Pillar via process
Assignee: NXP USA Inc
•
Filing: 1985-06-03
•
Granted: 1986-11-04
•
Expires: 2005-06-03
Abstract
Abstract A method is described for providing a conductive pillar in a via between multiple layers of conductors on planar electronic structures such as integrated circuits while at the same time exposing other large area contact regions such as a bonding pad. A first conductor layer is formed on the device substrate, etched to delineate the bonding pad and the first level interconnects, and covered with a differentially etchable intermediate conductive material which is delineated to form the conductive pillar. A dielectric planarizing layer is applied so as to have a smooth surface contour and a lower thickness above the conductive pillar than over the first level interconnects or the bonding pad. The planarizing dielectric is desirably a negative acting radiation sensitive material such as a polyimide. A mask is used to render the portions of this dielectric planarizing layer above the bonding pad soluble so that it may be dissolved away while leaving the remainder undisturbed. The resulting structure is then blanket etched to remove the smaller thickness of dielectric layer above the top of the pillar. The dielectric surface and pillar surface smoothly join. Another conductive layer is then applied over the surface of the dielectric planarizing layer and in contact with the top of the pillar and patterned in the conventional manner to form the second level interconnects. The resulting structure has a relatively smooth surface topology and little or no step at the pillars.
Inventors
- 👤 Willis R. Goodner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:49
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/063; H10W20/0633; H10W20/071; H10W20/092
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
150 words
A process for forming multi-layer conductors connected by conductive pillars, comprising: providing a substrate; applying a first conductor layer on said substrate, wherein said first conductor layer includes a first interconnect region and a bonding region; forming a conductive pillar on said first interconnect region; coating said substrate, bonding region, and pillar with a dielectric planarizing layer having a first thickness over said substrate, a second thickness over said bonding region, and a third thickness over said pillar, wherein said third thickness is less than said first and second thicknesses; removing a portion of said planarizing layer to expose a central part of said bonding region while leaving said first interconnect region and said pillar covered; uniformly etching said planarizing layer to expose an upper surface of said pillar; and applying a second conductive layer over said remaining planarizing layer and in contact with said upper surface of said pillar.
Claim 2
Dependent Claim
150 words
A process for forming multi-layer conductors connected by conductive pillars, comprising: providing a substrate; applying a first conductor layer on said substrate, wherein said first conductor layer includes a first interconnect region and a bonding region; forming a conductive pillar on said first interconnect region; coating said substrate, bonding region, and pillar with a dielectric planarizing layer having a first thickness over said substrate, a second thickness over said bonding region, and a third thickness over said pillar, wherein said third thickness is less than said first and second thicknesses; removing a portion of said planarizing layer to expose a central part of said bonding region while leaving said first interconnect region and said pillar covered; uniformly etching said planarizing layer to expose an upper surface of said pillar; and applying a second conductive layer over said remaining planarizing layer and in contact with said upper surface of said pillar.
Claim 3
Dependent Claim
71 words
The process of claim 1 wherein said planarizing layer is a radiation sensitive dielectric material and wherein said removing step comprises exposing said radiation sensitive planarizing dielectric layer through a mask which is adapted to render the portion of said radiation sensitive dielectric material layer above said central part of said bonding region soluble in a developer, and then developing said radiation sensitive dielectric material to remove the said soluble portion.
Claim 4
Dependent Claim
37 words
The process of claim 2 wherein said radiation sensitive material comprises a polyimide containing material and wherein said removing step further comprises, after said developing step, heating said radiation sensitive polyimide containing material to cure said material.
Claim 5
Dependent Claim
46 words
The process of claim 1 wherein said first forming step comprises applying an intermediate conductor layer on said first conductor layer, removing a first portion of said intermediate layer to leave a second portion of said intermediate layer on said interconnect region to form said pillar.
Claim 6
Dependent Claim
39 words
The process of claim 4 wherein said step of removing a first portion of said intermediate layer to leave a second portion on said interconnect region comprises leaving a third portion of said intermediate layer on said bonding region.
Claim 7
Dependent Claim
24 words
The process of claim 4 wherein said intermediate conductor layer comprises a material which is differentially etchable with respect to said first conductor layer.
Claim 8
Dependent Claim
211 words
A process for forming multi-layer interconnects for electronic devices having bonding pads, comprising: providing a substrate containing electronic devices; applying and patterning a first interconnect layer for interconnecting some of said devices and forming at least one bonding pad for an external connection; providing an intermediate conductor layer above said first interconnect layer; removing a first portion of said intermediate conductor layer to leave a pillar above a first portion of said first interconnect layer; covering portions of said substrate, said pillar, and portions of said first interconnect layer including said bonding pad with a dielectric planarizing layer having a first thickness above said pillar which is less than second and third thicknesses above, respectively, said substrate and said bonding pad; removing a portion of said dielectric planarizing layer above said bonding pad, while leaving said first thickness substantially undisturbed; then, without masking, etching said dielectric planarizing layer to expose the upper surface of said pillar while leaving portions of said first interconnect layer not under said bonding pad and said pillar still covered by remaining portions of said dielectric planarizing layer; and thereafter applying and patterning a second interconnect layer in contact with said upper surface of said pillar and lying on said remaining portions of said dielectric planarizing layer.
Claim 9
Dependent Claim
211 words
A process for forming multi-layer interconnects for electronic devices having bonding pads, comprising: providing a substrate containing electronic devices; applying and patterning a first interconnect layer for interconnecting some of said devices and forming at least one bonding pad for an external connection; providing an intermediate conductor layer above said first interconnect layer; removing a first portion of said intermediate conductor layer to leave a pillar above a first portion of said first interconnect layer; covering portions of said substrate, said pillar, and portions of said first interconnect layer including said bonding pad with a dielectric planarizing layer having a first thickness above said pillar which is less than second and third thicknesses above, respectively, said substrate and said bonding pad; removing a portion of said dielectric planarizing layer above said bonding pad, while leaving said first thickness substantially undisturbed; then, without masking, etching said dielectric planarizing layer to expose the upper surface of said pillar while leaving portions of said first interconnect layer not under said bonding pad and said pillar still covered by remaining portions of said dielectric planarizing layer; and thereafter applying and patterning a second interconnect layer in contact with said upper surface of said pillar and lying on said remaining portions of said dielectric planarizing layer.
Claim 10
Dependent Claim
24 words
The process of claim 8 wherein said intermediate layer is of a material which is differentially etchable with respect to said first interconnect layer.
Claim 11
Dependent Claim
30 words
The process of claim 8 wherein said step of removing a first portion of said intermediate layer comprises leaving a second portion of said intermediate layer on said bonding pad.
Claim 12
Dependent Claim
17 words
The process of claim 8 wherein said dielectric planarizing layer is a negative active radiation polymerizable layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-03 | 1990-05-05 | 1990-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-03 | 1994-05-05 | 1994-11-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-03 | 1998-05-05 | 1998-11-04 | $7700.00 | Window Closed / Lapsed |