Abstract
Abstract A clear solution is prepared by reacting metal alkoxide with a mixture of critical amounts of water and/or acid in an alcohol diluted medium. Alkoxides may be Ti(OR)4 or Ta(OR)5, or another metal alkoxide such as Si(OR)4 in admixture with these alkoxides. Acids may be HCl or HNO3. Quarter wave inorganic optical coatings are deposited by applying the alkoxide solution to a substrate then heating the coating at over 350 DEG C. The coatings reduce reflectivity on silicon solar cells. The index of refraction of the coating can be varied by several techniques, including altering the proportion of titanium and silicon in the coating firing temperature, firing atmosphere. Thicknesses of the coating can be controlled by varying the rpm in spin application, withdrawal rate in dipping application, by concentration of the solution, by the type of solvent or the degree of polymerization of the titanium complexes.
Inventors
- 👤 Bulent E. Yoldas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 01:24
CPC Classifications
C; C09; C09D; C09D185/00; C07; C07F; C07F7/00; C07F7/003; C07F7/02; C07F7/04; C08; C08G; C08G79/00; H; H10; H10F; H10F77/00; H10F77/30; H10F77/306; H10F77/311; H10F77/315; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
109 words
A clear stable solution which comprises: (A) alkoxide having the general formula M(OR) n where M is selected from the group consisting of 0 to 100% Ti, 0 to 25% Si, 0 to 100% Ta, and up to 15% of a metal ion which forms an alkoxide, R is alkyl from C 1 to C 6 , and n is the valence of M; (B) about 1.7 to about 4 moles of water per mole of alkoxide; (C) sufficient alcohol to give a solids content of about 0.1 to about 15% by weight based on equivalent oxide; and (D) a sufficient amount of a suitable acid to prevent cloudiness.
Claim 2
Dependent Claim
109 words
A clear stable solution which comprises: (A) alkoxide having the general formula M(OR) n where M is selected from the group consisting of 0 to 100% Ti, 0 to 25% Si, 0 to 100% Ta, and up to 15% of a metal ion which forms an alkoxide, R is alkyl from C 1 to C 6 , and n is the valence of M; (B) about 1.7 to about 4 moles of water per mole of alkoxide; (C) sufficient alcohol to give a solids content of about 0.1 to about 15% by weight based on equivalent oxide; and (D) a sufficient amount of a suitable acid to prevent cloudiness.
Claim 3
Dependent Claim
22 words
A solution according to claim 1 wherein the solids content is about 2 to about 8% by weight based on equivalent oxide.
Claim 4
Dependent Claim
20 words
A solution according to claim 1 which includes about 0.014 to about 0.2 mole of acid per mole of alkoxide.
Claim 5
Dependent Claim
23 words
A solution according to claim 3 wherein said acid is selected from the group consisting of nitric acid, hydrochloric acid, and mixtures thereof.
Claim 6
Dependent Claim
12 words
A solution according to claim 1 wherein said alcohol is ethyl alcohol.
Claim 7
Dependent Claim
21 words
A solution according to claim 1 wherein R is selected from the group consisting of ethyl, isopropyl, butyl, and mixtures thereof.
Claim 8
Dependent Claim
11 words
A solution according to claim 1 wherein M is all Ti.
Claim 9
Dependent Claim
15 words
A solution according to claim 1 wherein M is a mixture of Ti and Si.
Claim 10
Dependent Claim
20 words
A solution according to claim 1 wherein the amount of water is 1.8 to 2.2 moles per mole of alkoxide.
Claim 11
Dependent Claim
66 words
A method of preparing an oxide coating on a substrate, said coating having a predetermined index of refraction between about 1.4 and about 2.4 comprising: (A) preparing a clear solution according to claim 1 wherein M is a 0 to 25% Si and the remainder Ti; (B) applying said clear solution to said substrate; and (C) heating said substrate to about 300° to about 600° C.
Claim 12
Dependent Claim
14 words
A method according to claim 10 wherein said substrate is heated in a vacuum.
Claim 13
Dependent Claim
11 words
A method according to claim 10 wherein said substrate is silicon.
Claim 14
Dependent Claim
12 words
A method according to claim 10 wherein said application is by dipping.
Claim 15
Dependent Claim
23 words
A method according to claim 10 wherein said method is applied twice to the same substrate so that a two-layered coating is produced.
Claim 16
Dependent Claim
40 words
A method according to claim 14 wherein the lower layer is TiO 2 fired in vacuum and the top layer is 90% TiO 2 and 10% SiO 2 fired in air, and each layer is a quarter wavelength in thickness.
Claim 17
Independent Claim
132 words
A method of preparing a clear solution of a metal alkoxide comprising: (A) adding sufficient alcohol to give a final solids content of about 0.1 to about 15% by weight based on equivalent oxide to either or both of: (1) alkoxide having the general formula M(OR) n where M is selected from the group consisting of 0 to 100% Ti, 0 to 30% Si, 0 to 100% Ta, and up to 15% of another metal ion which forms an alkoxide, R is alkyl from C 1 to C 6 , and n is the valence of M; and (2) about 1.7 to about 4 moles of water per mole of alkoxide; (B) mixing together said alkoxide and said water; and (C) adding a sufficient amount of a suitable acid to prevent cloudiness.
Claim 18
Independent Claim
132 words
A method of preparing a clear solution of a metal alkoxide comprising: (A) adding sufficient alcohol to give a final solids content of about 0.1 to about 15% by weight based on equivalent oxide to either or both of: (1) alkoxide having the general formula M(OR) n where M is selected from the group consisting of 0 to 100% Ti, 0 to 30% Si, 0 to 100% Ta, and up to 15% of another metal ion which forms an alkoxide, R is alkyl from C 1 to C 6 , and n is the valence of M; and (2) about 1.7 to about 4 moles of water per mole of alkoxide; (B) mixing together said alkoxide and said water; and (C) adding a sufficient amount of a suitable acid to prevent cloudiness.
Claim 19
Dependent Claim
15 words
A method according to claim 16 wherein said alcohol is added entirely to said water.
Claim 20
Dependent Claim
22 words
A method according to claim 16 wherein titanium alkoxide is added to a mixture of said alcohol and partially hydrolyzed silicon alkoxide.
Claim 21
Dependent Claim
21 words
A method according to claim 16 wherein a mixture of alkoxides is used and each alkoxide is partially hydrolyzed before mixing.
Claim 22
Dependent Claim
27 words
A method according to claim 16 wherein said acid is added to a mixture of said water and said alcohol, which is then mixed with said alkoxide.
Claim 23
Dependent Claim
20 words
A method according to claim 16 wherein the amount of water is 1.8 to 2.2 moles per mole of alkoxide.
Claim 24
Dependent Claim
22 words
A method according to claim 16 wherein the solids content is about 2 to about 8% by weight based on equivalent oxide.
Claim 25
Dependent Claim
23 words
A method according to claim 16 wherein said acid is selected from the group consisting of nitric acid, hydrochloric acid, and mixtures thereof.
Claim 26
Dependent Claim
21 words
A method according to claim 16 wherein said water is diluted with said alcohol, which is then mixed with said alkoxide.
Claim 27
Dependent Claim
23 words
A method according to claim 16 wherein the amount of said acid is about 0.014 to about 0.2 moles per mole of alkoxide.
Claim 28
Dependent Claim
17 words
A method according to claim 16 wherein said solution is aged for several hours prior to use.
Claim 29
Dependent Claim
21 words
A method according to claim 16 wherein said solution is applied to a substrate by dipping said substrate into said solution.
Claim 30
Dependent Claim
115 words
A clear stable solution which comprises: (A) alkoxide having the general formula M(OR) n where at least 60% of M is selected from one of titanium and tantalum, up to 25% of M is silicon, and up to 15% of M is a metal which forms an alkoxide, each R is independently selected from C 1 to C 6 , and n is the valence of each M; (B) about 1.7 to about 4 moles of water per mole of alkoxide; (C) sufficient alcohol to give a solids content of about 0.1 to about 15% by weight based on equivalent oxide; and (D) about 0.014 to about 0.2 moles of acid per mole of alkoxide.
Claim 31
Dependent Claim
115 words
A clear stable solution which comprises: (A) alkoxide having the general formula M(OR) n where at least 60% of M is selected from one of titanium and tantalum, up to 25% of M is silicon, and up to 15% of M is a metal which forms an alkoxide, each R is independently selected from C 1 to C 6 , and n is the valence of each M; (B) about 1.7 to about 4 moles of water per mole of alkoxide; (C) sufficient alcohol to give a solids content of about 0.1 to about 15% by weight based on equivalent oxide; and (D) about 0.014 to about 0.2 moles of acid per mole of alkoxide.
Claim 32
Independent Claim
153 words
A method of coating a substrate with a solid continuous layer of a metal oxide comprising: (1) preparing a clear stable solution which comprises: (A) alkoxide having the general formula M(OR) n where at least 60% of M is selected from one of titanium and tantalum, up to 25% of M is silicon, and up to 15% of M is a metal which forms an alkoxide, each R is independently selected from C 1 to C 6 , and n is the valence of each M; (B) about 1.7 to about 4 moles of water per mole of alkoxide; (C) sufficient alcohol to give a solids content of about 0.1 to about 15% by weight based on equivalent oxide; and (D) about 0.014 to about 0.2 moles of acid per mole of alkoxide. (2) applying said clear stable solution to said substrate; (3) heating said substrate to about 300° to about 600° C.
Claim 33
Independent Claim
153 words
A method of coating a substrate with a solid continuous layer of a metal oxide comprising: (1) preparing a clear stable solution which comprises: (A) alkoxide having the general formula M(OR) n where at least 60% of M is selected from one of titanium and tantalum, up to 25% of M is silicon, and up to 15% of M is a metal which forms an alkoxide, each R is independently selected from C 1 to C 6 , and n is the valence of each M; (B) about 1.7 to about 4 moles of water per mole of alkoxide; (C) sufficient alcohol to give a solids content of about 0.1 to about 15% by weight based on equivalent oxide; and (D) about 0.014 to about 0.2 moles of acid per mole of alkoxide. (2) applying said clear stable solution to said substrate; (3) heating said substrate to about 300° to about 600° C.
References Cited (Backward Citations)
US2584905A
Cited
US2710267A
Cited
US2689858A
Cited
US2768909A
Cited
US3094436A
Cited
US3460956A
Cited
US3640093A
Cited
US3811918A
Cited
US3791808A
Cited
US3941719A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-29 | 1986-05-31 | 1986-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-29 | 1990-05-31 | 1990-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-29 | 1994-05-31 | 1994-11-30 | $7700.00 | Window Closed / Lapsed |