Ion implantation and annealing of compound semiconductor layers
Assignee: Kopin Corp
•
Filing: 1987-11-13
•
Granted: 1989-09-05
•
Expires: 2007-11-13
Abstract
Abstract A method for reducing the defect and dislocation density in III-V material layers deposited on dissimilar substrates is disclosed. The method involves ion implantation of dopant materials to create amorphous regions within the layers followed by an annealing step during which the amorphous regions are recrystallized to form substantially monocrystalline regions. The wafers produced by the process are particularly well suited for optoelectronic devices.
Inventors
- 👤 John C. C. Fan
- 👤 Jhang W. Lee
- 👤 Jagdish Narayan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 02:19
CPC Classifications
H; H10; H10H; H10H20/00; H10H20/01; H10H20/011; H10H20/013; H10H20/0133; H10P; H10P14/00; H10P14/20; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/32; H10P14/3202; H10P14/3214; H10P14/3221; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3418; H10P14/3421; H10P14/38; H10P14/3822; Y; Y10; Y10S; Y10S148/00; Y10S148/065; Y10S148/072; Y10S148/084; Y10S148/149; Y10S438/00; Y10S438/933
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
146 words
A method for producing a wafer having a III-V material layer on a single crystal or substantially single crystal semiconductor substrate, the III-V material layer being of a material different than that of the substrate, said method comprising: a. epitaxially depositing the layer of III-V material on the single crystal or substantially single crystal semiconductor substrate; b. performing an ion implantation into the layer of III-V material to form an amorphous region in the layer of III-V material near the surface of the substrate, but leaving substantially monocrystalline III-V material above or adjacent the amorphous region as well as near the surface of the III-V material layer; and c. annealing the wafer at a temperature substantially below the melting temperature of the III-V material to convert amorphous III-V material to monocrystalline III-V material by regrowing the III-V material from the remaining substantially crystalline III-V material region.
Claim 2
Independent Claim
146 words
A method for producing a wafer having a III-V material layer on a single crystal or substantially single crystal semiconductor substrate, the III-V material layer being of a material different than that of the substrate, said method comprising: a. epitaxially depositing the layer of III-V material on the single crystal or substantially single crystal semiconductor substrate; b. performing an ion implantation into the layer of III-V material to form an amorphous region in the layer of III-V material near the surface of the substrate, but leaving substantially monocrystalline III-V material above or adjacent the amorphous region as well as near the surface of the III-V material layer; and c. annealing the wafer at a temperature substantially below the melting temperature of the III-V material to convert amorphous III-V material to monocrystalline III-V material by regrowing the III-V material from the remaining substantially crystalline III-V material region.
Claim 3
Dependent Claim
21 words
A method as in claim 1 wherein the substrate is selected from the group consisting of monocrystalline Si and monocrystalline Ge/Si.
Claim 4
Dependent Claim
38 words
A method as in claim 1 wherein the III-V material comprises a combination of a material selected from the group consisting of Ga, Al and In, and a material selected from the group consisting of As and P.
Claim 5
Dependent Claim
22 words
A method as in claim 3 wherein the III-V material is selected from the group consisting of GaAs, AlGaAs, InGaAs and InP.
Claim 6
Dependent Claim
23 words
A method as in claim 1 wherein the ion implantation uses ion implantation species which are different than that of the III-V material.
Claim 7
Dependent Claim
29 words
A method as in claim 1 wherein the ion implantation uses ion implantation species selected from the class consisting of group IIIA and Group VA of the periodic table.
Claim 8
Dependent Claim
23 words
A method as in claim 5 wherein the ion implantation species is selected from the group consisting of n-type dopants and p-type dopants.
Claim 9
Dependent Claim
23 words
A method as in claim 7 wherein the ion implantation species is selected from the group consisting of B, Zn, Se and Si.
Claim 10
Dependent Claim
38 words
A method as in claim 1 wherein the ion implantation uses an ion beam having an energy selected to produce an implant having a maximum range lying near the interface between the III-V material layer and the substrate.
Claim 11
Dependent Claim
64 words
A method as in claim 9 wherein the ion beam is directed along the III-V material layer's crystal axis to thereby channel the ions through the monocrystalline III-V material layer to form an amorphous region in the III-V material layer near the substrate while leaving substantially monocrystalline III-V material in another region extending from the amorphitized region to the surface of the substrate layer.
Claim 12
Dependent Claim
56 words
A method as in claim 10 further comprising the steps of a. performing a second ion implantation to render amorphous the surface layer of III-V material which was left in a substantially monocrystalline state after the first ion implantation; and b. performing a second annealing step to convert the amorphous surface layer to monocrystalline III-V material.
Claim 13
Dependent Claim
56 words
A method as in claim 1 further comprising the steps of a. performing a second ion implantation to render amorphous the surface layer of III-V material which was left in a substantially monocrystalline state after the first ion implantation; and b. performing a second annealing step to convert the amorphous surface layer to monocrystalline III-V material.
Claim 14
Dependent Claim
14 words
A method as in claim 1 wherein the annealing step is a capless annealing.
Claim 15
Dependent Claim
28 words
A method as in claim 13 wherein the capless annealing is carried out at a temperature between about 550° and 950° C. using an arsenic or phospine overpressure.
Claim 16
Dependent Claim
14 words
A method as in claim 1 wherein the annealing step is a cap annealing.
Claim 17
Dependent Claim
18 words
A method as in claim 15 wherein the cap annealing uses an Si 3 N 4 encapsulating layer.
Claim 18
Dependent Claim
34 words
A method as in claim 16 wherein the cap annealing uses a cap having a Si 3 N 4 layer of about 1500 A covered with a Si0 2 layer of about 1000 A.
Claim 19
Dependent Claim
15 words
A method as in claim 11 wherein the second annealing step is a capless annealing.
Claim 20
Dependent Claim
28 words
A method as in claim 18 wherein the capless annealing is carried out at a temperature between about 550° and 950° C. using an arsenic or phosphine overpressure.
Claim 21
Dependent Claim
15 words
A method as in claim 12 wherein the second annealing step is a cap annealing.
Claim 22
Dependent Claim
18 words
A method as in claim 20 wherein the cap annealing uses an Si 3 N 4 encapsulating layer.
Claim 23
Dependent Claim
34 words
A method as in claim 21 wherein the cap annealing uses a cap having a Si 3 N 4 layer of about 1500 A covered with a Si0 2 layer of about 1000 A.
Claim 24
Dependent Claim
39 words
A method as in claim 1 wherein a screen is placed between a source of ion implantation and the wafer to selectively shield the wafer from ion implantation species, thereby producing amorphitization only in selected regions of the wafer.
Claim 25
Dependent Claim
38 words
A method as in claim 1 wherein ion implantation is carried out by scanning a focused ion beam across the surface of the wafer in a certain pattern, thereby producing amorphitization only in selected regions of the wafer.
Claim 26
Dependent Claim
19 words
A method as in claim 1 wherein the ion implantation step and the annealing step are carried out simultaneously.
Claim 27
Dependent Claim
14 words
A method as in claim 15 wherein ions are implanted through the annealing cap.
Claim 28
Dependent Claim
14 words
A method as in claim 20 wherein ions are implanted through the annealing cap.
Claim 29
Dependent Claim
27 words
A method as in claim 1 wherein a two step annealing process having a low temperatures annealing step followed by a high temperature annealing step is used.
Claim 30
Dependent Claim
25 words
A method as in claim 1 further comprising the step of growing a submicron III-V material layer upon the wafer subsequent to the annealing step.
Claim 31
Independent Claim
122 words
A method for producing a wafer having a III-V material layer on a single crystal or substantially single crystal semiconductor substrate, the III-V material layer being of a material different than that of the substrate, said method comprising: a. epitaxially depositing the III-V material on a surface of the single crystal or substantially single crystal semiconductor substrate, thereby forming a layered article; b. performing an ion implantation into the layered article to form an amorphous region extending above and below the substrate surface; and c. annealing the wafer at a temperature substantially below the melting temperature of the III-V material and the substrate to convert material in the amorphous region to monocrystalline material by regrowth from a region of substantially crystalline material.
Claim 32
Independent Claim
122 words
A method for producing a wafer having a III-V material layer on a single crystal or substantially single crystal semiconductor substrate, the III-V material layer being of a material different than that of the substrate, said method comprising: a. epitaxially depositing the III-V material on a surface of the single crystal or substantially single crystal semiconductor substrate, thereby forming a layered article; b. performing an ion implantation into the layered article to form an amorphous region extending above and below the substrate surface; and c. annealing the wafer at a temperature substantially below the melting temperature of the III-V material and the substrate to convert material in the amorphous region to monocrystalline material by regrowth from a region of substantially crystalline material.
Claim 33
Dependent Claim
21 words
A method as in claim 30 wherein the substrate is selected from the group consisting of monocrystalline Si and monocrystalline Ge/Si.
Claim 34
Dependent Claim
38 words
A method as in claim 30 wherein the III-V material comprises a combination of a material selected from the group consisting of Ga, Al and In, and a material selected from the group consisting of As and P.
Claim 35
Dependent Claim
22 words
A method as in claim 32 wherein the III-V material is selected from the group consisting of GaAs, AlGaAs, InGaAs and InP.
Claim 36
Dependent Claim
23 words
A method as in claim 30 wherein the ion implantation uses ion implantation species which are different than that of the III-V material.
Claim 37
Dependent Claim
29 words
A method as in claim 30 wherein the ion implantation uses ion implantation species selected from the class consisting of group IIIA and Group VA of the periodic table.
Claim 38
Dependent Claim
23 words
A method as in claim 34 wherein the ion implantation species is selected from the group consisting of n-type dopants and p-type dopants.
Claim 39
Dependent Claim
23 words
A method as in claim 36 wherein the ion implantation species is selected from the group consisting of B, Zn, Se and Si.
Claim 40
Dependent Claim
46 words
A method as in claim 30 wherein the amorphous region extends from below the substrate surface to the interior of the III-V material while leaving substantially monocrystalline III-V material above or adjacent the amorphous region as well as near the surface of the III-V material layer.
Claim 41
Dependent Claim
52 words
A method as in claim 38 wherein the layered article is annealed at a temperature substantially below the melting temperature of the III-V material and the substrate to convert material in the amorphous region to monocrystalline material by regrowing the III-V material from the remaining substantially crystalline III-V material and substrate regions.
Claim 42
Independent Claim
132 words
A method for producing a wafer having a III-V material layer on a single crystal or substantially single crystal semiconductor substrate, the III-V material layer being of a material different than that of the substrate, said method comprising: a. epitaxially depositing the layer of III-V material on the single crystal or substantially single crystal semiconductor substrate; b. performing an ion implantation into selected, isolated regions of the III-V material to form isolated amorphous regions of III-V material, but leaving substantially monocrystalline III-V material adjacent the III-V material layer; and c. annealing the wafer at a temperature substantially below the melting temperature of the III-V material to convert the isolated amorphous III-V material regions to monocrystalline III-V material by regrowing the III-V material from substantially crystalline III-V material adjacent to the amorphous regions.
Claim 43
Independent Claim
132 words
A method for producing a wafer having a III-V material layer on a single crystal or substantially single crystal semiconductor substrate, the III-V material layer being of a material different than that of the substrate, said method comprising: a. epitaxially depositing the layer of III-V material on the single crystal or substantially single crystal semiconductor substrate; b. performing an ion implantation into selected, isolated regions of the III-V material to form isolated amorphous regions of III-V material, but leaving substantially monocrystalline III-V material adjacent the III-V material layer; and c. annealing the wafer at a temperature substantially below the melting temperature of the III-V material to convert the isolated amorphous III-V material regions to monocrystalline III-V material by regrowing the III-V material from substantially crystalline III-V material adjacent to the amorphous regions.
Claim 44
Independent Claim
134 words
A method for producing a wafer having a III-V material layer on a single crystal or substantially single crystal semiconductor substrate, the III-V material layer being of a material different than that of the substrate, said method comprising: a. epitaxially depositing the layer of III-V material on a surface of the single crystal or substantially single crystal semiconductor substrate, thereby forming a layered article; b. performing an ion implantation into the surface of the III-V material to form an amorphous surface region in the III-V material, but leaving substantially monocrystalline III-V material below the amorphous region; and, c. annealing the wafer at a temperature substantially below the melting temperature of the III-V material to convert amorphous III-V material to monocrystalline III-V material by regrowing the III-V material from the substantially crystalline III-V material region.
Claim 45
Independent Claim
134 words
A method for producing a wafer having a III-V material layer on a single crystal or substantially single crystal semiconductor substrate, the III-V material layer being of a material different than that of the substrate, said method comprising: a. epitaxially depositing the layer of III-V material on a surface of the single crystal or substantially single crystal semiconductor substrate, thereby forming a layered article; b. performing an ion implantation into the surface of the III-V material to form an amorphous surface region in the III-V material, but leaving substantially monocrystalline III-V material below the amorphous region; and, c. annealing the wafer at a temperature substantially below the melting temperature of the III-V material to convert amorphous III-V material to monocrystalline III-V material by regrowing the III-V material from the substantially crystalline III-V material region.
References Cited (Backward Citations)
US4193182A
Cited
US4174982A
Cited
US4177084A
Cited
US4333226A
Cited
US4312681A
Cited
US4396437A
Cited
US4377437A
Cited
US4391651A
Cited
US4509990A
Cited
US4544417A
Cited
US4494997A
Cited
US4602965A
Cited
US4569124A
Cited
US4588447A
Cited
US4558509A
Cited
US4713354A
Cited
US4659392A
Cited
WO1987004563A1
Cited
WO1987004854A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-04 | 1993-03-06 | 1993-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-04 | 1997-03-06 | 1997-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-04 | 2001-03-06 | 2001-09-05 | $7700.00 | Window Closed / Lapsed |