Multipurpose copper alloys and processing therefor with moderate conductivity and high strength
Assignee: Olin Corp
•
Filing: 1985-12-30
•
Granted: 1988-03-01
•
Expires: 2005-12-30
Abstract
Abstract A multipurpose copper base alloy having an improved combination of ultimate tensile strength and electrical conductivity. The alloy can be tailored for applications such as in connectors or leadframes by processing. The alloy may be processed to provide improved bend formability at some sacrifice in strength. The alloy in the stabilized condition shows surprising improvement in stress relaxation resistance. The alloy comprises a Cu-Ni-Si alloy to which about 0.05 to about 0.45% by weight magnesium is added.
Inventors
- 👤 Ronald N. Caron
- 👤 John F. Breedis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:52
CPC Classifications
C; C22; C22C; C22C9/00; C22C9/06; H; H10; H10W; H10W70/00; H10W70/40; H10W70/456
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
128 words
A process for manufacturing a copper base alloy having an improved combination of strength and conductivity, said process comprising: (a) providing a copper base alloy consisting essentially of from about 2 to about 4.8% by weight nickel, from about 0.2 to about 1.4% by weight silicon, from about 0.05 to about 0.45% by weight magnesium and the balance copper; (b) casting said alloy into a desired shape; (c) hot working said alloy from a temperature of from about 750° to about 950° C.; (d) cold reducing said alloy at least about 30%; (e) aging said alloy at a temperature of from about 350° to 700° C. for a period of up to about 8 hours; and (f) finally reducing said alloy from about 10 to about 90% reduction.
Claim 2
Dependent Claim
128 words
A process for manufacturing a copper base alloy having an improved combination of strength and conductivity, said process comprising: (a) providing a copper base alloy consisting essentially of from about 2 to about 4.8% by weight nickel, from about 0.2 to about 1.4% by weight silicon, from about 0.05 to about 0.45% by weight magnesium and the balance copper; (b) casting said alloy into a desired shape; (c) hot working said alloy from a temperature of from about 750° to about 950° C.; (d) cold reducing said alloy at least about 30%; (e) aging said alloy at a temperature of from about 350° to 700° C. for a period of up to about 8 hours; and (f) finally reducing said alloy from about 10 to about 90% reduction.
Claim 3
Dependent Claim
57 words
A process as in claim 1 wherein steps (d) and (e) are repeated with the proviso that the aging temperature is lower than the aging temperature in the first sequence of steps (d) and (e) and is within a range from about 350° to about 490° C. for a period of about 1/2 to about 8 hours.
Claim 4
Dependent Claim
77 words
A process as in claim 1 wherein in place of step (e), said alloy is: (h) annealed at a temperature of from about 750° to about 950° C. for a period of from about 30 seconds to about 8 hours, followed by quenching; (i) cold worked at least about 10%; and (j) overaged by annealing at a temperature of from about 500° to about 700° C. for a period of from about 1/2 to about 8 hours.
Claim 5
Dependent Claim
26 words
A process as in claim 3 further including the step (g) stabilization annealing said alloy at a temperature of from about 200° to about 345° C.
Claim 6
Dependent Claim
13 words
A process as in claim 3 wherein steps (h) and (i) are repeated.
Claim 7
Dependent Claim
39 words
A process as in claim 3 wherein in place of step (j), said alloy is (k) aged at a temperature of from about 350° to less than about 500° C. for a period from about 1/2 to 8 hours.
Claim 8
Dependent Claim
26 words
A process as in claim 6 further including the step (g) stabilization annealing said alloy at a temperature of from about 200° to about 345° C.
Claim 9
Dependent Claim
13 words
A process as in claim 6 wherein steps (h) and (i) are repeated.
Claim 10
Dependent Claim
46 words
A process as in claim 1 wherein before step (c) or before step (d) or before step (e), said alloy is subjected to an homogenization anneal at a temperature of from about 550° to about 700° C. for a period from about 1 to 8 hours.
Claim 11
Dependent Claim
46 words
A process as in claim 3 wherein before step (c) or before step (d) or before step (e), said alloy is subjected to an homogenization anneal at a temperature of from about 550° to about 700° C. for a period from about 1 to 8 hours.
Claim 12
Dependent Claim
46 words
A process as in claim 6 wherein before step (c) or before step (d) or before step (e), said alloy is subjected to an homogenization anneal at a temperature of from about 550° to about 700° C. for a period from about 1 to 8 hours.
Claim 13
Dependent Claim
22 words
A process as in claim 4 wherein prior to or after step (g), said alloy is formed into an electrical connector member.
Claim 14
Dependent Claim
22 words
A process as in claim 7 wherein prior to or after step (g), said alloy is formed into an electrical connector member.
Claim 15
Dependent Claim
17 words
A process as in claim 3 wherein following step (f), said alloy is formed into a leadframe.
Claim 16
Dependent Claim
17 words
A process as in claim 6 wherein following step (f), said alloy is formed into a leadframe.
Claim 17
Dependent Claim
137 words
A process for manufacturing a copper base alloy having an improved combination of strength, bend formability and conductivity, said process comprising: (a) providing a copper base alloy consisting essentially of from about 0.05 to about 5.0% by weight nickel, from about 0.01 to about 2.0% by weight silicon, up to about 1% by weight magnesium and the balance copper; (b) casting said alloy into a desired shape; (c) solutionizing said alloy at a temperature of from about 750° to about 950° C. for a period of from about 30 seconds to about 8 hours; (d) cold reducing said alloy at least about 30%; and (e) overaging said alloy to provide improved bend formability by annealing at a temperature of from about 500° to about 700° C. for a period of from about 1/2 to about 8 hours.
Claim 18
Dependent Claim
137 words
A process for manufacturing a copper base alloy having an improved combination of strength, bend formability and conductivity, said process comprising: (a) providing a copper base alloy consisting essentially of from about 0.05 to about 5.0% by weight nickel, from about 0.01 to about 2.0% by weight silicon, up to about 1% by weight magnesium and the balance copper; (b) casting said alloy into a desired shape; (c) solutionizing said alloy at a temperature of from about 750° to about 950° C. for a period of from about 30 seconds to about 8 hours; (d) cold reducing said alloy at least about 30%; and (e) overaging said alloy to provide improved bend formability by annealing at a temperature of from about 500° to about 700° C. for a period of from about 1/2 to about 8 hours.
Claim 19
Dependent Claim
26 words
A process as in claim 16 further including the step (h) stabilization annealing said alloy at a temperature of from about 200° to about 345° C.
Claim 20
Dependent Claim
29 words
A process as in claim 16 wherein said solutionizing step (c) comprises hot working said alloy from said solutionizing temperature in a plurality of passes to a desired gauge.
Claim 21
Dependent Claim
22 words
A process as in claim 17 wherein prior to or after step (h), said alloy is formed into an electrical connector member.
Claim 22
Dependent Claim
17 words
A process as in claim 16 wherein following step (e), said alloy is formed into a leadframe.
Claim 23
Dependent Claim
15 words
A copper base alloy in the overaged condition processed by the process of claim 16.
Claim 24
Dependent Claim
37 words
A process as in claim 1 wherein said aging in step (e) is carried out at a temperature of from about 350° to about 500° C. for a period of from about 1/2 to about 8 hours.
Claim 25
Dependent Claim
26 words
A process as in claim 22 wherein in step (c) said hot working comprises hot rolling and wherein following said hot working said alloy is quenched.
Claim 26
Dependent Claim
42 words
A process as in claim 1 wherein step (e) comprises overaging said alloy to improve its bend formability by annealing at a temperature of from about 500° to about 700° C. for a period of from about 1/2 to about 8 hours.
Claim 27
Dependent Claim
26 words
A process as in claim 23 further including the step (g) stabilization annealing said alloy at a temperature of from about 200° to about 345° C.
Claim 28
Dependent Claim
22 words
A process as in claim 25 wherein prior to or after step (g), said alloy is formed into an electrical connector member.
Claim 29
Dependent Claim
52 words
A process as in claim 16 wherein intermediate said steps (d) and (e) said alloy is (f) annealed at a temperature of from about 750° to about 950° C. for a period of from about 30 seconds to about 8 hours, followed by quenching; and (g) cold worked at least about 10%.
Claim 30
Dependent Claim
22 words
A process as in claim 16 wherein following step (e) said alloy is cold reduced from about 10 to about 90% reduction.
Claim 31
Dependent Claim
23 words
A process as in claim 27 wherein following step (e) said alloy is finally cold reduced from about 10 to about 90% reduction.
Claim 32
Dependent Claim
17 words
A process as in claim 29 wherein following step (e), said alloy is formed into a leadframe.
Claim 33
Dependent Claim
13 words
A process as in claim 27 wherein steps (f) and (g) are repeated.
Claim 34
Dependent Claim
46 words
A process as in claim 29 wherein before step (c) or before step (d) or before step (f), said alloy is subjected to an homogenization anneal at a temperature of from about 550° to about 700° C. for a period from about 1 to 8 hours.
References Cited (Backward Citations)
US1658186A
Cited
US1778668A
Cited
US1988153A
Cited
US2069906A
Cited
US2241815A
Cited
US2137282A
Cited
US2157934A
Cited
GB522482A
Cited
US2185958A
Cited
US2851353A
Cited
US3046166A
Cited
US3072508A
Cited
US3841921A
Cited
FR2221524A1
Cited
US3855012A
Cited
US3882712A
Cited
US3929516A
Cited
US4047978A
Cited
US4025367A
Cited
US4191601A
Cited
US4260435A
Cited
US4233069A
Cited
US4233068A
Cited
US4366117A
Cited
US4395295A
Cited
US4466939A
Cited
US4434016A
Cited
JPS6045698A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-01 | 1991-08-31 | 1992-03-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-01 | 1995-08-31 | 1996-03-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-01 | 1999-08-31 | 2000-03-01 | $7700.00 | Window Closed / Lapsed |