Process for fabricating a semiconductor device
Assignee: Fujitsu Ltd
•
Filing: 1983-11-23
•
Granted: 1985-11-12
•
Expires: 2003-11-23
Abstract
Abstract A metal silicide interconnection technique selectively forming a metal silicide layer on a silicon layer followed by heat treating the layers so that a surface silicon dioxide layer is formed and the metal silicide layer is forced down and is buried under the silicon dioxide layer. This silicon dioxide layer has an even top surface.
Inventors
- 👤 Ryoichi Mukai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:13
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/064; H10W20/066; H10D; H10D64/00; H10D64/01; H10D64/011; H10P; H10P95/00
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
111 words
A process for fabricating a semiconductor device, comprising the steps of: forming a silicon layer on a substrate; forming a metal silicide layer on only a portion of the surface of the silicon layer, with the remaining portion of said surface of the silicon layer being uncovered by the metal silicide layer; and oxidizing both the metal silicide layer and said portion of the silicon layer which is not covered by the metal silicide layer, in a direction from the top surface to the inside thereof; wherein the silicon layer is entirely converted to a silicon dioxide layer and the metal silicide layer sinks in said silicon layer to said substrate.
Claim 2
Dependent Claim
111 words
A process for fabricating a semiconductor device, comprising the steps of: forming a silicon layer on a substrate; forming a metal silicide layer on only a portion of the surface of the silicon layer, with the remaining portion of said surface of the silicon layer being uncovered by the metal silicide layer; and oxidizing both the metal silicide layer and said portion of the silicon layer which is not covered by the metal silicide layer, in a direction from the top surface to the inside thereof; wherein the silicon layer is entirely converted to a silicon dioxide layer and the metal silicide layer sinks in said silicon layer to said substrate.
Claim 3
Dependent Claim
28 words
A process according to claim 1, wherein the metal silicide layer is selected from a group consisting of MoSi 2 , WSi 2 , and TaSi 2 .
Claim 4
Dependent Claim
14 words
A process according to claim 1, wherein the metal silicide layer is of PtSi.
Claim 5
Dependent Claim
22 words
A process according to claim 1, wherein the metal silicide layer is formed in a thickness of 240 nm to 300 nm.
Claim 6
Dependent Claim
21 words
A process according to claim 1, wherein the silicon layer is formed in a thickness of 300 nm to 400 nm.
Claim 7
Dependent Claim
72 words
A process according to claim 1, wherein, after the step of forming a metal silicide layer, an additional step is inserted, the additional step being that of etching the surface of the silicon layer except where the metal silicide layer covers the respective portion of the silicon layer, so that, after the oxidation step, the resultant layer consisting of the silicon dioxide layer and the metal silicide layer has a uniform thickness.
Claim 8
Dependent Claim
33 words
A process according to claim 1, wherein the silicon layer is formed with a sufficient thickness and is subsequently etched to a thickness of 40 nm to 50 nm before said oxidation step.
Claim 9
Dependent Claim
47 words
A process according to claim 1, wherein the step of forming said metal silicide layer comprises selectively forming a layer of the respective metal on said silicon layer and then heat treating said metal and silicon layers to form said metal silicide layer on the silicon layer.
Claim 10
Dependent Claim
53 words
A process according to claim 1, wherein the step of forming said metal silicide layer comprises forming a layer of the respective metal over said silicon layer, selectively exposing said metal and silicon layer to a high energy beam to form said metal silicide layer, and removing the remainder of the metal layer.
Claim 11
Dependent Claim
17 words
The process of claim 1, wherein said oxidation step comprises oxidation in a wet oxygen gas atmosphere.
Claim 12
Dependent Claim
48 words
The process of claim 1, wherein said oxidization step and the thickness of said layers are controlled such that all of said silicon layer is oxidized, except for the silicon of the sunken metal silicide layer, and said metal silicide layer is located beneath said silicon dioxide layer.
Claim 13
Dependent Claim
48 words
The process of claim 6, wherein said oxidation step and the thickness of said layers are controlled such that all of said silicon layer is oxidized, except for the silicon of the sunken metal silicide layer, and said metal silicide layer is located beneath said silicon dioxide layer.
Claim 14
Dependent Claim
49 words
The process of claim 7, said oxidation step being performed and said layers being formed with respective thicknesses such that all of said silicon layer is oxidized, except for the silicon of the sunken metal silicide layer, and said metal silicide layer is located beneath said silicon dioxide layer.
Claim 15
Dependent Claim
13 words
The process of claim 9, said high energy beam being a laser beam.
Claim 16
Dependent Claim
54 words
A process according to claim 1, wherein said metal silicide layer is formed by forming a layer of said metal on said silicon layer, and then reacting said metal with said silicon of said silicon layer only in the respective portion of the silicon layer where said metal silicide layer is to be formed.
Claim 17
Dependent Claim
43 words
A process according to claim 15, wherein said metal layer is patterned to remain only on the respective portion of said silicon layer where said metal silicide layer is to be formed, and heat treatment is then effected to form said metal silicide.
Claim 18
Dependent Claim
51 words
A process according to claim 15, wherein said metal layer is exposed to a high energy beam only on said portion of said silicon layer where said metal silicide layer is to be formed, thus forming said metal silicide layer, and the remaining metal of said metal layer is then etched.
Claim 19
Dependent Claim
52 words
A process according to claim 15, wherein after said metal silicide layer is formed, the uncovered surface of said silicon layer is selectively etched to a thickness such that after said oxidation the resultant layer of said silicon dioxide layer and said metal silicide layer on said substrate has a uniform thickness.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-11 | 1989-05-13 | 1989-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-11 | 1993-05-13 | 1993-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-11 | 1997-05-13 | 1997-11-12 | $7700.00 | Window Closed / Lapsed |