US4672740A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Beam annealed silicide film on semiconductor substrate
Assignee: Fujitsu Ltd
•
Filing: 1984-08-28
•
Granted: 1987-06-16
•
Expires: 2004-08-28
Abstract
Abstract A semiconductor device having contact windows between an aluminum or aluminum-alloy wiring layer and a diffused region in a semiconductor substrate, in which the contacts are formed by using a barrier film on a refractory metal silicide between the wiring layer and the diffused region. The barrier film comprising the refactory metal and silicon is beam annealed for a short period of time such as, 10 seconds or less, so that adverse effects of the barrier film can be prevented while an excellent electrical or ohmic contact between the wiring layer and the diffused layer can be obtained.
Inventors
- 👤 Kazunari Shirai
- 👤 Hajime Kamioka
- 👤 Shigeyoshi Koike
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:12
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; Y; Y10; Y10S; Y10S148/00; Y10S148/019; Y10S148/09
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
179 words
A process for fabricating a semiconductor device having a doped region containing dopants adjacent a surface of a semiconductor substrate, comprising the steps of: (a) forming an insulating layer on the surface of the semiconductor substrate with a contact window above a portion of the doped region; (b) depositing a film comprising a refractory metal and silicon on the insulating layer and through the contact window to contact the doped region of the semiconductor substrate and patterning the film; (c) beam annealing the film comprising the refractory metal and silicon for a period of time to ensure silicidation of said film into a resultant refractory metal silicide film and to stabilize the contact of the film with the doped region of the semiconductor substrate while avoiding substantial rediffusion of the dopants in the doped region; and (d) depositing a wiring layer of one of aluminum and an aluminum alloy onto the resultant refractory metal silicide film to form an electrical or ohmic contact between the wiring layer and the doped region in the semiconductor substrate through the contact window.
Claim 2
Dependent Claim
179 words
A process for fabricating a semiconductor device having a doped region containing dopants adjacent a surface of a semiconductor substrate, comprising the steps of: (a) forming an insulating layer on the surface of the semiconductor substrate with a contact window above a portion of the doped region; (b) depositing a film comprising a refractory metal and silicon on the insulating layer and through the contact window to contact the doped region of the semiconductor substrate and patterning the film; (c) beam annealing the film comprising the refractory metal and silicon for a period of time to ensure silicidation of said film into a resultant refractory metal silicide film and to stabilize the contact of the film with the doped region of the semiconductor substrate while avoiding substantial rediffusion of the dopants in the doped region; and (d) depositing a wiring layer of one of aluminum and an aluminum alloy onto the resultant refractory metal silicide film to form an electrical or ohmic contact between the wiring layer and the doped region in the semiconductor substrate through the contact window.
Claim 3
Dependent Claim
12 words
A process according to claim 1, wherein the semiconductor substrate is silicon.
Claim 4
Dependent Claim
17 words
A process according to claim 1, wherein the semiconductor substrate has n-type conductivity under the contact window.
Claim 5
Dependent Claim
19 words
A process according to claim 1, wherein the semiconductor substrate has an n-type doped region under the contact window.
Claim 6
Dependent Claim
21 words
A process according to claim 1, wherein the contact window has a size smaller than a square measuring 2 μm×2 μm.
Claim 7
Dependent Claim
18 words
A process according to claim 1, wherein the refractory metal is selected from molybdenum, tungsten, tantalum and titanium.
Claim 8
Dependent Claim
12 words
A process according to claim 6, wherein the refractory metal is molybdenum.
Claim 9
Dependent Claim
33 words
A process according to claim 1, wherein said depositing of the film comprising the refractory metal and silicon in step (d) comprises one of co-sputtering and hotpress-target-sputtering of the refractory metal and silicon.
Claim 10
Dependent Claim
26 words
A process according to claim 1, wherein the film comprising the refractory metal and silicon is deposited to a thickness of 10 nm to 50 nm.
Claim 11
Dependent Claim
13 words
A process according to claim 9, wherein the thickness is approximately 30 nm.
Claim 12
Dependent Claim
24 words
A process according to claim 1, wherein said beam annealing in step (c) comprises one of lamp annealing, laser annealing, and electron beam annealing.
Claim 13
Dependent Claim
17 words
A process according to claim 11, wherein said beam annealing in step (c) comprises halogen lamp annealing.
Claim 14
Dependent Claim
43 words
A process according to claim 1, wherein said beam annealing of the film comprising the refractory metal and silicon is carried out at a temperature of 700° C. to 1100° C. over a time period of less than or equal to one minute.
Claim 15
Dependent Claim
18 words
A process according to claim 13, wherein the time period is less than or equal to 20 seconds.
Claim 16
Dependent Claim
18 words
A process according to claim 14, wherein the time period is less than or equal to 10 seconds.
Claim 17
Dependent Claim
18 words
A process according to claim 15, wherein the time period is less than or equal to 5 seconds.
Claim 18
Dependent Claim
35 words
A process according to claim 13, wherein the refractory metal is selected from the group of molybdenum, tungsten and tantalum and said beam annealing is performed at a temperature of 900° C. to 1050° C.
Claim 19
Dependent Claim
27 words
A process according to claim 13, wherein the refractory metal is titanium and said beam annealing is performed at a temperature of 800° C. to 1000° C.
Claim 20
Dependent Claim
18 words
A process according to claim 7, wherein the resultant refractory metal silicide film is essentially MoSi 2 .
Claim 21
Dependent Claim
16 words
A process according to claim 1, wherein the aluminum alloy is one of aluminum-silicon and aluminum-copper.
Claim 22
Dependent Claim
13 words
A process according to claim 20, wherein the aluminum alloy is 1%-silicon aluminum.
Claim 23
Dependent Claim
32 words
A process according to claim 1, further comprising the step of patterning the layer of one of aluminum and aluminum-alloy and the resultant refractory metal silicide film to obtain a wiring pattern.
Claim 24
Dependent Claim
104 words
A process for fabricating a semiconductor device having a contact window through an insulating layer to a doped region of dopants in a semiconductor substrate, comprising the steps of: (a) depositing a film of a refractory metal and silicon on the insulating layer and through the contact window to contact the doped region of the semiconductor substrate; and (b) annealing the film using beam annealing for a period of time sufficient to ensure silicidation of the film and to stabilize the contact of the film with the doped region of the semiconductor substrate while avoiding substantial rediffusion of the dopants in the doped region.
Claim 25
Dependent Claim
104 words
A process for fabricating a semiconductor device having a contact window through an insulating layer to a doped region of dopants in a semiconductor substrate, comprising the steps of: (a) depositing a film of a refractory metal and silicon on the insulating layer and through the contact window to contact the doped region of the semiconductor substrate; and (b) annealing the film using beam annealing for a period of time sufficient to ensure silicidation of the film and to stabilize the contact of the film with the doped region of the semiconductor substrate while avoiding substantial rediffusion of the dopants in the doped region.
Claim 26
Dependent Claim
35 words
A process according to claim 23, wherein said beam annealing in step (b) is performed at a temperature between 700° C. and 1100° C. and the period of time is less than approximately one minute.
References Cited (Backward Citations)
US4141022A
Cited
US4385433A
Cited
EP0054259B1
Cited
US4392299A
Cited
EP0068897A2
Cited
EP0071029A2
Cited
US4510670A
Cited
US4485550A
Cited
US4551907A
Cited
US4505027A
Cited
US4569122A
Cited
US4577396A
Cited
JPS61145A
Cited
JPS63819A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-15 | 1990-12-15 | 1991-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-15 | 1994-12-15 | 1995-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-15 | 1998-12-15 | 1999-06-16 | $7700.00 | Window Closed / Lapsed |