Newtonian ceramic slip and process for using

Claim 1

A method for making a monolithic ceramic capacitor comprising: (a) dispersing a ceramic powder, having an average particle size from 0.5 to 1.5 μm, in a liquid vehicle consisting essentially of a solvent of a non-halogenated hydrocarbon plus 0-70% by weight of an alcohol, having dissolved therein a resin binder and a plasticizer, to form a water-insensitive Newtonian slip having a Brookfield viscosity of less than 700 centipoises over the range of 3 to 30 revolutions per minute of a number 2 Brookfield spindle; (b) providing a falling sheet of said Newtonian slip; (c) passing a flat porous substrate horizontally through said falling sheet to coat said substrate with a first level layer of said slip, and drying said first layer; (d) depositing film patches of an electroding ink in the pattern of a matrix on the surface of said first layer creating ink bumps on said first layer surface; (e) passing said substrate again through said falling sheet to deposit another level layer of said slip over said electroded first layer, said second level layer flowing and leveling to acquire an upper surface that is planar and free of irregularities reflecting said pattern of the underlying ink, and drying said second level layer; (f) repeating steps (d) and (e) as many times as is desired to produce a stack of dried level slip layers interleaved by patterns of electroding ink; (g) separating said stack into pieces each having at least one buried electrode and at least another electrode extending respectively to two-spaced apart surface portions of said each piece; (h) firing said pieces to burn out said binder and sinter said ceramic to maturity to transform said pieces to monolithic ceramic capacitor bodies; and (i) applying two terminations to each of said bodies at said two surface portions, respectively, to form monolithic ceramic capacitors.

Claim 2

A method for making a monolithic ceramic capacitor comprising: (a) dispersing a ceramic powder, having an average particle size from 0.5 to 1.5 μm, in a liquid vehicle consisting essentially of a solvent of a non-halogenated hydrocarbon plus 0-70% by weight of an alcohol, having dissolved therein a resin binder and a plasticizer, to form a water-insensitive Newtonian slip having a Brookfield viscosity of less than 700 centipoises over the range of 3 to 30 revolutions per minute of a number 2 Brookfield spindle; (b) providing a falling sheet of said Newtonian slip; (c) passing a flat porous substrate horizontally through said falling sheet to coat said substrate with a first level layer of said slip, and drying said first layer; (d) depositing film patches of an electroding ink in the pattern of a matrix on the surface of said first layer creating ink bumps on said first layer surface; (e) passing said substrate again through said falling sheet to deposit another level layer of said slip over said electroded first layer, said second level layer flowing and leveling to acquire an upper surface that is planar and free of irregularities reflecting said pattern of the underlying ink, and drying said second level layer; (f) repeating steps (d) and (e) as many times as is desired to produce a stack of dried level slip layers interleaved by patterns of electroding ink; (g) separating said stack into pieces each having at least one buried electrode and at least another electrode extending respectively to two-spaced apart surface portions of said each piece; (h) firing said pieces to burn out said binder and sinter said ceramic to maturity to transform said pieces to monolithic ceramic capacitor bodies; and (i) applying two terminations to each of said bodies at said two surface portions, respectively, to form monolithic ceramic capacitors.