Process for reducing edge roughness in patterned photoresist
Assignee: Axcelis Technologies Inc
•
Filing: 2002-10-09
•
Granted: 2004-03-23
•
Expires: 2022-10-09
Abstract
Abstract A process for reducing roughness from a surface of a patterned photoresist. The process includes exposing a substrate having the patterned photoresist thereon to a vapor, wherein the vapor penetrates into and/or reacts with the surface of the photoresist. The substrate having the patterned photoresist thereon is then heated to a temperature and for a time sufficient to cause the surface of the photoresist to flow and/or react with the vapor wherein the surface roughness decreases. Optionally, the substrate is exposed to radiation during the process to increase the etch resistance of the photoresist and/or facilitate the reaction of the vapor with the surface of the photoresist.
Inventors
- 👤 John S. Hallock
- 👤 Robert D. Mohondro
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:42
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/26; G03F7/40; G03F7/405; Y; Y10; Y10S; Y10S430/00; Y10S430/143; Y10S430/167; Y10S430/168
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
120 words
A process for reducing roughness from a surface of a patterned chemically amplified photoresist, the process comprising: a) exposing a substrate having patterned chemically amplified photoresist resulting from imaging and developing processing thereon to a vapor, wherein the vapor diffuses into the surface of the patterned photoresist; b) heating the substrate to a temperature and for a time sufficient to cause the surface of the patterned photoresist to flow wherein the surface roughness decreases; c) exposing the patterned photoresist to an activating radiation prior to, simultaneous with or subsequent to exposing the substrate to the vapor to form a compound, wherein the compound is reactive with the vapor; and d) reacting the vapor with the compound to form a polymer.
Claim 2
Dependent Claim
120 words
A process for reducing roughness from a surface of a patterned chemically amplified photoresist, the process comprising: a) exposing a substrate having patterned chemically amplified photoresist resulting from imaging and developing processing thereon to a vapor, wherein the vapor diffuses into the surface of the patterned photoresist; b) heating the substrate to a temperature and for a time sufficient to cause the surface of the patterned photoresist to flow wherein the surface roughness decreases; c) exposing the patterned photoresist to an activating radiation prior to, simultaneous with or subsequent to exposing the substrate to the vapor to form a compound, wherein the compound is reactive with the vapor; and d) reacting the vapor with the compound to form a polymer.
Claim 3
Dependent Claim
24 words
The process according to claim 1 wherein the compound is selected from the group consisting of a free radical, an acid, and a base.
Claim 4
Dependent Claim
39 words
The process according to claim 1 wherein the vapor is generated from a material selected from the group consisting of vinyl ethers, epoxides, acrylonitriles, furans, coumarins, indenes, styrenes, acrylate, aryl halides, halosilanes, alkynes, alkenes, cyclic ethers and sulfur dioxide.
Claim 5
Dependent Claim
43 words
The process according to claim 1 wherein the vapor reacts with the photoresist to increase a glass transition temperature for the photoresist surface relative to a glass transition temperature of bulk photoresist wherein the bulk photoresist is free from exposure to the vapor.
Claim 6
Dependent Claim
11 words
The process according to claim 1 wherein the vapor is 2,3-dihydrofuran.
Claim 7
Dependent Claim
23 words
The process according to claim 1 wherein the radiation that is used to expose the photoresist has a wavelength in the ultraviolet range.
Claim 8
Dependent Claim
23 words
The process according to claim 1 wherein the radiation that is used to expose the photoresist has a wavelength in the x-ray range.
Claim 9
Dependent Claim
17 words
The process according to claim 1 wherein the radiation consists of electrons generated from an electron beam.
Claim 10
Dependent Claim
27 words
The process according to claim 1 wherein the vapor is generated from a liquid with a boiling point less than about 200° C. at standard atmospheric conditions.
Claim 11
Dependent Claim
28 words
The process according to claim 1 wherein the vapor is a monomer selected from the group consisting of indenes, furans, vinyl ethers, epoxides, styrenes, acrylate, alkenes and alkynes.
Claim 12
Dependent Claim
101 words
A process for reducing roughness from a surface of a patterned photoresist, the process comprising: a) exposing a substrate having patterned photoresist resulting from imaging and developing processing thereon to a reactive vapor, wherein the vapor penetrates into the surface of the patterned photoresist; b) heating the substrate to a temperature and for a time sufficient to cause the surface of the patterned photoresist to flow wherein the surface roughness decreases; and c) polymerizing the reactive vapor within the photoresist by exposing the patterned photoresist to an activating energy whereby the vapor reacts in the patterned photoresist to form a compound.
Claim 13
Dependent Claim
101 words
A process for reducing roughness from a surface of a patterned photoresist, the process comprising: a) exposing a substrate having patterned photoresist resulting from imaging and developing processing thereon to a reactive vapor, wherein the vapor penetrates into the surface of the patterned photoresist; b) heating the substrate to a temperature and for a time sufficient to cause the surface of the patterned photoresist to flow wherein the surface roughness decreases; and c) polymerizing the reactive vapor within the photoresist by exposing the patterned photoresist to an activating energy whereby the vapor reacts in the patterned photoresist to form a compound.
Claim 14
Dependent Claim
28 words
The process according to claim 11 wherein the reactive vapor is selected from a material that reacts with a functional group on a polymer in the patterned photoresist.
Claim 15
Dependent Claim
30 words
The process according to claim 11 wherein the reactive vapor is selected from a material that reacts with a free radical in the patterned photoresist to form a nonvolatile compound.
Claim 16
Dependent Claim
26 words
The process according to claim 11 wherein the step of polymerizing the vapor comprises contacting the reactive vapor with an acid generated by the activating energy.
Claim 17
Dependent Claim
25 words
The process according to claim 11 wherein the step of polymerizing the vapor contacting the reactive vapor with a base generated by the activating energy.
Claim 18
Dependent Claim
14 words
The process according to claim 11 wherein the reactive vapor is a vinyl ether.
References Cited (Backward Citations)
US4548688A
Cited
US5173393A
Cited
US6127097A
Cited
US5347040A
Cited
US5487967A
Cited
US6124405A
Cited
US5879856A
Cited
US5858621A
Cited
US6045981A
Cited
US6096484A
Cited
US6280908B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2007-03-23 | 2007-09-22 | 2008-03-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2011-03-23 | 2011-09-22 | 2012-03-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2015-03-23 | 2015-09-22 | 2016-03-23 | $7700.00 | Window Closed / Lapsed |