US4795501A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Single crystal, heteroepitaxial, GaAlAs/CuInSe2 tandem solar cell and method of manufacture
Assignee: Boeing Co
•
Filing: 1987-07-13
•
Granted: 1989-01-03
•
Expires: 2007-07-13
Abstract
Abstract Solar cells having high efficiency and high specific power are prepared in an "upside-down" process by depositing a lattice mismatch transition zone of ZnS x Se x and Cd y Zn 1-y S z Se 1-z on a CLEFT, double-heterostructure, single crystal, Ga a Al 1-a As/GaAs thin film followed by deposition of a CuInSe 2 thin film on the transition zone.
Inventors
- 👤 Billy J. Stanbery
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 03:38
CPC Classifications
H; H10; H10F; H10F10/00; H10F10/10; H10F10/16; H10F10/167; H10F10/161; H10F10/162; H10F10/19; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/541; Y02E10/543; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 62
Claim 1
Independent Claim
47 words
A high efficiency tandem solar cell, comprising: (a) an Ga a Al 1-a As upper cell; (b) a transition zone attached to the upper cell to match the lattice structure of Ga a Al 1-a As to CuInSe 2 ; and (c) a CuInSe 2 lower cell.
Claim 2
Dependent Claim
47 words
A high efficiency tandem solar cell, comprising: (a) an Ga a Al 1-a As upper cell; (b) a transition zone attached to the upper cell to match the lattice structure of Ga a Al 1-a As to CuInSe 2 ; and (c) a CuInSe 2 lower cell.
Claim 3
Dependent Claim
16 words
The solar cell of claim 1 wherein the transition zone includes at least one II-VI alloy.
Claim 4
Dependent Claim
15 words
The solar cell of claim 2 wherein the upper cell is a double-heterostructure single crystal.
Claim 5
Dependent Claim
19 words
The solar cell of claim 2 wherein the CuInSe 2 lower cell is heteroepitaxially deposited on the transition zone.
Claim 6
Dependent Claim
40 words
The solar cell of claim 4 wherein the CuInSe 2 lower cell is p-type and comprises a first region deficient in copper, a second region forming the p-type bulk of the lower cell, and a third region rich in selenium.
Claim 7
Dependent Claim
47 words
The solar cell of claim 5 wherein the transition zone includes a first transition region of ZnS x Se 1-x attached to the Ga a Al 1-a As and a second transition region of Cd y Zn 1-y S z Se 1-z attached to the first region.
Claim 8
Dependent Claim
15 words
The solar cell of claim 6 wherein the upper cell is a double-heterostructure single crystal.
Claim 9
Dependent Claim
16 words
The solar cell of claim 7 having a specific power of at least about 1000 watts/kg.
Claim 10
Dependent Claim
18 words
The solar cell of claim 8 wherein x in ZnS x Se 1-x is approximately equal to 0.05.
Claim 11
Dependent Claim
14 words
The solar cell of claim 9 wherein for Ga a Al 1-a As, 1.0≦a≦0.6.
Claim 12
Dependent Claim
18 words
The solar cell of claim 10 wherein, for Cd y Zn 1-y S z Se 1-z , 0≦y≦0.90.
Claim 13
Dependent Claim
14 words
The solar cell of claim 11 wherein y=z=0 so that the material is ZnSe.
Claim 14
Dependent Claim
12 words
The solar cell of claim 12 wherein the ZnSe is degenerately doped.
Claim 15
Dependent Claim
15 words
The solar cell of claim 5 wherein the upper cell is a double-heterostructure single crystal.
Claim 16
Dependent Claim
36 words
The solar cell of claim 1 wherein the transition zone includes a first II-VI alloy forming an upper junction with the upper cell and a second II-VI alloy forming a lower junction with the lower cell.
Claim 17
Dependent Claim
46 words
The solar cell of claim 1 wherein the transition zone includes a first region of ZnS x Se 1-x attached to the upper cell and a second region of Cd y Zn 1-y S z Se 1-z attached to the first region and the lower cell.
Claim 18
Dependent Claim
13 words
The solar cell of claim 1 wherein the upper cell includes a double-heterostructure.
Claim 19
Dependent Claim
14 words
The solar cell of claim 17 wherein the upper cell is a single crystal.
Claim 20
Dependent Claim
16 words
The solar cell of claim 18 wherein the upper cell is formed by the CLEFT process.
Claim 21
Dependent Claim
42 words
The solar cell of claim 18 wherein the transition zone includes a first region of ZnS x Se 1-x attached to the upper cell and a second region of Cd y Zn 1-y S z Se 1-z attached to the first region.
Claim 22
Dependent Claim
40 words
The solar cell of claim 1 wherein the CuInSe 2 lower cell is p-type and comprises a first region deficient in copper, a second region comprising the p-type bulk of the lower cell, and a third region rich in selenium.
Claim 23
Independent Claim
62 words
A method for making a high efficiency tandem solar cell comprising the steps of: (a) forming an upper thin film of Ga a Al 1-a As; (b) depositing Cd y Zn 1-y S z Se 1-z on the upper thin film; and (c) depositing a lower thin film of CuInSe 2 on the Cd y Zn 1-y S x Se 1-x .
Claim 24
Independent Claim
62 words
A method for making a high efficiency tandem solar cell comprising the steps of: (a) forming an upper thin film of Ga a Al 1-a As; (b) depositing Cd y Zn 1-y S z Se 1-z on the upper thin film; and (c) depositing a lower thin film of CuInSe 2 on the Cd y Zn 1-y S x Se 1-x .
Claim 25
Dependent Claim
47 words
The method of claim 22 wherein step (b) includes the substeps of depositing a first layer of ZnS z Se 1-z on the upper thin film and grading the composition from ZnS z Se 1-z to Cd y Zn 1-y S z Se 1-z , wherein 0≦y≦0.90.
Claim 26
Dependent Claim
22 words
The method of claim 22 wherein the step of forming the upper thin film includes the substep of forming a double heterostructure.
Claim 27
Dependent Claim
54 words
The method of claim 24 wherein the step of depositing the lower thin film includes the substeps of depositing a copper-deficient CuInSe 2 region on the Cd y Zn 1-y S z Se 1-z , grading the CuInSe 2 to a bulk region, and grading the bulk region to a selenium-rich CuInSe 2 region.
Claim 28
Dependent Claim
21 words
The method of claim 25 further comprising the step of depositing a back surface reflector on the selenium-rich CuInSe 2 region.
Claim 29
Dependent Claim
8 words
The product of the process of claim 26.
Claim 30
Independent Claim
58 words
A method for making a monolithic, single crystal, tandem solar cell comprising the steps of: (a) making a single crystal upper thin film cell of a III-V alloy; (b) heteroepitaxially depositing a lower thin cell of a I-III-VI 2 alloy on the upper thin film cell; and (c) depositing a back contact on the lower thin film cell
Claim 31
Independent Claim
58 words
A method for making a monolithic, single crystal, tandem solar cell comprising the steps of: (a) making a single crystal upper thin film cell of a III-V alloy; (b) heteroepitaxially depositing a lower thin cell of a I-III-VI 2 alloy on the upper thin film cell; and (c) depositing a back contact on the lower thin film cell
Claim 32
Dependent Claim
31 words
The method of claim 28 wherein making the upper thin film cell includes depositing Ga, Al, and As and depositing the lower thin film cell includes depositing Cu, In, and Se.
Claim 33
Dependent Claim
25 words
The method of claim 29 further comprising the step of heteroepitaxially depositing a lattice mismatch transition zone between the upper cell and the lower cell.
Claim 34
Dependent Claim
24 words
The method of claim 30 wherein the lower cell is deposited at low temperatures to minimize the diffusion of copper into the transition zone.
Claim 35
Independent Claim
66 words
A method for making a solar cell comprising the steps of: (a) making an upper thin film cell of a III-V alloy; (b) depositing a lattice mismatch transition zone of at least one II-VI alloy on the III-V upper cell; (c) depositing a lower thin film of a I-III-VI 2 alloy on the transition zone; and (d) depositing a back contact on the lower thin film.
Claim 36
Independent Claim
66 words
A method for making a solar cell comprising the steps of: (a) making an upper thin film cell of a III-V alloy; (b) depositing a lattice mismatch transition zone of at least one II-VI alloy on the III-V upper cell; (c) depositing a lower thin film of a I-III-VI 2 alloy on the transition zone; and (d) depositing a back contact on the lower thin film.
Claim 37
Dependent Claim
21 words
The method of claim 32 wherein the transition zone includes a graded Zn y Cd 1-y S z Se 1-z layer.
Claim 38
Dependent Claim
23 words
The method of claim 32 wherein the step of making the upper thin film cell includes preparing a double-heterostructure, single crystal, AlGaAs cell.
Claim 39
Dependent Claim
15 words
The method of claim 34 wherein the upper cell is made by the CLEFT process.
Claim 40
Dependent Claim
20 words
The method of claim 34 further comprising the step of applying at least one antireflection coating to the upper cell.
Claim 41
Dependent Claim
42 words
The method of claim 32 wherein the step of making the upper thin film includes epitaxially forming the upper thin film on a removable substrate and wherein the method further includes the step of removing the substrate from the upper thin film.
Claim 42
Dependent Claim
8 words
The product of the process of claim 32.
Claim 43
Independent Claim
81 words
A method for making a high efficiency tandem cell having a high specific power, comprising the steps of: (a) making a double-heterostructure, single crystal, thin film, upper cell including Ga a Al 1-a As, wherein 1.0≦a≦0.60; (b) depositing a graded Cd y Zn 1-y S z Se 1-z thin film transition zone on the upper cell, beginning with a layer of ZnS 0 .05 Se 0 .95 ; and (c) depositing a lower cell of CuInSe 2 on the transition zone.
Claim 44
Independent Claim
81 words
A method for making a high efficiency tandem cell having a high specific power, comprising the steps of: (a) making a double-heterostructure, single crystal, thin film, upper cell including Ga a Al 1-a As, wherein 1.0≦a≦0.60; (b) depositing a graded Cd y Zn 1-y S z Se 1-z thin film transition zone on the upper cell, beginning with a layer of ZnS 0 .05 Se 0 .95 ; and (c) depositing a lower cell of CuInSe 2 on the transition zone.
Claim 45
Dependent Claim
26 words
The method of claim 39 wherein the deposition of step (c) is done at low temperatures to minimize the diffusion of copper into the transition zone.
Claim 46
Dependent Claim
41 words
The method of claim 39 wherein the upper cell is made according to the method of Gale, so that the upper cell has an n + -type first region, a p-type bulk region, and a p + -type minority carrier region.
Claim 47
Dependent Claim
24 words
The method of claim 39 wherein the CuInSe 2 includes a copper-deficient region adjacent the transition zone, a bulk region, and a selenium-rich region.
Claim 48
Dependent Claim
18 words
The method of claim 39 further comprising depositing a back surface reflector and contact onto the lower cell.
Claim 49
Dependent Claim
15 words
The method of claim 43 further comprising applying an antireflection coating onto the upper cell.
Claim 50
Dependent Claim
8 words
The product of the process of claim 44.
Claim 51
Independent Claim
171 words
A method for making a high efficiency, tandem solar cell having a high specific power, comprising the steps of: (a) making a double-heterostructure, single crystal Ga a Al 1-a As upper cell including an n + -type first AlGaAs layer, a p-type bulk layer adjacent the first layer, and a p + -type AlGaAs minority carrier mirror on the bulk layer, wherein 1.0≦a≦0.60; (b) depositing a lattice mismatch transition zone on the p + -type minority carrier by initially depositing a ZnS 0 .05 Se 0 .95 thin film and grading the composition subsequently to Cd y Zn 1-y S z Se 1-z wherein 0≦y≦0.90 and z may assume any value between 0 and 1.0; (c) depositing CuInSe 2 thin film on the transition zone at low temperature to minimize the diffusion of copper into the transition zone; (d) depositing a back surface reflector and contact on the CuInSe 2 thin film; and (e) depositing at least one antireflection coating on the n + -type first layer of the upper cell.
Claim 52
Independent Claim
171 words
A method for making a high efficiency, tandem solar cell having a high specific power, comprising the steps of: (a) making a double-heterostructure, single crystal Ga a Al 1-a As upper cell including an n + -type first AlGaAs layer, a p-type bulk layer adjacent the first layer, and a p + -type AlGaAs minority carrier mirror on the bulk layer, wherein 1.0≦a≦0.60; (b) depositing a lattice mismatch transition zone on the p + -type minority carrier by initially depositing a ZnS 0 .05 Se 0 .95 thin film and grading the composition subsequently to Cd y Zn 1-y S z Se 1-z wherein 0≦y≦0.90 and z may assume any value between 0 and 1.0; (c) depositing CuInSe 2 thin film on the transition zone at low temperature to minimize the diffusion of copper into the transition zone; (d) depositing a back surface reflector and contact on the CuInSe 2 thin film; and (e) depositing at least one antireflection coating on the n + -type first layer of the upper cell.
Claim 53
Dependent Claim
22 words
The method of claim 46 further comprising the step of separating the upper cell from a substrate after steps (b) and (c).
Claim 54
Dependent Claim
8 words
The product of the process of claim 47.
Claim 55
Dependent Claim
14 words
The method of claim 46 wherein making the upper cell uses the CLEFT process.
Claim 56
Dependent Claim
32 words
The method of claim 46 wherein the CuInSe 2 thin film is a graded film having a copper-deficient region adjacent the transition zone and a selenium-rich region adjacent the back surface reflector.
Claim 57
Dependent Claim
8 words
The product of the process of claim 46.
Claim 58
Dependent Claim
8 words
The product of the process of claim 49.
Claim 59
Dependent Claim
78 words
A high efficiency tandem solar cell, comprising: (a) an upper cell comprising at least one III-V alloy, (b) a lattice mismatch transition zone comprising at least two II-VI alloys, one alloy attached to the upper cell by a heteroepitaxial technique, (c) a lower cell comprising at least one I-III-VI 2 alloy attached to the transition zone, (d) a back surface reflector attached to the lower cell, and (e) at least one antireflection coating attached to the upper cell.
Claim 60
Dependent Claim
78 words
A high efficiency tandem solar cell, comprising: (a) an upper cell comprising at least one III-V alloy, (b) a lattice mismatch transition zone comprising at least two II-VI alloys, one alloy attached to the upper cell by a heteroepitaxial technique, (c) a lower cell comprising at least one I-III-VI 2 alloy attached to the transition zone, (d) a back surface reflector attached to the lower cell, and (e) at least one antireflection coating attached to the upper cell.
Claim 61
Dependent Claim
64 words
An intermediate useful in preparing high efficiency tandem, heteroepitaxial photovoltaic devices, comprising: (a) a substrate, (b) a III-V alloy removably deposited by an epitaxial technique on the substrate, (c) a lattice mismatch transition zone deposited on the III-V alloy, and (d) a second photoactive semiconductor alloy having a different lattice constant from the III-V alloy deposited on the transition zone by a heteroepitaxial technique.
Claim 62
Dependent Claim
64 words
An intermediate useful in preparing high efficiency tandem, heteroepitaxial photovoltaic devices, comprising: (a) a substrate, (b) a III-V alloy removably deposited by an epitaxial technique on the substrate, (c) a lattice mismatch transition zone deposited on the III-V alloy, and (d) a second photoactive semiconductor alloy having a different lattice constant from the III-V alloy deposited on the transition zone by a heteroepitaxial technique.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-01-03 | 1992-07-04 | 1993-01-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-01-03 | 1996-07-04 | 1997-01-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-01-03 | 2000-07-04 | 2001-01-03 | $7700.00 | Window Closed / Lapsed |