Waterbased acrylic silane and polyurethane containing coating composition
Assignee: EIDP Inc
•
Filing: 1990-08-16
•
Granted: 1993-04-20
•
Expires: 2010-08-16
Abstract
Abstract A waterbased coating composition containing about 10-30% by weight of film forming binder dispersed in an aqueous carrier; wherein the binder contains a. an acrylic silane polymer of polymerized monomers of alkyl methacrylate, alkyl acrylate or mixtures thereof, a silane containing alkyl acrylate or methacrylate and the polymer has an acid no. of 2-100 and a hydroxyl no. of up to 100, a glass transition temperature of -40° to 25° C. and a weight average molecular weight of 500,000 to 3,000,000; and b. a polyurethane selected from the following group: polyester urethane, polyether urethane or polyacrylourethane; the composition is useful for painting and refinishing the exterior of automobiles and trucks.
Inventors
- 👤 Ervin R. Werner, Jr.
- 👤 Eileen E. Konsza
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:46
CPC Classifications
C; C09; C09D; C09D143/00; C09D143/04; C08; C08L; C08L75/00; C08L75/04
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
174 words
A waterbased coating composition comprising about 10-30% by weight of film forming binder dispersed in an aqueous carrier and has a pH of about 7-10; wherein the binder consist essentially of about a. 60-90% by weight, based on the weight of the binder, of an acrylic silane polymer consisting essentially of polymerized monomers of alkyl methacrylate, alkyl acrylate or mixtures thereof, 1-10% by weight based on the weight of the acrylic silane polymer, of silane containing alkyl acrylate or methacrylate, sufficient monoethylenically unsaturated acid to provide the polymer with an acid number of 2-100 and sufficient hydroxy alkyl acrylate or hydroxy alkyl methacrylate to provide the polymer with a hydroxyl number of about 5-100, a glass transition temperature of -40° to +25° C. and a weight average molecular weight of 500,000 to 3,000,000 and the acid groups of the polymer are reacted with ammonia or an amine; b. 10-40% by weight, based on the weight of the binder, of the dispersed polyurethane selected from the group consisting of polyester urethane, polyether urethane or polyacrylourethane.
Claim 2
Dependent Claim
174 words
A waterbased coating composition comprising about 10-30% by weight of film forming binder dispersed in an aqueous carrier and has a pH of about 7-10; wherein the binder consist essentially of about a. 60-90% by weight, based on the weight of the binder, of an acrylic silane polymer consisting essentially of polymerized monomers of alkyl methacrylate, alkyl acrylate or mixtures thereof, 1-10% by weight based on the weight of the acrylic silane polymer, of silane containing alkyl acrylate or methacrylate, sufficient monoethylenically unsaturated acid to provide the polymer with an acid number of 2-100 and sufficient hydroxy alkyl acrylate or hydroxy alkyl methacrylate to provide the polymer with a hydroxyl number of about 5-100, a glass transition temperature of -40° to +25° C. and a weight average molecular weight of 500,000 to 3,000,000 and the acid groups of the polymer are reacted with ammonia or an amine; b. 10-40% by weight, based on the weight of the binder, of the dispersed polyurethane selected from the group consisting of polyester urethane, polyether urethane or polyacrylourethane.
Claim 3
Dependent Claim
18 words
The coating composition of claim 1 containing pigment in a pigment to binder weight ratio of about 1:100-200:100.
Claim 4
Dependent Claim
74 words
The coating composition of claim 1 in which the acrylic silane polymer consists essentially of polymerized monomers of an alkyl methacrylate, an alkyl acrylate or mixtures thereof each having 1-12 carbon atoms in the alkyl group, 2-10% by weight of a hydroxy alkyl methacrylate or acrylate having 2-4 carbon atoms in the alkyl group, 0.1-10% by weight of a monoethylenically unsaturated carboxylic acid and 1-10% by weight of an silane containing acrylate or methacrylate.
Claim 5
Dependent Claim
99 words
The coating composition of claim 3 in which the silane containing acrylate or methacrylate has the following structural formula: ##STR3## wherein: R is selected from the group consisting of CH 3 , CH 3 CH 2 , CH 3 O, or CH 3 CH 2 O; R 1 and R 2 are individually selected from the group consisting of CH 3 or CH 3 CH 2 ; and R 3 is selected from the group consisting of H, CH 3 , or CH 3 CH 2 and n is 0 or a positive integer of not greater than 8.
Claim 6
Dependent Claim
23 words
The coating composition of claim 4 in which the silane is selected from the group consisting of gamma trimethoxysilylpropyl methacrylate and gamma trimethoxysilylpropylacrylate.
Claim 7
Dependent Claim
21 words
The coating composition of claim 1 in which the acrylic silane polymer contains up to 20% by weight of polymerized styrene.
Claim 8
Dependent Claim
23 words
The coating composition of claim 1 which the acrylic silane polymer contains up to 10% by weight of polymerized methacrylamide or allyl methacrylate.
Claim 9
Dependent Claim
46 words
The coating composition of claim 1 in which the acrylic silane polymer consists essentially of about 40-50% by weight methyl methacrylate, 40-50% by weight of 2-ethylhexyl acrylate, 2-6% by weight gamma trimethoxysilyl propyl methacrylate, 2-5% by weight of hydroxyethyl acrylate and 1-3% by weight methacrylic acid.
Claim 10
Dependent Claim
47 words
The coating composition of claim 1 in which the acrylic silane polymer consists essentially of about 25-35% by weight methyl methacrylate, 10-20% by weight styrene, 40-50% by weight 2-ethylhexyl acrylate, 2-6% by weight gamma trimethoxysilylpropyl methacrylate 2-5% by weight hydroxyethyl acrylate and 1-3% by weight methacrylic acid.
Claim 11
Dependent Claim
94 words
The coating composition of claim 1 in which the acrylic silane is a graft copolymer formed by a two stage polymerization in which stage I monomers are polymerized and stage II monomers are added and polymerized and grafted to polymerized stage I monomers wherein stage I monomers consist essentially of about 10-30% by weight of methyl methacrylate and 70-90% by weight butyl acrylate and stage II monomers consist essentially of about 70-80% by weight of butyl acrylate, 6-10% by weight gamma trimethoxysilylpropyl methacrylate, 8-12% by weight hydroxyethyl acrylate and 5-9% by weight methacrylic acid.
Claim 12
Dependent Claim
113 words
The coating composition of claim 1 in which the acrylic silane is a graft copolymer formed by a two stage polymerization in which stage I monomers are polymerized and stage II monomers are added and polymerized and grafted to polymerized stage I monomers wherein stage I monomers consist essentially of about 30-40% by weight of methyl methacrylate, 10-20% by weight styrene, 40-50% by weight butyl acrylate and 1-5% by weight gamma trimethoxysilylpropyl methacrylate and stage II monomers consist essentially of about 25-30% by weight of methyl methacrylate, 10-15% by weight styrene, 30-40% by weight butyl acrylate, 6-10% by weight gamma trimethoxysilylpropyl methacrylate, 8-12% by weight hydroxyethyl acrylate and 5-9% by weight methacrylic acid.
Claim 13
Dependent Claim
84 words
The coating composition of claim 1 in which the acrylic silane is a graft copolymer formed by a three stage polymerization in which stage I monomers are polymerized, stage II monomers are added and polymerized and grafted to polymerized stage I monomers and stage III monomers are added and grafted onto polymerized stage I and stage II monomers wherein stages I and II monomers comprise methyl methacrylate, allyl methacrylate, butyl acrylate, and stage III monomers comprise methyl methacrylate, butyl acrylate and gamma trimethoxysilyl-propyl methacrylate.
Claim 14
Dependent Claim
14 words
The coating composition of claim 1 in which the polyurethane is a polyester urethane.
Claim 15
Dependent Claim
64 words
The coating composition of claim 13 in which the polyester urethane consists essentially of polyester polyol of a polyol and a dicarboxylic acid or an anhydride thereof, said polyester polyol is reacted with an organic diisocyanate which in turn is reacted with a hydroxy containing carboxylic acid, said acid being neutralized with a tertiary amine and the resulting product chain extended with a diamine.
Claim 16
Dependent Claim
61 words
The coating composition of claim 13 in which the polyester urethane consists essentially of a polyester polyol of a lactone reacted with a polyol, said polyester polyol is reacted with an organic diisocyanate which in turn is reacted with a hydroxy containing carboxylic acid, said acid being neutralized with a tertiary amine and the resulting product chain extended with a diamine.
Claim 17
Dependent Claim
14 words
The coating composition of claim 1 in which the polyurethane is a polyether urethane.
Claim 18
Dependent Claim
62 words
The coating composition of claim 16 in which the polyether urethane consists of a polyalkylene glycol having a weight average molecular weight of about 400-4500, said polyalkylene glycol is reacted with an organic diisocyanate which in turn is reacted with a hydroxy containing carboxylic acid, said acid being neutralized with a tertiary amine and the resulting product chain extended with a diamine.
Claim 19
Dependent Claim
16 words
The coating composition of claim 17 in which the polyalkylene glycol consists essentially of polypropylene glycol.
Claim 20
Dependent Claim
13 words
The coating composition of claim 1 in which the polyurethane is a polyacrylourethane.
Claim 21
Dependent Claim
78 words
The coating composition of claim 19 in which the polyacrylourethane consists essentially of a functional acrylic polymer of polymerized ethylenically unsaturated acrylic esters and ethylenically unsaturated monomers containing functional groups selected from the group consisting of carboxyl, hydroxyl, cyano, or glycidyl groups, said functional acrylic polymer is reacted with diisocyanate which in turn is reacted with a hydroxy containing carboxylic acid, said acid being neutralized with a tertiary amine and the resulting product chain extended with a diamine.
Claim 22
Dependent Claim
191 words
The coating composition of claim 1 in which the acrylic silane polymer consisting essentially of polymerized monomers of alkyl methacrylate, alkyl acrylate or mixtures thereof, 1-10% by weight, based on the weight of the acrylic silane polymer, of silane containing alkyl acrylate having the following structural formula ##STR4## wherein: R is selected from the group consisting of CH 3 , CH 3 CH 2 , CH 3 O, or CH 3 CH 2 ; and R 1 and R 2 are individually selected from the group consisting of CH 3 or CH 3 CH 2 ; and R 3 is selected from the group consisting of H, CH 3 , or CH 3 CH 2 and n is 0 or a positive integer of not greater than 8, and in which the polyurethane is a polyester urethane consisting essentially of a polyester polyol of a polyol and a dicarboxylic acid or an anhydride thereof said polyester polyol is reacted with an organic diisocyanate which in turn is reacted with a hydroxy containing carboxylic acid said acid being neutralized with a tertiary amine and the resulting product chain extended with a diamine.
References Cited (Backward Citations)
US3561996A
Cited
US3551391A
Cited
US3729438A
Cited
US3814716A
Cited
US3951893A
Cited
US3935155A
Cited
US4062451A
Cited
US4035540A
Cited
US4093673A
Cited
US3997485A
Cited
US4147688A
Cited
US4043953A
Cited
US4045602A
Cited
US4133938A
Cited
US4147685A
Cited
US4191713A
Cited
US4291136A
Cited
US4181687A
Cited
US4310640A
Cited
US4384013A
Cited
US4395463A
Cited
JPS5712058A
Cited
US4368297A
Cited
US4371664A
Cited
US4399261A
Cited
US4435536A
Cited
US4518726A
Cited
JPS57179261A
Cited
US4356233A
Cited
US4491508A
Cited
US4451602A
Cited
US4575535A
Cited
JPS5838766A
Cited
US4489135A
Cited
US4491650A
Cited
US4567107A
Cited
US4587290A
Cited
US4543403A
Cited
US4499150A
Cited
US4499151A
Cited
US4578417A
Cited
JPS60168769A
Cited
JPS60221450A
Cited
EP0173278A2
Cited
US4689369A
Cited
US4684697A
Cited
US4611040A
Cited
US4603064A
Cited
US4614777A
Cited
US4652610A
Cited
JPS62292820A
Cited
JPS62295969A
Cited
DE3630793A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-04-19 | 1996-10-19 | 1997-04-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-04-19 | 2000-10-19 | 2001-04-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-04-19 | 2004-10-19 | 2005-04-20 | $7700.00 | Window Closed / Lapsed |