Molding of fiber reinforced plastic articles
Assignee: Wiggins Teape Group Ltd
•
Filing: 1989-03-16
•
Granted: 1989-11-21
•
Expires: 2009-03-16
Abstract
Abstract A shaped article of fiber reinforced material is made by forming a foamed aqueous dispersion having single discrete fibers, and unconsolidated particulate thermoplastic or thermosetting material, laying down and draining the dispersion to form a web, transferring the web to an oven and heating it to form a self-sustaining permeable sheet, transferring the sheet to a through-air heating oven, passing heated air through the sheet to cause substantially uniform and homogeneous heating of the thermoplastic component, transferring the heated sheet to a compression mold, and subjecting the sheet to compression molding to form a shaped fiber reinforced plastic article.
Inventors
- 👤 Bronislaw Radvan
- 👤 Anthony J. Willis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 07:11
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/10; B29C70/12; B29C35/00; B29C35/02; B29C35/04; B29C67/00; B29C67/20; B29C70/28; B29C70/40; B29C70/42; B29C70/46; B29C35/045; B29K; B29K2105/00; B29K2105/04; B29K2105/045; B29K2105/06; B29K2105/12; B29K2105/25; B29K2105/251; B29K2995/00; B29K2995/0037; B29K2995/0046; B29K2995/0065; B29K2995/0068
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
238 words
A process for making a shaped article of fiber reinforced synthetic plastics material comprising the steps of forming a foamed aqueous dispersion comprising from 20% to 60% by weight of single discrete fibers having a modulus of elasticity higher than 10,000 mega pascals, and between 7 and 50 millimeters long, and from 40% to 80% by weight of unconsolidated particulate plastics material selected from the group consisting of a thermoplastic material and a thermosetting material, the particulate plastics material having a particle size of less than about 1.5 millimeters; laying down and draining said dispersion on a foraminous support so as to form a web; transferring said web to a heating oven; heating said web first so as to remove residual moisture therefrom and then so as to bond the fibrous and plastics components together into a self-sustaining permeable sheet while substantially maintaining the particulate form of the plastics material; transferring said self-sustaining sheet to a through air heating oven; passing heated air through said sheet so as to cause substantially uniform and homogeneous heating of the components thereof to a temperature at which the viscosity of the thermoplastic constituting the particulate component is sufficiently low to permit the sheet to be molded into a shaped article; transferring said heated permeable sheet to a compression mold; and subjecting said sheet to a compression molding at a predetermined pressure so as to form a shaped fiber reinforced plastic article.
Claim 2
Dependent Claim
238 words
A process for making a shaped article of fiber reinforced synthetic plastics material comprising the steps of forming a foamed aqueous dispersion comprising from 20% to 60% by weight of single discrete fibers having a modulus of elasticity higher than 10,000 mega pascals, and between 7 and 50 millimeters long, and from 40% to 80% by weight of unconsolidated particulate plastics material selected from the group consisting of a thermoplastic material and a thermosetting material, the particulate plastics material having a particle size of less than about 1.5 millimeters; laying down and draining said dispersion on a foraminous support so as to form a web; transferring said web to a heating oven; heating said web first so as to remove residual moisture therefrom and then so as to bond the fibrous and plastics components together into a self-sustaining permeable sheet while substantially maintaining the particulate form of the plastics material; transferring said self-sustaining sheet to a through air heating oven; passing heated air through said sheet so as to cause substantially uniform and homogeneous heating of the components thereof to a temperature at which the viscosity of the thermoplastic constituting the particulate component is sufficiently low to permit the sheet to be molded into a shaped article; transferring said heated permeable sheet to a compression mold; and subjecting said sheet to a compression molding at a predetermined pressure so as to form a shaped fiber reinforced plastic article.
Claim 3
Dependent Claim
18 words
A process as claimed in claim 1 in which the heating oven is a through air heating oven.
Claim 4
Dependent Claim
22 words
A process as claimed in claim 1 in which the components are bonded together by surface fusion of the particulate plastics material.
Claim 5
Dependent Claim
23 words
A process as claimed in claim 1 in which the components are bonded together by a binder added during formation of the web.
Claim 6
Dependent Claim
26 words
A process as claimed in claim 4 in which the binder is selected from the group consisting of polyvinyl alcohol, polyvinyl acetate, carboxymethyl cellulose and starch.
Claim 7
Dependent Claim
22 words
A process as claimed in claim 1 in which the fibers are glass fibers having a diameter smaller than about 13 microns.
Claim 8
Dependent Claim
38 words
A process as claimed in claim 1 in which the plastics material is a thermoplastic material and is selected from the group consisting of polyethylene, polypropylene, polystyrene, acrylonitrylstyrene butadiene, polyethylene terephthalate, and polyvinyl chloride, both plasticized and unplasticized.
Claim 9
Dependent Claim
31 words
A process as claimed in claim 1 in which the degree of bonding is controlled to cohere the components while still retaining sufficient flexibility to permit the structure to be reeled.
Claim 10
Dependent Claim
23 words
A process as claimed in claim 1 in which the degree of bonding is controlled to produce a rigid but air permeable sheet.
Claim 11
Dependent Claim
22 words
A process as claimed in claim 1 in which the sheet is impregnated with a liquid thermosetting resin before or after molding.
Claim 12
Dependent Claim
36 words
A process as claimed in claim 10 in which the resins are selected from the groups consisting of phenol formaldehyde resin, urea and melamine formaldehyde resins, epoxy resins, unsaturated polyesters, polyurethanes and phenolic and polyester resins.
Claim 13
Dependent Claim
199 words
A process for making a shaped article of fiber reinforced synthetic plastics material comprising the steps of forming a foamed aqueous dispersion comprising from 20% to 60% by weight of single discrete fibers having a modulus of elasticity higher than 10,000 mega pascals, and between 7 and 50 millimeters long, and from 40% to 80% by weight of unconsolidated particulate plastics material selected from the group consisting of a thermoplastic material and a thermosetting material, the particulate plastics material having a particle size of less than about 1.5 millimeters; laying down and draining said dispersion on a foraminous support so as to form a web; transferring said web to a through air heating oven; passing heated air through said web, first so as to remove residual moisture and then so as to cause substantially uniform and homogeneous heating of the components thereof to a temperature at which the viscosity of the thermoplastic constituting the particulate component is sufficiently low to permit the web to be molded into a shaped article; transferring said heated web to a compression mold, and subjecting said web to compression molding at a predetermined pressure so as to form a shaped fiber reinforced plastic article.
Claim 14
Dependent Claim
199 words
A process for making a shaped article of fiber reinforced synthetic plastics material comprising the steps of forming a foamed aqueous dispersion comprising from 20% to 60% by weight of single discrete fibers having a modulus of elasticity higher than 10,000 mega pascals, and between 7 and 50 millimeters long, and from 40% to 80% by weight of unconsolidated particulate plastics material selected from the group consisting of a thermoplastic material and a thermosetting material, the particulate plastics material having a particle size of less than about 1.5 millimeters; laying down and draining said dispersion on a foraminous support so as to form a web; transferring said web to a through air heating oven; passing heated air through said web, first so as to remove residual moisture and then so as to cause substantially uniform and homogeneous heating of the components thereof to a temperature at which the viscosity of the thermoplastic constituting the particulate component is sufficiently low to permit the web to be molded into a shaped article; transferring said heated web to a compression mold, and subjecting said web to compression molding at a predetermined pressure so as to form a shaped fiber reinforced plastic article.
Claim 15
Dependent Claim
22 words
A process as claimed in claim 13 in which the fibers are glass fibers having a diameter smaller than about 13 microns.
Claim 16
Dependent Claim
38 words
A process as claimed in claim 13 in which the plastics material is a thermoplastic material and is selected from the group consisting of polyethylene, polypropylene, polystyrene, acrylonitrylstyrene butadiene, polyethylene terephthalate, and polyvinyl chloride, both plasticized and unplasticized.
Claim 17
Dependent Claim
22 words
A process as claimed in claim 13 in which the sheet is impregnated with a liquid thermosetting resin before or after molding.
Claim 18
Dependent Claim
36 words
A process as claimed in claim 1 in which the resins are selected from the groups consisting of phenol formaldehyde resin, urea and melamine formaldehyde resins, epoxy resins, unsaturated polyesters, polyurethanes and phenolic and polyester resins.
References Cited (Backward Citations)
DE24181C
Cited
US1875018A
Cited
US1901382A
Cited
GB448138A
Cited
US2653870A
Cited
US2715755A
Cited
FR1040359A
Cited
GB703023A
Cited
GB729381A
Cited
US2892107A
Cited
US2795524A
Cited
GB855132A
Cited
GB843154A
Cited
GB871117A
Cited
US3200181A
Cited
US3216841A
Cited
GB1058932A
Cited
US3428518A
Cited
US3489827A
Cited
GB1008833A
Cited
GB1113792A
Cited
US3396062A
Cited
CH462024A
Cited
GB1134785A
Cited
GB1110659A
Cited
GB1129757A
Cited
US3897533A
Cited
GB1198324A
Cited
US4153760A
Cited
US3975483A
Cited
FR1553537A
Cited
GB1204039A
Cited
US3452128A
Cited
FR1529133A
Cited
GB1230789A
Cited
GB1231937A
Cited
GB1305982A
Cited
GB1306145A
Cited
US3621092A
Cited
GB1263812A
Cited
GB1348896A
Cited
US3734985A
Cited
US3837986A
Cited
GB1330485A
Cited
US3856614A
Cited
US3832115A
Cited
US3980511A
Cited
US3850723A
Cited
GB1412642A
Cited
US3865661A
Cited
GB1329409A
Cited
US3903343A
Cited
GB1424682A
Cited
US3891738A
Cited
US3980613A
Cited
US4007083A
Cited
US3930917A
Cited
US4104340A
Cited
US4081318A
Cited
US4234652A
Cited
US4104435A
Cited
US4159294A
Cited
US4178411A
Cited
US4273981A
Cited
US4469543A
Cited
US4498957A
Cited
US4327164A
Cited
US4242404A
Cited
GB2051170B
Cited
US4386943A
Cited
JPS5637373A
Cited
US4339490A
Cited
GB2065016A
Cited
FR2475970A1
Cited
US4508777A
Cited
US4362778A
Cited
US4399085A
Cited
GB2093474B
Cited
US4503116A
Cited
GB2096195A
Cited
US4359132A
Cited
US4451539A
Cited
EP0071219A1
Cited
US4426470A
Cited
US4481248A
Cited
US4562033A
Cited
AU559853B2
Cited
US4383154A
Cited
US4440819A
Cited
US4512836A
Cited
US4495238A
Cited
US4543288A
Cited
US4543288B1
Cited
EP0152994A2
Cited
US4690860A
Cited
US4670331A
Cited
US4734321A
Cited
EP0148760A2
Cited
DE3420195A1
Cited
US4595617A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-20 | 1993-05-22 | 1993-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-20 | 1997-05-22 | 1997-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-20 | 2001-05-22 | 2001-11-21 | $7700.00 | Window Closed / Lapsed |