US4555301A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Formation of heterostructures by pulsed melting of precursor material
Assignee: Nokia Bell Labs
•
Filing: 1983-06-20
•
Granted: 1985-11-26
•
Expires: 2003-06-20
Abstract
Abstract A method for forming heterostructures comprising multiconstituent epitaxial material, on a substrate comprises formation of a layer of "precursor" material on the substrate, and momentarily melting the precursor material by pulsed irradiation. The precursor material has the same major chemical constituents as the multiconstituent material to be formed, albeit not necessarily in the same proportions. In at least some systems (e.g., nickel or cobalt silicides on Si), solid state annealing of the re-solidified material often improves substantially the quality of the epitaxial material formed, resulting in substantially defect-free, substantially monocrystalline, material. An exemplary application of the inventive method is the formation of single crystal epitaxial NiSi 2 on Si(100).
Inventors
- 👤 John M. Gibson
- 👤 Dale C. Jacobson
- 👤 John M. Poate
- 👤 Raymond T. Tung
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:20
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; C; C30; C30B; C30B11/00; C30B13/00; C30B13/16; C30B13/22; C30B13/24; C30B29/00; C30B29/10; C30B29/60; Y; Y10; Y10S; Y10S117/00; Y10S117/903; Y10S117/904; Y10S117/905; Y10S148/00; Y10S148/14
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
208 words
Method of producing a heterostructure comprising a layer of multiconstituent first material on a single crystal second material substrate, the first material comprising at least a first major constituent and a second major constituent, chemical elements A and B being the first and second major constituent, respectively, the chemical composition of the substrate differing from the chemical composition of the first material, the first material selected from the group consisting of the metals, the semiconductors, and the insulators, the second material selected from the group consisting of Si, Ge, the III-V compound semiconductors, and the II-VI compound semiconductors, the method comprising (a) providing the single crystal second material substrate; (b) forming a layer of precursor material on at least a part of the substrate, the precursor material having the same major constituents as the first material, (c) melting momentarily at least a part of the precursor material by causing pulsed radiation to be incident on the precursor material, the pulsed radiation being electromagnetic radiation, or electron beam radiation, or ion beam radiation, the incident pulsed radiation adjusted to melt the part of the precursor material to at least the substrate/precursor material interface, and (d) permitting the melted precursor material to re-solidify, the re-solidified material being said first material.
Claim 2
Dependent Claim
208 words
Method of producing a heterostructure comprising a layer of multiconstituent first material on a single crystal second material substrate, the first material comprising at least a first major constituent and a second major constituent, chemical elements A and B being the first and second major constituent, respectively, the chemical composition of the substrate differing from the chemical composition of the first material, the first material selected from the group consisting of the metals, the semiconductors, and the insulators, the second material selected from the group consisting of Si, Ge, the III-V compound semiconductors, and the II-VI compound semiconductors, the method comprising (a) providing the single crystal second material substrate; (b) forming a layer of precursor material on at least a part of the substrate, the precursor material having the same major constituents as the first material, (c) melting momentarily at least a part of the precursor material by causing pulsed radiation to be incident on the precursor material, the pulsed radiation being electromagnetic radiation, or electron beam radiation, or ion beam radiation, the incident pulsed radiation adjusted to melt the part of the precursor material to at least the substrate/precursor material interface, and (d) permitting the melted precursor material to re-solidify, the re-solidified material being said first material.
Claim 3
Dependent Claim
16 words
Method of claim 1, wherein at least part of the first material is epitaxial crystalline material.
Claim 4
Dependent Claim
13 words
Method of claim 1, wherein the pulse length is at most 1 μsec.
Claim 5
Dependent Claim
14 words
Method of claim 1, wherein the layer of first material is a patterned layer.
Claim 6
Dependent Claim
32 words
Method of claim 1, wherein the concentration of no major constituent of the precursor material differs by more than 50 percent from the concentration of that major constituent in the first material.
Claim 7
Dependent Claim
25 words
Method of claim 1, wherein the first material substantially consists of material selected from the group consisting of the metal silicides and the metal germanates.
Claim 8
Dependent Claim
22 words
Method of claim 6, wherein the second material consists substantially of silicon, and the first material consists substantially of a metal silicide.
Claim 9
Dependent Claim
42 words
Method of claim 7, wherein the metal silicide has a composition MSi x , with M being an element selected from the group consisting of Ni, Co, Pd, Pt, Cr, W, Ti, Zr, Hf, V, Nb, Ta, Fe, Mg, Rh, and Mo.
Claim 10
Dependent Claim
17 words
Method of claim 8 wherein the precursor material has an average composition MSi y , with 0<y<x.
Claim 11
Dependent Claim
43 words
Method of claim 9, wherein the precursor material is formed by a process comprising depositing an effective amount of element M on the substrate, and maintaining the substrate at a temperature for a time effective to form the precursor material on the substrate.
Claim 12
Dependent Claim
40 words
Method of claim 8, further comprising maintaining, subsequent to step (c) of claim 1, the substrate at a temperature of at least about 500° C. for a time effective to result in formation of substantially defect-free, substantially monocrystalline, first material.
Claim 13
Dependent Claim
16 words
Method of claim 7, wherein the precursor material is formed by co-deposition of metal and silicon.
Claim 14
Dependent Claim
10 words
Method of claim 1, wherein the radiation is laser radiation.
Claim 15
Dependent Claim
95 words
Method of claim 1, wherein chemical element B is a major constituent of the substrate, the layer of precursor material being formed by a method comprising (i) depositing a layer of third material onto at least a part of the substrate, the third material comprising chemical element A and containing a lower concentration than the precursor material of at least the chemical element B, and (ii) maintaining the substrate at a temperature for a time effective for producing precursor material by transport of chemical element B from the substrate into the layer of third material.
Claim 16
Dependent Claim
166 words
Method for producing a heterostructure comprising a layer of silicide of composition MSi x on a major surface of a single crystal Si substrate, the major surface being substantially parallel to a [111] or a [100] crystal plane, M being a chemical element selected from the group consisting of Ni, Co, Pd, Pt, Cr, W, Ti, Zr, Hf, V, Nb, Ta, Fe, Mg, Rh, and Mo, the method comprising (a) providing the single crystal Si substrate; (b) forming a layer of a precursor material on at least a part of the major surface of the substrate, the precursor material having average composition MSi y , with 0<y≦x, (c) melting momentarily at least a part of the precursor material by causing pulsed laser radiation or pulsed electron radiation to be incident on the precursor material, the incident radiation adjusted to melt the precursor material at least to the substrate/precursor material interface, and (d) permitting the melted precursor material to re-solidify, the re-solidified material being said first material.
Claim 17
Dependent Claim
166 words
Method for producing a heterostructure comprising a layer of silicide of composition MSi x on a major surface of a single crystal Si substrate, the major surface being substantially parallel to a [111] or a [100] crystal plane, M being a chemical element selected from the group consisting of Ni, Co, Pd, Pt, Cr, W, Ti, Zr, Hf, V, Nb, Ta, Fe, Mg, Rh, and Mo, the method comprising (a) providing the single crystal Si substrate; (b) forming a layer of a precursor material on at least a part of the major surface of the substrate, the precursor material having average composition MSi y , with 0<y≦x, (c) melting momentarily at least a part of the precursor material by causing pulsed laser radiation or pulsed electron radiation to be incident on the precursor material, the incident radiation adjusted to melt the precursor material at least to the substrate/precursor material interface, and (d) permitting the melted precursor material to re-solidify, the re-solidified material being said first material.
Claim 18
Dependent Claim
60 words
Method of claim 15, wherein at least some of the metal silicide is epitaxial metal silicide, the pulse length is at most 1 μsec, and the method further comprises maintaining the substrate with the re-solidified material thereon at a temperature of at least 500° C. for a time sufficient to result in formation of substantially defect-free, substantially monocrystalline, metal silicide.
Claim 19
Dependent Claim
64 words
Method of claim 15, wherein the precursor material is formed by a method comprising depositing a layer consisting substantially of element M on the at least part of the major surface, and maintaining the substrate at a temperature for a time effective to result in formation of the precursor material by transport of Si from the substrate into the deposited layer of element M.
References Cited (Backward Citations)
DE1244732B
Cited
DE2053536A1
Cited
US4284467A
Cited
US3928092A
Cited
US4275093A
Cited
US4292091A
Cited
JPS5623781A
Cited
US4249962A
Cited
JPS5658224A
Cited
US4395433A
Cited
US4279688A
Cited
US4318752A
Cited
JPS5723218A
Cited
US4359486A
Cited
US4359485A
Cited
US4477308A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-25 | 1989-05-27 | 1989-11-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-25 | 1993-05-27 | 1993-11-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-25 | 1997-05-27 | 1997-11-26 | $7700.00 | Window Closed / Lapsed |