US5334545A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for forming self-aligning cobalt silicide T-gates of silicon MOS devices
Assignee: Honeywell International Inc
•
Filing: 1993-02-01
•
Granted: 1994-08-02
•
Expires: 2013-02-01
Abstract
Abstract A process for producing a cobalt silicide T-gate on a silicon substrate (10) in which a silicon oxide gate layer (12) is formed in the silicon substrate (10). The silicon oxide gate layer (12) is covered with a polysilicon layer (14) and a masking oxide layer (16). An opening (18) is formed in the masking oxide layer (16) through to the polysilicon layer (14) which defines a gate region (22) for the device being fabricated (16). A cobalt layer (20) is deposited on the masking oxide layer (16) and the surface of the polysilicon layer (14) in the gate region (22). The substrate (10) is then heated to react the cobalt layer (20) with the polysilicon layer (14) to form a cobalt silicide layer (24) in the gate region (22). The unreacted portion of the cobalt layer (20) and masking oxide layer (16) are removed and the polysilicon layer (14) etched using the cobalt silicide layer (24) as a mask. The etching undercuts a portion of the polysilicon layer (14) under the cobalt silicide layer (24) forming a self-aligned cobalt silicide T-gate structure.
Inventors
- 👤 Anthony L. Caviglia
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 12:53
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/0131; H10D64/01324; H10P; H10P50/00; H10P50/71
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
165 words
A process for making a self-aligned cobalt silicide T-gate for silicon MOS devices comprising the steps of: forming a gate oxide layer on a top surface of a silicon substrate; forming a polysilicon layer on said gate oxide layer; forming a masking oxide layer on said polysilicon layer, said masking oxide layer having an opening exposing a gate region on said polysilicon layer; depositing a layer of cobalt on said masking oxide layer and said gate region of the polysilicon layer; heating said substrate to react said cobalt layer with said polysilicon layer in said opening to form a cobalt silicide layer in said gate region, said cobalt layer deposited on said masking oxide layer remaining unreacted; removing said unreacted portion of said cobalt layer and said masking oxide layer to expose said polysilicon layer in the region not covered by said cobalt silicide layer; and etching said exposed polysilicon layer using said cobalt silicide as a mask to form said self-aligned cobalt silicide T-gate.
Claim 2
Dependent Claim
165 words
A process for making a self-aligned cobalt silicide T-gate for silicon MOS devices comprising the steps of: forming a gate oxide layer on a top surface of a silicon substrate; forming a polysilicon layer on said gate oxide layer; forming a masking oxide layer on said polysilicon layer, said masking oxide layer having an opening exposing a gate region on said polysilicon layer; depositing a layer of cobalt on said masking oxide layer and said gate region of the polysilicon layer; heating said substrate to react said cobalt layer with said polysilicon layer in said opening to form a cobalt silicide layer in said gate region, said cobalt layer deposited on said masking oxide layer remaining unreacted; removing said unreacted portion of said cobalt layer and said masking oxide layer to expose said polysilicon layer in the region not covered by said cobalt silicide layer; and etching said exposed polysilicon layer using said cobalt silicide as a mask to form said self-aligned cobalt silicide T-gate.
Claim 3
Dependent Claim
26 words
The process of claim 1 wherein said step of forming said polysilicon layer comprises the step of depositing a layer of polysilicon approximately 4,000 Å thick.
Claim 4
Dependent Claim
49 words
The process of claim 1 wherein said step of heating comprises the step of heating said substrate to a temperature in the range from 600° C. to 700° C. for a time sufficient for said cobalt layer to react with said polysilicon layer to form said cobalt silicide layer.
Claim 5
Dependent Claim
50 words
The process of claim 1 wherein said step of removing said masking oxide layer and said unreacted cobalt layer comprises the steps of: wet etching to remove said unreacted cobalt layer from said masking oxide layer; and reactive ion etching to remove said masking oxide layer from said polysilicon layer.
Claim 6
Dependent Claim
96 words
A process for forming a cobalt silicide T-gate on a silicon substrate comprising the steps of: forming a gate silicon oxide layer on a surface of said silicon substrate; depositing a polysilicon layer on said gate silicon oxide layer; forming a masking layer on said polysilicon layer, said masking layer having an opening exposing a gate region on said polysilicon layer; forming a cobalt silicide layer in said gate region; etching to remove said masking layer; and selective etching said polysilicon layer using said cobalt silicide layer as a mask to form said cobalt silicide T-gate.
Claim 7
Dependent Claim
96 words
A process for forming a cobalt silicide T-gate on a silicon substrate comprising the steps of: forming a gate silicon oxide layer on a surface of said silicon substrate; depositing a polysilicon layer on said gate silicon oxide layer; forming a masking layer on said polysilicon layer, said masking layer having an opening exposing a gate region on said polysilicon layer; forming a cobalt silicide layer in said gate region; etching to remove said masking layer; and selective etching said polysilicon layer using said cobalt silicide layer as a mask to form said cobalt silicide T-gate.
Claim 8
Dependent Claim
59 words
The process of claim 5 wherein said step of forming a silicide layer comprises the steps of: depositing a layer of cobalt on said masking layer and on said polysilicon layer within said gate; and heating said silicon substrate to react said layer of cobalt with said polysilicon layer in said gate region to form said cobalt silicide layer.
Claim 9
Dependent Claim
47 words
The process of claim 6 wherein said step of heating comprises the step of heating said silicon substrate to a temperature between 600° C. to 700° C. for a time sufficient for said cobalt layer to react with said polysilicon layer to form said cobalt silicide layer.
References Cited (Backward Citations)
US4285761A
Cited
US4362597A
Cited
US4378628A
Cited
US4470189A
Cited
US4528066A
Cited
US4901121A
Cited
US4912061A
Cited
US5089863A
Cited
US5064773A
Cited
US5115290A
Cited
US5034791A
Cited
US5086017A
Cited
US5120668A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-01 | 1998-01-31 | 1998-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-01 | 2002-01-31 | 2002-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-01 | 2006-01-31 | 2006-08-02 | $7700.00 | Window Closed / Lapsed |