and having a bandgap lower than that of the first region; (d) a mixed ternary n-type semiconductor layer of Zn y Cd l-y S deposited on the second region of the p-type semiconductor to form a photoactive heterojunction the layer including, (i) an undoped region adjacent the heterojunction, and (ii) a low resistivity doped region overlying the undoped region and remote from the heterojunction; (e) a collector deposited on the n-type semiconductor layer remote from the heterojunction, comprising at least one layer of ZnO; and (f) an antireflection coating deposited over the collector, wherein 0<x<0.1 and 0<y<0.50.
Claim 105
Dependent Claim
197 words
A thin film polycrystalline heterojunction solar cell, comprising: (a) a substrate; (b) a base contact on one surface of the substrate; (c) a mixed ternary CuIn l-x Ga x Se 2 l p-type semiconductor layer deposited on the base contact and including, (i) a first region adjacent the contact and being simultaneously rich in copper relative to the ratio of Ga and In and rich in Ga relative to In; (ii) a second region on the first region being simultaneously deficient in copper relative to the ratio of Ga and In and deficient in Ga relative to the first region, and having a bandgap lower than that of the first region; (d) a mixed ternary n-type semiconductor layer of Zn y Cd l-y S deposited on the second region of the p-type semiconductor to form a photoactive heterojunction the layer including, (i) an undoped region adjacent the heterojunction, and (ii) a low resistivity doped region overlying the undoped region and remote from the heterojunction; (e) a collector deposited on the n-type semiconductor layer remote from the heterojunction, comprising at least one layer of ZnO; and (f) an antireflection coating deposited over the collector, wherein 0<x<0.1 and 0<y<0.50.
References Cited (Backward Citations)
JPS5128493A
Cited
US4335266A
Cited
USRE31968E
Cited
US4523051A
Cited
US4611091A
Cited
US4612411A
Cited
US4680422A
Cited
US4795501A
Cited
US4867801A
Cited
US4703131A
Cited
US4684761A
Cited
US4735662A
Cited
US4915745A
Cited
US4915745B1
Cited
US5028274A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-08-25 | 1996-02-24 | 1996-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-08-25 | 2000-02-24 | 2000-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-08-25 | 2004-02-24 | 2004-08-25 | $7700.00 | Window Closed / Lapsed |