Thin film magnetic recording disk and fabrication process
Assignee: HGST Netherlands BV
•
Filing: 1988-04-28
•
Granted: 1990-06-19
•
Expires: 2008-04-28
Abstract
Abstract A discrete track thin film metal alloy or metal oxide magnetic recording disk is fabricated by forming a thin film of magnetic material on a substrate, patterning the magnetic film with a chemically etchable support layer and a high resolution photoresist layer, removing portions of the magnetic film and refilling with nonmagnetic material to form concentric nonmagnetic guard bands, and then applying a top layer of additional nonmagnetic material as a passivating and protective disk overcoat after removal of the remaining support layer and photoresist. The exposed photoresist and portions of the chemically etchable support layer beneath the side walls of the patterned photoresist defining the edges of the magnetic tracks are removed in a photoresist developer which also creates undercuts in the support layer beneath the side walls. The undercuts prevent "fences" and provide smooth interfaces between the magnetic tracks and the nonmagnetic guard bands. In one embodiment of the disk, a continuous layer of nonmagnetic material serves as both the guard bands and the protective overcoat and has a height in the guard band regions greater than the height of the adjacent magnetic tracks so as to prevent damage to the magnetic tracks in the event the magnetic tracks are contacted by the slider which supports the read/write head.
Inventors
- 👤 Mohamad T. Krounbi
- 👤 Alvin M. Patlach
- 👤 Ian L. Sanders
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:07
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/74; G11B5/82; B; B82; B82Y; B82Y10/00; G11B5/743; G11B5/84; G11B5/855; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24521; Y10T428/24537; Y10T428/24545
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
221 words
A method of fabricating a discrete track metal alloy or metal oxide magnetic recording disk comprising the steps of: forming a continuous film of magnetic metal alloy or metal oxide on a disk substrate; forming a support layer of chemically etchable material on the magnetic film; forming a layer of photoresist on the support layer; exposing selected regions of the photoresist layer to radiation; developing the photoresist layer to define a predetermined pattern of unexposed photoresist over the magnetic film, said pattern including concentric rings having side walls oriented generally perpendicularly to the disk substrate; removing the support layer material from areas between the concentric rings of the unexposed photoresist and from beneath the side walls of the concentric rings of the unexposed photoresist; removing the metal alloy or metal oxide from the magnetic film in areas not patterned by the unexposed photoresist so as to leave magnetic metal alloy or metal oxide on the substrate, the remaining metal alloy or metal oxide defining a pattern of concentric tracks corresponding to the pattern of concentric rings of unexposed photoresist; refilling the voids created by the removal of the metal alloy or metal oxide with nonmagnetic material to a height at least as high as the height of the magnetic tracks; and removing the remaining photoresist and the remaining support layer material.
Claim 2
Independent Claim
221 words
A method of fabricating a discrete track metal alloy or metal oxide magnetic recording disk comprising the steps of: forming a continuous film of magnetic metal alloy or metal oxide on a disk substrate; forming a support layer of chemically etchable material on the magnetic film; forming a layer of photoresist on the support layer; exposing selected regions of the photoresist layer to radiation; developing the photoresist layer to define a predetermined pattern of unexposed photoresist over the magnetic film, said pattern including concentric rings having side walls oriented generally perpendicularly to the disk substrate; removing the support layer material from areas between the concentric rings of the unexposed photoresist and from beneath the side walls of the concentric rings of the unexposed photoresist; removing the metal alloy or metal oxide from the magnetic film in areas not patterned by the unexposed photoresist so as to leave magnetic metal alloy or metal oxide on the substrate, the remaining metal alloy or metal oxide defining a pattern of concentric tracks corresponding to the pattern of concentric rings of unexposed photoresist; refilling the voids created by the removal of the metal alloy or metal oxide with nonmagnetic material to a height at least as high as the height of the magnetic tracks; and removing the remaining photoresist and the remaining support layer material.
Claim 3
Dependent Claim
44 words
A method according to claim 1 wherein the steps of developing the photoresist layer and removing the support layer material consist of the single step of subjecting the photoresist layer and the support layer to a developer in which the support layer is soluble.
Claim 4
Dependent Claim
35 words
A method according to claim 1 further comprising the step of, after removing the remaining photoresist and remaining support layer material, forming a protective overcoat over the metal alloy or metal oxide and nonmagnetic material.
Claim 5
Dependent Claim
28 words
A method according to claim 3 wherein the step of forming the overcoat includes the step of depositing material identical to the nonmagnetic material refilled in the voids.
Claim 6
Dependent Claim
40 words
A method according to claim 1 wherein the refilling step includes the step of refilling to a height generally equal to the height of the metal alloy or metal oxide, whereby the surface of the completed disk is substantially planar.
Claim 7
Dependent Claim
30 words
A method according to claim 1 wherein the refilling step includes the step of refilling to a height slightly higher than the height of the metal alloy or metal oxide.
Claim 8
Dependent Claim
52 words
A method according to claim 1 wherein the step of removing the metal alloy or metal oxide includes the step of sputter etching the magnetic film, and wherein the step of refilling the voids includes the step of sputter depositing the nonmagnetic material immediately after the sputter etching step without breaking vacuum.
Claim 9
Dependent Claim
44 words
A method according to claim 1 wherein the step of exposing selected regions of the photoresist layer to radiation further comprises the steps of: providing a mask having a radiation-opaque pattern including concentric tracks; and directing radiation through the mask to expose the photoresist.
Claim 10
Dependent Claim
30 words
A method according to claim 1 wherein the step of exposing selected regions of the photoresist layer to radiation comprises the step of directly exposing said regions with an E-beam.
Claim 11
Dependent Claim
39 words
A method according to claim 1 wherein the step of forming a magnetic film on the substrate further comprises the steps of forming a nucleating film on the substrate and forming a magnetic film directly on the nucleating film.
Claim 12
Dependent Claim
115 words
A discrete track film metal alloy or metal oxide magnetic recording disk comprising: a disk substrate; a plurality of discrete concentric tracks of magnetic metal alloy or metal oxide formed on the substrate, the top surfaces of the discrete tracks being generally coplanar; and a layer of continuous nonmagnetic material formed over the top surfaces of the tracks and over the substrate between the tracks, said nonmagnetic material layer forming a plurality of concentric guard bands between the tracks and forming a protective overcoat, and the height of said layer in the regions between the tracks being at least as high as the height of said layer in the regions on top of the tracks.
Claim 13
Dependent Claim
115 words
A discrete track film metal alloy or metal oxide magnetic recording disk comprising: a disk substrate; a plurality of discrete concentric tracks of magnetic metal alloy or metal oxide formed on the substrate, the top surfaces of the discrete tracks being generally coplanar; and a layer of continuous nonmagnetic material formed over the top surfaces of the tracks and over the substrate between the tracks, said nonmagnetic material layer forming a plurality of concentric guard bands between the tracks and forming a protective overcoat, and the height of said layer in the regions between the tracks being at least as high as the height of said layer in the regions on top of the tracks.
Claim 14
Dependent Claim
42 words
The disk according to claim 11 further comprising a nonmagnetic metal or metal alloy nucleating film formed between the substrate and the tracks, and wherein the layer of nonmagnetic material is formed on the nucleating film in the regions between the tracks.
Claim 15
Dependent Claim
34 words
The disk according to claim 11 wherein the height of said layer in the regions between the tracks is greater than the height of said layer in the regions on top of the tracks.
Claim 16
Dependent Claim
117 words
A discrete track thin film metal alloy magnetic recording disk for use in a disk file of the type wherein an air-bearing slider supports the read/write head, the disk comprising: a disk substrate; a plurality of discrete concentric tracks of magnetic cobalt-based alloy sputter deposited over the substrate to form guard bands on the substrate in the area between the magnetic tracks, the top surfaces of the guard bands of nonmagnetic material being generally coplanar and higher than the top surfaces of the magnetic tracks; and a continuous overcoat layer of nonmagnetic material sputter deposited to a generally uniform thickness over the top surfaces of the guard bands and the magnetic tracks to form a protective overcoat.
Claim 17
Dependent Claim
117 words
A discrete track thin film metal alloy magnetic recording disk for use in a disk file of the type wherein an air-bearing slider supports the read/write head, the disk comprising: a disk substrate; a plurality of discrete concentric tracks of magnetic cobalt-based alloy sputter deposited over the substrate to form guard bands on the substrate in the area between the magnetic tracks, the top surfaces of the guard bands of nonmagnetic material being generally coplanar and higher than the top surfaces of the magnetic tracks; and a continuous overcoat layer of nonmagnetic material sputter deposited to a generally uniform thickness over the top surfaces of the guard bands and the magnetic tracks to form a protective overcoat.
Claim 18
Dependent Claim
18 words
The disk according to claim 14 wherein said nonmagnetic overcoat layer consists essentially of alumina or amorphous carbon.
Claim 19
Dependent Claim
18 words
The disk according to claim 14 wherein said nonmagnetic guard bands consist essentially of amorphous carbon or alumina.
Claim 20
Dependent Claim
71 words
The disk according to claim 14 wherein the disk substrate is formed of an aluminum alloy with a nickel-phosphorus surface film thereon, further comprising a film of chromium or chromium alloy formed on the nickel-phosphorus film between the nickel-phosphorus film and the sputter deposited magnetic tracks, and wherein the nonmagnetic guard band material is sputter deposited directly on the chromium or chromium alloy film in the area between the magnetic tracks.
Claim 21
Dependent Claim
21 words
The disk according to claim 14 wherein the nonmagnetic guard bands and the overcoat layer are made from the same material.
References Cited (Backward Citations)
US3655441A
Cited
US4057831A
Cited
US4109045A
Cited
GB1443248A
Cited
US4560641A
Cited
US4517616A
Cited
JPS58212624A
Cited
JPS59112434A
Cited
US4746580A
Cited
US4610911A
Cited
US4554217A
Cited
US4689260A
Cited
US4624740A
Cited
US4687541A
Cited
US4708766A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-06-18 | 1993-12-18 | 1994-06-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-06-18 | 1997-12-18 | 1998-06-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-06-18 | 2001-12-18 | 2002-06-19 | $7700.00 | Window Closed / Lapsed |