Copper-nickel-silicon-chromium alloy having improved electrical conductivity

Assignee: Ampco Pittsburgh Corp
•
Filing: 1979-07-02
•
Granted: 1981-04-07
•
Expires: 1999-07-02
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A copper-nickel-silicon-chromium alloy having a high hardness and improved electrical conductivity. The alloy is composed by weight of 2.0% to 3.0% nickel, 0.4% to 0.8% silicon, 0.1% to 0.5% chromium, and the balance copper. The silicon is used in excess of the stoichiometric relationship with nickel to provide excess silicon, and the chromium is used in excess of the stoichiometric relationship with the excess silicon. The alloy is heat treated by initially heating the alloy to a temperature in the range of 1600 DEG F. to 1800 DEG F. and is thereafter quenched. The quenched alloy is then subjected to a two-step aging treatment in which the alloy is initially aged at a temperature of 900 DEG F. to 1100 DEG F. to precipitate the metal silicides and develop a hardness in excess of 90 Rockwell B (185 Brinell) and subsequently is subjected to a second aging at a temperature in the range of 750 DEG F. to 900 DEG F., which serves to precipitate the excess chromium from solution and increase the electrical conductivity to a value greater than 45%.

Inventors

  • 👤 Walter W. Edens
  • 👤 Quentin F. Ingerson

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-26 12:48
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/222; C; C22; C22C; C22C9/00; C22C9/06; C22F; C22F1/00; C22F1/08

Claims Analysis

Total Claims: 3
Claim 1
Independent Claim 149 words
A precipitation hardened copper base alloy, consisting essentially by weight of 2.0% to 3.0% of a metal selected from the group consisting of nickel, cobalt, and mixtures thereof, 0.4% to 0.8% silicon, 0.1% to 0.5% chromium, and the balance copper, said silicon being present in an amount in excess of the stoichiometric amount necessary to form silicides of said metal, and said chromium being present in excess of the stoichiometric amount required to form chromium silicide with the excess silicon not combined as said metal silicides, said alloy having a metallographic structure composed of a copper matrix containing precipitated silicides of said metal, precipitated chromium silicide and precipitated particles of elemental chromium, said matrix being substantially completely free of silicon and said metal and chromium in solid solution, said alloy having an electrical conductivity in excess of 45% of pure copper and a hardness greater than 90 Rockwell B.
Claim 2
Dependent Claim 149 words
A precipitation hardened copper base alloy, consisting essentially by weight of 2.0% to 3.0% of a metal selected from the group consisting of nickel, cobalt, and mixtures thereof, 0.4% to 0.8% silicon, 0.1% to 0.5% chromium, and the balance copper, said silicon being present in an amount in excess of the stoichiometric amount necessary to form silicides of said metal, and said chromium being present in excess of the stoichiometric amount required to form chromium silicide with the excess silicon not combined as said metal silicides, said alloy having a metallographic structure composed of a copper matrix containing precipitated silicides of said metal, precipitated chromium silicide and precipitated particles of elemental chromium, said matrix being substantially completely free of silicon and said metal and chromium in solid solution, said alloy having an electrical conductivity in excess of 45% of pure copper and a hardness greater than 90 Rockwell B.
Claim 3
Dependent Claim 60 words
The alloy of claim 1, wherein the metal is nickel and the silicon is present in an amount slightly in excess of the weight ratio of 1 part silicon to 4.18 parts of nickel, and said chromium is present in an amount in excess of the weight ratio of 3.18 parts of chromium to 1 part of said excess silicon.

References Cited (Backward Citations)

US1658186A Cited
US1778668A Cited
US1763303A Cited
US3072508A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1984-04-06 1984-10-06 1985-04-07 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1988-04-06 1988-10-06 1989-04-07 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1992-04-06 1992-10-06 1993-04-07 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag