Method of fabricating high-conductivity silicide-on-polysilicon structures for MOS devices
Assignee: Agere Systems LLC
•
Filing: 1981-01-19
•
Granted: 1982-12-07
•
Expires: 2001-01-19
Abstract
Abstract It is known to deposit a refractory metal silicide on a polysilicon gate layer to form a low-resistivity composite structure. For VLSI MOS devices, very-high-resolution patterning of the composite structure is required. In accordance with this invention, a silicide pattern is formed on polysilicon by a lift-off technique. In turn, the patterned silicide is utilized as a mask for anisotropic etching of the underlying polysilicon. High-conductivity composite silicide-on-polysilicon gate structures for VLSI MOS devices are thereby achieved.
Inventors
- 👤 David B. Fraser
- 👤 Eliezer Kinsbron
- 👤 Frederick Vratny
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 05:02
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01326; H10D64/01306; H10D64/01308; H10D64/01312; H10D64/60; H10D64/66; H10D64/661; H10D64/662; H10D64/663; H10P; H10P50/00; H10P50/71
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
139 words
A method of fabricating high-conductivity silicide-on-polysilicon structures in an MOS device, said method comprising the steps of forming a high-resolution pattern overlying a polysilicon layer of said device to define selected regions of said layer, depositing a metal-containing layer on top of said pattern and on said selected regions, the metallic constituent in said layer being selected from the group consisting of titanium, tantalum, molybdenum, tungsten, nickel and cobalt, which metal-containing layer is of the type that, upon sintering, will form a silicide, lifting off said pattern thereby leaving on said device only the metal-containing layer deposited on said selected regions, sintering said remaining metal-containing deposits to form composite silicide-on-polysilicon structures in said selected regions, and, utilizing said sintered metal-containing deposits as an etch-resistant mask, anisotropically etching said polysilicon layer to remove all portions thereof except said silicide-on-polysilicon structures.
Claim 2
Independent Claim
139 words
A method of fabricating high-conductivity silicide-on-polysilicon structures in an MOS device, said method comprising the steps of forming a high-resolution pattern overlying a polysilicon layer of said device to define selected regions of said layer, depositing a metal-containing layer on top of said pattern and on said selected regions, the metallic constituent in said layer being selected from the group consisting of titanium, tantalum, molybdenum, tungsten, nickel and cobalt, which metal-containing layer is of the type that, upon sintering, will form a silicide, lifting off said pattern thereby leaving on said device only the metal-containing layer deposited on said selected regions, sintering said remaining metal-containing deposits to form composite silicide-on-polysilicon structures in said selected regions, and, utilizing said sintered metal-containing deposits as an etch-resistant mask, anisotropically etching said polysilicon layer to remove all portions thereof except said silicide-on-polysilicon structures.
Claim 3
Dependent Claim
35 words
a method as in claim 1 wherein, prior to said depositing step, the surfaces of the selected regions of said polysilicon layer are isotropically etched to thin the polysilicon layer to its final desired thickness.
Claim 4
Dependent Claim
43 words
A method as in claim 1 wherein an intermediate layer is formed on top of said polysilicon layer, and wherein, prior to said depositing step, said intermediate layer is patterned in an isotropic etching step to expose surface regions of said polysilicon layer.
Claim 5
Independent Claim
216 words
A method of fabricating a high-conductivity gate structure in an MOS device that comprises a silicon substrate having a gate oxide layer formed on said substrate and a doped polysilicon layer overlying said gate oxide layer, said method comprising the steps of forming a high-resolution masking pattern with substantially vertical sidewalls on said polysilicon layer to cover all but selected surface regions of said polysilicon layer, isotropically etching said selected surface regions to thin the polysilicon layer to its final desired thickness, depositing a metal-containing layer on top of said masking pattern and on said selected surface regions, the metallic constituent in said layer being selected from the group consisting of titanium, tantalum, molybdenum, tungsten, nickel and cobalt, which metal-containing layer is of the type that, upon sintering, will form a silicide, removing said masking pattern from said polysilicon layer thereby lifting off those portions of said metal-containing layer deposited on top of said masking pattern and leaving in place on said selected surface regions those portions of said metal-containing layer deposited on said regions, sintering the remaining portions of said metal-containing layer to form composite silicide-on-polysilicon structures in said selected regions, and, utilizing said remaining sintered portions as a mask, anisotropically etching said polysilicon layer to define a high-conductivity silicide-on-polysilicon gate structure in said device.
Claim 6
Independent Claim
216 words
A method of fabricating a high-conductivity gate structure in an MOS device that comprises a silicon substrate having a gate oxide layer formed on said substrate and a doped polysilicon layer overlying said gate oxide layer, said method comprising the steps of forming a high-resolution masking pattern with substantially vertical sidewalls on said polysilicon layer to cover all but selected surface regions of said polysilicon layer, isotropically etching said selected surface regions to thin the polysilicon layer to its final desired thickness, depositing a metal-containing layer on top of said masking pattern and on said selected surface regions, the metallic constituent in said layer being selected from the group consisting of titanium, tantalum, molybdenum, tungsten, nickel and cobalt, which metal-containing layer is of the type that, upon sintering, will form a silicide, removing said masking pattern from said polysilicon layer thereby lifting off those portions of said metal-containing layer deposited on top of said masking pattern and leaving in place on said selected surface regions those portions of said metal-containing layer deposited on said regions, sintering the remaining portions of said metal-containing layer to form composite silicide-on-polysilicon structures in said selected regions, and, utilizing said remaining sintered portions as a mask, anisotropically etching said polysilicon layer to define a high-conductivity silicide-on-polysilicon gate structure in said device.
Claim 7
Independent Claim
227 words
A method of fabricating a high-conductivity gate structure in an MOS device that comprises a silicon substrate having a gate oxide layer formed on said substrate, a doped polysilicon layer overlying said gate oxide layer and an intermediate layer overlying said polysilicon layer, said method comprising the steps of forming a high-resolution masking pattern with substantially vertical sidewalls on said intermediate layer to cover all but selected surface regions of said intermediate layer, isotropically etching said intermediate layer to expose surface regions of said polysilicon layer, said masking pattern and on said surface regions of said polysilicon layer, the metallic constituent in said layer being selected from the group consisting of titanium, tantalum, molybdenum, tungsten, nickel and cobalt, which metal-containing layer is of the type that, upon sintering, will form a silicide, removing said masking pattern from said intermediate layer thereby lifting off those portions of said metal-containing layer deposited on top of said masking pattern and leaving in place on said surface regions of said polysilicon layer those portions of said metal-containing layer deposited on said regions, removing the remaining portions of said intermediate layer, sintering the remaining portions of said metal-containing layer to form composite silicide-on-polysilicon structures in said selected regions, and, utilizing said remaining sintered portions as a mask, anisotropically etching said polysilicon layer to define a high-conductivity silicide-on-polysilicon gate structure in said device.
Claim 8
Independent Claim
227 words
A method of fabricating a high-conductivity gate structure in an MOS device that comprises a silicon substrate having a gate oxide layer formed on said substrate, a doped polysilicon layer overlying said gate oxide layer and an intermediate layer overlying said polysilicon layer, said method comprising the steps of forming a high-resolution masking pattern with substantially vertical sidewalls on said intermediate layer to cover all but selected surface regions of said intermediate layer, isotropically etching said intermediate layer to expose surface regions of said polysilicon layer, said masking pattern and on said surface regions of said polysilicon layer, the metallic constituent in said layer being selected from the group consisting of titanium, tantalum, molybdenum, tungsten, nickel and cobalt, which metal-containing layer is of the type that, upon sintering, will form a silicide, removing said masking pattern from said intermediate layer thereby lifting off those portions of said metal-containing layer deposited on top of said masking pattern and leaving in place on said surface regions of said polysilicon layer those portions of said metal-containing layer deposited on said regions, removing the remaining portions of said intermediate layer, sintering the remaining portions of said metal-containing layer to form composite silicide-on-polysilicon structures in said selected regions, and, utilizing said remaining sintered portions as a mask, anisotropically etching said polysilicon layer to define a high-conductivity silicide-on-polysilicon gate structure in said device.
Claim 9
Independent Claim
40 words
A method of patterning a doped polysilicon layer, comprising the steps of forming on the surface of said polysilicon layer a pattern made of a silicide, and, utilizing said silicide pattern as an etch-resistant mask, anisotropically etching said polysilicon layer.
Claim 10
Independent Claim
40 words
A method of patterning a doped polysilicon layer, comprising the steps of forming on the surface of said polysilicon layer a pattern made of a silicide, and, utilizing said silicide pattern as an etch-resistant mask, anisotropically etching said polysilicon layer.
Claim 11
Dependent Claim
31 words
A method as in claim 6 wherein said silicide comprises, TaSi 2 , and wherein said etching step constitutes a reactive ion etching step utilizing chlorine as the active reactant species.
References Cited (Backward Citations)
US4004044A
Cited
US4244799A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-06 | 1986-06-07 | 1986-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-06 | 1990-06-07 | 1990-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-06 | 1994-06-07 | 1994-12-07 | $7700.00 | Window Closed / Lapsed |