US3951893A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Film-forming silane crosslinked acrylate interpolymers having water-barrier properties
Assignee: Johnson and Johnson
•
Filing: 1974-09-12
•
Granted: 1976-04-20
•
Expires: 1994-09-12
Abstract
Abstract Polymeric compositions having desirable film-forming characteristics and water-barrier properties at substantially neutral pH's and yet solubilizable and thus disposable at substantially non-neutral pH's comprise a silane crosslinked interpolymer of an alkyl acrylate and a monomer interpolymerizable therewith such as, in the preferred alkaline labile embodiment, acrylic acid. The silane crosslinking monomer is preferably 3-(trimethoxysilyl)-propyl methacrylate or 3-(trimethoxysilyl)-propyl acrylate. The resultant pH-sensitive polymeric composition may be used, for example, as a binder for other materials, such as webs of non-woven water-dispersible fibers, or may be used in film form either by itself or preferably laminated to other dispersible materials to produce a variety of products which are completely disposable at selected non-neutral pH's.
Inventors
- 👤 Robert J. Gander
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:40
CPC Classifications
C; C08; C08F; C08F220/00; C08F220/02; C08F220/10; C08F220/12; C08F220/16; C08F220/18; C08F220/1802; C08F220/34; C08F220/52; C08F220/54; C08F230/00; C08F230/04; C08F230/08; C08F230/085; A; A61; A61F; A61F13/00; A61F13/15; A61F13/53; A61F13/534; A61F13/539; A61F2013/15008; A61F2013/15048; A61F13/15203; A61F13/15211; A61F2013/15227; A61F2013/530131; A61F2013/53445; A61F2013/5395; A61G; A61G9/00; A61G9/003
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
224 words
A film-forming polymeric composition having water-barrier properties at neutral pH's in the range of between about 4.5 and about 8.5 and solubilizable at a pH substantially outside said neutral pH range, said composition comprising a silane-crosslinked interpolymer of about 0.5 to 5 parts by weight of a first monomer selected from the group consisting of the alkyl acrylates wherein the alkyl group has from one to eight carbon atoms, and about 1 part by weight of a second monomer selected from the group consisting of acrylic acid, methacrylic acid, fumaric acid, maleic acid, maleic anhydride, itaconic acid, dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, tert.-butylaminoethyl acrylate and tert.-butylaminoethyl methacrylate, and about 0.9 to 1.5% by weight, based on the combined weight of said first and second monomers, of a crosslinking monomer selected from the group consisting of the silane monomers having the structural formula: ##EQU2## wherein: R is selected from the group consisting of CH 3 --, CH 3 CH 2 --, CH 3 O-- and CH 3 CH 2 O--; R 1 and R 2 are each selected from the group consisting of CH 3 --and CH 3 CH 2 --; R 3 is selected from the group consisting of H, CH 3 -- and CH 3 CH 2 --; and n is 0 or a positive integer not greater than 8.
Claim 2
Dependent Claim
224 words
A film-forming polymeric composition having water-barrier properties at neutral pH's in the range of between about 4.5 and about 8.5 and solubilizable at a pH substantially outside said neutral pH range, said composition comprising a silane-crosslinked interpolymer of about 0.5 to 5 parts by weight of a first monomer selected from the group consisting of the alkyl acrylates wherein the alkyl group has from one to eight carbon atoms, and about 1 part by weight of a second monomer selected from the group consisting of acrylic acid, methacrylic acid, fumaric acid, maleic acid, maleic anhydride, itaconic acid, dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, tert.-butylaminoethyl acrylate and tert.-butylaminoethyl methacrylate, and about 0.9 to 1.5% by weight, based on the combined weight of said first and second monomers, of a crosslinking monomer selected from the group consisting of the silane monomers having the structural formula: ##EQU2## wherein: R is selected from the group consisting of CH 3 --, CH 3 CH 2 --, CH 3 O-- and CH 3 CH 2 O--; R 1 and R 2 are each selected from the group consisting of CH 3 --and CH 3 CH 2 --; R 3 is selected from the group consisting of H, CH 3 -- and CH 3 CH 2 --; and n is 0 or a positive integer not greater than 8.
Claim 3
Dependent Claim
29 words
The polymeric composition of claim 1 wherein said first monomer is ethyl acrylate and said silane monomer is selected from the group consisting of 3-(trimethoxysilyl)-propyl methacrylate and 3-(trimethoxysilyl)-propyl acrylate.
Claim 4
Dependent Claim
32 words
The alkaline soluble polymeric composition of claim 2 wherein said second monomer is selected from the group consisting of acrylic acid, methacrylic acid, fumaric acid, maleic acid, maleic anhydride and itaconic acid.
Claim 5
Dependent Claim
32 words
The acid soluble polymeric composition of claim 2 wherein said second monomer is selected from the group consisting of dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, tert.-butylaminoethyl acrylate and tert.-butylaminoethyl methacrylate.
Claim 6
Dependent Claim
13 words
The polymeric composition of claim 3 wherein said second monomer is acrylic acid.
Claim 7
Dependent Claim
13 words
The polymeric composition of claim 4 wherein said second monomer is dimethylaminoethyl methacrylate.
Claim 8
Dependent Claim
14 words
The polymeric composition of claim 6 which further comprises a tack-diminishing quantity of N-isopropylacrylamide.
Claim 9
Dependent Claim
26 words
The polymeric composition of claim 1 which further comprises about 1 to 20% by weight, based on the weight of said interpolymer, of a humectant-type plasticizer.
Claim 10
Dependent Claim
29 words
The polymeric composition of claim 8 wherein said humectant-type plasticizer is selected from the group consisting of glycerin, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol and tripropylene glycol.
Claim 11
Dependent Claim
28 words
The polymeric composition of claim 1 which further comprises about 1 to 20% by weight, based on the weight of said interpolymer, of a plasticizer having release-agent properties.
Claim 12
Dependent Claim
23 words
The polymeric composition of claim 10 wherein said plasticizer is selected from the group consisting of lauric acid, myristic acid and palmitic acid.
Claim 13
Dependent Claim
201 words
A film-forming polymeric composition having water-barrier properties at pH's below about 8.5 and solubilizable at pH's above about 9, said composition comprising a silane-crosslinked interpolymer of about 1.5 to 4 parts by weight of a first monomer selected from the group consisting of the alkyl acrylates wherein the alkyl group has from one to eight carbon atoms, and about 1 part by weight of a second monomer selected from the group consisting of acrylic acid, methacrylic acid, fumaric acid, maleic acid, maleic anhydride and itaconic acid, and about 0.9 to 1.5% by weight, based on the combined weight of said first and second monomers, of a crosslinking monomer selected from the group consisting of the silane monomers having this structural formula: ##EQU3## wherein: R is selected from the group consisting of CH 3 --, CH 3 CH 2 --, CH 3 O-- and CH 3 CH 2 O--; R 1 and R 2 are each selected from the group consisting of CH 3 -- and CH 3 CH 2 --; R 3 is selected from the group consisting of H--, CH 3 -- and CH 3 CH 2 --; and n is 0 or a positive integer not greater than 8.
Claim 14
Dependent Claim
201 words
A film-forming polymeric composition having water-barrier properties at pH's below about 8.5 and solubilizable at pH's above about 9, said composition comprising a silane-crosslinked interpolymer of about 1.5 to 4 parts by weight of a first monomer selected from the group consisting of the alkyl acrylates wherein the alkyl group has from one to eight carbon atoms, and about 1 part by weight of a second monomer selected from the group consisting of acrylic acid, methacrylic acid, fumaric acid, maleic acid, maleic anhydride and itaconic acid, and about 0.9 to 1.5% by weight, based on the combined weight of said first and second monomers, of a crosslinking monomer selected from the group consisting of the silane monomers having this structural formula: ##EQU3## wherein: R is selected from the group consisting of CH 3 --, CH 3 CH 2 --, CH 3 O-- and CH 3 CH 2 O--; R 1 and R 2 are each selected from the group consisting of CH 3 -- and CH 3 CH 2 --; R 3 is selected from the group consisting of H--, CH 3 -- and CH 3 CH 2 --; and n is 0 or a positive integer not greater than 8.
Claim 15
Dependent Claim
24 words
The polymeric composition of claim 1 in the form of a film having a thickness in the range of about 1 to 20 mils.
Claim 16
Independent Claim
251 words
A method of forming a polymeric composition having film-forming characteristics such that the resultant film has barrier properties at neutral pH's in the range of between about 4.5 and about 8.5 and yet is solubilizable at a pH substantially outside said neutral range, said method comprising the step of interpolymerizing at elevated temperatures about 0.5 to 5 parts by weight of a first monomer selected from the group consisting of alkyl acrylates wherein the alkyl group has from one to eight carbon atoms, and about 1 part by weight of a second monomer selected from the group consisting of acrylic acid, methacrylic acid, fumaric acid, maleic acid, maleic anhydride, itaconic acid, dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, tert.-butylaminoethyl acrylate and tert.-butylaminoethyl methacrylate, and about 0.9 to 1.5% by weight, based on the combined weight of said first and second monomers, of a cross-linking monomer selected from the group consisting of the silane monomers having the structural formula: ##EQU4## wherein: R is selected from the group consisting of CH 3 --, CH 3 CH 2 --, CH 3 O-- and CH 3 CH 2 O; R 1 and R 2 are each selected from the group consisting of CH 3 --, and CH 3 CH 2 --; R 3 is selected from the group consisting of --H, CH 3 --, and CH 3 CH 2 --; and n is 0 or a positive integer not greater than 8; in the presence of a catalytic amount of a polymerization catalyst therefor.
Claim 17
Independent Claim
251 words
A method of forming a polymeric composition having film-forming characteristics such that the resultant film has barrier properties at neutral pH's in the range of between about 4.5 and about 8.5 and yet is solubilizable at a pH substantially outside said neutral range, said method comprising the step of interpolymerizing at elevated temperatures about 0.5 to 5 parts by weight of a first monomer selected from the group consisting of alkyl acrylates wherein the alkyl group has from one to eight carbon atoms, and about 1 part by weight of a second monomer selected from the group consisting of acrylic acid, methacrylic acid, fumaric acid, maleic acid, maleic anhydride, itaconic acid, dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, tert.-butylaminoethyl acrylate and tert.-butylaminoethyl methacrylate, and about 0.9 to 1.5% by weight, based on the combined weight of said first and second monomers, of a cross-linking monomer selected from the group consisting of the silane monomers having the structural formula: ##EQU4## wherein: R is selected from the group consisting of CH 3 --, CH 3 CH 2 --, CH 3 O-- and CH 3 CH 2 O; R 1 and R 2 are each selected from the group consisting of CH 3 --, and CH 3 CH 2 --; R 3 is selected from the group consisting of --H, CH 3 --, and CH 3 CH 2 --; and n is 0 or a positive integer not greater than 8; in the presence of a catalytic amount of a polymerization catalyst therefor.
Claim 18
Dependent Claim
53 words
The method of claim 14 further comprising forming said film by diluting the polymerized reaction product to a solids contents of less than about 35% with a solvent for said polymerized product, casting the resulting diluted interpolymer reaction product in the form of a thin film, removing said solvent, and curing the film.
Claim 19
Dependent Claim
37 words
The method of claim 15 wherein said thin film is cast by coating the diluted interpolymer reaction product on a release surface, said method further comprising the step of separating the dried film from the release surface.
Claim 20
Dependent Claim
29 words
The method of claim 15 further comprising the step of adding a catalytic amount of a promoter of siloxane condensation reactions to said polymerized reaction product prior to casting.
Claim 21
Dependent Claim
11 words
The method of claim 14 wherein said polymerization catalyst is 2,2'-azobis-(2-methylpropionitrile).
Claim 22
Dependent Claim
12 words
The method of claim 17 wherein said promoter is dibutyl tin di-2-ethylhexoate.
Claim 23
Dependent Claim
34 words
The method of claim 15 further comprising the step of adding at least one of humectant-type plasticizer and a plasticizer having release-agent properties to the diluted polymerized product prior to casting said thin film.
Claim 24
Dependent Claim
20 words
The method of claim 20 wherein said humectant-type plasticizer is glycerin and said plasticizer having release-agent properties is lauric acid.
Claim 25
Dependent Claim
16 words
The method of claim 15 wherein the solvent used in diluting the polymerized product comprises isopropanol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-20 | 1979-10-20 | 1980-04-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-20 | 1983-10-20 | 1984-04-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-20 | 1987-10-20 | 1988-04-20 | $7700.00 | Window Closed / Lapsed |