Dispersion process for ceramic green body
Assignee: Dow Chemical Co
•
Filing: 1987-09-01
•
Granted: 1989-03-28
•
Expires: 2007-09-01
Abstract
Abstract A process is described for the preparation of a ceramic green body by hydrolyzing at least one alkoxide selected from each of two specified groups to form a dispersion of their reaction product, concentrating the dispersion to a sediment without drying it, and admixing a binder and a plasticizer with the sediment to make a ceramic slip formulation. A release agent can optionally be admixed. The slip formulation is then cast as a ceramic green body. The proportions of alkoxides can be adjusted, as desired, to produce a ceramic green body which is dielectric and useful for microcapacitors or as a conductor.
Inventors
- 👤 A. Dale Harley
- 👤 Larwrence G. Duquette
- 👤 Issam A. Khoury
- 👤 Iwao Kohatsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:28
CPC Classifications
A; A61; A61L; A61L2/00; A61L2/02; A61L2/022; A61M; A61M1/00; A61M1/34; B; B01; B01D; B01D69/00; B01D69/02; B01D69/08; B82; B82Y; B82Y30/00; C; C01; C01B; C01B13/00; C01B13/14; C01B13/32; C01G; C01G23/00; C01G23/003; C01G23/006; C01G25/00; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; C04B35/4684; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/636; C04B35/6365; A61L2103/00; A61L2103/05; A61M2205/00; A61M2205/33; A61M2205/3368; A61M2205/75; A61M2205/7509; A61M2205/7554; A61M2205/7581; C01P; C01P2002/00; C01P2002/02; C01P2002/30; C01P2002/34; C01P2002/60; C01P2004/00; C01P2004/30; C01P2004/32; C01P2004/50; C01P2004/60; C01P2004/61; C01P2004/64; C01P2006/00; C01P2006/12; C01P2006/60
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
243 words
A process for preparing a ceramic green body comprising: (a) forming a hydrolyzable solution of at least one compound of the formula A(OR) x wherein A is Be, Mg, Ca, Sr, Ba, Ge, Pb, Nd, Y, La, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Sb, Bi or a mixture thereof, at least one compound of the formula B(OR) x wherein B is Ti, Zr, Sc, Y, La, Nb, Fe, Ta, W, Mn, Sn, Mg, Cu, Zn, Ni, Co, Mo or a mixture thereof, wherein R is a group of the formula C y H z wherein y is an integer from 1 to 10, z is an integer y, 2y, 2y+1 or 2y-1, and x is independently an integer from 1 to 7, such that said compounds of the formulas A(OR) x and B(OR) x are suitable to be hydrolyzed to form a compound of the formula ABO 3- Δ wherein Δ is a number from 0 to 1.33, and an alcohol suitable to dissolve said compounds of the formulas A(OR) x and B(OR) x ; (b) hydrolyzing said hydrolyzable solution to form a hydrolyzed dispersion of said compound of the formula ABO 3- Δ in said alcohol; (c) concentrating at least a portion of said dispersion to form a sediment; (d) admixing a binder solution and a plasticizer with said sediment to make a ceramic slip formulation; and (e) preparing a ceramic green body from said slip formulation.
Claim 2
Dependent Claim
243 words
A process for preparing a ceramic green body comprising: (a) forming a hydrolyzable solution of at least one compound of the formula A(OR) x wherein A is Be, Mg, Ca, Sr, Ba, Ge, Pb, Nd, Y, La, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Sb, Bi or a mixture thereof, at least one compound of the formula B(OR) x wherein B is Ti, Zr, Sc, Y, La, Nb, Fe, Ta, W, Mn, Sn, Mg, Cu, Zn, Ni, Co, Mo or a mixture thereof, wherein R is a group of the formula C y H z wherein y is an integer from 1 to 10, z is an integer y, 2y, 2y+1 or 2y-1, and x is independently an integer from 1 to 7, such that said compounds of the formulas A(OR) x and B(OR) x are suitable to be hydrolyzed to form a compound of the formula ABO 3- Δ wherein Δ is a number from 0 to 1.33, and an alcohol suitable to dissolve said compounds of the formulas A(OR) x and B(OR) x ; (b) hydrolyzing said hydrolyzable solution to form a hydrolyzed dispersion of said compound of the formula ABO 3- Δ in said alcohol; (c) concentrating at least a portion of said dispersion to form a sediment; (d) admixing a binder solution and a plasticizer with said sediment to make a ceramic slip formulation; and (e) preparing a ceramic green body from said slip formulation.
Claim 3
Dependent Claim
31 words
The process of claim 1 wherein said hydrolyzable solution is hydrolyzed by adding water in an amount from about 0.5 percent to about 70 percent by weight of said hydrolyzable solution.
Claim 4
Dependent Claim
24 words
The process of claim 1 wherein said compound of the formula A(OR) x and said compound of the formula B(OR) x are hydrolyzed together.
Claim 5
Dependent Claim
52 words
The process of claim 1 wherein the hydrolysis is conducted by adding water to the hydrolyzable solution at a rate of from about [0.2 cc/min.] 0.012 percent of total volume of the hydrolazable solution per minute to about [0.4 cc/min] 0.26 percent of the total volume of the hydrolyzable solution per minute.
Claim 6
Dependent Claim
16 words
The process of claim 1 wherein A is Mg, Ca, Sr, Ba, Y, La, or Pb.
Claim 7
Dependent Claim
21 words
The process of claim 1 wherein B is Ti, Zr, Sc, Y, La, Nb, Ta, W, Sn, Mg, Cu or Zn.
Claim 8
Dependent Claim
22 words
The process of claim 1 wherein said alcohol comprises from about 30 to about 99 percent by weight of said hydrolyzable solution.
Claim 9
Dependent Claim
32 words
The process of claim 1 wherein said hydrolyzable solution comprises in total from about 1 to about 70 percent by weight of compounds of the formulas A(OR) x and B(OR) x .
Claim 10
Dependent Claim
27 words
The process of claim 1 wherein from about 0.002 to about 0.5 percent by weight of a dispersant is admixed with said hydrolyzed dispersion or said sediment.
Claim 11
Dependent Claim
29 words
The process of claim 9 wherein said dispersant is selected from the group consisting of ethanol, polyacrylate, polymethacrylate, amine salts of alkyaryl sulfonate, menhaden fish oil, and mixtures thereof.
Claim 12
Dependent Claim
18 words
The process of claim 1 wherein a release agent is admixed with said hydrolyzed dispersion or said sediment.
Claim 13
Dependent Claim
28 words
The process of claim 10 wherein said release agent is in an amount of from about 0.01 percent to about 5 percent by weight of said hydrolyzed dispersion.
Claim 14
Dependent Claim
23 words
The process of claim 10 wherein said release agent is selected from the group consisting of a polyol, mineral oil, or mixtures thereof.
Claim 15
Dependent Claim
11 words
The process of claim 12 wherein said release agent is 1,2,4-butanetriol.
Claim 16
Dependent Claim
23 words
The process of claim 1 wherein said binder solution comprises from about 0.1 to about 5 percent by weight of said hydrolyzed dispersion.
Claim 17
Dependent Claim
21 words
The process of claim 15 wherein said binder solvent comprises from 1 to 6 percent by weight of said hydrolyzed dispersion.
Claim 18
Dependent Claim
23 words
The process of claim 15 wherein said binder is selected from the group consisting of ethylcellulose, methylcellulose, ethyl hydroxyethyl cellulose, and mixtures thereof.
Claim 19
Dependent Claim
20 words
The process of claim 1 wherein said plasticizer comprises from 0.01 to 5 percent by weight of said hydrolyzed dispersion.
Claim 20
Dependent Claim
27 words
The process of claim 1 wherein said plasticizer is selected from the group consisting of dioctyl phthalate, dimethyl formamide, benzyl butyl phthalate, propylene glycol, and mixtures thereof.
Claim 21
Dependent Claim
12 words
The process of claim 1 wherein said hydrolyzed dispersion comprises excess water.
Claim 22
Dependent Claim
18 words
The process of claim 20 wherein said excess water is substantially removed prior to admixing said binder solution.
Claim 23
Dependent Claim
17 words
The process of claim 21 wherein said excess water is substantially removed by means of azeotropi distillation.
Claim 24
Dependent Claim
18 words
The process of claim 21 wherein said excess water is substantially removed by means of a drying agent.
Claim 25
Dependent Claim
13 words
The process of claim 1 wherein said slip formulation comprises a sintering aid.
Claim 26
Dependent Claim
15 words
The process of claim 24 wherein said sintering aid comprises a low-melting eutectic oxide mixture.
Claim 27
Dependent Claim
17 words
The process of claim 24 wherein said sintering aid is prepared by hydrolysis of a suitable alkoxide.
Claim 28
Dependent Claim
23 words
The process of claim 25 wherein said alkoxide comprises from about 0.01 percent to about 2 percent by weight of said hydrolyzed dispersion.
Claim 29
Dependent Claim
21 words
The process of claim 1 wherein said ceramic green body is from about 1 μm to about 50 μm in thickness.
Claim 30
Dependent Claim
21 words
The process of claim 1 wherein said ceramic green body is from about 3 μm to about 10 μm in thickness.
Claim 31
Dependent Claim
32 words
The process of claim 1 wherein said compounds of the formulas A(OR) x and B(OR) x are used in a ratio of from about 1 to 1 to about 1.1 to 1.
Claim 32
Dependent Claim
26 words
The process of claim 1 wherein said compounds of the formulas A(OR) x and B(OR) x are used in a ratio of about 1 to 1.
Claim 33
Dependent Claim
14 words
The process of claim 1 wherein said Δ has a value of about 0.
Claim 34
Dependent Claim
18 words
The process of claim 1 wherein said Δ has a value of from about 2/3 to about 5/6.
Claim 35
Dependent Claim
235 words
A process for preparing a ceramic green body comprising: (a) forming a hydrolyzable solution of at least one compound of the formula A(OR) x , wherein A is Be, Mg, Ca, Sr, Ba, Ge, Pb, Nd, Y, La, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Sb, Bi or a mixture thereof, at least one compound of the formula B(OR) x , wherein B is Ti, Zr, Sc, Y, La, Nb, Fe, Ta, W, Mn, Sn, Mg, Cu, Zn, Ni, Co, Mo or a mixture thereof, wherein R is a group of the formula C y H z wherein y is an integer from 1 to 10, z is an integer y, 2y, 2y+1 or 2y-1, and such that said compounds of the formula A(OR) x and B(OR) x are suitable to be hydrolyzed to form a compound of the formula ABO 3- Δ, wherein Δ is a number from 0 to 1.33, x is independently an integer from 1 to 7, and an alcohol suitable to disolve said compounds of the formula A(OR) x and B(OR) x ; (b) hydrolyzing said hydrolable solution to form a hydrolyzed dispersion of said compound of the formula ABO 3- Δ in said alcohol; (c) incorporating a binder solution and a plasticizer and concentrating said hydrolyzed dispersion to make a ceramic slip formulation; and (d) preparing a ceramic green body from said ceramic slip formulation.
Claim 36
Dependent Claim
235 words
A process for preparing a ceramic green body comprising: (a) forming a hydrolyzable solution of at least one compound of the formula A(OR) x , wherein A is Be, Mg, Ca, Sr, Ba, Ge, Pb, Nd, Y, La, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Sb, Bi or a mixture thereof, at least one compound of the formula B(OR) x , wherein B is Ti, Zr, Sc, Y, La, Nb, Fe, Ta, W, Mn, Sn, Mg, Cu, Zn, Ni, Co, Mo or a mixture thereof, wherein R is a group of the formula C y H z wherein y is an integer from 1 to 10, z is an integer y, 2y, 2y+1 or 2y-1, and such that said compounds of the formula A(OR) x and B(OR) x are suitable to be hydrolyzed to form a compound of the formula ABO 3- Δ, wherein Δ is a number from 0 to 1.33, x is independently an integer from 1 to 7, and an alcohol suitable to disolve said compounds of the formula A(OR) x and B(OR) x ; (b) hydrolyzing said hydrolable solution to form a hydrolyzed dispersion of said compound of the formula ABO 3- Δ in said alcohol; (c) incorporating a binder solution and a plasticizer and concentrating said hydrolyzed dispersion to make a ceramic slip formulation; and (d) preparing a ceramic green body from said ceramic slip formulation.
References Cited (Backward Citations)
US2948648A
Cited
US3292994A
Cited
US3330697A
Cited
US3458552A
Cited
US3413083A
Cited
US3647364A
Cited
US3637531A
Cited
US4049789A
Cited
US4293514A
Cited
US4361598A
Cited
US4414337A
Cited
US4447853A
Cited
US4510175A
Cited
US4710227A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-27 | 1992-09-26 | 1993-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-27 | 1996-09-26 | 1997-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-27 | 2000-09-26 | 2001-03-28 | $7700.00 | Window Closed / Lapsed |