Moulded fibre reinforced plastics articles
Assignee: Wiggins Teape Group Ltd
•
Filing: 1985-01-04
•
Granted: 1987-06-02
•
Expires: 2005-01-04
Abstract
Abstract A process for moulding articles of fibre reinforced plastics material which includes heating and moulding a sheet of consolidated thermoplastics material which has dispersed therein from 20% to 70% by weight of reinforcing fibres which have a high modulus of elasticity (as herein defined) and between about 7 and about 50 millimeters long so that the stresses embodied in the glass fibres cause the matrix to expand into the configuration of the mould and become porous.
Inventors
- 👤 Bronislaw Radvan
- 👤 William T. H. Skelding
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 17:49
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/42; B29C70/46; B29C67/00; B29C67/20; B29C70/06; B29C70/08; B29C70/10; B29C70/12; B29C70/54; B29C70/56; D; D21; D21H; D21H13/00; D21H13/36; D21H13/38; D21H13/40; B29K; B29K2105/00; B29K2105/04; B29K2105/06; B29K2105/12; B29K2995/00; B29K2995/0037; B29K2995/0046; B29K2995/0068; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249924; Y10T428/24994; Y10T428/24995; Y10T428/249952; Y10T428/249953; Y10T428/249962; Y10T428/249964
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
151 words
A process for moulding a porous article from fibre reinforced plastics material, comprising the steps of: providing a sheet of thermoplastics material which has been consolidated under heat and pressure and having dispersed therein from 20% to 70% by weight of flexurally stressed glass reinforcing fibres between about 7 and 50 millimeters long; heating said sheet to a temperature above the softening temperature of the thermoplastic material so that said sheet is mouldable and the flexural stresses in the fibres are released to cause the sheet to expand and become porous; shaping the expanded sheet into a porous article by subjecting said sheet to a moulding process in a moulding apparatus; and controlling expansion of the sheet in the moulding apparatus to a value less than free unrestricted expansion of the sheet such that at least a portion of the porosity of the expanded sheet is retained in the porous article.
Claim 2
Dependent Claim
151 words
A process for moulding a porous article from fibre reinforced plastics material, comprising the steps of: providing a sheet of thermoplastics material which has been consolidated under heat and pressure and having dispersed therein from 20% to 70% by weight of flexurally stressed glass reinforcing fibres between about 7 and 50 millimeters long; heating said sheet to a temperature above the softening temperature of the thermoplastic material so that said sheet is mouldable and the flexural stresses in the fibres are released to cause the sheet to expand and become porous; shaping the expanded sheet into a porous article by subjecting said sheet to a moulding process in a moulding apparatus; and controlling expansion of the sheet in the moulding apparatus to a value less than free unrestricted expansion of the sheet such that at least a portion of the porosity of the expanded sheet is retained in the porous article.
Claim 3
Dependent Claim
77 words
A process as claimed in claim 1 in which the moulding process is performed in moulding apparatus having a forming tool, in which the apparatus has means for holding the position of the forming tool relative to a second mould part, and in which the degree of expansion is controlled by setting the dimensions of the forming tool to clearances less than the final thickness which would be achieved by free un-restricted expansion of said thermoplastic sheet.
Claim 4
Dependent Claim
20 words
A process as claimed in claim 2 in which the thermoplastics material has a least 30% by weight glass fibres.
Claim 5
Dependent Claim
20 words
A process as claimed in claim 2 in which the thermoplastics material has at least 30% by weight glass fibres.
Claim 6
Dependent Claim
18 words
A process as claimed in claim 3 in which the thermoplastics material has 50% by weight glass fibres.
Claim 7
Dependent Claim
32 words
A process as claimed in claim 5 in which the sheet is formed of at least two layers of plastics material of different compositions which are laminated together in the moulding process.
Claim 8
Dependent Claim
27 words
A process as claimed in claim 1 including the step of laminating at least two layers of plastics material of different compositions together in the moulding process.
Claim 9
Dependent Claim
32 words
A process as claimed in claim 7 including the step of laminating at least three layers, the outer layers having a lower fibre content by weight than the inner layer or layers.
Claim 10
Dependent Claim
80 words
A process as claimed in claim 8 in which the sheet is heated in an oven and then transferred to moulding apparatus having at least two parts, sufficient pressure is applied to the sheet in the moulding apparatus to conform the sheet to the two parts, the pressure is then released and at least two of the mould parts are separated to allow the fibre content of the moulded article to recover and expand the moulding to render it porous.
Claim 11
Dependent Claim
65 words
A process as claimed in claim 1 in which the sheet is heated in an oven to cause said sheet to expand and then transferred to moulding apparatus having at least two parts in which sufficient moulding pressure is applied to conform the sheet to the shape of the mould parts so that an article between the mould parts retains porosity from the expanded sheet.
Claim 12
Dependent Claim
62 words
A process as claimed in claim 10 in which sufficient moulding pressure is applied to said sheet in said moulding apparatus to conform said sheet to said two mould parts and then released and at least two of the mould parts are separated to allow the fibre content of the moulded article to recover and expand the moulding to render it porous.
Claim 13
Dependent Claim
29 words
A process as claimed in claim 1 in which the moulding apparatus has mould parts which are again closed after the moulding has expanded to partly consolidate the moulding.
Claim 14
Dependent Claim
29 words
A process as claimed in claim 1 which includes arranging for the sheet to be at a temperature sufficient to render it mouldable by heating in said moulding apparatus.
Claim 15
Dependent Claim
31 words
A process as claimed in claim 13 which includes arranging for the stresses embodied in the glass fibres to cause the matrix to expand into the configuration of said moulding apparatus.
Claim 16
Dependent Claim
17 words
An article of moulded fibre reinforced plastics material made by the process set forth in claim 1.
References Cited (Backward Citations)
US2715755A
Cited
GB1129757A
Cited
US3621092A
Cited
GB1306145A
Cited
GB1305982A
Cited
GB1348896A
Cited
GB1329409A
Cited
US3891738A
Cited
US4178411A
Cited
US4273981A
Cited
US4399085A
Cited
US4426470A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-01 | 1990-12-01 | 1991-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-01 | 1994-12-01 | 1995-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-01 | 1998-12-01 | 1999-06-02 | $7700.00 | Window Closed / Lapsed |