Copper-nickel-silicon-chromium alloy having improved electrical conductivity
Assignee: Ampco Pittsburgh Corp
•
Filing: 1979-02-12
•
Granted: 1980-03-04
•
Expires: 1999-02-12
Abstract
Abstract A copper-nickel-silicon-chromium alloy having a high hardness and improved electrical conductivity. The alloy is composed by weight of 2.0% to 3.0% nickel, 0.4% to 0.8% silicon, 0.1% to 0.5% chromium, and the balance copper. The silicon is used in excess of the stoichiometric relationship with nickel to provide excess silicon, and the chromium is used in excess of the stoichiometric relationship with the excess silicon. The alloy is heat treated by initially heating the alloy to a temperature in the range of 1600 DEG F. to 1800 DEG F. and is thereafter quenched. The quenched alloy is then subjected to a two-step aging treatment in which the alloy is initially aged at a temperature of 900 DEG F. to 1100 DEG F. to precipitate the metal silicides and develop a hardness in excess of 90 Rockwell B (185 Brinell) and subsequently is subjected to a second aging at a temperature in the range of 750 DEG F. to 900 DEG F., which serves to precipitate the excess chromium from solution and increase the electrical conductivity to a value greater than 45%.
Inventors
- 👤 Walter W. Edens
- 👤 Quentin F. Ingerson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 11:55
CPC Classifications
C; C21; C21D; C21D9/00; B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J27/00; B01J27/06; B01J27/08; C21D1/00; C22; C22F; C22F1/00; C22F1/08; B23; B23K; B23K35/00; B23K35/22; B23K35/222
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
165 words
A method of heat treating a copper base alloy, consisting essentially by weight of 2.0% to 3.0% of a metal selected from the group consisting of nickel and cobalt and mixtures thereof, silicon in an amount slightly in excess of the stoichiometric amount necessary to form silicides of said metal, chromium in an amount in excess of the stoichiometric amount required to form chromium silicide with the excess silicon not combined as said metal silicides and the balance copper, comprising the steps of heating the alloy to a solution temperature, quenching the alloy, aging the alloy at a first aging temperature in the range of 900° F. to 1100° F. for a period of time sufficient to precipitate silicides, and aging the alloy at a second aging temperature in the range of 750° F. to 900° F. for a period of time sufficient to precipitate the excess chromium from solution and increase the electrical conductivity of the alloy to a value in excess of 45%.
Claim 2
Independent Claim
165 words
A method of heat treating a copper base alloy, consisting essentially by weight of 2.0% to 3.0% of a metal selected from the group consisting of nickel and cobalt and mixtures thereof, silicon in an amount slightly in excess of the stoichiometric amount necessary to form silicides of said metal, chromium in an amount in excess of the stoichiometric amount required to form chromium silicide with the excess silicon not combined as said metal silicides and the balance copper, comprising the steps of heating the alloy to a solution temperature, quenching the alloy, aging the alloy at a first aging temperature in the range of 900° F. to 1100° F. for a period of time sufficient to precipitate silicides, and aging the alloy at a second aging temperature in the range of 750° F. to 900° F. for a period of time sufficient to precipitate the excess chromium from solution and increase the electrical conductivity of the alloy to a value in excess of 45%.
Claim 3
Dependent Claim
30 words
The method of claim 1, wherein the alloy is held at the first aging temperature for a period of time sufficient to develop a hardness greater than 90 Rockwell B.
Claim 4
Dependent Claim
67 words
The method of claim 1, wherein the solution temperature is in the range of 1600° F. to 1800° F. and the alloy is held at said solution temperature for a period of 1 to 3 hours, is held at said first aging temperature for a period of 1 to 5 hours and is held at the second aging temperature for a period of 1 to 5 hours.
Claim 5
Dependent Claim
34 words
The method of claim 1, and including the step of cooling the alloy from the first aging temperature to a temperature below 750° F. and then reheating the alloy to said second aging temperature.
Claim 6
Dependent Claim
24 words
The method of claim 1, and including the step of furnace cooling the alloy from said first aging temperature to said second aging temperature.
Claim 7
Independent Claim
223 words
A method of heat treating a precipitation-hardenable cooper base alloy containing by weight from 2.0% to 3.0% of a metal selected from the group consisting of nickel and cobalt and mixtures thereof, 0.4% to 0.8% silicon, 0.1% to 0.5% chromium, and the balance copper, said silicon being present in an amount in excess of the stoichiometric amount necessary to form silicides of said metal, and said chromium being present in excess of the stoichiometric amount required to form chromium silicide with the excess silicon not combined as said metal silicides, comprising the steps of heating the alloy to a temperature in the range of 1600° F. to 1800° F. for a period of time to ensure a substantially solid solution of the alloying elements in the copper matrix, quenching the alloy, aging the alloy at a first aging temperature in the range of 900° F. to 1100° F. for a period of time sufficient to precipitate silicides and attain a room temperature hardness of greater than 90 Rockwell B, and aging the alloy at a second aging temperature of 750° F. to 900° F. for a period of time sufficient to precipitate the chromium in excess of that combined as chromium silicides and thereby increase the electrical conductivity of the alloy to a value in excess of 45% after cooling to room temperature.
Claim 8
Independent Claim
223 words
A method of heat treating a precipitation-hardenable cooper base alloy containing by weight from 2.0% to 3.0% of a metal selected from the group consisting of nickel and cobalt and mixtures thereof, 0.4% to 0.8% silicon, 0.1% to 0.5% chromium, and the balance copper, said silicon being present in an amount in excess of the stoichiometric amount necessary to form silicides of said metal, and said chromium being present in excess of the stoichiometric amount required to form chromium silicide with the excess silicon not combined as said metal silicides, comprising the steps of heating the alloy to a temperature in the range of 1600° F. to 1800° F. for a period of time to ensure a substantially solid solution of the alloying elements in the copper matrix, quenching the alloy, aging the alloy at a first aging temperature in the range of 900° F. to 1100° F. for a period of time sufficient to precipitate silicides and attain a room temperature hardness of greater than 90 Rockwell B, and aging the alloy at a second aging temperature of 750° F. to 900° F. for a period of time sufficient to precipitate the chromium in excess of that combined as chromium silicides and thereby increase the electrical conductivity of the alloy to a value in excess of 45% after cooling to room temperature.
Claim 9
Dependent Claim
32 words
The method of claim 6, and including the step of cooling the alloy from said first aging temperature to substantially room temperature and thereafter reheating the alloy to said second aging temperature.
Claim 10
Dependent Claim
24 words
The method of claim 6, and including the step of furnace cooling the alloy from said first aging temperature to said second aging temperature.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-04 | 1983-09-03 | 1984-03-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-04 | 1987-09-03 | 1988-03-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-04 | 1991-09-03 | 1992-03-04 | $7700.00 | Window Closed / Lapsed |