Aromatic polyamide paper-like sheet and processes for producing the same
Assignee: Teijin Ltd
•
Filing: 1983-09-15
•
Granted: 1985-02-12
•
Expires: 2003-09-15
Abstract
Abstract An aromatic polyamide paper-like sheet having excellent heat- and chemical- resistances and electric insulating properties, comprises an artificial pulp ingredient comprising a number of amorphous pulp particles consisting of an aromatic polyamide material, and a fiber ingredient consisting of a number of short fibers bonded to each other with the amorphous pulp particles, the ratio in weight of the artificial pulp ingredient to the fiber ingredient being in a range of from 1:9 to 9:1 and the aromatic polyamide molecules contained at least in the amorphous pulp particles being cross-linked with a cross-linking agent.
Inventors
- 👤 Hideharu Sasaki
- 👤 Keizo Shimada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 07:29
CPC Classifications
D; D21; D21H; D21H13/00; D21H13/10; D21H13/20; D21H13/26; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/31504; Y10T428/31725
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
331 words
A process for producing an aromatic polyamide paper-like sheet, comprising the steps of: dissolving in an organic solvent an aromatic polyamide material together with a cross-linking agent comprising at least one compound selected from the group consisting of (A) cyanurate and isocyanurate type epoxy compounds of the formula (A-II) and (A-III): ##STR12## wherein Q 1 represents a di-, tri- or tetra-valent organic radical Q 2 represents a single bond or a di- or more valent organic radical; at least two members of E 1 through E 5 respectively represent, independently from each other, a radical selected from those of the formulae (A-IV) and (A-V): ##STR13## in which R 9 , R 10 , and R 11 respectively represent, independently from each other, a hydrogen atom or an organic radical, and the remaining members thereof respectively represent, independently from each other, a radical selected from those of the formulae (A-IV) and (A-V) and a monovalent radical corresponding to the radical represented by Q 1 ; r represents zero or 1; p represents zero or an integer of from 1 to 10, and; q represents an integer of from 1 to 3; bringing said polymer solution into contact with a coagulating liquid while vigorously stirring said coagulating liquid to prepare a number of amorphous particles of a mixture of said aromatic polyamide material with said cross-linking agent; separating said amorphous particles from said coagulating liquid to provide an artificial pulp; suspending said artificial pulp together with a fiber comprising a number of short fibers in water, to prepare a slurry by which the ratio in weight of said artificial pulp to said fiber is in a range of from 1:9 to 9:1; forming a precursory paper-like sheet from said slurry by a paper-making method, and; cross-linking the molecules of said aromatic polyamide with said cross-linking agent in said precursory paper-like sheet by applying radiation of at least one member selected from ultraviolet rays and electron beams or heat to said precursory paper-like sheet.
Claim 2
Dependent Claim
331 words
A process for producing an aromatic polyamide paper-like sheet, comprising the steps of: dissolving in an organic solvent an aromatic polyamide material together with a cross-linking agent comprising at least one compound selected from the group consisting of (A) cyanurate and isocyanurate type epoxy compounds of the formula (A-II) and (A-III): ##STR12## wherein Q 1 represents a di-, tri- or tetra-valent organic radical Q 2 represents a single bond or a di- or more valent organic radical; at least two members of E 1 through E 5 respectively represent, independently from each other, a radical selected from those of the formulae (A-IV) and (A-V): ##STR13## in which R 9 , R 10 , and R 11 respectively represent, independently from each other, a hydrogen atom or an organic radical, and the remaining members thereof respectively represent, independently from each other, a radical selected from those of the formulae (A-IV) and (A-V) and a monovalent radical corresponding to the radical represented by Q 1 ; r represents zero or 1; p represents zero or an integer of from 1 to 10, and; q represents an integer of from 1 to 3; bringing said polymer solution into contact with a coagulating liquid while vigorously stirring said coagulating liquid to prepare a number of amorphous particles of a mixture of said aromatic polyamide material with said cross-linking agent; separating said amorphous particles from said coagulating liquid to provide an artificial pulp; suspending said artificial pulp together with a fiber comprising a number of short fibers in water, to prepare a slurry by which the ratio in weight of said artificial pulp to said fiber is in a range of from 1:9 to 9:1; forming a precursory paper-like sheet from said slurry by a paper-making method, and; cross-linking the molecules of said aromatic polyamide with said cross-linking agent in said precursory paper-like sheet by applying radiation of at least one member selected from ultraviolet rays and electron beams or heat to said precursory paper-like sheet.
Claim 3
Dependent Claim
135 words
An aromatic polyamide paperlike sheet produced by the process of claim 1, wherein said aromatic polyamide material comprises at least one aromatic polyamide containing at least 75 molar % of repeating units selected from the group consisting of those of the formulae (I) and (II): ##STR14## wherein Ar 1 , Ar 2 and Ar 3 respectively represent, independently from each other, an unsubstituted or substituted divalent aromatic radical which comprises a single aromatic ring, or two or more aromatic rings that are condensed together, or are linked together bly a single bond, or by a bridging atom or radical, and which is oriented either meta or para, and R 1 , R 2 and R 3 respectively represent, independently from each other, a hydrogen atom or an alkyl radical having 1 to 3 carbon atoms.
Claim 4
Dependent Claim
126 words
An aromatic polyamide paper-like sheet as claimed in claim 2, wherein said Ar 1 , Ar 2 and Ar 3 in said formulae (I) and (II) are respectively selected, independently from each other, from the group consisting of the radicals of the formulae: ##STR15## wherein R represents a member selected from the group consisting of lower alkyl radicals having 1 to 6 carbon atoms, lower alkoxy radicals having 1 to 6 carbon atoms, halogen atoms and a nitro radical, n represents zero or an integer of from 1 to 4 and X represents a member selected from the group consisting of: ##STR16## wherein Y represents a member selected from the group consisting of a hydrogen atom and lower alkyl radicals having 1 to 6 carbon atoms.
Claim 5
Dependent Claim
25 words
An aromatic polyamide paper-like sheet as claimed in claim 1, wherein said short fibers are inorganic fibers selected from glass fibers, asbestos, and silica fibers.
Claim 6
Dependent Claim
22 words
An aromatic polyamide paper-like sheet as claimed in claim 1 wherein said short fibers are organic fibers selected from aromatic polyamide fibers.
Claim 7
Dependent Claim
28 words
An aromatic polyamide paper-like sheet as claimed in claim 5, wherein the aromatic polyamide molecules in said short aromatic polyamide fibers are also cross-linked with said cross-linking agent.
Claim 8
Dependent Claim
25 words
An aromatic polyamide paperlike sheet produced by the process of claim 1, wherein said short fibers each have a denier of from 0.5 to 10.
Claim 9
Dependent Claim
26 words
An aromatic polyamide paperlike sheet produced by the process of claim 1, wherein said short fibers each have a length of from 1 to 10 mm.
Claim 10
Dependent Claim
40 words
An aromatic polyamide paper-like sheet produced by the process of claim 1, wherein said cross-linking agent is used in an amount of 10% or less based on the entire weight of said aromatic polyamide material contained in said paper-like sheet.
Claim 11
Dependent Claim
18 words
A process as claimed in claim 1, wherein said organic solvent is selected from amide type organic solvents.
Claim 12
Dependent Claim
25 words
A process as claimed in claim 10, wherein said amide type organic solvent is selected from the group consisting of N-methyl-2-pyrrolidone, N-N-dimethyl-formamide and N,N-dimethyl acetamide.
Claim 13
Dependent Claim
37 words
A process as claimed in claim 1, wherein the content of said aromatic polyamide material in said polymer solution is in a range of from 2 to 15% based on the entire weight of said polymer solution.
Claim 14
Dependent Claim
26 words
A process as claimed in claim 1, wherein said polymer solution contains 1 to 10% of water based on the entire weight of said polymer solution.
Claim 15
Dependent Claim
36 words
A process as claimed in claim 1, wherein the amount of said cross-linking agent in said polymer solution is in a range of from 0.1 to 10% based on the weight of said aromatic polyamide material.
Claim 16
Dependent Claim
24 words
A process as claimed in claim 1, wherein said coagulating liquid consists of an aqueous solution of 10 to 48% by weight of N-methyl-2-pyrrolidone.
Claim 17
Dependent Claim
20 words
A process as claimed in claim 1, wherein said coagulating liquid has a temperature of from 5° to 80° C.
Claim 18
Dependent Claim
50 words
A process as claimed in claim 1, wherein said cross-linking operation is carried out by applying ultraviolet rays from an ultra-violet ray source having an output of from 0.5 to 5 KW to said precursory paper-like sheet spaced 1 to 100 cm from said source, for 10 to 1,000 seconds.
Claim 19
Dependent Claim
32 words
A process as claimed in claim 1 wherein said cross-linking operation is carried out by applying an electron beam to said precursory paper-like sheet at a dose of 0.5 Mrad or more.
Claim 20
Dependent Claim
29 words
A process as claimed in claim 1, wherein said cross-linking operation is carried out by heating said precursory paper-like sheet at a temperature of from 110° to 360° C.
Claim 21
Dependent Claim
28 words
A process as claimed in claim 1, wherein after or during said cross-linking operation, said paper-like sheet is pressed under a pressure of 400 kg/cm 2 or less.
References Cited (Backward Citations)
US2940953A
Cited
US2947725A
Cited
US2999788A
Cited
US3409497A
Cited
US3734887A
Cited
US3676249A
Cited
US3756908A
Cited
US3779949A
Cited
US4230766A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-12 | 1988-08-13 | 1989-02-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-12 | 1992-08-13 | 1993-02-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-12 | 1996-08-13 | 1997-02-12 | $7700.00 | Window Closed / Lapsed |