Process for forming multi-level coplanar conductor/insulator films employing photosensitive polymide polymer compositions
Assignee: International Business Machines Corp
•
Filing: 1990-04-30
•
Granted: 1993-07-20
•
Expires: 2010-04-30
Abstract
Abstract Disclosed is a process for producing multi-level conductor/insulator films on a processed semiconductor substrate having a conductor pattern. The insulator layers, each comprise a photosensitive polyimide polymer composition, and this allows the desired wiring channels and stud vias to be formed directly in the insulator layers, without the use of separate masking layers and resulting image transfer steps, thus providing a less cumbersome and costly process.
Inventors
- 👤 John E. Cronin
- 👤 Carter W. Kaanta
- 👤 Pei-Ing P. Lee
- 👤 Rosemary A. Previti-Kelly
- 👤 James G. Ryan
- 👤 Jung H. Yoon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 09:05
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/093; H10W20/097; H05; H05K; H05K3/00; H05K3/0011; H05K3/0017; H05K3/0023; H05K3/46; H05K3/4644; H05K3/467; H10W20/081; H10W20/084; H10W20/095; H10W20/40; H10W20/41; H10W20/42; H05K2201/00; H05K2201/01; H05K2201/0137; H05K2201/0154; H05K3/02; H05K3/04; H05K3/045; H05K3/10; H05K3/107; H05K3/465
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
143 words
A process for forming multi-level coplanar conductor/insulator films on a substrate having a conductor pattern, comprising the steps of: applying a first layer comprising a photosensitive polyimide polymer composition to said substrate; exposing said first layer to a pattern of ultraviolet radiation; applying a second layer comprising a photosensitive polyimide polymer composition to said first layer; exposing said second layer to a pattern of ultraviolet radiation; simultaneously developing said first and second layers so as to selectively expose regions of said substrate, the openings in said first layer being in alignment with at least a portion of the openings formed in said second layer; depositing a conductor material on said second layer and in said openings in said first and second layers; and removing said conductor material which overlies said second layer to coplanarize the surfaces of conductor material and said second layer.
Claim 2
Dependent Claim
143 words
A process for forming multi-level coplanar conductor/insulator films on a substrate having a conductor pattern, comprising the steps of: applying a first layer comprising a photosensitive polyimide polymer composition to said substrate; exposing said first layer to a pattern of ultraviolet radiation; applying a second layer comprising a photosensitive polyimide polymer composition to said first layer; exposing said second layer to a pattern of ultraviolet radiation; simultaneously developing said first and second layers so as to selectively expose regions of said substrate, the openings in said first layer being in alignment with at least a portion of the openings formed in said second layer; depositing a conductor material on said second layer and in said openings in said first and second layers; and removing said conductor material which overlies said second layer to coplanarize the surfaces of conductor material and said second layer.
Claim 3
Dependent Claim
53 words
The process of claim 1, wherein said photosensitive polyimide polymer composition comprises a fully imidized solvent soluble polyimide with a structural unit having the general formula ##STR2## where R represents an aliphatic group, and R' represents an optional aliphatic substituent which may be the same as or different from R, and a solvent.
Claim 4
Dependent Claim
19 words
The process of claim 1, wherein said conductor is a metal selected from aluminum, copper, Al-Cu, Al-Si and tungsten.
Claim 5
Dependent Claim
35 words
The process of claim 1, wherein said first layer has a thickness ranging from about 0.2 to about 1 microns; and said second layer has a thickness ranging from about 0.5 to about 1.2 microns.
Claim 6
Dependent Claim
20 words
The process of claim 1, wherein said conductor material which overlies said second layer is removed by using chemical-mechanical polishing.
Claim 7
Dependent Claim
16 words
The process of claim 1, wherein said steps are repeated to form additional coplanar conductor/insulator films.
Claim 8
Dependent Claim
154 words
A process for forming multi-level coplanar metal/insulator films on a substrate having a conductor pattern, comprising the steps of; depositing a first layer comprising a photosensitive polyimide polymer composition over said substrate; exposing said layer to a pattern of ultraviolet radiation; depositing a second layer comprising a photosensitive polyimide polymer composition over said first layer; exposing said second layer to a pattern of ultraviolet radiation; spraying said substrate with a developer so as to simultaneously remove portions of said first and second layers and to selectively expose regions of said substrate, the openings formed in said first layer being in alignment with at least a portion of the openings formed in said second layer; depositing a metal over said second layer and in said openings in said first and second layers; and removing said metal which overlies said second layer by using chemical-mechanical polishing to coplanarize the surfaces of metal and said second layer.
Claim 9
Dependent Claim
154 words
A process for forming multi-level coplanar metal/insulator films on a substrate having a conductor pattern, comprising the steps of; depositing a first layer comprising a photosensitive polyimide polymer composition over said substrate; exposing said layer to a pattern of ultraviolet radiation; depositing a second layer comprising a photosensitive polyimide polymer composition over said first layer; exposing said second layer to a pattern of ultraviolet radiation; spraying said substrate with a developer so as to simultaneously remove portions of said first and second layers and to selectively expose regions of said substrate, the openings formed in said first layer being in alignment with at least a portion of the openings formed in said second layer; depositing a metal over said second layer and in said openings in said first and second layers; and removing said metal which overlies said second layer by using chemical-mechanical polishing to coplanarize the surfaces of metal and said second layer.
Claim 10
Dependent Claim
53 words
The process of claim 7, wherein said photosensitive polyimide polymer composition comprises a fully imidized solvent soluble polyimide with a structural unit having the general formula ##STR3## where R represents an aliphatic group, and R' represents an optional aliphatic substituent which may be the same as or different from R, and a solvent.
Claim 11
Dependent Claim
19 words
The process of claim 8, wherein said conductor is a metal selected from aluminum, copper, Al-Cu, Al-Si and tungsten.
Claim 12
Dependent Claim
35 words
The process of claim 9, wherein said first layer has a thickness ranging from about 0.6 to about 0.7 microns; and said second layer has a thickness ranging from about 0.2 to about 0.5 microns.
Claim 13
Dependent Claim
16 words
The process of claim 10, wherein said steps are repeated to form additional coplanar metal/insulator films.
References Cited (Backward Citations)
US4347306A
Cited
US4328262A
Cited
US4657832A
Cited
US4629777A
Cited
US4656116A
Cited
US4735891A
Cited
US4698295A
Cited
US4621045A
Cited
US4665007A
Cited
US4786569A
Cited
EP0223920A2
Cited
US4789648A
Cited
US4842991A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-07-19 | 1997-01-18 | 1997-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-07-19 | 2001-01-18 | 2001-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-07-19 | 2005-01-18 | 2005-07-20 | $7700.00 | Window Closed / Lapsed |